Search results for: tests

Authors: Md. Jahidul Islam, A. K. M. Rakinul Islam, M. Salamah Meherier

Abstract:

This study investigates the suitability of using plastic, such as polyethylene terephthalate (PET), as a partial replacement of natural coarse and fine aggregates (for example, brick chips and natural sand) to produce lightweight concrete for load bearing structural members. The plastic coarse aggregate (PCA) and plastic fine aggregate (PFA) were produced from melted polyethylene terephthalate (PET) bottles. Tests were conducted using three different water–cement (w/c) ratios, such as 0.42, 0.48, and 0.57, where PCA and PFA were used as 50% replacement of coarse and fine aggregate respectively. Fresh and hardened properties of concrete have been compared for natural aggregate concrete (NAC), PCA concrete (PCC) and PFA concrete (PFC). The compressive strength of concrete at 28 days varied with the water–cement ratio for both the PCC and PFC. Between PCC and PFC, PFA concrete showed the highest compressive strength (23.7 MPa) at 0.42 w/c ratio and also the lowest compressive strength (13.7 MPa) at 0.57 w/c ratio. Significant reduction in concrete density was mostly observed for PCC samples, ranging between 1977–1924 kg/m³. With the increase in water–cement ratio PCC achieved higher workability compare to both NAC and PFC. It was found that both the PCA and PFA contained concrete achieved the required compressive strength to be used for structural purpose as partial replacement of the natural aggregate; but to obtain the desired lower density as lightweight concrete the PCA is most suited.

Keywords: polyethylene terephthalate, plastic aggregate, concrete, fresh and hardened properties

Procedia PDF Downloads 422

Authors: Murast Dicleli, Ali SalemMilani

Abstract:

In this paper, a summary of analytical and experimental studies into the behavior of a new hysteretic damper, designed for seismic protection of structures is presented. The Multi-directional Torsional Hysteretic Damper (MRSD) is a patented invention in which a symmetrical arrangement of identical cylindrical steel cores is so configured as to yield in torsion while the structure experiences planar movements due to earthquake shakings. The new device has certain desirable properties. Notably, it is characterized by a variable and controllable-via-design post-elastic stiffness. The mentioned property is a result of MRSD’s kinematic configuration which produces this geometric hardening, rather than being a secondary large-displacement effect. Additionally, the new system is capable of reaching high force and displacement capacities, shows high levels of damping, and very stable cyclic response. The device has gone through many stages of design refinement, multiple prototype verification tests and development of design guide-lines and computer codes to facilitate its implementation in practice. Practicality of the new device, as offspring of an academic sphere, is assured through extensive collaboration with industry in its final design stages, prototyping and verification test programs.

Keywords: seismic, isolation, damper, adaptive stiffness

Procedia PDF Downloads 443

Authors: Mary Butler

Abstract:

Background: Screening programmes for older drivers in Europe (though not the UK), and in many states in the US and in Australia are based on medical assessment of fitness to drive. These programmes require physicians (including general practitioners) to carry out an assessment of fitness to drive in their offices. In 2006, New Zealand changed from doing on-road driving tests with all older drivers from the age of 80, to a screening programme that uses medical assessment of fitness to drive only. Aim: This study set out to understand the experience of New Zealand GPs as they manage the process of medical assessment of fitness to drive assessments for older people. In particular, it aimed to establish how GPs understand the role of specialist driving assessment and rehabilitation carried out by occupational therapists. Design and setting: The study used an interpretive descriptive approach to analyze data from ten interviews with GPs in New Zealand. Results: The results indicated that GPs lack understanding about how occupational therapists can assist their patients, and tend to refer only when there is a disagreement with the patient. Conclusion: There are problems with the medical assessment of fitness to drive carried out by GPs, and there is a need for a more comprehensive community approach to driving cessation. Patients, families and the multidisciplinary team all have a role in deciding when driving cessation should occur. Occupational therapists have a particular responsibility for strategic leadership in this area of practice.

Keywords: assessment, driving, older people, occupational therapy

Procedia PDF Downloads 122

Authors: Neda Azari Dodaran, Hamid Ahmadi

Abstract:

Results of 405 finite element (FE) analyses were used in the present research to study the effect of the joint geometry on the ultimate strength and initial stiffness of tubular K-joints subjected to axial loading at fire-induced elevated temperatures. The FE models were validated against the data available from experimental tests. Structural behavior under different temperatures (200ºC, 400ºC, 500ºC, and 700ºC) was investigated and compared to the behavior at ambient temperature (20ºC). A parametric study was conducted to investigate the effect of dimensionless geometrical parameters (β, γ, θ, and τ) on the ultimate strength and initial stiffness. Afterwards, ultimate strength data extracted from the FE analyses were compared with the values calculated from the equations proposed by available design codes in which the ultimate strength of the joint at elevated temperatures is obtained by replacing the yield stress of the steel at ambient temperature with the corresponding value at elevated temperature. It was indicated that this method may not have acceptable accuracy for K-joints under axial loading. Hence, a design formula was developed, through nonlinear regression analyses, to determine the ultimate strength of K-joints subjected to balanced axial loads at elevated temperatures.

