Search results for: steel moment connection
2704 Radiation Stability of Structural Steel in the Presence of Hydrogen
Authors: E. A. Krasikov
Abstract:
As the service life of an operating nuclear power plant (NPP) increases, the potential misunderstanding of the degradation of aging components must receive more attention. Integrity assurance analysis contributes to the effective maintenance of adequate plant safety margins. In essence, the reactor pressure vessel (RPV) is the key structural component determining the NPP lifetime. Environmentally induced cracking in the stainless steel corrosion-preventing cladding of RPV’s has been recognized to be one of the technical problems in the maintenance and development of light-water reactors. Extensive cracking leading to failure of the cladding was found after 13000 net hours of operation in JPDR (Japan Power Demonstration Reactor). Some of the cracks have reached the base metal and further penetrated into the RPV in the form of localized corrosion. Failures of reactor internal components in both boiling water reactors and pressurized water reactors have increased after the accumulation of relatively high neutron fluences (5´1020 cm–2, E>0,5MeV). Therefore, in the case of cladding failure, the problem arises of hydrogen (as a corrosion product) embrittlement of irradiated RPV steel because of exposure to the coolant. At present when notable progress in plasma physics has been obtained practical energy utilization from fusion reactors (FR) is determined by the state of material science problems. The last includes not only the routine problems of nuclear engineering but also a number of entirely new problems connected with extreme conditions of materials operation – irradiation environment, hydrogenation, thermocycling, etc. Limiting data suggest that the combined effect of these factors is more severe than any one of them alone. To clarify the possible influence of the in-service synergistic phenomena on the FR structural materials properties we have studied hydrogen-irradiated steel interaction including alternating hydrogenation and heat treatment (annealing). Available information indicates that the life of the first wall could be expanded by means of periodic in-place annealing. The effects of neutron fluence and irradiation temperature on steel/hydrogen interactions (adsorption, desorption, diffusion, mechanical properties at different loading velocities, post-irradiation annealing) were studied. Experiments clearly reveal that the higher the neutron fluence and the lower the irradiation temperature, the more hydrogen-radiation defects occur, with corresponding effects on the steel mechanical properties. Hydrogen accumulation analyses and thermal desorption investigations were performed to prove the evidence of hydrogen trapping at irradiation defects. Extremely high susceptibility to hydrogen embrittlement was observed with specimens which had been irradiated at relatively low temperature. However, the susceptibility decreases with increasing irradiation temperature. To evaluate methods for the RPV’s residual lifetime evaluation and prediction, more work should be done on the irradiated metal–hydrogen interaction in order to monitor more reliably the status of irradiated materials.Keywords: hydrogen, radiation, stability, structural steel
Procedia PDF Downloads 2602703 Influence of Graphene Content on Corrosion Behavior of Electrodeposited Zinc–Graphene Composite Coatings
Authors: Bin Yang, Xiaofang Chen, Guangxin Wang
Abstract:
Zinc coating as a sacrificial protection plays an important role in the traditional steel anticorrosion field. Adding second-phase reinforcement particles into zinc matrix is an interesting approach to further enhance its corrosion performance. In this paper, pure Zn and Zn–graphene composite coatings of different graphene contents were prepared by direct current electrodeposition on 304 stainless steel substrate. The coatings were characterized by XRD, SEM/EDS, and Raman spectroscopy. Tafel polarization and electrochemical impedance spectroscopic methods were used to study their corrosion behavior. Result obtained have shown that the concentration of grapheme oxide (GO) in zinc sulfate bath has an important effect on textured structure and surface morphology of Zn–graphene composite coatings. The coating prepared with 1.0g/L GO has shown the best corrosion resistance compared to other coatings prepared in this study.Keywords: Zn-graphene coatings, electrodeposition, microstructure, corrosion behavior
Procedia PDF Downloads 2492702 Evaluating the Seismic Stress Distribution in the High-Rise Structures Connections with Optimal Bracing System
Authors: H. R. Vosoughifar, Seyedeh Zeinab. Hosseininejad, Nahid Shabazi, Seyed Mohialdin Hosseininejad
Abstract:
In recent years, structure designers advocate further application of energy absorption devices for lateral loads damping. The Un-bonded Braced Frame (UBF) system is one of the efficient damping systems, which is made of a smart combination of steel and concrete or mortar. In this system, steel bears the earthquake-induced axial force as compressive or tension forces without loss of strength. Concrete or mortar around the steel core acts as a constraint for brace and prevents brace buckling during seismic axial load. In this study, the optimal bracing system in the high-rise structures has been evaluated considering the seismic stress distribution in the connections. An actual 18-story structure was modeled using the proper Finite Element (FE) software where braced with UBF, Eccentrically Braced Frames (EBF) and Concentrically Braced Frame (CBF) systems. Nonlinear static pushover and time-history analyses are then performed so that the acquired results demonstrate that the UBF system reduces drift values in the high-rise buildings. Further statistical analyses show that there is a significant difference between the drift values of UBF system compared with those resulted from the EBF and CBF systems. Hence, the seismic stress distribution in the connections of the proposed structure which braced with UBF system was investigated.Keywords: optimal bracing system, high-rise structure, finite element analysis (FEA), seismic stress
Procedia PDF Downloads 4222701 Studying on Pile Seismic Operation with Numerical Method by Using FLAC 3D Software
Authors: Hossein Motaghedi, Kaveh Arkani, Siavash Salamatpoor
Abstract:
Usually the piles are important tools for safety and economical design of high and heavy structures. For this aim the response of single pile under dynamic load is so effective. Also, the agents which have influence on single pile response are properties of pile geometrical, soil and subjected loads. In this study the finite difference numerical method and by using FLAC 3D software is used for evaluation of single pile behavior under peak ground acceleration (PGA) of El Centro earthquake record in California (1940). The results of this models compared by experimental results of other researchers and it will be seen that the results of this models are approximately coincide by experimental data's. For example the maximum moment and displacement in top of the pile is corresponding to the other experimental results of pervious researchers. Furthermore, in this paper is tried to evaluate the effective properties between soil and pile. The results is shown that by increasing the pile diagonal, the pile top displacement will be decreased. As well as, by increasing the length of pile, the top displacement will be increased. Also, by increasing the stiffness ratio of pile to soil, the produced moment in pile body will be increased and the taller piles have more interaction by soils and have high inertia. So, these results can help directly to optimization design of pile dimensions.Keywords: pile seismic response, interaction between soil and pile, numerical analysis, FLAC 3D
