Processing of Al-19.4Si alloy by high intensive electron beam has been carried out and multiple increase in fatigue life of the material has been revealed. Investigations of structure and surface modified layer destruction of Al-19.4Si alloy subjected to multicycle fatigue tests to fracture have been carried out by methods of scanning electron microscopy. The factors responsible for the increase of fatigue life of Al-19.4Si alloy have been revealed and analyzed.

Keywords: Al-19.4Si alloy, high intensive electron beam, multicycle fatigue, structure

Procedia PDF Downloads 548

Authors: B. Daheche, M. T. Hannachi, H. Djebaili

Abstract:

In this approach, we tried to describe the flare test tubes welded by high frequency induction HF, and its experimental application. The test is carried out ENTTPP (National company of pipe mill and processing of flat products). Usually, the final products (tube) undergo a series of destructive testing (CD) in order to see the efficiency of welding. This test performed on sections of pipe with a length defined in the notice is made under a determined effort (pressure), which depends on its share of other parameters namely mechanical (fracture resistance) and geometry (thickness tube, outside diameter), the variation of this effort is well researched and recorded.

Keywords: flare, destructive testing, pressure, drafts tube, tube finished

Procedia PDF Downloads 313

Authors: Ashraf Nawaz Khan, R. Alagirusamy, Apurba Das, Puneet Mahajan

Abstract:

The thermoplastic-based fibre composites are acquiring a market sector of conventional as well as thermoset composites. However, replacing the thermoset with a thermoplastic composite has never been an easy task. The inherent high viscosity of thermoplastic resin reveals poor interface properties. In this work, a homo-polymer towpreg is produced through an electrostatic powder spray coating methodology. The produced flexible towpreg offers a low melt-flow distance during the consolidation of the laminate. The reduced melt-flow distance demonstrates a homogeneous fibre/matrix distribution (and low void content) on consolidation. The composite laminate has been fabricated with two manufacturing techniques such as conventional film stack (FS) and powder-coated (PC) technique. This helps in understanding the distinct response of produced laminates on applying load since the laminates produced through the two techniques are comprised of the same constituent fibre and matrix (constant fibre volume fraction). The changed behaviour is observed mainly due to the different fibre/matrix configurations within the laminate. The interface adhesion influences the load transfer between the fibre and matrix. Therefore, it influences the elastic, plastic, and failure patterns of the laminates. Moreover, the effect of preform geometries (plain weave and satin weave structure) are also studied for corresponding composite laminates in terms of various mechanical properties. The fracture analysis is carried out to study the effect of resin at the interlacement points through micro-CT analysis. The PC laminate reveals a considerably small matrix-rich and deficient zone in comparison to the FS laminate. The different load tensile, shear, fracture toughness, and drop weight impact test) is applied to the laminates, and corresponding damage behaviour is analysed in the successive stage of failure. The PC composite has shown superior mechanical properties in comparison to the FS composite. The damage that occurs in the laminate is captured through the SEM analysis to identify the prominent mode of failure, such as matrix cracking, fibre breakage, delamination, debonding, and other phenomena.

Keywords: composite, damage, fibre, manufacturing

Procedia PDF Downloads 133

Authors: S. Lecheb, A. Chellil, H. Mechakra, S. Attou, H. Kebir

Abstract:

Although leaf springs are one of the oldest suspension components they are still frequently used, especially in commercial vehicles. Being able to capture the leaf spring characteristics is of significant importance for vehicle handling dynamics studies. The main function of leaf spring is not only to support vertical load but also to isolate road induced vibrations. It is subjected to millions of load cycles leading to fatigue failure. It needs to have excellent fatigue life. The objective of this work is its use of Abaqus software to locate the most stressed areas and predict the areas in which it occurs in fatigue and crack of leaf spring and calculate the stress and frequencies of this model.

Keywords: leaf spring, crack, stress, natural frequencies

Procedia PDF Downloads 455

Authors: Amin Masoumiganjgah, Luke Salmon, Julianne Burnton, Fahimeh Bagheri, Gavin Lenton, S. L. Ezekial Tan

Abstract:

Introduction: The incidence of proximal biceps tenodesis and acute distal biceps repair is increasing, and rehabilitation protocols following both are variable. Golf is a popular sport within Australia, and the Gold Coast has become a Mecca for golfers, with more courses per capita than anywhere else in the world. Currently, there are no clear guidelines regarding return to golf play following biceps procedures. The aim of this study was to determine biceps brachii activation during the golf swing through electromyographic analysis, and subsequently, aid in rehabilitation guidelines and return to golf following tenodesis and repair. Methods: Subjects were amateur golfers with no previous upper limb surgery. Surface electromyography (EMG) and high-speed video recording were used to analyse activation of the left and right biceps brachii and the anterior deltoid during the golf swing. Each participant’s maximum voluntary contraction (MVC) was recorded, and they were then required to hit a golf ball aiming for specific distances of 2, 50, 100 and 150 metres at a driving range. Noraxon myoResearch and Matlab were used for data analysis. Mean % MVC was calculated for leading and trailing arms during the full swing and its’ 4 phases: back-swing, acceleration, early follow-through and late follow-through. Results: 12 golfers (2 female and 10 male), participated in the study. Median age was 27 (25 – 38), with all being right handed. Over all distances, the mean activation of the short and long head of biceps brachii was < 10% through the full swing. When breaking down the 50, 100 and 150m swing into phases, mean MVC activation was lowest in backswing (5.1%), followed by acceleration (9.7%), early follow-through (9.2%), and late follow-through (21.4%). There was more variation and slightly higher activation in the right biceps (trailing arm) in backswing, acceleration, and early follow-through; with higher activation in the leading arm in late follow-through (25.4% leading, 17.3% trailing). 2m putts resulted in low MVC values (3.1% ) with little variation across swing phases. There was considerable individual variation in results – one tense subject averaged 11.0% biceps MVC through the 2m putting stroke and others recorded peak mean MVC biceps activations of 68.9% at 50m, 101.3% at 100m, and 111.3% at 150m. Discussion: Previous studies have investigated the role of rotator cuff, spine, and hip muscles during the golf swing however, to our knowledge, this is the first study that investigates the activation of biceps brachii. Many rehabilitation programs following a biceps tenodesis or repair allow active range against gravity and restrict strengthening exercises until 6 weeks, and this does not appear to be associated with any adverse outcome. Previous studies demonstrate a range of < 10% MVC is similar to the unloaded biceps brachii during walking(1), active elbow flexion with the hand positioned either in pronation or supination will produce MVC < 20% throughout range(2) and elbow flexion with a 4kg dumbbell can produce mean MVC’s of around 40%(3). Our study demonstrates that increasing activation is associated with the leading arm, increasing shot distance and the late follow-through phase. Although the cohort mean MVC of the biceps brachii is <10% through the full swing, variability is high and biceps activation reach peak mean MVC’s of over 100% in different swing phases for some individuals. Given these EMG values, caution is advised when advising patients post biceps procedures to return to long distance golf shots, particularly when the leading arm is involved. Even though it would appear that putting would be as safe as having an unloaded hand out of a sling following biceps procedures, the variability of activation patterns across different golfers would lead us to caution against accelerated golf rehabilitation in those who may be particularly tense golfers. The 50m short iron shot was too long to consider as a chip shot and more work can be done in this area to determine the safety of chipping.

