Search results for: prickly pear powder

Authors: Shihab Ibrahim

Abstract:

Geopolymer binders as an alternative binder system to ordinary Portland cement are the focus of the past 2 decades of researches. In order to eliminate CO2 emission by cement manufacturing and utilizing construction waste as a source material, clean waste clay bricks which are the waste from Levent Brick factory was activated with a mixture of sodium hydroxide and sodium silicate solution. 12 molarity of sodium hydroxide solution was used and the ratio of sodium silicate to sodium hydroxide was 2.5. Alkaline solution to clay brick powder ratio of 0.35, 0.4, 0.45, and 0.5 was studied. Alkaline solution to powder ratio of 0.4 was found to be optimum ratio to have the same workability as ordinary Portland cement paste. Compressive strength of the clay brick based geopolymer paste samples was evaluated under different curing temperatures and curing durations. One day compressive strength of 57.3 MPa after curing at 85C for 24 hours was obtained which was higher than 7 days compressive strength of ordinary Portland cement paste. The highest compressive strength 71.4 MPa was achieved at seventh day age for the geopolymer paste samples cured at 85C for 24 hours. It was found that 8 hour curing at elevated temperature 85C, is sufficient to get 96% of total strength. 37.4 MPa strength at seventh day of clay brick based geopolymer sample cured at room temperature was achieved. Water absorption around 10% was found for clay brick based geopolymer samples cured at different temperatures with compare to 9.14% water absorption of ordinary Portland cement paste. The clay brick based geopolymer binder can have the potentiality to be used as an alternative binder to Portland cement in a case that the heat treatment provided. Further studies are needed in order to produce the binder in a way that can harden and gain strength without any elevated curing.

Keywords: construction and demolition waste, geopolymer, clay brick, compressive strength.

Procedia PDF Downloads 221

Authors: Asif Mahmood, Yousef Alzeghayer

Abstract:

The size effects of a precursor Y2BaCuO5 (Y211) powder on the microstructure and critical current density (Jc) of liquid infiltration growth (LIG)-processed YBa2Cu3O7-y (Y123) bulk superconductors were investigated in terms of milling time (t). YBCO bulk samples having high Jc values have been selected for the flywheel energy storage system. Y211 powders were attrition-milled for 0-10 h in 2 h increments at a fixed rotation speed of 400 RPM. Y211 pre-forms were made by pelletizing the milled Y211 powders followed by subsequent sintering, after which an LIG process with top seeding was applied to the Y211/Ba3Cu5O8 (Y035) pre-forms. Spherical pores were observed in all LIG-processed Y123 samples, and the pore density gradually decreased as t increased from 0 h to 8 h. In addition to the reduced pore density, the Y211 particle size in the final Y123 products also decreased with increasing t. As t increased further to 10 h, unexpected Y211 coarsening and large pore evolutions were observed. The magnetic susceptibility-temperature curves showed that the onset superconducting transition temperature (Tc, onset) of all samples was the same (91.5 K), but the transition width became greater as t increased. The Jc of the Y123 bulk superconductors fabricated in this study was observed to correlate well with t of the Y211 precursor powder. The maximum Jc of 1.0×105 A cm-2 (at 77 K, 0 T) was achieved at t = 8 h, which is attributed to the reduction in pore density and Y211 particle size. The prolonged milling time of t = 10 h decreased the Jc of the LIG-processed Y123 superconductor owing to the evolution of large pores and exaggerated Y211 growth. YBCO bulk samples having high Jc (samples prepared using 8 h milled powders) have been used for the energy storage system in flywheel energy storage system.