Keywords: axial loading, elevated temperature, parametric equation, static strength, tubular K-joint

Procedia PDF Downloads 137

Authors: U. Achutha Kini, S. S. Sharma, K. Jagannath, P. R. Prabhu, M. C. Gowri Shankar

Abstract:

Aluminium matrix composites with alumina reinforcements give superior mechanical & physical properties. Their applications in several fields like automobile, aerospace, defense, sports, electronics, bio-medical and other industrial purposes are becoming essential for the last several decades. In the present work, fabrication of hybrid composite was done by Stir casting technique using Al 6061 as a matrix with alumina and silicon carbide (SiC) as reinforcement materials. The weight percentage of alumina is varied from 2 to 4% and the silicon carbide weight percentage is maintained constant at 2%. Hardness and wear tests are performed in the as cast and heat treated conditions. Age hardening treatment was performed on the specimen with solutionizing at 550°C, aging at two temperatures (150 and 200°C) for different time durations. Hardness distribution curves are drawn and peak hardness values are recorded. Hardness increase was very sensitive with respect to the decrease in aging temperature. There was an improvement in wear resistance of the peak aged material when aged at lower temperature. Also increase in weight percent of alumina, increases wear resistance at lower temperature but opposite behavior was seen when aged at higher temperature.

Keywords: hybrid composite, hardness test, wear test, heat treatment, pin on disc wear testing machine

Procedia PDF Downloads 309

Authors: Sijia Hu

Abstract:

Tensile creep tests were performed along the normal direction on the as-solutioned (AS) and as-aged (AA) samples of a commercial ZK60 alloy in this work. The results showed that the AA sample obtained a stronger 0.2% proof stress but a poorer creep resistance in comparison to the AS sample. It was revealed that the creep deformation in the AS sample was attributed to basal slip and twinning, while the creep behavior of the AA sample was controlled by basal slip, pyramidal slip and twinning. Besides, the reasons for the poorer creep resistance of the AA sample were unveiled. Pyramidal dislocations towards various moving directions were found to accelerate the creep deformation, and basal dislocations kinking at twin boundaries were found to induce heavy stress concentration. Furthermore, massive dynamic precipitates, including beta 1 prime and beta 2 prime types, were formed in the AS sample during the creep exposure, contributing to the superior creep resistance. But in the AA sample, plentiful beta 1 prime and beta 2 prime phases generated during the prior peak-aging treatment dissolved into the matrix fast and only beta 1 prime re-precipitated during the creep process. With the decreased area fractions of precipitates, the age-hardening effect slacked off and failed to enhance the creep resistance.

Keywords: Mg alloy, creep, precipitation, microstructure

Procedia PDF Downloads 16

Authors: Sami Ibrahim Jafar, Israa Abud Alkadir, Samah Abdul Kareem Khashin

Abstract:

The aim of this work is to assess the influence of tensile pre-stresses on the microstructure and corrosion behavior of the AISI304 stainless steel in 1N H2SO4 austenitic stainless steel. Samples of this stainless steel either with pre-stresses, corresponding to [255, 305, 355, 405, 455, 505, 555, 605 and σf] MPa induced by tensile tests, or without pre-stresses (as received), were characterized regarding their microstructure to investigate the pre-tensile stress effects on the corrosion behavior. The results showed that the corrosion rate of elastic pre-stresses 304 stainless steel was very little increased compared with that of as received specimens. The corrosion rate increases after applying pre-stress between (σ255 - σ 455) MPa. The microstructure showed that the austenitic grains begin to deform in the direction of applied pre-stresses. The maximum hardness at this region was (229.2) Hv, but at higher pre-stress (σ455 – σ 605) MPa unanticipated occurrence, the corrosion rate decreases. The microstructure inspection shows the deformed austenitic grain and ά-martensitic phase needle are appeared inside austenitic grains and the hardness reached the maximum value (332.433) Hv. The results showed that the corrosion rate increases at the values of pre-stresses between (σ605 – σf) MPa., which is inspected the result. The necking of gauge length of specimens occurs in specimens and this leads to deterioration in original properties and the corrosion rate reaches the maximum value.

Keywords: tensile pre-stresses, corrosion rate, austenitic stainless steel, hardness

Procedia PDF Downloads 389

Authors: Morteza Raei Dehaghi, Seyed Mohammad Mirhashemi

Abstract:

The current study explored the effect of economic development, financial development and institutional quality on environmental destruction in upper-middle income countries during the time period of 1999-2011. The dependent variable is logarithm of carbon dioxide emissions that can be considered as an index for destruction or quality of the environment given to its effects on the environment. Financial development and institutional development variables as well as some control variables were considered. In order to study cross-sectional correlation among the countries under study, Pesaran and Friz test was used. Since the results of both tests show cross-sectional correlation in the countries under study, seemingly unrelated regression method was utilized for model estimation. The results disclosed that Kuznets’ environmental curve hypothesis is confirmed in upper-middle income countries and also, financial development and institutional quality have a significant effect on environmental quality. The results of this study can be considered by policy makers in countries with different income groups to have access to a growth accompanied by improved environmental quality.