Keywords: electromyographic analysis, biceps brachii rupture, golf swing, tendon surgery

Procedia PDF Downloads 72

Authors: Michael Kassner

Abstract:

Elevated-temperature creep tests were performed on additively manufactured (AM) Inconel 625 over a relatively wide range of stress. The behavior was compared to conventional wrought alloy. It was found that the steady-state creep rates of the AM alloys were comparable, or even more favorable, than that of the wrought Inconel. However, the ductility of the AM alloy was significantly less than the wrought alloy. The ductility however was recovered with hot isostatic pressing (HIP) of the AM specimens. The basis for the loss and recovery of the ductility will be discussed in terms of the differences in the details of the microstructures. In summary, it appears that HIP AM Inconel 625, over the long-term testing of a year, has very favorable mechanical properties compared to the conventional alloy.

Keywords: Inconel, creep, additive, manufacturing

Procedia PDF Downloads 158

Authors: Kumudini Achchi

Abstract:

India, being known for its rich cultural values has given a special place to women who are also been victims of humiliation, torture, and exploitation. The major share of Human Trafficking goes to sex trafficking which is recognised as world’s second most huge social evil. The original form of sex trafficking in India is prostitution with and without religious sanction. Today the situation of such women reached as an issue of human rights where they rights are denied severely. This situation demanded intervention to protect them from the exploitative situation. NGO are the proactive initiatives which offer support to the exploited women in sex trade. To understand the intervention programs of NGOs in South India, a study was conducted covering four states and a union territory considering 32 NGOs based on their preparedness to participate in the research study. Descriptive and diagnostic research design was adopted along with interview schedule as a tool for collecting data. The study reveals that these NGOs believes in the possibility of mainstreaming commercially sexually exploited women and found adopted seven different programs in the process such as rescue, rehabilitation, reintegration, prevention, developmental, advocacy and research. Each area involves different programs to reach and prepare the exploited women towards mainstreamed society which has been discussed in the paper. Implementation of these programs is not an easy task for the organizations rather they are facing hardships in the areas such as social, legal, financial, political which are hindering the successful operations. Rescue, advocacy, and research are the least adopted areas by the NGOs because of lack of support as well as knowledge in the area. Rehabilitation stands as the most adopted area in implementation. The paper further deals with the challenges in the implementation of the programs as well as the remedial measures in social work point of view having Indian cultural background.

Keywords: NGOs, commercially sexually exploited women, programmes, South India

Procedia PDF Downloads 246

Authors: Jifeng Zhang , Yongpeng Lei

Abstract:

Continuous carbon fiber reinforced polyamide 6 (CF/PA6) composites are potential for application in the automotive industry due to their high specific strength and stiffness. However, PA6 resin is sensitive to the moisture in the hydrothermal environment and CF/PA6 composites might undergo several physical and chemical changes, such as plasticization, swelling, and hydrolysis, which induces a reduction of mechanical properties. So far, little research has been reported on the assessment of the effects of hydrothermal aging on the mechanical properties of continuous CF/PA6 composite. This study deals with the effects of hydrothermal aging on moisture absorption and mechanical properties of polyamide 6 (PA6) and polyamide 6 reinforced with continuous carbon fibers composites (CF/PA6) by immersion in distilled water at 30 ℃, 50 ℃, 70 ℃, and 90 ℃. Degradation of mechanical performance has been monitored, depending on the water absorption content and the aging temperature. The experimental results reveal that under the same aging condition, the PA6 resin absorbs more water than the CF/PA6 composite, while the water diffusion coefficient of CF/PA6 composite is higher than that of PA6 resin because of interfacial diffusion channel. In mechanical properties degradation process, an exponential reduction in tensile strength and elastic modulus are observed in PA6 resin as aging temperature and water absorption content increases. The degradation trend of flexural properties of CF/PA6 is the same as that of tensile properties of PA6 resin. Moreover, the water content plays a decisive role in mechanical degradation compared with aging temperature. In contrast, hydrothermal environment has mild effect on the tensile properties of CF/PA6 composites. The elongation at breakage of PA6 resin and CF/PA6 reaches the highest value when their water content reaches 6% and 4%, respectively. Dynamic mechanical analysis (DMA) and scanning electron microscope (SEM) were also used to explain the mechanism of mechanical properties alteration. After exposed to the hydrothermal environment, the Tg (glass transition temperature) of samples decreases dramatically with water content increase. This reduction can be ascribed to the plasticization effect of water. For the unaged specimens, the fibers surface is coated with resin and the main fracture mode is fiber breakage, indicating that a good adhesion between fiber and matrix. However, with absorbed water content increasing, the fracture mode transforms to fiber pullout. Finally, based on Arrhenius methodology, a predictive model with relate to the temperature and water content has been presented to estimate the retention of mechanical properties for PA6 and CF/PA6.