Procedia PDF Downloads 3772700 Study of Tool Shape during Electrical Discharge Machining of AISI 52100 Steel
Authors: Arminder Singh Walia, Vineet Srivastava, Vivek Jain
Abstract:
In Electrical Discharge Machining (EDM) operations, the workpiece confers to the shape of the tool. Further, the cost of the tool contributes the maximum effect on total operation cost. Therefore, the shape and profile of the tool become highly significant. Thus, in this work, an attempt has been made to study the effect of process parameters on the shape of the tool. Copper has been used as the tool material for the machining of AISI 52100 die steel. The shape of the tool has been evaluated by determining the difference in out of roundness of tool before and after machining. Statistical model has been developed and significant process parameters have been identified which affect the shape of the tool. Optimum process parameters have been identified which minimizes the shape distortion.Keywords: discharge current, flushing pressure, pulse-on time, pulse-off time, out of roundness, electrical discharge machining
Procedia PDF Downloads 2762699 Effect of Variation of Temperature Distribution on Mechanical Properties of Shield Metal Arc Welded Duplex Stainless Steel
Authors: Arvind Mittal, Rajesh Gupta
Abstract:
Influence of heat input on the micro structure and mechanical properties of shield metal arc welded of duplex stainless steel UNSNO.S-31803 has been investigated. Three heat input combinations designated as low heat (0.675 KJ/mm), medium heat (0.860 KJ/mm) and high heat (1.094 KJ/mm) and weld joints made using these combinations were subjected to micro structural evaluations and tensile and impact testing so as to analyze the effect of thermal arc energy on the micro structure and mechanical properties of these joints. The result of this investigation shows that the joints made using low heat input exhibited higher tensile strength than those welded with medium and high heat input. Heat affected zone of welded joint made with medium heat input has austenitic ferritic grain structure with some patchy austenite provide high toughness. Significant grain coarsening was observed in the heat affected zone (HAZ) of medium and high heat input welded joints, whereas low heat input welded joint shows the fine grain structure in the heat affected zone with small amount of dendritic formation and equiaxed grain structure where inner zone indicates slowly cooled grains in the direction of heat dissipation. This is the main reason for the observable changes of tensile properties of weld joints welded with different arc energy inputs.Keywords: microstructure, mechanical properties, shield metal arc welded, duplex stainless steel
Procedia PDF Downloads 2732698 Non-Chronological Approach in Crane Girder and Composite Steel Beam Installation: Case Study
Authors: Govindaraj Ramanathan
Abstract:
The time delay and the structural stability are major issues in big size projects due to several factors. Improper planning and poor coordination lead to delay in construction, which sometimes result in reworking or rebuilding. This definitely increases the cost and time of project. This situation stresses the structural engineers to plan out of the limits of contemporary technology utilizing non-chronological approach with creative ideas. One of the strategies to solve this issue is through structural integrity solutions in a cost-effective way. We have faced several problems in a project worth 470 million USD, and one such issue is crane girder installation with composite steel beams. We have applied structural integrity approach with the proper and revised planning schedule to solve the problem efficiently with minimal expenses.Keywords: construction management, delay, non-chronological approach, composite beam, structural integrity
Procedia PDF Downloads 2302697 Stability Analysis and Experimental Evaluation on Maxwell Model of Impedance Control
Authors: Le Fu, Rui Wu, Gang Feng Liu, Jie Zhao
Abstract:
Normally, impedance control methods are based on a model that connects a spring and damper in parallel. The series connection, namely the Maxwell model, has emerged as a counterpart and draw the attention of robotics researchers. In the theoretical analysis, it turns out that the two pattern are both equivalents to some extent, but notable differences of response characteristics exist, especially in the effect of damping viscosity. However, this novel impedance control design is lack of validation on realistic robot platforms. In this study, stability analysis and experimental evaluation are achieved using a 3-fingered Barrett® robotic hand BH8-282 endowed with tactile sensing, mounted on a torque-controlled lightweight and collaborative robot KUKA® LBR iiwa 14 R820. Object handover and incoming objects catching tasks are executed for validation and analysis. Experimental results show that the series connection pattern has much better performance in natural impact or shock absorption, which indicate promising applications in robots’ safe and physical interaction with humans and objects in various environments.Keywords: impedance control, Maxwell model, force control, dexterous manipulation
Procedia PDF Downloads 4932696 Selective Oxidation of 6Mn-2Si Advanced High Strength Steels during Intercritical Annealing Treatment
Authors: Maedeh Pourmajidian, Joseph R. McDermid
Abstract:
Advanced High Strength Steels are revolutionizing both the steel and automotive industries due to their high specific strength and ability to absorb energy during crash events. This allows manufacturers to design vehicles with significantly increased fuel efficiency without compromising passenger safety. To maintain the structural integrity of the fabricated parts, they must be protected from corrosion damage through continuous hot-dip galvanizing process, which is challenging due to selective oxidation of Mn and Si on the surface of this AHSSs. The effects of process atmosphere oxygen partial pressure and small additions of Sn on the selective oxidation of a medium-Mn C-6Mn-2Si advanced high strength steel was investigated. Intercritical annealing heat treatments were carried out at 690˚C in an N2-5%H2 process atmosphere under dew points ranging from –50˚C to +5˚C. Surface oxide chemistries, morphologies, and thicknesses were determined at a variety of length scales by several techniques, including SEM, TEM+EELS, and XPS. TEM observations of the sample cross-sections revealed the transition to internal oxidation at the +5˚C dew point. EELS results suggested that the internal oxides network was composed of a multi-layer oxide structure with varying chemistry from oxide core towards the outer part. The combined effect of employing a known surface active element as a function of process atmosphere on the surface structure development and the possible impact on reactive wetting of the steel substrates by the continuous galvanizing zinc bath will be discussed.Keywords: 3G AHSS, hot-dip galvanizing, oxygen partial pressure, selective oxidation