Keywords: economic development, environmental destruction, financial development, institutional development, seemingly unrelated regression

Procedia PDF Downloads 331

Authors: H. Meddah, M. Berediaf-Bourahla, B. El-Djouzi, N. Bourahla

Abstract:

Shear walls made of cold formed steel are used as lateral force resisting components in residential and low-rise commercial and industrial constructions. The seismic design analysis of such structures is often complex due to the slenderness of members and their instability prevalence. In this context, a simplified modeling technique across the panel is proposed by using the finite element method. The approach is based on idealizing the whole panel by a nonlinear shear link element which reflects its shear behavior connected to rigid body elements which transmit the forces to the end elements (studs) that resist the tension and the compression. The numerical model of the shear wall panel was subjected to cyclic loads in order to evaluate the seismic performance of the structure in terms of lateral displacement and energy dissipation capacity. In order to validate this model, the numerical results were compared with those from literature tests. This modeling technique is particularly useful for the design of cold formed steel structures where the shear forces in each panel and the axial forces in the studs can be obtained using spectrum analysis.

Keywords: cold-formed steel, cyclic loading, modeling technique, nonlinear analysis, shear wall panel

Procedia PDF Downloads 278

Authors: Mitzi S. Brammer

Abstract:

Given that the cultural make-up of programs of study in institutions of higher learning is becoming increasingly diverse, much has been written about cultural diversity from a university-level perspective. However, there are little data in the way of specific programs and how they address inclusive practices when teaching and working with marginalized populations. This research study aimed to discover baseline knowledge and attitudes of health sciences faculty, instructional staff, and students related to inclusive teaching/learning and interactions. Quantitative data were collected via an anonymous online survey (one designed for students and another designed for faculty/instructional staff) using a web-based program called Qualtrics. Quantitative data were analyzed amongst the faculty/instructional staff and students, respectively, using descriptive and comparative statistics (t-tests). Additionally, some participants voluntarily engaged in a focus group discussion in which qualitative data were collected around these same variables. Collecting qualitative data to triangulate the quantitative data added trustworthiness to the overall data. The research team analyzed collected data and compared identified categories and trends, comparing those data between faculty/staff and students, and reported results as well as implications for future study and professional practice.

Keywords: inclusion, higher education, pedagogy, equity, diversity

Procedia PDF Downloads 47

Authors: Victor H. Benitez, Ramon V. Armas-Flores, Jesus H. Pacheco-Ramirez

Abstract:

Systems transforming solar energy into electrical power have emerged as a viable source of clean, renewable energy. Solar power tower technology is a good example of this type of system, which consists of several mobile mirrors, called heliostats, which reflect the sun's radiation to the same point, located on top of a tower at the center of heliostat field, for collection or transformation into another type of energy. The so-called Hermosillo’s Solar Platform (Plataforma Solar de Hermosillo, PSH, in Spanish) is a facility constituted with several heliostats, its aim and scope is for research purposes. In this paper, the implementation of a wireless communication system based on intelligent nodes is proposed in order to allow the communication and control of the heliostats in PSH. Intelligent nodes transmit information from one point to another, and can perform other actions that allow them to adapt to the conditions and limitations of a field of heliostats, thus achieving effective communication system. After deployment of the nodes in the heliostats, tests were conducted to measure the effectiveness of the communication, and determine the feasibility of using the proposed technologies. The test results were always positive, exceeding expectations held for its operation in the field of heliostats. Therefore, it was possible to validate the efficiency of the wireless communication system to be implemented in PSH, allowing communication and control of the heliostats.

Keywords: heliostat, intelligent node, solar energy, wireless communication

Procedia PDF Downloads 395

Authors: Hadjadj Abdechafik, Kious Mecheri, Ameur Aissa

Abstract:

The objective of this study is to develop a process of treatment of the vibratory signals generated during a horizontal high speed milling process without applying any coolant in order to establish a monitoring system able to improve the machining performance. Thus, many tests were carried out on the horizontal high speed centre (PCI Météor 10), in given cutting conditions, by using a milling cutter with only one insert and measured its frontal wear from its new state that is considered as a reference state until a worn state that is considered as unsuitable for the tool to be used. The results obtained show that the first harmonic follow well the evolution of frontal wear, on another hand a wavelet transform is used for signal processing and is found to be useful for observing the evolution of the wavelet approximations through the cutting tool life. The power and the Root Mean Square (RMS) values of the wavelet transformed signal gave the best results and can be used for tool wear estimation. All this features can constitute the suitable indicators for an effective detection of tool wear and then used for the input parameters of an online monitoring system. Although we noted the remarkable influence of the machining cycle on the quality of measurements by the introduction of a bias on the signal, this phenomenon appears in particular in horizontal milling and in the majority of studies is ignored.