Keywords: continuous carbon fiber reinforced polyamide 6 composite, hydrothermal aging, Arrhenius methodology, interface

Procedia PDF Downloads 117

Authors: Elena Kokkoni, Prasanna Kannappan, Ashkan Zehfroosh, Effrosyni Mavroudi, Kristina Strother-Garcia, James C. Galloway, Jeffrey Heinz, Rene Vidal, Herbert G. Tanner

Abstract:

Early immobility affects the motor, cognitive, and social development. Current pediatric rehabilitation lacks the technology that will provide the dosage needed to promote mobility for young children at risk. The addition of socially assistive robots in early interventions may help increase the mobility dosage. The aim of this study is to examine the feasibility of an early intervention paradigm where non-walking infants experience independent mobility while socially interacting with robots. A dynamic environment is developed where both the child and the robot interact and learn from each other. The environment involves: 1) a range of physical activities that are goal-oriented, age-appropriate, and ability-matched for the child to perform, 2) the automatic functions that perceive the child’s actions through novel activity recognition algorithms, and decide appropriate actions for the robot, and 3) a networked visual data acquisition system that enables real-time assessment and provides the means to connect child behavior with robot decision-making in real-time. The environment was tested by bringing a two-year old boy with Down syndrome for eight sessions. The child presented delays throughout his motor development with the current being on the acquisition of walking. During the sessions, the child performed physical activities that required complex motor actions (e.g. climbing an inclined platform and/or staircase). During these activities, a (wheeled or humanoid) robot was either performing the action or was at its end point 'signaling' for interaction. From these sessions, information was gathered to develop algorithms to automate the perception of activities which the robot bases its actions on. A Markov Decision Process (MDP) is used to model the intentions of the child. A 'smoothing' technique is used to help identify the model’s parameters which are a critical step when dealing with small data sets such in this paradigm. The child engaged in all activities and socially interacted with the robot across sessions. With time, the child’s mobility was increased, and the frequency and duration of complex and independent motor actions were also increased (e.g. taking independent steps). Simulation results on the combination of the MDP and smoothing support the use of this model in human-robot interaction. Smoothing facilitates learning MDP parameters from small data sets. This paradigm is feasible and provides an insight on how social interaction may elicit mobility actions suggesting a new early intervention paradigm for very young children with motor disabilities. Acknowledgment: This work has been supported by NIH under grant #5R01HD87133.

Keywords: activity recognition, human-robot interaction, machine learning, pediatric rehabilitation

Procedia PDF Downloads 287

Authors: Fils Olivier Kamanzi

Abstract:

This research Paper shows that materials CFRP were used to rehabilitate 9 Beams and retrofitting of 9 Beams with size (125x250x2300) mm each for M50 grade of concrete with 20% of Volume of Cement replaced by GGBS as a mineral Admixture. Superplasticizer (ForscoConplast SP430) used to reduce the water-cement ratio and maintaining good workability of fresh concrete (Slump test 57mm). Concrete Mix ratio 1:1.56:2.66 with a water-cement ratio of 0.31(ACI codebooks). A sample of 6cubes sized (150X150X150) mm, 6cylinders sized (150ФX300H) mm and 6Prisms sized (100X100X500) mm were cast, cured, and tested for 7,14&28days by compressive, tensile and flexure test; finally, mix design reaches the compressive strength of 59.84N/mm2. 21 Beams were cast and cured for up to 28 days, 3Beams were tested by a two-point loading machine as Control beams. 9 Beams were distressed in flexure by adopting failure up to final Yielding point under two-point loading conditions by taking 90% off Ultimate load. Three sets, each composed of three distressed beams, were rehabilitated by using CFRP sheets, one, two & three layers, respectively, and after being retested up to failure mode. Another three sets were freshly retrofitted also by using CFRP sheets one, two & three layers, respectively, and being tested by a two-point load method of compression strength testing machine. The aim of this study is to determine the flexural Strength & behaviors of repaired and retrofitted Beams by CFRP sheets for gaining good strength and considering economic aspects. The results show that rehabilitated beams increase its strength 47 %, 78 % & 89 %, respectively, to thickness of CFRP sheets and 41%, 51 %& 68 %, respectively too, for retrofitted Beams. The conclusion is that three layers of CFRP sheets are the best applicable in repairing and retrofitting the bonded beams method.

Keywords: retrofitting, rehabilitation, cfrp, rcc beam, flexural strength and behaviors, ggbs, and epoxy resin

Procedia PDF Downloads 100

Authors: Hardisiswo Soedjana, Inne Caroline

Abstract:

Deep dermal or full thickness burns are inevitably lead to post-burn contractures. These contractures remain to be one of the most concerning late complications of burn injuries. Surgical management includes releasing the contracture followed by resurfacing the defect accompanied by post-operative rehabilitation. Optimal treatment of post-burn contractures depends on the characteristics of the contractures. This study is aimed to describe clinical characteristics, problems, and management of post-burn contractures in adults and children. A retrospective analysis was conducted from medical records of patients suffered from contractures after burn injuries admitted to Hasan Sadikin general hospital between January 2016 and January 2018. A total of 50 patients with post burn contractures were included in the study. There were 17 adults and 33 children. Most patients were male, whose age range within 15-59 years old and 5-9 years old. Educational background was mostly senior high school among adults, while there was only one third of children who have entered school. Etiology of burns was predominantly flame in adults (82.3%); whereas flame and scald were the leading cause of burn injury in children (11%). Based on anatomical regions, hands were the most common affected both in adults (35.2%) and children (48.5%). Contractures were identified in 6-12 months since the initial burns. Most post-burn hand contractures were resurfaced with full-thickness skin graft (FTSG) both in adults and children. There were 11 patients who presented with recurrent contracture after previous history of contracture release. Post-operative rehabilitation was conducted for all patients; however, it is important to highlight that it is still challenging to control splinting and exercise when patients are discharged and especially the compliance in children. In order to improve quality of life in patients with history of deep burn injuries, prevention of contractures should begin right after acute care has been established. Education for the importance of splinting and exercise should be administered as comprehensible as possible for adult patients and parents of pediatric patients.