Keywords: critical current, bulk superconductor, liquid infiltration, bioinformatics

Procedia PDF Downloads 189

Authors: Obafemi Akinwotu, Aylin Tas, Tony Taylor, Bukola Onarinde

Abstract:

The study was conducted to explore the methods and tools to improve texture and preserve the total phenolic and antioxidant compounds of dysphagia foods produced from carrot-based puree with decolourised Chlorella algae. Textural properties (Texture profile analysis [TPA]; the International Dysphagia Diet Standardization Initiative, particle size test [PST]) and rheological properties (viscosity and viscoelastic properties) of carrot puree defrosted by different treatments (microwave, steamer, oven), were characterised using hydrocolloids (guar gum, k. carrageenan, and xanthan gum), and the results were compared to a level 4 commercial sample. DPPH (2,2-diphenyl-1-picrylhydrazyl) antiradical scavenging radicals and total phenolic contents were employed to evaluate the total phenolics, and radical scavenging properties of defrosted carrot puree sonicated carrot puree (20 Hz, 30 min, 60 oC), and vacuum-dried carrot powder with the addition of algae. Results show that the viscosity, viscoelasticity test, TPA, and PST of the commercial sample were comparable to those of guar gum and xanthan gum containing puree, suggesting that they could be used as dysphagia diets. There was no noticeable decolourisation of the Chlorella pigment. Additionally, the use of the microwave, stemmer, and oven for defrosting treatment had an impact on the textural characteristics of the moulded samples upon cooling and also contributed to the reduction in the total phenolic and antioxidant properties of the samples. Sonication treatments of algae exposure reduced the cloudiness of the green pigment and lightened the colour of the samples containing algae, and they also reduced the drying time from 2.5 to 1.5 hours during the preliminary work. The low-temperature vacuum- and freeze-dried samples increased the concentration of the powder and resulted in an increase in the total phenolic content of the dry samples. The dried products may therefore have the potential to become more nutrient-dense to benefit the health of individuals with dysphagia.

Keywords: dysphagia, elderly, hydrocolloids, carrot puree

Procedia PDF Downloads 37

Authors: Roberto Cassino, Valeria Dissette, Carlo Alberto Bignozzi, Daniele Pazzi

Abstract:

Background and Aims: The aim of this work was to investigate, both ‘in vitro’ and ‘in vivo’, if the new SCX technology (SiO2-Ag+Chlorex) can easily defeat infections and it is really more effective than SSD (SilverSulfaDiazine). ‘In vitro’ methods: we tested ‘in vitro’ the effectiveness of both silver materials using a pool of 5 strains: Pseudomonas Aeruginosa, Staphylococcus aureus, Escherichia Coli, Enterococcus hirae and Candida Albicans. 100 µl of this pool have been seeded on Petri dishes and kept for 24 hours in incubation at 37 C°. ‘In vivo’ methods: we enrolled patients with multiple infectious chronic wounds (according with cutting & harding criteria for infection); after a qualitative evaluation of the wounds bacterial population, taking a sample by plug, we included in the study 6 patients for a total of 10 wounds, infected by one or more of the microorganisms used for the ‘in vitro’ test. The protocol consisted of a treatment with a spray powder of SSD every 48 hours for 14 days; in case of worsening we should have to start a new treatment with a spray powder containing silicon dioxide, ionic silver and chlorexidine (SiO2-Ag+Chlorex) every 48 hours for 14 days. We evaluated the number of clinical signs of infection and the disappearance or not of the wound edge erithema. ‘In vitro’ results: SSD demonstrated a wide zone of inhibition within 24 hours, but after 5 days there was no more signs of inhibition; on the contrary SCX had a good inhibition ring that lasted more than 5 days. ‘In vivo’ results: all wounds treated with SSD got worse; the signs of infection increased and the wound edge erithema did not disappear. According with the protocol, we treated then all wounds with SCX and they all improved within the period of observation with complete disappearance of clinical signs of infection and no more wound edge erithema. Conclusions: the study demonstrated the effectiveness of SiO2-Ag+Chlorex, especially in terms of long lasting antimicrobial action. We had the same results ‘in vitro’, so that there has been a perfect correspondence between the laboratory outcomes and the clinical ones.