Keywords: flank wear, vibration, milling, signal processing, monitoring

Procedia PDF Downloads 586

Authors: Hasan Izhar Khan, Naiqiang Zhang, Hong Xu, Zhongliang Zhu, Dongfang Jiang

Abstract:

Inconel 617, a nickel-based alloy designed for high-temperature applications, got an excellent amalgamation of strength and oxidation resistance at high temperatures. For a better understanding of its suitability to be used in superheater and reheater tubes in ultra-supercritical power plants, stress corrosion cracking (SCC) susceptibility must be evaluated. In the present study, the effect of medium environment on SCC behavior of Inconel 617, in the form of a round bar tensile specimen, was tested via slow strain rate tensile tests in steam and supercritical water (SCW) at 650 °C. The results showed that SCC susceptibility has a linear relationship with exposed pressure and increases monotonically with an increase in pressure. A severe SCC susceptibility was observed in SCW followed by that in a steam environment. Fracture and gage surface showed apparent characteristics of brittle fracture. Intergranular cracks initiated from the edge region and propagated into the matrix through cross section until ductile rupture. When dissolved oxygen contents were decreased in SCW environment, it showed no noticeable effect on mechanical properties but SCC susceptibility slightly decreased. The research revealed the influence of environment on SCC susceptibility of Inconel 617 in steam and SCW.

Keywords: Inconel 617, steam, supercritical water, stress corrosion cracking

Procedia PDF Downloads 138

Authors: Amir Mahyar Khorasani, Ian Gibson, Moshe Goldberg, Mohammad Masoud Movahedi, Guy Littlefair

Abstract:

One of the important factors in manufacturing processes especially machining operations is surface quality. Improving this parameter results in improving fatigue strength, corrosion resistance, creep life and surface friction. The reliability and clearance of removable joints such as thread and nuts are highly related to the surface roughness. In this work, the effect of different cutting parameters such as cutting fluid pressure, feed rate and cutting speed on the surface quality of the crest of thread in the high-speed milling of Brass C3600 have been determined. Two popular neural networks containing MLP and RBF coupling with Taguchi L32 have been used to model surface roughness which was shown to be highly adept for such tasks. The contribution of this work is modelling surface roughness on the crest of the thread by using precise profilometer with nanoscale resolution. Experimental tests have been carried out for validation and approved suitable accuracy of the proposed model. Also analysing the interaction of parameters two by two showed that the most effective cutting parameter on the surface value is feed rate followed by cutting speed and cutting fluid pressure.

Keywords: artificial neural networks, cutting conditions, high-speed machining, surface roughness, thread milling

Procedia PDF Downloads 363

Authors: Phillip Garrad, Saritha Unnikrishnan

Abstract:

The recent popularity of connected and autonomous vehicles (CAV) corresponds with an increase in the risk of cyber-attacks. These cyber-attacks have been instigated by both researchers or white-coat hackers and cyber-criminals. As Connected Vehicles move towards full autonomy, the impact of these cyber-attacks also grows. The current research details challenges faced in cybersecurity testing of CAV, including access and cost of the representative test setup. Other challenges faced are lack of experts in the field. Possible solutions to how these challenges can be overcome are reviewed and discussed. From these findings, a software simulated CAV network is established as a cost-effective representative testbed. Penetration tests are then performed on this simulation, demonstrating a cyber-attack in CAV. Studies have shown Artificial Intelligence (AI) to improve runtime, increase efficiency and comprehensively cover all the typical test aspects in penetration testing in other industries. There is an attempt to introduce similar AI models to the software simulation. The expectation from this implementation is to see similar improvements in runtime and efficiency for the CAV model. If proven to be an effective means of penetration test for CAV, this methodology may be used on a full CAV test network.

Keywords: cybersecurity, connected vehicles, software simulation, artificial intelligence, penetration testing

Procedia PDF Downloads 88

Authors: Matthew J. Flynn

Abstract:

In early 2022, a thirty-mile column of Russian armor and assault vehicles sat poised to move south on the road to Kiev. That force has withdrawn as the Russians concentrate on attacking eastern Ukraine. Vladimir Putin’s armies appear content to destroy cities in an effort to attrit the Ukrainian will to continue fighting. That pivot signifies the acceptance of the ascendancy of the defense that now dictates any battlefield world-wide. To defeat what military theorist Carl von Clausewitz labeled “the stronger form of war” with a successful offensive requires an exercise in future war. In the past, the ascendancy of the defense has been overcome by a number of things including the application of superior leadership, better technology, organizational adaptation, and surpassing environmental limitations. A look at how each of these factors came to impact battle can tell us a great deal about what Ukraine means to tomorrow’s fight, and where the focus should lie to win the next war. Civilians presently secure the defensive ascendancy impacting warfare by dominating the shifts from domain to domain thanks to controlling access to cyberspace. That mandate will be tested and eventually falter. This paper tests the desirability of that proposition, as well as hoping for something more from humanity other than repeated and frequent wars making future war look much like past wars. As nations struggle to control cyberspace, a referendum on war as part of the human condition comes into focus.