Keywords: burn, contracture, education, exercise, splinting

Procedia PDF Downloads 118

Authors: Ahmed R. Z. Baghdadi,  Mona H. Gamal Eldein

Abstract:

Background: With the perceived pain and poor function experienced following knee arthroplasty, patients usually feel unsatisfied. Yet, a controversy still persists on the appropriate operative technique that doesn’t affect proprioception much. Purpose: This study compared the effects of Cruciate Retaining (CR) and Posterior Stabilized (PS) total knee arthroplasty (TKA on dynamic balance, pain and functional performance following rehabilitation. Methods: Thirty patients with CRTKA (group I), thirty with PSTKA (group II) and fifteen indicated for arthroplasty but weren’t operated on yet (group III) participated in the study. The mean age was 54.53±3.44, 55.13±3.48 and 55.33±2.32 years and BMI 35.7±3.03, 35.7±1.99 and 35.73±1.03 kg/m2 for group I, II, and III respectively. The Berg Balance Scale (BBS), WOMAC pain subscale and Timed-Up-and-Go (TUG) and Stair-Climbing (SC) tests were used for assessment. Assessments were conducted four weeks pre- and post-operatively, three, six and twelve months post-operatively with the control group being assessed at the same time intervals. The post-operative rehabilitation involved hospitalization (1st week), home-based (2nd-4th weeks), and outpatient clinic (5th-12th weeks) programs, follow-up to all groups for twelve months. Results: The Mixed design MANOVA revealed that group I had significantly lower pain scores and SC time compared with group II three, six and twelve months post-operatively. Moreover, the BBS scores increased significantly and the pain scores and TUG and SC time decreased significantly six months post-operatively compared with four weeks pre- and post-operatively and three months post-operatively in group I and II with the opposite being true four weeks post-operatively. But no significant differences in BBS scores, pain scores and TUG and SC time between six and twelve months post-operatively in group I and II. Interpretation/Conclusion: CRTKA is preferable to PSTKA, possibly due to the preserved human proprioceptors in the un-excised PCL.

Keywords: dynamic balance, functional performance, knee arthroplasty, long-term

Procedia PDF Downloads 405

Authors: Alfred Hasanaj , Ardit Gjeta, Miranda Kullolli

Abstract:

The approach in analyzing defects on different pipe lines is conducted through Failure Assessment Diagram (FAD). These methods of analyses have further extended in recent years. This approach is used to identify and stress out a solution for the defects which randomly occur with gas pipes such are corrosion defects, gauge defects, and combination of defects where gauge and dents are included. Few of the defects are to be analyzed in this paper where our main focus will be the fracture of cast Iron pipes, elastic-plastic failure and plastic collapse of X52 steel pipes for gas transport. We need to conduct a calculation of probability of the defects in order to predict and avoid such costly defects.

Keywords: defects, failure assessment diagrams, steel pipes, safety factor

Procedia PDF Downloads 443

Authors: Nisha James, Shubha Ranganathan

Abstract:

Sex trafficking is a type of human trafficking involving prostitution of individuals for sexual exploitation. The stigma and social isolation they face in the society often makes it difficult for them to become rehabilitated from trafficking, due to which many of them continue in prostitution for years after being sex trafficked. Victims are subjected to violations of their fundamental human rights, deprived of basic medical facilities and undergo long-term abuse. This paper focuses on the role of Non-Governmental Organizations (NGOs) in the rescue and rehabilitation of victims of sex trafficking. Semi-structured interviews were conducted with 26 survivors of sex trafficking, five sex workers and 14 non-community staff members of a project running NGO in the city of Chennai in South India. Chennai has a number of NGOs that are involved in HIV/AIDS awareness and prevention programs. In many cases, rehabilitation of sex trafficking victims is also a mandate of these NGOs. This particular NGO was also involved in development activities towards the eradication of HIV/AIDS. For instance, they were engaged in inculcating safe sex practices among high-risk groups such as sex workers or in fighting for sex worker rights. The study found that the NGO’s role in combatting sex trafficking is overrun by the way it approaches these issue related to HIV/AIDS. Further, their activities are dependent solely on funding. Given that gradually, international funding for HIV/AIDS has slowly been withdrawn, there have been problems such as reduction in the salary of the project staff, the outreach workers and peer educators, many of whom were survivors of sex trafficking who have been able to survive on their wages instead of continuing in prostitution. Therefore, till date, the project funding has helped in making them aware of the health and social consequences of continuing in prostitution, and in supporting them socioeconomically, but the lack of funding may also lead the NGO workers into a state of unemployment, poverty and eventually into being re-trafficked. The study concludes by pointing to the need for disengaging anti-trafficking efforts from the HIV/AIDS related programs.

Keywords: non-governmental organization role, non-governmental organization staff, sex trafficking survivors, sex workers

Procedia PDF Downloads 297

Authors: M. Hirani, M. Devine, O. Obisesan, C. Bryant

Abstract:

Introduction: The use of four or more implants to support a fixed prosthesis in the edentulous mandible is well documented, with high levels of clinical outcomes recorded. Despite this, the use of three implant-supported fixed prostheses offers the potential to deliver a more cost-effective method of oral rehabilitation in the lower arch, an important consideration given that edentulism is most prevalent in low-income subpopulations. The purpose of this study aimed to evaluate the implant and prosthetic survival rate, changes in marginal bone level, and patient satisfaction associated with a three-implant-supported fixed prosthesis for rehabilitation of the edentulous mandible over a follow-up period of at least one year. Methods: A comprehensive literature search was performed to evaluate studies that met the selection criteria. The information extracted included the study design and population, participant demographics, observation period, loading protocol, and the number of implants placed together with the required outcome measures. Mean values and standard deviations (SD) were calculated using SPSS® (IBM Corporation, New York, USA), and the level of statistical significance across all comparative studies described was set at P < 0.05. Results: The eligible studies included a total of 1968 implants that were placed in 652 patients. The subjects ranged in age from 33-89 years, with a mean of 63.2 years. The mean cumulative implant and prosthetic survival rates were 95.5% and 96.2%, respectively, over a mean follow-up period of 3.25 years. The mean marginal bone loss recorded was 1.04 mm, and high patient satisfaction rates were reported across the studies. Conclusion: Current evidence suggests that a three implant-supported fixed prosthesis for the edentulous mandible is a successful treatment strategy presenting high implant and prosthetic survival rates over the short-to-medium term. Further well-designed controlled clinical trials are required to evaluate longer-term outcomes, with supplemental data correlating implant dimensions and prosthetic design.