Procedia PDF Downloads 3902695 Novel Poly Schiff Bases as Corrosion Inhibitors for Carbon Steel in Sour Petroleum Conditions
Authors: Shimaa A. Higazy, Olfat E. El-Azabawy, Ahmed M. Al-Sabagh, Notaila M. Nasser, Eman A. Khamis
Abstract:
In this work, two novel Schiff base polymers (PSB1 and PSB₂) with extra-high protective barrier features were facilely prepared via Polycondensation reactions. They were applied for the first time as effective corrosion inhibitors in the sour corrosive media of petroleum environments containing hydrogen sulfide (H₂S) gas. For studying the polymers' inhibitive action on the carbon steel, numerous corrosion testing methods including potentiodynamic polarization (PDP), open circuit potential, and electrochemical impedance spectroscopy (EIS) have been employed at various temperatures (298-328 K) in the oil wells formation water with H₂S concentrations of 100, 400, and 700 ppm as aggressive media. The activation energy (Ea) and other thermodynamic parameters were computed to describe the mechanism of adsorption. The corrosion morphological traits and steel samples' surfaces composition were analyzed by field emission scanning electron microscope and energy dispersive X-ray analysis. The PSB2 inhibited sour corrosion more effectively than PSB1 when subjected to electrochemical testing. The 100 ppm concentration of PSB2 exhibited 82.18 % and 81.14 % inhibition efficiencies at 298 K in PDP and EIS measurements, respectively. While at 328 K, the inhibition efficiencies were 61.85 % and 67.4 % at the same dosage and measurements. These poly Schiff bases exhibited fascinating performance as corrosion inhibitors in sour environment. They provide a great corrosion inhibition platform for the sustainable future environment.Keywords: schiff base polymers, corrosion inhibitors, sour corrosive media, potentiodynamic polarization, H₂S concentrations
Procedia PDF Downloads 862694 Mechanical and Tribological Performances of (Nb: H-D: a-C) Thin Films for Biomedical Applications
Authors: Sara Khamseh, Kambiz Javanruee, Hamid Khorsand
Abstract:
Plenty of metallic materials are used for biomedical applications like hip joints and screws. Besides, it is reported that metal platforms such as stainless steel show significant deterioration because of wear and friction. The surface of metal substrates has been coated with a variety of multicomponent coatings to prevail these problems. The carbon-based multicomponent coatings such as metal-added amorphous carbon and diamond coatings are crucially important because of their remarkable tribological performance and chemical stability. In the current study, H-D contained Nb: (a-C) multicomponent coatings (H-D: hexagonal diamond, a-C: amorphous carbon) coated on A 304 steel substrates using an unbalanced magnetron (UBM) sputtering system. The effects of Nb and H-D content and ID/IG ratio on microstructure, mechanical and tribological characteristics of (Nb: H-D: a-C) composite coatings were investigated. The results of Raman spectroscopy represented that a-C phase with a Graphite-like structure (GLC with high value of sp2 carbon bonding) is formed, and its domain size increased with increasing Nb content of the coatings. Moreover, the Nb played a catalyst for the formation of the H-D phase. The nanoindentation hardness value of the coatings ranged between ~17 to ~35 GPa and (Nb: H-D: a-C) composite coatings with more H-D content represented higher hardness and plasticity index. It seems that the existence of extra-hard H-D particles straightly increased hardness. The tribological performance of the coatings was evaluated using the pin-on-disc method under the wet environment of SBF (Simulated Body Fluid). The COF value of the (Nb: H-D: a-C) coatings decreased with an increasing ID/IG ratio. The lower coefficient of friction is a result of the lamelliform array of graphitic domains. Also, the wear rate of the coatings decreased with increasing H-D content of the coatings. Based on the literature, a-C coatings with high hardness and H3/E2 ratio represent lower wear rates and better tribological performance. According to the nanoindentation analysis, hardness and H3/E2 ratio of (Nb: H-D: a-C) multicomponent coatings increased with increasing H-D content, which in turn decreased the wear rate of the coatings. The mechanical and tribological potency of (Nb: H-D: a-C) composite coatings on A 304 steel substrates paved the way for the development of innovative advanced coatings to ameliorate the performance of A 304 steel for biomedical applications.Keywords: COF, mechanical properties, (Nb: H-D: a-C) coatings, wear rate
Procedia PDF Downloads 902693 The Role of Smartphones on Iranian Couples' Relationship: An Analysis
Authors: Niloofar Hooman
Abstract:
The present study aims at investigating the positive and negative effects of using Smartphones on couples committed relationships. Despite the fact that many couples may benefit from the positive aspects of Smartphones, it is not clear how their feeling of trust, intimacy and connection in their relationships get affected by Smartphones. This is important as it highlights the ambivalent influences of Smartphones on couple’s relationships. On the one hand, Smartphones can enhance their social and emotional interactions and on the other hand, they can cause mistrust and isolation between them. Trust, intimacy and honesty are of important factors through which a stable relationship can be constructed. Nevertheless, some characteristics of Smartphones such as being fluid and personalized can harm the relationship and consequently destroy it. Thus, it is necessary to investigate how Iranian couples in committed relationships use Smartphone to manage their relationship and how couples feel Smartphone have enhanced or detracted a sense of trust, intimacy and connection with their partner? In the first phase of the study, in-depth-interview will be conducted with 30 couples and data will be analyzed using NVIVO software. In the next phase of the study, 1500 participants aged 20 and above will be selected based on cluster sampling. Data will be analyzed both qualitatively and quantitatively.Keywords: couple, family, internet, intimacy, Smartphone, trust
Procedia PDF Downloads 3822692 Modal Analysis of Functionally Graded Materials Plates Using Finite Element Method
Authors: S. J. Shahidzadeh Tabatabaei, A. M. Fattahi
Abstract:
Modal analysis of an FGM plate composed of Al2O3 ceramic phase and 304 stainless steel metal phases was performed in this paper by ABAQUS software with the assumption that the behavior of material is elastic and mechanical properties (Young's modulus and density) are variable in the thickness direction of the plate. Therefore, a sub-program was written in FORTRAN programming language and was linked with ABAQUS software. For modal analysis, a finite element analysis was carried out similar to the model of other researchers and the accuracy of results was evaluated after comparing the results. Comparison of natural frequencies and mode shapes reflected the compatibility of results and optimal performance of the program written in FORTRAN as well as high accuracy of finite element model used in this research. After validation of the results, it was evaluated the effect of material (n parameter) on the natural frequency. In this regard, finite element analysis was carried out for different values of n and in simply supported mode. About the effect of n parameter that indicates the effect of material on the natural frequency, it was observed that the natural frequency decreased as n increased; because by increasing n, the share of ceramic phase on FGM plate has decreased and the share of steel phase has increased and this led to reducing stiffness of FGM plate and thereby reduce in the natural frequency. That is because the Young's modulus of Al2O3 ceramic is equal to 380 GPa and Young's modulus of SUS304 steel is 207 GPa.Keywords: FGM plates, modal analysis, natural frequency, finite element method
Procedia PDF Downloads 3832691 Creating Moments and Memories: An Evaluation of the Starlight 'Moments' Program for Palliative Children, Adolescents and Their Families
Authors: C. Treadgold, S. Sivaraman
Abstract:
The Starlight Children's Foundation (Starlight) is an Australian non-profit organisation that delivers programs, in partnership with health professionals, to support children, adolescents, and their families who are living with a serious illness. While supporting children and adolescents with life-limiting conditions has always been a feature of Starlight's work, providing a dedicated program, specifically targeting and meeting the needs of the paediatric palliative population, is a recent area of focus. Recognising the challenges in providing children’s palliative services, Starlight initiated a research and development project to better understand and meet the needs of this group. The aim was to create a program which enhances the wellbeing of children, adolescents, and their families receiving paediatric palliative care in their community through the provision of on-going, tailored, positive experiences or 'moments'. This paper will present the results of the formative evaluation of this unique program, highlighting the development processes and outcomes of the pilot. The pilot was designed using an innovation methodology, which included a number of research components. There was a strong belief that it needed to be delivered in partnership with a dedicated palliative care team, helping to ensure the best interests of the family were always represented. This resulted in Starlight collaborating with both the Victorian Paediatric Palliative Care Program (VPPCP) at the Royal Children's Hospital, Melbourne, and the Sydney Children's Hospital Network (SCHN) to pilot the 'Moments' program. As experts in 'positive disruption', with a long history of collaborating with health professionals, Starlight was well placed to deliver a program which helps children, adolescents, and their families to experience moments of joy, connection and achieve their own sense of accomplishment. Building on Starlight’s evidence-based approach and experience in creative service delivery, the program aims to use the power of 'positive disruption' to brighten the lives of this group and create important memories. The clinical and Starlight team members collaborate to ensure that the child and family are at the centre of the program. The design of each experience is specific to their needs and ensures the creation of positive memories and family connection. It aims for each moment to enhance quality of life. The partnership with the VPPCP and SCHN has allowed the program to reach families across metropolitan and regional locations. In late 2019 a formative evaluation of the pilot was conducted utilising both quantitative and qualitative methodologies to document both the delivery and outcomes of the program. Central to the evaluation was the interviews conducted with both clinical teams and families in order to gain a comprehensive understanding of the impact of and satisfaction with the program. The findings, which will be shared in this presentation, provide practical insight into the delivery of the program, the key elements for its success with families, and areas which could benefit from additional research and focus. It will use stories and case studies from the pilot to highlight the impact of the program and discuss what opportunities, challenges, and learnings emerged.Keywords: children, families, memory making, pediatric palliative care, support
Procedia PDF Downloads 912690 Utilization of Watermelon Rind Extract as Green Anti-Scalent for Cooling Water Systems
Authors: Elsayed G. Zaki, Nora A. Hamad, Hadeel G. El-Shorbagy
Abstract:
The effect of watermelon rind extract as green inhibitors for the formation of calcium sulphate scale have been investigated using conductivity measurements concurrently with the scanning electron microscopy (SEM), and optical microscopic examinations. Mineral scales were deposited from the brine solution by cathodic polarization of the steel surface. The results show up that the anti-scaling property of the extracts could be attributed to the presence of citrulline. In solution, citrulline retards calcium sulphate precipitation via formation of a complex with the calcium cations. Thin, smooth and non adherent film formed over the steel surface, under cathodic polarization, by the deposition of the calcium- citrulline complex. The stability of the aqueous extracts with time was also investigated.Keywords: anti-scaling, scale inhibitor, green extracts, water treatment
Procedia PDF Downloads 2632689 Effect of Forging Pressure on Mechanical Properties and Microstructure of Similar and Dissimilar Friction Welded Joints (Aluminium, Copper, Steel)
Authors: Sagar Pandit
Abstract:
The present work focuses on the effect of various process parameters on the mechanical properties and microstructure of joints produced by continuous drive friction welding and linear friction welding. An attempt is made to investigate the feasibility of obtaining an acceptable weld joint between similar as well as dissimilar components and the microstructural changes have also been assessed once the good weld joints were considered (using Optical Microscopy and Scanning Electron Microscopy techniques). The impact of forging pressure in the microstructure of the weld joint has been studied and the variation in joint strength with varying forge pressure is analyzed. The weld joints were obtained two pair of dissimilar materials and one pair of similar materials, which are listed respectively as: Al-AA5083 & Cu-C101 (dissimilar), Aluminium alloy-3000 series & Mild Steel (dissimilar) and High Nitrogen Austenitic Stainless Steel pair (similar). Intermetallic phase formation was observed at the weld joints in the Al-Cu joint, which consequently harmed the properties of the joint (less tensile strength). It was also concluded that the increase in forging pressure led to both increment and decrement in the tensile strength of the joint depending on the similarity or dissimilarity of the components. The hardness was also observed to possess maximum as well as minimum values at the weld joint depending on the similarity or dissimilarity of workpieces. It was also suggested that a higher forging pressure is needed to obtain complete joining for the formation of the weld joint.Keywords: forging pressure, friction welding, mechanical properties, microstructure