Keywords: cyber, domains, future war, Putin, Ukraine

Procedia PDF Downloads 90

Authors: Abdu Feroz Maluleke

Abstract:

Digital literacy skills among first-year university students has been under scrutiny in recent years. This is largely due to the pressure faced by the South African higher education sector as the battle to integrate educational technologies into the teaching curriculum. This study aims to investigate the relationship between the Technology Acceptance Model (TAM) and the digital literacy skills of first-year students at the Tshwane University of Technology in South Africa. A positivism quantitative research methodology will be employed to collect data from 468 first-year students at a higher education institution through a validated questionnaire. Descriptive analyses, T-tests, ANOVA, and Spearman's correlation will be conducted using SPSS. Anticipated findings suggest that various demographic factors, such as previous school, self-efficacy, and age, significantly influence learners' digital literacy competency. Furthermore, the projected findings highlight the importance of rural secondary schools adopting and implementing technological pedagogies in their curriculum. This research aims to make a substantial contribution to the development of ICT adoption guidelines for the secondary school curriculum, which would aid the basic educational sector in South Africa.

Keywords: technology acceptance model, digital literacy skills, secondary schools, south africa

Procedia PDF Downloads 56

Authors: Mahdi Taghipour Masoumi, Ali Abdi Kordani, Mahmoud Nazirizad

Abstract:

Geosynthetics utilization plays an important role in the construction of highways with no additive layers, such as asphalt concrete or cement concrete, or in a subgrade layer which affects the bearing capacity of unbounded layers. This laboratory experimental study was carried out to evaluate changes in the load bearing capacity of reinforced soil with these materials in highway roadbed with regard to geotextile properties. California Bearing Ratio (CBR) test samples were prepared with two types of soil: Clayey and sandy containing non-reinforced and reinforced soil. The samples comprised three types of geotextiles with different characteristics (150, 200, 300 g/m²) and depths (H= 5, 10, 20, 30, 50, 100 mm), and were grouped into two forms, one-layered and two-layered, based on the sample materials in order to perform defined tests. The results showed that the soil bearing characteristics increased when one layer of geotextile was used in clayey and sandy samples reinforced by geotextile. However, the bearing capacity of the soil, in the presence of a geotextile layer material with depth of more than 30 mm, had no remarkable effect. Furthermore, when the two-layered geotextile was applied in material samples, although it increased the soil resistance, it also showed that through the addition of a number or weights of geotextile into samples, the natural composition of the soil changed and the results are unreliable.

Keywords: reinforced soil, geosynthetics, geotextile, transportation capacity, CBR experiments

Procedia PDF Downloads 274

Authors: J. Alvarez Muñoz, Dominguez Lepe J. A.

Abstract:

A suitable mixing time of the concrete, allows form a homogeneous mass, quality that leads to greater compressive strength and durability. Although there are recommendations as ASTM C94 standard these mention the time and the number of minimum and maximum speed for a ready-mix concrete of good quality, the specific behavior that would have a concrete mixed on site to variability of the mixing time is unknown. In this study was evaluated the behavior a design of mixture structural of f´c=250 kg/cm2, elaborate on site with limestone aggregate in warm sub-humid climate, subjected to different mixing times. Based on the recommendation for ready-mixed concrete ASTM C94, different times were set at 70, 90, 100, 110, 120, 140 total revolutions. A field study in which 14 works were observed where structural concrete made on site was used, allowed to set at 24 the number of revolutions to the reference mixture. For the production of concrete was used a hand feed concrete mixer with drum speed 28 RPM, the ratio w/c was 0.36 corrected, with a slump of 5-6 cm, for all mixtures. The compressive strength tests were performed at 3, 7, 14, and 28 days. The most outstanding results show increases in resistance in the mixtures of 24 to 70 revolutions between 8 and 17 percent and 70 to 90 revolutions of 3 to 8 percent. Increasing the number of revolutions at 110, 120 and 140, there was a reduction of the compressive strength of 0.5 to 8 percent. Regarding mixtures consistencies, they had a slump of 5 cm to 24, 70 and 90 rpm and less than 5 cm from 100 revolutions. Clearly, those made with more than 100 revolutions mixtures not only decrease the compressive strength but also the workability.