Keywords: implants, mandible, fixed, prosthesis

Procedia PDF Downloads 127

Authors: Surjit Angra, Gajanan Rane, Vinod Kumar, Sushma Rani

Abstract:

This paper presents metallurgical investigation of failed helical gear of diesel engine gear box used in a car. The failure had occurred near the bottomland of the tooth spacing. The failed surface was studied under Scanning Electron Microscope (SEM) and also visually investigated. The images produced through SEM at various magnifications were studied. Detailed metallurgical study indicates that failure was due to foreign material inclusion which is a casting defect. Further study also revealed pitting, spalling and inter-granular fracture as the causes of gear failure.

Keywords: helical gear, scanning electron microscope, casting defect, pitting

Procedia PDF Downloads 445

Authors: Parisa Hasanpour, Bahram Borooghani, Vahid Asadi

Abstract:

In the current research, a catastrophic failure of a 304 stainless steel flange at pipeline transportation of ethylene in a petrochemical refinery was studied. Cracking was found in the flange after about 78840h service. Through the chemical analysis, tensile tests in addition to microstructural analysis such as optical microscopy and Scanning Electron Microscopy (SEM) on the failed part, it found that the fatigue was responsible for the fracture of the flange, which originated from bumps and depressions on the outer surface and propagated by vibration caused by the working condition.

Keywords: failure analysis, 304 stainless steel, fatigue, flange, petrochemical refinery

Procedia PDF Downloads 63

Authors: Hee Yong Kang, Hyeon Ho Shin, Jung Cheol Yoo, Il Taek Lee, Sung Mo Yang

Abstract:

Lightweight technology using composites is being developed for vehicle seat structures, and its design must meet the safety requirements. According to the Federal Motor Vehicle Safety Standard (FMVSS) 207 seating systems test procedure, the back moment load is applied to the seat back frame structure for the safety evaluation of the vehicle seat. The seat back frame using the composites is divided into three parts: upper part frame, and left- and right-side frame parts following the manufacturing process. When a rear moment load is applied to the seat back frame, the side frame receives the bending load and the torsional load at the same time. This results in the largest loaded strength. Therefore, strength test of the component unit is required. In this study, a component test method based on the FMVSS 207 seating systems test procedure was proposed for the strength analysis of bending load and torsional load of the automotive Bulk Molding Compound (BMC) Seat Back Side Frame. Moreover, strength evaluation according to the carbon band reinforcement was performed. The back-side frame parts of the seat that are applied to the test were manufactured through BMC that is composed of vinyl ester Matrix and short carbon fiber. Then, two kinds of reinforced and non-reinforced parts of carbon band were formed through a high-temperature compression molding process. In addition, the structure that is applied to the component test was constructed by referring to the FMVSS 207. Then, the bending load and the torsional load were applied through the displacement control to perform the strength test for four load conditions. The results of each test are shown through the load-displacement curves of the specimen. The failure strength of the parts caused by the reinforcement of the carbon band was analyzed. Additionally, the fracture characteristics of the parts for four strength tests were evaluated, and the weakness structure of the back-side frame of the seat structure was confirmed according to the test conditions. Through the bending and torsional strength test methods, we confirmed the strength and fracture characteristics of BMC Seat Back Side Frame according to the carbon band reinforcement. And we proposed a method of testing the part strength of a seat back frame for vehicles that can meet the FMVSS 207.

Keywords: seat back frame, bending and torsional strength, BMC (Bulk Molding Compound), FMVSS 207 seating systems

Procedia PDF Downloads 205

Authors: Razali Bin Abidin

Abstract:

This paper presents the development of a portable water jet cutter for soft materials such as meat. Twelve geometries of nozzles were simulated using finite element method. Water pressure was set to 1500 lb/in². Through the simulation, highest average water output speed was 133.04 m/s. The nozzle was fabricated from Al - alloy 5052 with the Factor of Safety~ 3. This indicates that the nozzle made of Al-alloy 5052 is capable of performing the cutting process without any fracture. Preliminary design of mobile water jet hand tool is presented at the end of this paper.

Keywords: water jet, finite element, Al-alloy 5052, nozzle geometry

Procedia PDF Downloads 369

Authors: Hong Je Kang, Young Chae Choi, Jin Sung Park, Isac Kim

Abstract:

Purpose: Osteoporotic fractures are an important among postmenopausal women. When osteoporotic distal radial fractures occur, osteoporosis must be treated to prevent the hip and spine fractures. Intravenous injection of Zoledronic acid is expected to improve preventing osteoporotic fractures. Many articles reported the effect of intravenous Zoledronic acid to BMD of the hip and spine fracture or non-fracture patients with low BMD. However, that with distal radial fractures has rarely been reported. Therefore, the authors decided to study the effect of Zoledronic acid in BMD score, bone union, and bone turnover markers in the patients who underwent volar plating due to osteoporotic distal radial fractures. Materials: From April 2018 to May 2022, postmenopausal women aged 55 years or older who had osteoporotic distal radial fractures and who underwent surgical treatment using volar plate fixation were included. Zoledronic acid (5mg) was injected intravenously between 3 and 5 days after surgery. BMD scores after 1 year of operation were compared with the initial scores. Bone turnover markers were measured before surgery, after 3 months, and after 1 year. Radiological follow-up was performed every 2 weeks until the bone union and at 1 year postoperatively. Clinical outcome indicators were measured one year after surgery, and the occurrence of side effects was observed. Result: Total of 23 patients were included, with a lumbar BMD T score of -2.89±0.2 before surgery to -2.27±0.3 one year after surgery (p=0.012) and a femoral neck BMD T score of -2.45±0.3 before surgery to -2.36±0.3 (p=0.041) after one year, and all were statistically significant. Measured as bone resorption markers, serum CTX-1 was 337.43±10.4 pg/mL before surgery, 160.86±8.7 pg/mL (p=0.022) after three months, and 250.12±12.7 pg/mL (p=0.031) after one year. Urinary NTX-1 was 39.24±2.2 ng/mL before surgery, 24.46±1.2 ng/mL (p=0.014) after three months and 30.35±1.6 ng/mL (p=0.042) after one year. Measured as bone formation markers, serum osteocalcin was 13.04±1.1 ng/mL before surgery, 8.84±0.7 ng/mL (p=0.037) after 3 months and 11.1±0.4 ng/mL (p=0.026) after one year. Serum bone-specific ALP was 11.24±0.9 IU/L before surgery, 8.25±0.9 IU/L (p=0.036) after three months, and 10.2±0.9 IU/L (p=0.027) after one year. All were statistically significant. All cases showed bone union within an average of 6.91±0.3 weeks without any signs of failure. Complications were found in 5 out of 23 cases (21.7%), such as headache, nausea, muscle pain, and fever. Conclusion: When Zoledronic acid was used, BMD was improved in both the spine and femoral neck. This may reduce the likelihood and subsequent morbidity of additional osteoporotic fractures. This study is meaningful in that there was no difference in the duration of bone union and radiological characteristics in patients with distal radial fractures administrated with intravenous BP early after the fractures, and improvement in BMD and bone turnover indicators was measured.