Keywords: chronic wounds, infections, ionic silver, SSD

Procedia PDF Downloads 293

Authors: Pomila Sharma

Abstract:

The rapid urbanization in India was not accompanied by the establishment of waste water treatment facility at similar and same pace. The inland fresh water ecosystem is increasingly subjected to great stress from various human activities. Jalmahal Lake is located in Jaipur city of Rajasthan state; the lake was constructed about 400 years ago and surrounded by hills. The lake was approximately 139 hectare in full spread and has catchment area of 23.5 sq. kilometer. Out of the total catchment area approximate 40% falls inside dense urban area of Jaipur city. During the showers, the treated and untreated waste waters and runoff waters get mixed and enter the lake through the various influx channels, and the lake water quality gets affected by the inflow of waste water. The main objective of this work was to use the Moringa oleifera seeds as a natural adsorbent for the treatment of wastewater in lake. Moringa oleifera is a tropical, multipurpose tree whose seeds contain high-quality edible oil 40% by weight and water soluble, non-toxic protein that act as an effective coagulant for the removal of organic matter in water and waste water treatment. Laboratory Jar test procedure had been used for coagulation studies; an experiment runs using lake water. Water extracts/powder of Moringa seed applied to treat polluted water of lake. In present study various doses of Moringa oleifera seed coagulant viz. 100 mg/L, 200 mg/L, and 400 mg/L were taken and checked for the efficiency dose on treated and untreated polluted water. Turbidity and color removal is one of the important steps in a waste water treatment processes. The results indicate significant reduction in turbidity and color. Standard plate count was significantly reduced fecal coliform levels too. All parameters were reduced with the increased dose of Moringa oleifera. It was clear from the study Moringa oleifera seed was shown to be a potential bio-coagulant, for treatment of sewage laden polluted water in the lake.

Keywords: coagulant, Moringa oleifera, plate count, turbidity, wastewater

Procedia PDF Downloads 369

Authors: Rupas Kumar M., Saravana Kumar M., Amarendra Kumar S., Likhita Komal V., Sree Deepthi M.

Abstract:

The demand for water is increasing at an alarming rate due to rapid urbanization and increase in population. Due to freshwater scarcity, Groundwater became the necessary source of potable water to major parts of the world. This problem of freshwater scarcity and groundwater dependency is very severe particularly in developing countries and overpopulated regions like India. The present study aimed at evaluating the Ground Water Quality Index (GWQI), which represents overall quality of water at certain location and time based on water quality parameters. To evaluate the GWQI, sixteen water quality parameters have been considered viz. colour, pH, electrical conductivity, total dissolved solids, turbidity, total hardness, alkalinity, calcium, magnesium, sodium, chloride, nitrate, sulphate, iron, manganese and fluorides. The groundwater samples are collected from Kadapa City in Andhra Pradesh, India and subjected to comprehensive physicochemical analysis. The high value of GWQI has been found to be mainly from higher values of total dissolved solids, electrical conductivity, turbidity, alkalinity, hardness, and fluorides. in the present study, citrus limetta (sweet lemon) peel powder has used as a coagulant and GWQI values are recorded in different concentrations to improve GWQI. Sensitivity analysis is also carried out to determine the effect of coagulant dosage, mixing speed and stirring time on GWQI. The research found the maximum percentage improvement in GWQI values are obtained when the coagulant dosage is 100ppm, mixing speed is 100 rpm and stirring time is 10 mins. Alum is also used as a coagulant aid and the optimal ratio of citrus limetta and alum is identified as 3:2 which resulted in best GWQI value. The present study proposes Citrus limetta peel powder as a potential natural coagulant to treat Groundwater and to improve GWQI.

Keywords: alum, Citrus limetta, ground water quality index, physicochemical analysis

Procedia PDF Downloads 202

Authors: Vishal Mahale, Jayashree Bijwe, Sujeet K. Sinha

Abstract:

Range of thermal conductivity (TC) of Friction Materials (FMs) is a critical issue since lower TC leads to accumulation of frictional heat on the working surface, which results in excessive fade while higher TC leads to excessive heat flow towards back-plate resulting in boiling of brake-fluid leading to ‘spongy brakes’. This phenomenon prohibits braking action, which is most undesirable. Therefore, TC of the FMs across the brake pads should not be high while along the brake pad, it should be high. To enhance TC, metals in the forms of powder and fibers are used in the FMs. Apart from TC improvement, metals provide strength and structural integrity to the composites. Due to higher TC Copper (Cu) powder/fiber is a most preferred metallic ingredient in FM industry. However, Cu powders/fibers are responsible for metallic wear debris generation, which has harmful effects on aquatic organisms. Hence to get rid of a problem of metallic wear debris generation and to keep the positive effect of TC improvement, incorporation of Cu fabric in NAO brake-pads can be an innovative solution. Keeping this in view, two realistic multi-ingredient FM composites with identical formulations were developed in the form of brake-pads. Out of which one composite series consisted of a single layer of Cu fabric in the body of brake-pad and designated as C1 while double layer of Cu fabric was incorporated in another brake-pad series with designation of C2. Distance of Cu fabric layer from the back-plate was kept constant for C1 and C2. One more composite (C0) was developed without Cu fabric for the sake of comparison. Developed composites were characterized for physical properties. Tribological performance was evaluated on full scale inertia dynamometer by following JASO C 406 testing standard. It was concluded that Cu fabric successfully improved fade resistance by increasing conductivity of the composite and also showed slight improvement in wear resistance. Worn surfaces of pads and disc were analyzed by SEM and EDAX to study wear mechanism.

Keywords: brake inertia dynamometer, copper fabric, non-asbestos organic (NAO) friction materials, thermal conductivity enhancement

Procedia PDF Downloads 111

Authors: P. Serrão, E. Costa, A. Ribeiro, V. Infante

Abstract:

The characteristic sonority of the Portuguese guitar is in great part what makes Fado so distinguishable from other traditional song styles. The Portuguese guitar is a pear-shaped plucked chordophone with six courses of double strings. This study compares the two types of plain strings available for Portuguese guitar and used by the musicians. One is stainless steel spring wire, the other is high carbon spring steel (music wire). Some musicians mention noticeable differences in sound quality between these two string materials, such as a little more brightness and sustain in the steel strings. Experimental tests were performed to characterize string tension at pitch; mechanical strength and tuning stability using the universal testing machine; dimensional control and chemical composition analysis using the scanning electron microscope. The string dynamical behaviour characterization experiments, including frequency response, inharmonicity, transient response, damping phenomena and were made in a monochord test set-up designed and built in-house. Damping factor was determined for the fundamental frequency. As musicians are able to detect very small damping differences, an accurate a characterization of the damping phenomena for all harmonics was necessary. With that purpose, another improved monochord was set and a new system identification methodology applied. Due to the complexity of this task several adjustments were necessary until obtaining good experimental data. In a few cases, dynamical tests were repeated to detect any evolution in damping parameters after break-in period when according to players experience a new string sounds gradually less dull until reaching the typically brilliant timbre. Finally, each set of strings was played on one guitar by a distinguished player and recorded. The recordings which include individual notes, scales, chords and a study piece, will be analysed to potentially characterize timbre variations.

Keywords: damping factor, music wire, portuguese guitar, string dynamics

Procedia PDF Downloads 528

Authors: Snezana Rajkovic, Miroslava Markovic, Ljubinko Rakonjac, Aleksandar Lucic, Radoslav Rajkovic

Abstract:

Woolly apple aphid, Eriosoma lanigerum (Hausmann) is a widely distributed pest of apple trees, especially where its parasites have been killed by insecticides. It can also be found on pear, hawthorn, mountain ash, and elm trees. Relatively small to medium-sized aphids, characterized by a reddish-brown body, a blood-red stain when crushed and a fluffy, flocculent wax covering. Specialized dermal glands produce the characteristic fluffy or powdery wax, which gives E. lanigerum its characteristic 'woolly' appearance. Also, woolly apple aphid is a problemm in nursery production of spure.The experiments were carried out in the nursery “Nevade” in Gornji Milanovac, "Srbijasume" on the spruce seedlings, aged 2 years. In this study, organic insecticide King Bo, aqueous solution (a. i. oxymatrine 0.2% + psoralen 0.4%), manufacturer Beijing Kingbo Biotech Co. Ltd., Beijing, China. extracted from plants and used as pesticides in nursery production were investigated. King Bo, bioinsecticide is manufactured from refined natural herbal extract several wild medicinal plants, such as Sophora flavescens Ait, Veratrum nigrum L, A. Carmichael, etc. Oxymatrine 2.4 SL is a stomach poison that has antifeeding and repellent action. This substance stimulates development and growth in a host plant and also controls the appearance of downy mildew.The trials were set according to instructions of methods-monitoring of changes in the number of larvae and adults compared to before treatment. The treatment plan was made according to fully randomized block design. The experiment was conducted in four repetitions. The basic plot had the area of 25 m2. Phytotoxicity was estimated by PP methods 1/135 (2), the intensity of infection according to Towsend-Heuberger, the efficiency by Abbott, the analysis of variance with Ducan test and PP/181 (2).

Keywords: bioinsecticide, efficacy, nurssery production, woolly apple aphid

Procedia PDF Downloads 502

Authors: Gonzalo Reyes, Magdalena Walczak, Esteban Ramos-Moore, Jorge Ramos-Grez

Abstract:

Metal additive manufacture technologies have gained strong support and acceptance as a promising and alternative method to manufacture high performance complex geometry products. The main purpose of the present work is to study the microstructure and phase transformation temperatures of Cu-Al-Ni shape memory alloys fabricated from a direct laser additive process using metallic powders as precursors. The potential application is to manufacture self-centering seismic dampers for earthquake protection of buildings out of a copper based alloy by an additive process. In this process, the Cu-Al-Ni alloy is melted, inside of a high temperature and vacuum chamber with the aid of a high power fiber laser under inert atmosphere. The laser provides the energy to melt the alloy powder layer. The process allows fabricating fully dense, oxygen-free Cu-Al-Ni specimens using different laser power levels, laser powder interaction times, furnace ambient temperatures, and cooling rates as well as modifying concentration of the alloying elements. Two sets of specimens were fabricated with a nominal composition of Cu-13Al-3Ni and Cu-13Al-4Ni in wt.%, however, semi-quantitative chemical analysis using EDX examination showed that the specimens’ resulting composition was closer to Cu-12Al-5Ni and Cu-11Al-8Ni, respectively. In spite of that fact, it is expected that the specimens should still possess shape memory behavior. To confirm this hypothesis, phase transformation temperatures will be measured using DSC technique, to look for martensitic and austenitic phase transformations at 150°C. So far, metallographic analysis of the specimens showed defined martensitic microstructures. Moreover, XRD technique revealed diffraction peaks corresponding to (0 0 18) and (1 2 8) planes, which are too associated with the presence of martensitic phase. We conclude that it would be possible to obtain fully dense Cu-Al-Ni alloys having shape memory effect behavior by direct laser fabrication process, and to advance into fabrication of self centering seismic dampers by a controllable metal additive manufacturing process.

Keywords: Cu-Al-Ni alloys, direct laser fabrication, shape memory alloy, self-centering seismic dampers

Procedia PDF Downloads 495

Authors: Yi Sun, George Ed Rainger, Steve P. Watson

Abstract:

Background: Beyond the classical roles in haemostasis and thrombosis, platelets are important in the initiation and development of various thrombo-inflammatory diseases. In atherosclerosis and deep vein thrombosis, for example, platelets bridge monocytes with endothelium and form heterotypic aggregates with monocytes in the circulation. This can alter monocyte phenotype by inducing their activation, stimulating adhesion and migration. These interactions involve cell surface receptor-ligand pairs on both cells. This list is likely incomplete as new interactions of importance to platelet biology are continuing to be discovered as illustrated by our discovery of PEAR-1 binding to FcεR1α. Results: We have developed a highly sensitive avidity-based assay to identify novel extracellular interactions among 126 recombinantly-expressed platelet cell surface and secreted proteins involved in platelet aggregation. In this study, we will use this method to identify novel platelet-monocyte interactions. We aim to identify ligands for orphan receptors and novel partners of well-known proteins. Identified interactions will be studied in preliminary functional assays to demonstrate relevance to the inflammatory processes supporting atherogenesis. Conclusions: Platelet-monocyte interactions are essential for the development of thromboinflammatory disease. Up until relatively recently, technologies only allow us to limit our studies on each individual protein interaction at a single time. These studies propose for the first time to study the cell surface platelet-monocyte interactions in a systematic large-scale approach using a reliable screening method we have developed. If successful, this will likely to identify previously unknown ligands for important receptors that will be investigated in details and also provide a list of novel interactions for the field. This should stimulate studies on developing alternative therapeutic strategies to treat vascular inflammatory disorders such as atherosclerosis, DVT and sepsis and other clinically important inflammatory conditions.