Keywords: compressive strength, concrete, mixing time, workability

Procedia PDF Downloads 388

Authors: G. Tanbayeva, Z. Myrzabekov, O. Tagayev, B. Barakhov, M. Tokayeva

Abstract:

Mastitis is widely spread among dairy cows bringing large economic damage resulting in decreased milk yield, deterioration of the milk quality, gastrointestinal tract disorders among young animals, culling of breeding stock, and expenses for sick animal treatment. Up-to-date and accurate diagnostics of subclinical (latent) mastitis in dairy cows has huge practical and economical significance. The aim of the research was to develop a new optimal alternative rapid method for the diagnosis of subclinical mastitis in cows. The study was performed in the laboratory of the Hygiene and Sanitation of Kazakh National Agrarian University. The first stage was to evaluate the different percentages of “Promastit” preparation. It showed that the best diagnostics capacity had 10% dilution. The second stage was to compare “Promastit” with some of the domestic and foreign analogues “Somatic-Test” (Denmark), “MastTest” (Russia), “Mastidin” (Ukraine), “Diagmast” (Kazakhstan). The observation was carried out on 520 dairy cows with subclinical mastitis on farms of Almaty region of Kazakhstan. The effectiveness was checked by milk sedimentation test. Our research tends to show that the diagnostic test "Promastitis" revealed subclinical mastitis in 193 out of 520 lactating cows (37.1% of those examined). At the same time, in the case of using other diagnostic tests, the given index was as follows: 35.5% (mastidin), 34.4% (masttest-AF), 33.8% (somatic-test Ecotest), 30.7% (diagmast).

Keywords: dairy cows, diagnostics, subclinical mastitis, test Promastit

Procedia PDF Downloads 339

Authors: Olaniyi Awe, Adelana R. Adetunji, Abraham Adeleke

Abstract:

Mining of alluvial gold ore by artisanal miners has been going on for decades at Itagunmodi, Southwestern Nigeria. In order to optimize the traditional panning gravity separation method commonly used in the area, a mineral particle size analysis study is critical. This study analyzed alluvial gold ore samples collected at identified five different locations in the area with a view to determine the ore particle size distributions. 500g measured of as-received alluvial gold ore sample was introduced into the uppermost sieve of an electrical sieve shaker consisting of sieves arranged in the order of decreasing nominal apertures of 5600μm, 3350μm, 2800μm, 355μm, 250μm, 125μm and 90μm, and operated for 20 minutes. The amount of material retained on each sieve was measured and tabulated for analysis. A screen analysis graph using the Gaudin Schuman method was drawn for each of the screen tests on the alluvial samples. The study showed that the percentages of fine particle size -125+90 μm fraction were 45.00%, 36.00%, 39.60%, 43.00% and 36.80% for the selected samples. These primary ore characteristic results provide reference data for the alluvial gold ore processing method selection, process performance measurement and optimization.

Keywords: alluvial gold ore, sieve shaker, particle size, Gaudin Schumann

Procedia PDF Downloads 29

Authors: Jui-Pui Hung, Yong-Run Chen, Wei-Cheng Shih, Shen-He Tsui, Kung-Da Wu

Abstract:

This paper presents the effect on the tooling conditions on the machining stabilities of a milling machine tool. The machining stability was evaluated in different feeding direction in the X-Y plane, which was referred as the orientation-dependent machining stability. According to the machining mechanics, the machining stability was determined by the frequency response function of the cutter. Thus, we first conducted the vibration tests on the spindle tool of the milling machine to assess the tool tip frequency response functions along the principal direction of the machine tool. Then, basing on the orientation dependent stability analysis model proposed in this study, we evaluated the variation of the dynamic characteristics of the spindle tool and the corresponding machining stabilities at a specific feeding direction. Current results demonstrate that the stability boundaries and limited axial cutting depth of a specific cutter were affected to vary when it was fixed in the tool holder with different overhang length. The flute of the cutter also affects the stability boundary. When a two flute cutter was used, the critical cutting depth can be increased by 47 % as compared with the four flute cutter. The results presented in study provide valuable references for the selection of the tooling conditions for achieving high milling performance.

Keywords: tooling condition, machining stability, milling machine, chatter

Procedia PDF Downloads 417

Authors: Yung-Shan Lu, Chia-Fone Lee, Shang-Hsuan Li, Chien-Hao Liu

Abstract:

Recently, various bioelectronic devices have been developed for neurologic disease treatments via electro-stimulations such as cochlear implants and retinal prosthesis. Since the electric signal needs electrodes to be transmitted to an organism, electrodes play an important role of stimulations. The materials of stimulation electrodes affect the efficiency of the delivered currents. The higher the efficiency of the electrodes, the lower the threshold current can be used to stimulate the organism which minimizes the potential damages to the adjacent tissues. In this study, we proposed a biocompatible composite electrode composed of high-charge-capacity iridium oxide (IrOₓ) film for a bone-guide extra-cochlear implant. IrOₓ was exploited to decrease the threshold current due to its high capacitance and low impedance. The IrOₓ electrode was fabricated via microelectromechanical systems (MEMS) photolithography and examined with in-vivo tests with guinea pigs. Based on the measured responses of brain waves to sound, the results demonstrated that IrOₓ electrodes have a lower threshold current compared with the Platinum (Pt) electrodes. The research results are expected to be beneficial for implantable and biocompatible electrodes for electrical stimulations.