Keywords: zeoldreonic acid, BMD, osteoporosis, distal radius

Procedia PDF Downloads 109

Authors: Gerhard Gritsch, Ana Skupch, Manfred Hartmann, Wolfgang Frühwirt, Hannes Perko, Dieter Grossegger, Tilmann Kluge

Abstract:

Rehabilitation of stroke patients is dominated by classical physiotherapy. Nowadays, a field of research is the application of neurofeedback techniques in order to help stroke patients to get rid of their motor impairments. Especially, if a certain limb is completely paralyzed, neurofeedback is often the last option to cure the patient. Certain exercises, like the imagination of the impaired motor function, have to be performed to stimulate the neuroplasticity of the brain, such that in the neighboring parts of the injured cortex the corresponding activity takes place. During the exercises, it is very important to keep the motivation of the patient at a high level. For this reason, the missing natural feedback due to a movement of the effected limb may be replaced by a synthetic feedback based on the motor-related brain function. To generate such a synthetic feedback a system is needed which measures, detects, localizes and visualizes the motor related µ-rhythm. Fast therapeutic success can only be achieved if the feedback features high specificity, comes in real-time and without large delay. We describe such an approach that offers a 3D visualization of µ-rhythms in real time with a delay of 500ms. This is accomplished by combining smart EEG preprocessing in the frequency domain with source localization techniques. The algorithm first selects the EEG channel featuring the most prominent rhythm in the alpha frequency band from a so-called motor channel set (C4, CZ, C3; CP6, CP4, CP2, CP1, CP3, CP5). If the amplitude in the alpha frequency band of this certain electrode exceeds a threshold, a µ-rhythm is detected. To prevent detection of a mixture of posterior alpha activity and µ-activity, the amplitudes in the alpha band outside the motor channel set are not allowed to be in the same range as the main channel. The EEG signal of the main channel is used as template for calculating the spatial distribution of the µ - rhythm over all electrodes. This spatial distribution is the input for a inverse method which provides the 3D distribution of the µ - activity within the brain which is visualized in 3D as color coded activity map. This approach mitigates the influence of lid artifacts on the localization performance. The first results of several healthy subjects show that the system is capable of detecting and localizing the rarely appearing µ-rhythm. In most cases the results match with findings from visual EEG analysis. Frequent eye-lid artifacts have no influence on the system performance. Furthermore, the system will be able to run in real-time. Due to the design of the frequency transformation the processing delay is 500ms. First results are promising and we plan to extend the test data set to further evaluate the performance of the system. The relevance of the system with respect to the therapy of stroke patients has to be shown in studies with real patients after CE certification of the system. This work was performed within the project ‘LiveSolo’ funded by the Austrian Research Promotion Agency (FFG) (project number: 853263).

Keywords: real-time EEG neuroimaging, neurofeedback, stroke, EEG–signal processing, rehabilitation

Procedia PDF Downloads 379

Authors: Jeounghee Kim

Abstract:

Objective: To describe the incidence of complication, according to the stage of Traumatic Spinal Cord Injury (TSCI) which was treated at Asan Medical Center (AMC), Korea. Hereafter, it should be developed in nursing management protocol of traumatic SCI. Methods. Retrospectively reviewed hospital records about the patients who were admitted AMC Patients with traumatic spinal cord injury until January 2005 and December 2016 were analyzed (n=97). AMC is a single institution of 2,700 beds where patients with trauma and severe trauma can be treated. Patients who were admitted to the emergency room due to spinal cord injury and who underwent intensive care unit, general ward, and rehabilitation ward. To identify long-term complications, we excluded patients who were operated on to other hospitals after surgery. Complications such as respiratory(pneumonia, atelectasis, pulmonary embolism, and others), cardiovascular (hypotension), urinary (autonomic dysreflexia, urinary tract infection (UTI), neurogenic bladder, and others), and skin systems (pressure ulcers) from the time of admission were examined through medical records and images. Results: SCI was graded according to ASIA scale. The initial grade was checked at admission. (grade A 55(56.7%), grade B 14(14.4)%, grade C 11(11.3%), grade D 15(15.5%), and grade E 2(2.1%). The grade was rechecked when the patient was discharged after treatment. (grade A 43(44.3%), grade B 15(15.5%), grade C 12(12.4%), grade D 21(21.6%), and grade E 6(6.2%). The most common complication after SCI was UTI 24cases (mean 36.5day), sore 24cases (40.5day), and Pneumonia which was 23 cases after 10days averagely. The other complications after SCI were neuropathic pain 19 cases, surgical site infection 4 cases. 53.6% of patient who had SCI were educated about intermittent catheterization at discharge from hospital. The mean hospital stay of all SCI patients was 61days. Conclusion: The Complications after traumatic SCI were developed at various stages from acute phase to chronic phase. Nurses need to understand fully the time-course of complication in traumatic SCI to provide evidence-based practice.