Procedia PDF Downloads 1112688 Influence of Yield Stress and Compressive Strength on Direct Shear Behaviour of Steel Fibre-Reinforced Concrete
Authors: Bensaid Boulekbache, Mostefa Hamrat, Mohamed Chemrouk, Sofiane Amziane
Abstract:
This study aims in examining the influence of the paste yield stress and compressive strength on the behaviour of fibre-reinforced concrete (FRC) versus direct shear. The parameters studied are the steel fibre contents, the aspect ratio of fibres and the concrete strength. Prismatic specimens of dimensions 10x10x35cm made of concrete of various yield stress reinforced with steel fibres hooked at the ends with three fibre volume fractions (i.e. 0, 0.5, and 1%) and two aspects ratio (65 and 80) were tested to direct shear. Three types of concretes with various compressive strength and yield stress were tested, an ordinary concrete (OC), a self-compacting concrete (SCC) and a high strength concrete (HSC). The concrete strengths investigated include 30 MPa for OC, 60 MPa for SCC and 80 MPa for HSC. The results show that the shear strength and ductility are affected and have been improved very significantly by the fibre contents, fibre aspect ratio and concrete strength. As the compressive strength and the volume fraction of fibres increase, the shear strength increases. However, yield stress of concrete has an important influence on the orientation and distribution of the fibres in the matrix. The ductility was much higher for ordinary and self-compacting concretes (concrete with good workability). The ductility in direct shear depends on the fibre orientation and is significantly improved when the fibres are perpendicular to the shear plane. On the contrary, for concrete with poor workability, an inadequate distribution and orientation of fibres occurred, leading to a weak contribution of the fibres to the direct shear behaviour.Keywords: concrete, fibre, direct shear, yield stress, orientation, strength
Procedia PDF Downloads 5322687 Load Relaxation Behavior of Ferritic Stainless Steels
Authors: Seok Hong Min, Tae Kwon Ha
Abstract:
High-temperature deformation behavior of ferritic stainless steels such as STS 409L, STS 430J1L, and STS 429EM has been investigated in this study. Specimens with fully annealed microstructure were obtained by heat treatment. A series of load relaxation tests has been conducted on these samples at temperatures ranging from 200 to 900oC to construct flow curves in the strain rate range from 10-6 s-1 to 10-3 s-1. Strain hardening was not observed at high temperatures above 800oC in any stainless steels. Load relaxation behavior at the temperature was closely related with high-temperature mechanical properties such as the thermal fatigue and tensile behaviors. Load drop ratio of 436L stainless steel was much higher than that of the other steels. With increasing temperature, strength and load drop ratio of ferritic stainless steels showed entirely different trends.Keywords: ferritic stainless steel, high temperature deformation, load relaxation, microstructure, strain rate sensitivity
Procedia PDF Downloads 3272686 Hydrogen Induced Fatigue Crack Growth in Pipeline Steel API 5L X65: A Combined Experimental and Modelling Approach
Authors: H. M. Ferreira, H. Cockings, D. F. Gordon
Abstract:
Climate change is driving a transition in the energy sector, with low-carbon energy sources such as hydrogen (H2) emerging as an alternative to fossil fuels. However, the successful implementation of a hydrogen economy requires an expansion of hydrogen production, transportation and storage capacity. The costs associated with this transition are high but can be partly mitigated by adapting the current oil and natural gas networks, such as pipeline, an important component of the hydrogen infrastructure, to transport pure or blended hydrogen. Steel pipelines are designed to withstand fatigue, one of the most common causes of pipeline failure. However, it is well established that some materials, such as steel, can fail prematurely in service when exposed to hydrogen-rich environments. Therefore, it is imperative to evaluate how defects (e.g. inclusions, dents, and pre-existing cracks) will interact with hydrogen under cyclic loading and, ultimately, to what extent hydrogen induced failure will limit the service conditions of steel pipelines. This presentation will explore how the exposure of API 5L X65 to a hydrogen-rich environment and cyclic loads will influence its susceptibility to hydrogen induced failure. That evaluation will be performed by a combination of several techniques such as hydrogen permeation testing (ISO 17081:2014), fatigue crack growth (FCG) testing (ISO 12108:2018 and AFGROW modelling), combined with microstructural and fractographic analysis. The development of a FCG test setup coupled with an electrochemical cell will be discussed, along with the advantages and challenges of measuring crack growth rates in electrolytic hydrogen environments. A detailed assessment of several electrolytic charging conditions will also be presented, using hydrogen permeation testing as a method to correlate the different charging settings to equivalent hydrogen concentrations and effective diffusivity coefficients, not only on the base material but also on the heat affected zone and weld of the pipelines. The experimental work is being complemented with AFGROW, a useful FCG modelling software that has helped inform testing parameters and which will also be developed to ultimately help industry experts perform structural integrity analysis and remnant life characterisation of pipeline steels under representative conditions. The results from this research will allow to conclude if there is an acceleration of the crack growth rate of API 5L X65 under the influence of a hydrogen-rich environment, an important aspect that needs to be rectified instandards and codes of practice on pipeline integrity evaluation and maintenance.Keywords: AFGROW, electrolytic hydrogen charging, fatigue crack growth, hydrogen, pipeline, steel
Procedia PDF Downloads 962685 Anticorrosive Performances of “Methyl Ester Sulfonates” Biodegradable Anionic Synthetized Surfactants on Carbon Steel X 70 in Oilfields
Authors: Asselah Amel, Affif Chaouche M'yassa, Toudji Amira, Tazerouti Amel
Abstract:
This study covers two aspects ; the biodegradability and the performances in corrosion inhibition of a series of synthetized surfactants namely Φ- sodium methyl ester sulfonates (Φ-MES: C₁₂-MES, C₁₄-MES and C₁₆-MES. The biodegradability of these organic compounds was studied using the respirometric method, ‘the standard ISO 9408’. Degradation was followed by analysis of dissolved oxygen using the dissolved oxygen meter over 28 days and the results were compared with that of sodium dodecyl sulphate (SDS). The inoculum used consists of activated sludge taken from the aeration basin of the biological wastewater treatment plant in the city of Boumerdes-Algeria. In addition, the anticorrosive performances of Φ-MES surfactants on a carbon steel "X70" were evaluated in an injection water from a well of Hassi R'mel region- Algeria, known as Baremian water, and are compared to sodium dodecyl sulphate. Two technics, the weight loss and the linear polarization resistance corrosion rate (LPR) are used allowing to investigate the relationships between the concentrations of these synthetized surfactants and their surface properties, surface coverage and inhibition efficiency. Various adsorption isotherm models were used to characterize the nature of adsorption and explain their mechanism. The results show that the MES anionic surfactants was readily biodegradable, degrading faster than SDS, about 88% for C₁₂-MES compared to 66% for the SDS. The length of their carbon chain affects their biodegradability; the longer the chain, the lower the biodegradability. The inhibition efficiency of these surfactants is around 78.4% for C₁₂-MES, 76.60% for C₁₄-MES and 98.19% for C₁₆-MES and increases with their concentration and reaches a maximum value around their critical micelle concentrations ( CMCs). Scanning electron microscopy coupled to energy dispersive X-ray spectroscopy allowed to the visualization of a good adhesion of the protective film formed by the surfactants to the surface of the steel. The studied surfactants show the Langmuirian behavior from which the thermodynamic parameters as adsorption constant (Kads), standard free energy of adsorption (〖∆G〗_ads^0 ) are determined. Interaction of the surfactants with steel surface have involved physisorptions.Keywords: corrosion, surfactants, adsorption, adsorption isotherems
Procedia PDF Downloads 882684 Seismic Behaviour of RC Knee Joints in Closing and Opening Actions
Authors: S. Mogili, J. S. Kuang, N. Zhang
Abstract:
Knee joints, the beam column connections found at the roof level of a moment resisting frame buildings, are inherently different from conventional interior and exterior beam column connections in the way that forces from adjoining members are transferred into joint and then resisted by the joint. A knee connection has two distinct load resisting mechanisms, each for closing and opening actions acting simultaneously under reversed cyclic loading. In spite of many distinct differences in the behaviour of shear resistance in knee joints, there are no special design provisions in the major design codes available across the world due to lack of in-depth research on the knee connections. To understand the relative importance of opening and closing actions in design, it is imperative to study knee joints under varying shear stresses, especially at higher opening-to-closing shear stress ratios. Three knee joint specimens, under different input shear stresses, were designed to produce a varying ratio of input opening to closing shear stresses. The design was carried out in such a way that the ratio of flexural strength of beams with consideration of axial forces in opening to closing actions are maintained at 0.5, 0.7, and 1.0, thereby resulting in the required variation of opening to closing joint shear stress ratios among the specimens. The behaviour of these specimens was then carefully studied in terms of closing and opening capacities, hysteretic behaviour, and envelope curves to understand the differences in joint performance based on which an attempt to suggest design guidelines for knee joints is made emphasizing the relative importance of opening and closing actions. Specimens with relatively higher opening stresses were observed to be more vulnerable under the action of seismic loading.Keywords: Knee-joints, large-scale testing, opening and closing shear stresses, seismic performance
Procedia PDF Downloads 2132683 Study the Effect of Sensitization on the Microstructure and Mechanical Properties of Gas Tungsten Arc Welded AISI 304 Stainless Steel Joints
Authors: Viranshu Kumar, Hitesh Arora, Pradeep Joshi
Abstract:
SS 304 is Austenitic stainless steel with Chromium and Nickel as basic constituents. It has excellent corrosion resistance properties and very good weldability. Austenitic stainless steels have superior mechanical properties at high temperatures and are used extensively in a range of applications. SS 304L has wide applications in various industries viz. Nuclear, Pharmaceutical, marine, chemical etc. due to its excellent applications and ease of joining this material has become very popular for fabrication as well as weld surfacing. Austenitic stainless steels have a tendency to form chromium depleted zones at the grain boundaries during welding and heat treatment, where chromium combines with available carbon in the vicinity of the grain boundaries, to produce an area depleted in chromium, and thus becomes susceptible to intergranular corrosion. This phenomenon is known as sensitization.Keywords: sensitization, SS 304, GTAW, mechanical properties, carbideprecipitationHAZ, microstructure, micro hardness, tensile strength
Procedia PDF Downloads 3902682 Fractal Analysis of Some Bifurcations of Discrete Dynamical Systems in Higher Dimensions
Authors: Lana Horvat Dmitrović
Abstract:
The main purpose of this paper is to study the box dimension as fractal property of bifurcations of discrete dynamical systems in higher dimensions. The paper contains the fractal analysis of the orbits near the hyperbolic and non-hyperbolic fixed points in discrete dynamical systems. It is already known that in one-dimensional case the orbit near the hyperbolic fixed point has the box dimension equal to zero. On the other hand, the orbit near the non-hyperbolic fixed point has strictly positive box dimension which is connected to the non-degeneracy condition of certain bifurcation. One of the main results in this paper is the generalisation of results about box dimension near the hyperbolic and non-hyperbolic fixed points to higher dimensions. In the process of determining box dimension, the restriction of systems to stable, unstable and center manifolds, Lipschitz property of box dimension and the notion of projective box dimension are used. The analysis of the bifurcations in higher dimensions with one multiplier on the unit circle is done by using the normal forms on one-dimensional center manifolds. This specific change in box dimension of an orbit at the moment of bifurcation has already been explored for some bifurcations in one and two dimensions. It was shown that specific values of box dimension are connected to appropriate bifurcations such as fold, flip, cusp or Neimark-Sacker bifurcation. This paper further explores this connection of box dimension as fractal property to some specific bifurcations in higher dimensions, such as fold-flip and flip-Neimark-Sacker. Furthermore, the application of the results to the unit time map of continuous dynamical system near hyperbolic and non-hyperbolic singularities is presented. In that way, box dimensions which are specific for certain bifurcations of continuous systems can be obtained. The approach to bifurcation analysis by using the box dimension as specific fractal property of orbits can lead to better understanding of bifurcation phenomenon. It could also be useful in detecting the existence or nonexistence of bifurcations of discrete and continuous dynamical systems.Keywords: bifurcation, box dimension, invariant manifold, orbit near fixed point