Keywords: cochlear implants, electrode, electrical stimulation, iridium oxide

Procedia PDF Downloads 173

Authors: Li Guoyou, Zhang Tao, Ji Wenzhan, Huo Liang, Lin Xiqiang, Zhang Nan

Abstract:

The three dimensional (3D) printing technology has undergone rapid development in the last few years and it is possible to print engineering structures. 3D printing buildings use wastes from constructions, industries and mine tailings as “ink”, and mix it with property improved materials, such as cement, fiber etc. This paper presents a study of the Thermodynamic performance of 3D printed walls using cement and steel slag powder. Analyses the thermal simulation regarding 3D printed walls and solid brick wall by the way of the hot-box methods and the infrared technology, and the results were contrasted with theoretical calculation. The results show that the excellent thermodynamic performance of 3D printed concrete wall made it suitable as the partial materials for self-thermal insulation walls in residential buildings. The thermodynamic performance of 3D printed concrete walls depended on the density of materials, distribution of holes, and the filling materials. Decreasing the density of materials, increasing the number of holes or replacing the filling materials with foamed concrete could improve its thermodynamic performance significantly. The average of heat transfer coefficient and thermal inertia index of 3D printed steel slag powder concrete wall all better than the traditional solid brick wall with a thickness of 240mm.

Keywords: concrete, 3D printed walls, thermodynamic performance, steel slag powder

Procedia PDF Downloads 172

Authors: Hassan. A. Abas, Saad A. Aiban

Abstract:

Soil improvement by means of stone column method is used to improve sabkha soils in order to limit total and differential settlement and to achieve the required bearing capacity. Full-scale plate test was performed on site to confirm the achievement of required bearing capacity at the specified settlement. Despite the fact that this technique is widely used to improve sabkha soils, there are no studies focusing on the behavior of stone columns in such problematic soils. Sabkha soils are known for its high compressibility, low strength and water sensitivity due to loss of salt cementation upon flooding during installation of stone columns. Numerical modeling of plate load test assist to understand complicated behavior of sabkha – stone column interaction. This paper presents a three-dimensional Finite element model, using PLAXIS 3D software, to simulate vertical plate load tests on a stone column installed in sabkha. The predicted settlement values are in reasonable agreement with the field measure values and the field load - settlement curve can be predicted with good accuracy.

Keywords: soil improvement, stone column, sabkha, PLAXIS 3D

Procedia PDF Downloads 366

Authors: A. Araceli Sánchez, I. Manuel H. De la Torre, S. Fernando Mendoza, R. Cesar Tavera, R. Manuel de J. Briones

Abstract:

Recycling, as part of any sustainable environment, is continuously evolving and impacting on new materials in manufacturing. One example of this is the recycled solid waste of Tetra Pak ™ packaging, which is a highly pollutant waste as it is not biodegradable since it is manufactured with different materials. The Tetra Pak ™ container consists of thermally joined layers of paper, aluminum and polyethylene. Once disposed, this packaging is recycled by completely separating the paperboard from the rest of the materials. The aluminum and the polyethylene remain together and are used to create the poly-aluminum, which is widely used to manufacture roof tiles. These recycled tiles have different thermal and acoustic properties compared with traditional manufactured ceramic and cement tiles. In this work, we compare a group of tiles using nondestructive optical testing to measure the superficial micro deformations of the tiles under well controlled experiments. The results of the acoustic and thermal tests show remarkable differences between the recycled tile and the traditional ones. These results help to determine which tile could be better suited to the specific environmental conditions in countries where extreme climates, ranging from tropical, desert-like, to very cold are experienced throughout the year.

Keywords: acoustic, digital holographic interferometry, isolation, recycled, roof tiles, sustainable, thermal

Procedia PDF Downloads 447

Authors: Mohammad Karimizadehardakani, Hooman Minoonejad, Reza Rajabi, Ali Sharifnejad

Abstract:

Background: Ankle sprain is one of the most important risk factor of anterior cruciate ligament (ACL) injury. Also, functional ankle instability (FAI) population has alterations in lower extremity sagittal plane biomechanics during landing task. We want to examine whether biomechanical alterations demonstrated by FAI patients are associated with the mechanism of ACL injury during high risk and sport related tasks. Methods: Sixteen basketball player with FAI and 16 non-injured control performed a single-leg cross drop landing. Knee sagittal and frontal (ATSF) was calculated. Independent t-tests, multiple linear regression, and Pearson correlation were used for analysis data. Result: Subject with FAI showed more peak ATFS, posterior ground reaction force (GRF) and less knee flexion, compared to the controls (P= 0.001, P= 0.004, P= 0.011). Knee flexion (r= −0.824, P = 0.011) and posterior GRF (r= 0.901, P = .001) were correlated with ATSF; Posterior GRF was factor that most explained the variance in ATSF (R2= 0.645; P = .001) in the FAI group. Conclusions: Result of our study showed there is a potential biomechanical relationship between the presence of FAI and risk factors associated with ACL injury mechanism.