Keywords: spinal cord injury, complication, nursing, rehabilitation

Procedia PDF Downloads 208

Authors: Salem Alsanusi, Abdulla Alakad

Abstract:

An experimental investigation to study the behaviour of under flexure reinforced concrete T-Beams. Those Beams were loaded to pre-designated stress levels as percentage of calculated collapse loads. Repairing these beans by either reinforced concrete jacket, or by externally bolted steel plates were utilized. Twelve full scale beams were tested in this experimental program scheme. Eight out of the twelve beams were loaded under different loading levels. Tests were performed for the beams before and after repair with Reinforced Concrete Jacket (RCJ). The applied Load levels were 60%, 77% and 100% of the calculated collapse loads. The remaining four beams were tested before and after repair with Bolted Steel Plate (BSP). Furthermore, out previously mentioned four beams two beams were loaded to the calculated failure load 100% and the remaining two beams were not subjected to any load. The eight beams recorded for the RCJ test were repaired using reinforced concrete jacket. The four beams recorded for the BSP test were all repaired using steel plate at the bottom. All the strengthened beams were gradually loaded until failure occurs. However, in each loading case, the beams behaviour, before and after strengthening, were studied through close inspection of the cracking propagation, and by carrying out an extensive measurement of deformations and strength. The stress-strain curve for reinforcing steel and the failure strains measured in the tests were utilized in the calculation of failure load for the beams before and after strengthening. As a result, the calculated failure loads were close to the actual failure tests in case of beams before repair, ranging from 85% to 90% and also in case of beams repaired by reinforced concrete jacket ranging from 70% to 85%. The results were in case of beams repaired by bolted steel plates ranging from (50% to 85%). It was observed that both jacketing and bolted steel plate methods could effectively restore the full flexure capacity of the damaged beams. However, the reinforced jacket has increased the failure load by about 67%, whereas the bolted steel plates recovered the failure load.

Keywords: rehabilitation, strengthening, reinforced concrete, beams deflection, bending stresses

Procedia PDF Downloads 301

Authors: Lateef Hakim Zai Khyber, Syed Rashid Ali

Abstract:

In the post 9/11 era, a new trend has developed of terrorist profiling on the basis of the ethnic, religious, political, psychological, social, and economic background of the terrorists to anticipate and assess the possible risk and to prevent and prosecute the suspected before they commit any violent act. The same profiling approach was adopted in different militant or terrorist de-radicalization and rehabilitation programs across the world in order to evaluate and identify the reasons and causes for joining terrorism in terms of push and pull factors. This paper attempts to explore and investigate the profiles of the detainees in the Sabaoon de-radicalization and Emancipation program, which aimed at de-radicalizing the former militants of Tehrik-e-Taliban (TTP) Pakistan in the Swat valley of Pakistan. This research attempted to use qualitative methods for collecting data, including a number of formal and informal open-ended interviews with the former staff members of Sabaoon to explore various aspects of the program, such as various approaches used at Sabaoon for terrorist profiling. It conducts a thorough examination of the profiles of the terrorist through their socioeconomic, ideological, emotional, intellectual, and psychological conditions and orientations, personal details, family issues, social preferences, etc. The study finds out that the majority of the terrorists belonged to the marginalized groups or lower class, including underprivileged tenants and poor laborers, of society having no access to land. They possess almost the same profiles, including low socioeconomic status, absence of a father or strict behavior of parents, large and combined families, lack of education, lack of religious understanding, etc. They also possess some common traits such as anxiety disorder, emotional instability, aggressive impulses and insecurity, depression, inferiority complex, lack of critical thinking and logical reasoning, authority-seeking behavior, and revenge-seeking behavior.

Keywords: terrorist profiling, Sabaoon, de-radicalization, rehabilitation, Swat, Pakistan, juvenile militants

Procedia PDF Downloads 149

Authors: M. K. Manoj, V. Pancholi, S. K. Nath

Abstract:

Microalloyed dual phase steels have been prepared by intercritical austenitisation (ICA) treatment of normalized steel at different temperature and time. Water quenching wad carried to obtain different martensite volume fraction (MVF) in DP steels. DP steels and normalized steels have been characterized by optical and scanning electron microscopy, Vickers hardness measurements and tensile properties determination. The effect of MVF and martensite morphology on mechanical properties and fracture behavior of microalloyed dual phase steels have been explained in the present work.

Keywords: dual phase steel, martensite morphology, hardness, tensile strength

Procedia PDF Downloads 323

Authors: J. Ismail, F. Zaïri, M. Naït-Abdelaziz, Z. Azari

Abstract:

In this work, a combined approach of continuum damage mechanics (CDM) and fracture mechanics is applied to model a glass plate behavior under static indentation. A spherical indenter is used and a CDM based constitutive model with an anisotropic damage tensor was selected and implemented into a finite element code to study the damage of glass. Various regions with critical damage values were predicted in good agreement with the experimental observations in the literature. In these regions, the directions of crack propagation, including both cracks initiating on the surface as well as in the bulk, were predicted using the strain energy density factor.

Keywords: finite element modeling, continuum damage mechanics, indentation, cracks

Procedia PDF Downloads 414

Authors: Sibel Ecemiş Kılıç, Muhammed Aydoğan

Abstract:

The rapid development of culture tourism has drawn attention to conserving cultural values especially by developing countries that would like to benefit from the economic contribution this type of tourism attracts. Tourism can have both positive and negative outcomes for historical settlements and their residents. The accommodation-purposed rehabilitation and revitalization project in “Sigacik Old City Zone” are to be discussed with spatial, economic, social and organizational dimensions. It is aimed to evaluate the relationship between the development of tourism and sustainable heritage conservation.