Procedia PDF Downloads 2412681 Inhibition of Pipelines Corrosion Using Natural Extracts
Authors: Eman Alzahrani, Hala M. Abo-Dief, Ashraf T. Mohamed
Abstract:
The present work is aimed at examining carbon steel oil pipelines corrosion using three natural extracts (Eruca Sativa, Rosell and Mango peels) that are used as inhibitors of different concentrations ranging from 0.05-0.1wt. %. Two sulphur compounds are used as corrosion mediums. Weight loss method was used for measuring the corrosion rate of the carbon steel specimens immersed in technical white oil at 100ºC at various time intervals in absence and presence of the two sulphur compounds. The corroded specimens are examined using the chemical wear test, scratch test and hardness test. The scratch test is carried out using scratch loads from 0.5 Kg to 2.0 Kg. The scratch width is obtained at various scratch load and test conditions. The Brinell hardness test is carried out and investigated for both corroded and inhibited specimens. The results showed that three natural extracts can be used as environmentally friendly corrosion inhibitors.Keywords: inhibition, natural extract, oil pipelines corrosion, sulphur compounds
Procedia PDF Downloads 4982680 Characterization of Nano Coefficient of Friction through Lfm of Superhydrophobic/Oleophobic Coatings Applied on 316l Ss
Authors: Hamza Shams, Sajid Saleem, Bilal A. Siddiqui
Abstract:
This paper investigates the coefficient of friction at nano-levels of commercially available superhydrophobic/oleophobic coatings when applied over 316L SS. 316L Stainless Steel or Marine Stainless Steel has been selected for its widespread uses in structures, marine and biomedical applications. The coatings were investigated in harsh sand-storm and sea water environments. The particle size of the sand during the procedure was carefully selected to simulate sand-storm conditions. Sand speed during the procedure was carefully modulated to simulate actual wind speed during a sand-storm. Sample preparation was carried out using prescribed methodology by the coating manufacturer. The coating’s adhesion and thickness was verified before and after the experiment with the use of Scanning Electron Microscopy (SEM). The value for nano-level coefficient of friction has been determined using Lateral Force Microscopy (LFM). The analysis has been used to formulate a value of friction coefficient which in turn is associative of the amount of wear the coating can bear before the exposure of the base substrate to the harsh environment. The analysis aims to validate the coefficient of friction value as marketed by the coating manufacturers and more importantly test the coating in real-life applications to justify its use. It is expected that the coating would resist exposure to the harsh environment for a considerable amount of time. Further, it would prevent the sample from getting corroded in the process.Keywords: 316L SS, scanning electron microscopy, lateral force microscopy, marine stainless steel, oleophobic coating, superhydrophobic coating
Procedia PDF Downloads 4782679 Study of Porous Metallic Support for Intermediate-Temperature Solid Oxide Fuel Cells
Authors: S. Belakry, D. Fasquelle, A. Rolle, E. Capoen, R. N. Vannier, J. C. Carru
Abstract:
Solid oxide fuel cells (SOFCs) are promising devices for energy conversion due to their high electrical efficiency and eco-friendly behavior. Their performance is not only influenced by the microstructural and electrical properties of the electrodes and electrolyte but also depends on the interactions at the interfaces. Nowadays, commercial SOFCs are electrically efficient at high operating temperatures, typically between 800 and 1000 °C, which restricts their real-life applications. The present work deals with the objectives to reduce the operating temperature and to develop cost-effective intermediate-temperature solid oxide fuel cells (IT-SOFCs). This work focuses on the development of metal-supported solid oxide fuel cells (MS-IT-SOFCs) that would provide cheaper SOFC cells with increased lifetime and reduced operating temperature. In the framework, the local company TIBTECH brings its skills for the manufacturing of porous metal supports. This part of the work focuses on the physical, chemical, and electrical characterizations of porous metallic supports (stainless steel 316 L and FeCrAl alloy) under different exposure conditions of temperature and atmosphere by studying oxidation, mechanical resistance, and electrical conductivity of the materials. Within the target operating temperature (i.e., 500 to 700 ° C), the stainless steel 316 L and FeCrAl alloy slightly oxidize in the air and H2, but don’t deform; whereas under Ar atmosphere, they oxidize more than with previously mentioned atmospheres. Above 700 °C under air and Ar, the two metallic supports undergo high oxidation. From 500 to 700 °C, the resistivity of FeCrAl increases by 55%. But nevertheless, the FeCrAl resistivity increases more slowly than the stainless steel 316L resistivity. This study allows us to verify the compatibility of electrodes and electrolyte materials with metallic support at the operating requirements of the IT-SOFC cell. The characterizations made in this context will also allow us to choose the most suitable fabrication process for all functional layers in order to limit the oxidation of the metallic supports.Keywords: stainless steel 316L, FeCrAl alloy, solid oxide fuel cells, porous metallic support
Procedia PDF Downloads 852678 Numerical Simulation of Footing on Reinforced Loose Sand
Authors: M. L. Burnwal, P. Raychowdhury
Abstract:
Earthquake leads to adverse effects on buildings resting on soft soils. Mitigating the response of shallow foundations on soft soil with different methods reduces settlement and provides foundation stability. Few methods such as the rocking foundation (used in Performance-based design), deep foundation, prefabricated drain, grouting, and Vibro-compaction are used to control the pore pressure and enhance the strength of the loose soils. One of the problems with these methods is that the settlement is uncontrollable, leading to differential settlement of the footings, further leading to the collapse of buildings. The present study investigates the utility of geosynthetics as a potential improvement of the subsoil to reduce the earthquake-induced settlement of structures. A steel moment-resisting frame building resting on loose liquefiable dry soil, subjected to Uttarkashi 1991 and Chamba 1995 earthquakes, is used for the soil-structure interaction (SSI) analysis. The continuum model can simultaneously simulate structure, soil, interfaces, and geogrids in the OpenSees framework. Soil is modeled with PressureDependentMultiYield (PDMY) material models with Quad element that provides stress-strain at gauss points and is calibrated to predict the behavior of Ganga sand. The model analyzed with a tied degree of freedom contact reveals that the system responses align with the shake table experimental results. An attempt is made to study the responses of footing structure and geosynthetics with unreinforced and reinforced bases with varying parameters. The result shows that geogrid reinforces shallow foundation effectively reduces the settlement by 60%.Keywords: settlement, shallow foundation, SSI, continuum FEM