Keywords: functional ankle instability, anterior cruciate ligament, biomechanics, risk factor

Procedia PDF Downloads 209

Authors: Jean Yves Uwamungu, Fiston Bizimana, Chunsheng Hu

Abstract:

Although pesticides are used in crop productivity, their use is highly harming the soil environment, and measures must be taken in the future to eradicate soil and groundwater pollution. The primary aim was to determine the effect of biochar addition on the imidacloprid adsorption on soil prior to no-tillage (NT) and rotational tillage (RT) conditions. In the laboratory, batch tests were conducted to determine the imidacloprid adsorption on soil using equilibrium and kinetic modelling with the addition of biochar. The clay level of the soil was found to be more significant when no-tillage was applied (22.42) than when rotational tillage was applied (14.27). The imidacloprid adsorption equilibrium was significantly shortened to 25 min after biochar addition. The isotherms and kinetic findings confirmed that the adsorption occurred according to Freundlich and pseudo-second-order kinetic models, respectively. The adsorption capacity of imidacloprid (40<35<25 °C) increased with decreasing temperature, indicating an exothermic adsorption behaviour, whereas negative Gibbs free energy (G) values of -6980.5 and 5983.93 Jmol-1, respectively, for soil prior to NT and RT at 25 °C, asserted spontaneous adsorption. The negative values of entropy (ΔS); -22.83 and -38.15 Jmol-1K-1, prior to NT and RT applications, respectively, described a lowered randomness process. The enthalpy was greater when RT was applied (-17533 J mol-1) than when NT was applied (-450 J mol-1). Lastly, it was shown that NTtreatment enhanced imidacloprid adsorption capacity more than RT treatment and that biochar addition enhanced pesticide adsorption in both treatments.

Keywords: adsorption, biochar, imidacloprid, soil, tillage

Procedia PDF Downloads 130

Authors: Meryem Saban Guler, Saniye Bilici

Abstract:

Malnutrition is a problem that significantly affects patients with cancer throughout the course of their illness, and it may be present from the moment of diagnosis until the end of treatment. We searched electronic databases using key terms such as ‘malnutrition in cancer patients’ or ‘nutritional status in cancer’ or ‘nutritional screening tools’ etc. Decline in nutritional status and continuing weight loss are associated with an increase in number and severity of complications, impaired quality of life and decreased survival rate. Nutrition is an important factor in the treatment and progression of cancer. Cancer patients are particularly susceptible to nutritional depletion due to the combined effects of the malignant disease and its treatment. With increasing incidence of cancer, identification and management of nutritional deficiencies are needed. Early identification of malnutrition, is substantial to minimize or prevent undesirable outcomes throughout clinical course. In determining the nutritional status; food consumption status, anthropometric methods, laboratory tests, clinical symptoms, psychosocial data are used. First-line strategies must include routine screening and identification of inpatients or outpatients at nutritional risk with the use of a simple and standardized screening tool. There is agreement among international nutrition organizations and accredited health care organizations that routine nutritional screening should be a standard procedure for every patient admitted to a hospital. There are f management of all cancer patients therefore routine nutritional screening with validated tools can identify cancer patients at risk.

Keywords: cancer, malnutrition, nutrition, nutritional screening

Procedia PDF Downloads 187

Authors: Ning Li, Yaner Yan, Yajun Qiao, Shu-qing An

Abstract:

Although seed dispersal is considered to be a key process determining the spatial structure and spread of invasive plant populations, few studies have explicitly addressed the link between dispersal vector behaviour, and seedling recruitment to gain insight into the process of exotic species invasion within a urban landscape. The present study tests the effects of native bird species on the dispersal and recruitment of invasive Phytolacca Americana in an urban garden. We found the invasive population of American pokeweed attracted both generalist species and specialist species to forage and disperse its seeds, with generalists Pycnonotus sinensis and Urocissa erythrorhyncha being by far the most important dispersers. Seedling numbers of P. Americana was strongly affected by perching behavior of bird dispersers. Moreover, two main disperser species, P. sinensis and U. erythrorhyncha govern a high quality dispersal service for P. Americana. Our results highlight the ability of invasive P. americana to recruit seed dispersal agents in urban habitats. However, if the newly recruited species could use the seedling safe site for perching shelter, the invasive plants will get a high regenerate rate in the invasive new habitats thus enhancing their invasive ability.

Keywords: frugivorous birds, phytolacca americana, seed dispersal, urban landscape

Procedia PDF Downloads 527