Keywords: Sığacık, urban conservation, sustainable tourism, Seferihisar

Procedia PDF Downloads 501

Authors: Siphesihle Hlongwane

Abstract:

Background: Globally, alcohol consumption, smoking, and the use of illicit drugs kill more than 11.8 million people each year. In sub-Saharan Africa, substance abuse is responsible for more than 6.4% of all deaths recorded and about 4.7% of all Disability Adjusted Life Years (DALYs), with numbers still expected to grow if no drastic measures are taken to curb and address drug use. In a setting where substance use is rife, understanding contextual factors that influence an individual’s perceived eligibility to seek rehabilitation is paramount. Using the candidacy framework, we unpack how situational factors influence an individual’s perceived eligibility for healthcare uptake in adolescents and youth with substance use disorder (SUD). Methods: The candidacy framework is concerned with how people consider their eligibility for accessing a health service. The study collected and analyzed primary qualitative data to answer the research question. Data were collected between January and July 2022 on participants aged between 18 and 35 for drug users and 18 to 60 for family members. Participants include 20 previous and current drug users and 20 family members that experience the effects of addiction. A pre-drafted semi-structured interview guide was administered to a conveniently sampled population supplemented with a referral sampling method. Data were thematically analyzed using the NVivo 12pro software to manage the data. Findings: Our findings show that people with substance use disorders are aware of their drug use habits and acknowledge their candidacy for health services. Candidacy for health services is also acknowledged by those around them, such as family members and peers, and as such, information on the navigation of health services for drug users is shared by those who have attended health services, those affected by drug use, and this includes health service research by family members to identify accessible health services. While participants reported willingness to quit drug use if assistance is provided, the permeability of health care services is hindered by both individual determinations to quit drug use from long-time use and the availability of health services for drug users, such as rehabilitation centers. Our findings also show that drug users are conscious and can articulate their ailments; however, the hunt for the next dose of drugs and long waiting cues for health service acquisition overshadows their claim to health services. Participants reported a mixture of treatments prescribed, with some more gruesome than others prescribed, thus serving as both a facilitator and barrier for health service uptake. Despite some unorthodox forms of treatments prescribed in health care, the majority of those who enter treatment complete the process of treatment, although some are met with setbacks and sometimes relapse after treatment has finished. Conclusion: Drug users are able to ascertain their candidacy for health services; however, individual and environmental characteristics relating to drug use hinder the use of health services. Drug use interventions need to entice health service uptake as a way to improve candidacy for health use.

Keywords: substance use disorder, rehabilitation, drug use, relapse, South Africa, candidacy framework

Procedia PDF Downloads 86

Authors: Manjinder Singh, Jasvinder Singh

Abstract:

Existing theories of Titanic/Liberty ship, Sydney bridge accidents and practical experience generated an interest in developing weldments those has high toughness under sub-zero temperature conditions. The purpose was to protect the joint from undergoing DBT (Ductile to brittle transition), when ambient temperature reach sub-zero levels. Metallurgical improvement such as low carbonization or addition of deoxidization elements like Mn and Si was effective to prevent fracture in weldments (crack) at low temperature. In the present research, an attempt has been made to investigate the reason behind ductile to brittle transition of mild steel weldments when subjected to sub-zero temperatures and method of its mitigation. Nickel is added to weldments using manual metal arc welding (MMAW) preventing the DBT, but progressive reduction in charpy impact values as temperature is lowered. The variation in toughness with respect to nickel content being added to the weld pool is analyzed quantitatively to evaluate the rise in toughness value with increasing nickel amount. The impact performance of welded specimens was evaluated by Charpy V-notch impact tests at various temperatures (20 °C, 0 °C, -20 °C, -40 °C, -60 °C). Notch is made in the weldments, as notch sensitive failure is particularly likely to occur at zones of high stress concentration caused by a notch. Then the effect of nickel to weldments is investigated at various temperatures was studied by mechanical and metallurgical tests. It was noted that a large gain in impact toughness could be achieved by adding nickel content. The highest yield strength (462J) in combination with good impact toughness (over 220J at – 60 °C) was achieved with an alloying content of 16 wt. %nickel. Based on metallurgical behavior it was concluded that the weld metals solidify as austenite with increase in nickel. The microstructure was characterized using optical and high resolution SEM (scanning electron microscopy). At inter-dendritic regions mainly martensite was found. In dendrite core regions of the low carbon weld metals a mixture of upper bainite, lower bainite and a novel constituent coalesced bainite formed. Coalesced bainite was characterized by large bainitic ferrite grains with cementite precipitates and is believed to form when the bainite and martensite start temperatures are close to each other. Mechanical properties could be rationalized in terms of micro structural constituents as a function of nickel content.

Keywords: MMAW, Toughness, DBT, Notch, SEM, Coalesced bainite

Procedia PDF Downloads 523

Authors: Radek Novotny, Michal Novak, Daniela Marusakova, Monika Sipova, Hugo Fuentes, Peter Borst

Abstract:

This research has been conducted within the European HORIZON 2020 project ECC-SMART. The main objective is to assess whether it is feasible to design and develop a small modular reactor (SMR) that would be cooled by supercritical water (SCW). One of the main objectives for material research concerns the corrosion of the candidate cladding materials. The experimental part has been conducted in support of the qualification procedure of the future SCW-SMR constructional materials. The last objective was to identify the gaps in current norms and guidelines. Apart from corrosion, resistance testing of candidate materials stresses corrosion cracking susceptibility tests have been performed in supercritical water. This paper describes part of these tests, in particular, those slow strain rate tensile loading applied for tangential ring shape specimens of two candidate materials, Alloy 800H and 310S stainless steel. These ring tensile tests are one the methods used for tensile testing of nuclear cladding. Here full circular heads with dimensions roughly equal to the inner diameter of the sample and the gage sections are placed in the parallel direction to the applied load. Slow strain rate tensile tests have been conducted in 380 or 500oC supercritical water applying two different elongation rates, 1x10-6 and 1x10-7 s-1. The effect of temperature and dissolved oxygen content on the SCC susceptibility of Alloy 800H and 310S stainless steel was investigated when two different temperatures and concentrations of dissolved oxygen were applied in supercritical water. The post-fracture analysis includes fractographic analysis of the fracture surfaces using SEM as well as cross-sectional analysis on the occurrence of secondary cracks. Assessment of the effect of environment and dissolved oxygen content was by comparing to the results of the reference tests performed in air and N2 gas overpressure. The effect of high temperature on creep and its role in the initiation of SCC was assessed as well. It has been concluded that the applied test method could be very useful for the investigation of stress corrosion cracking susceptibility of candidate cladding materials in supercritical water.

Keywords: stress corrosion cracking, ring tensile tests, super-critical water, alloy 800H, 310S stainless steel

Procedia PDF Downloads 81