Procedia PDF Downloads 1852677 The Impact of Childhood Cancer on the Quality of Life of Survivor: A Qualitative Analysis of Functionality and Participation
Authors: Catarina Grande, Barbara Mota
Abstract:
The main goal of the present study was to understand the impact of childhood cancer on the quality of life of survivors and the extent to which oncologic disease affects the functionality and participation of survivors at the present time, compared to the time of diagnosis. Six survivors of pediatric cancer participated in the study. Participants were interviewed using a semi-structured interview, adapted from two instruments present in the literature - QALY and QLACS - and piloted through a previous study. This study is based on a qualitative approach using content analysis, allowing the identification of categories and subcategories. Subsequently, the correspondence between the units of meaning and the codes in the International Classification of Functioning, Disability, and Health for Children and Young, which contributed to a more detailed analysis of the impact on the quality of life of survivors in relation to the domains under study. The results showed significant changes between the moment of diagnosis and the present moment, concretely at the microsystem of the survivor. Regarding functionality and participation, the results show that the functions of the body are the most affected domain, emphasizing the emotional component that currently has a greater impact on the quality of life of survivors. The present study allowed identifying a set of codes for the development of a CIF-CJ core set for pediatric cancer survivors. He also indicated the need for future studies to validate and deepen these issues.Keywords: cancer, participation, quality of life, survivor
Procedia PDF Downloads 2302676 Analyzing Oil Seeps Manifestations and Petroleum Impregnation in Northwestern Tunisia From Aliphatic Biomarkers and Statistical Data
Authors: Sawsen Jarray, Tahani Hallek, Mabrouk Montacer
Abstract:
The tectonically damaged terrain in Tunisia's Northwest is seen in the country's numerous oil leaks. Finding a genetic link between these oil seeps and the area's putative source rocks is the goal of this investigation. Here, we use aliphatic biomarkers assessed by GC-MS to describe the organic geochemical data of 18 oil seeps samples and 4 source rocks (M'Cherga, Fahdene, Bahloul, and BouDabbous). In order to establish correlations between oil and oil and oil and source rock, terpanes, hopanes, and steranes biomarkers were identified. The source rocks under study were deposited in a marine environment and were suboxic, with minor signs of continental input for the M'Cherga Formation. There is no connection between the Fahdene and Bahloul source rocks and the udied oil seeps. According to the biomarkers C27 18-22,29,30trisnorneohopane (Ts) and C27 17-22,29,30-trisnorhopane (Tm), these source rocks are mature and have reached the oil window. Regarding oil seeps, geochemical data indicate that, with the exception of four samples that showed some continental markings, the bulk of samples were deposited in an open marine environment. These most recent samples from oil seeps have a unique lithology (marl) that distinguishes them from the others (carbonate). There are two classes of oil seeps, according to statistical analysis of relationships between oil and oil and oil and source rocks. The first comprised samples that showed a positive connection with carbonate-lithological and marine-derived BouDabbous black shales. The second is a result of M'Cherga source rock and is made up of oil seeps with remnants of the terrestrial environment and a lithology with a marl trend. The Fahdene and Bahloul source rocks have no connection to the observed oil seeps. There are two different types of hydrocarbon spills depending on their link to tectonic deformations (oil seeps) and outcropping mature source rocks (oil impregnations), in addition to the existence of two generations of hydrocarbon spills in Northwest Tunisia (Lower Cretaceous/Ypresian).Keywords: petroleum seeps, source rocks, biomarkers, statistic, Northern Tunisia
Procedia PDF Downloads 582675 Origins of the Tattoo: Decoding the Ancient Meanings of Terrestrial Body Art to Establish a Connection between the Natural World and Humans Today
Authors: Sangeet Anand
Abstract:
Body art and tattooing have long been practiced as a form of self-expression for centuries, and this study studies and analyzes the pertinence of tattoo culture in our everyday lives and ancient past. Individuals of different cultures represent ideas, practices, and elements of their cultures through symbolic representation. These symbols come in all shapes and sizes and can be as simple as the makeup you put on every day to something more permanent such as a tattoo. In the long run, these individuals who choose to display art on their bodies are seeking to express their individuality. In addition, these visuals are ultimately a reflection of our own appropriate cultures deem as beautiful, important, and powerful to the human eye. They make us known to the world and give us a plausible identity in an ever-changing world. We have lived through and seen a rise in hippie culture today. This type of bodily decoration displayed by this fad has made it seem as though body art is a visual language that is relatively new. But quite to the contrary, it is not. Through cultural symbolic exploration, we can answer key questions to ideas that have been raised for centuries. Through careful, in-depth interviews, this study takes a broad subject matter-art, and symbolism-and culminates it into a deeper philosophical connection between the world and its past. The basic methodologies used in this sociocultural study include interview questionnaires and textual analysis, which encompass a subject and interviewer as well as source material. The major findings of this study contain a distinct connection between cultural heritage and the day-to-day likings of an individual. The participant that was studied during this project demonstrated a clear passion for hobbies that were practiced even by her ancestors. We can conclude, through these findings, that there is a deeper cultural connection between modern day humans, the first humans, and the surrounding environments. Our symbols today are a direct reflection of the elements of nature that our human ancestors were exposed to, and, through cultural acceptance, we can adorn ourselves with these representations to help others identify our pasts. Body art embraces the different aspects of different cultures and holds significance, tells stories, and persists, even as the human population rapidly integrates. With this pattern, our human descendents will continue to represent their cultures and identities in the future. Body art is an integral element in understanding how and why people identify with certain aspects of life over others and broaden the scope for conducting more analysis cross-culturally.Keywords: natural, symbolism, tattoo, terrestrial
Procedia PDF Downloads 101