Keywords: membrane proteins, large-scale screening, platelets, recombinant expression

Procedia PDF Downloads 119

Authors: Judith Awacorach, Quentin Gausset

Abstract:

Wood charcoal and firewood are the primary sources of energy for cooking fuel in most Sub-Saharan African countries, including Uganda. This leads to unsustainable forest use and to rapid deforestation. Green charcoal (made out of agricultural residues that are carbonized, reduced in char powder, and glued in briquettes, using a binder such as sugar molasse, cassava flour or clay) is a promising and sustainable alternative to wood charcoal and firewood. It is considered as renewable energy because the carbon emissions released by the combustion of green charcoal are immediately captured again in the next agricultural cycle. If practiced on a large scale, this has the potential to replace wood charcoal and stop deforestation. However, the uptake of green charcoal for cooking remains low in Uganda despite the introduction of the technology 15 years ago. The present paper reviews the barriers to the production and commercialization of green charcoal. The paper is based on the study of 13 production sites, recording the raw materials used, the production techniques, the quantity produced, the frequency of production, and the business model. Observations were made on each site, and interviews were conducted with the managers of the facilities and with one or two employees in the larger facilities. We also interviewed project administrators from four funding agencies interested in financing green charcoal production. The results of our research identify the main barriers as follows: 1) The price of green charcoal is not competitive (it is more labor and capital-intensive than wood charcoal). 2) There is a problem with quality control and labeling (one finds a wide variety of green charcoal with very different performances). 3) The carbonization of agricultural crop residues is a major bottleneck in green char production. Most briquettes are produced with wood charcoal dust or powder, which is a by-product of wood charcoal. As such, they increase the efficiency of wood charcoal but do not yet replace it. 4) There is almost no marketing chain for the product (most green charcoal is sold directly from producer to consumer without any middleman). 5) The financing institutions are reluctant to lend money for this kind of activity. 6) Storage can be challenging since briquettes can dissolve due to moisture. In conclusion, a number of important barriers need to be overcome before green charcoal can become a serious alternative to wood charcoal.

Keywords: briquettes, competitiveness, deforestation, green charcoal, renewable energy

Procedia PDF Downloads 22

Authors: Gülşah Çelik Gül, Figen Kurtuluş

Abstract:

Cesium molybdates with general formula CsMIII(MoO4)2, where MIII = Bi, Dy, Pr, Er, exhibit rich polymorphism, and crystallize in a layered structure. These properties cause intensive studies on cesium molybdates. CsBi(MoO4)2 was synthesized by microwave method by using cerium sulphate, bismuth oxide and molybdenum (VI) oxide in an appropriate molar ratio. Characterizations were done by x-ray diffraction (XRD), fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy/energy dispersive analyze (SEM/EDS), thermo gravimetric/differantial thermal analysis (TG/DTA).

Keywords: cesium bismuth dimolybdate, microwave synthesis, powder x-ray diffraction, rare earth dimolybdates

Procedia PDF Downloads 491

Authors: Heba A. Hazzah, Ragwa M. Farid, Maha M. A. Nasra, Mennatallah Zakria, Magda A. El Massik, Ossama Y. Abdallah

Abstract:

Introduction: Curcumin (Cur) is a polyphenol derived from the herbal remedy and dietary spice turmeric. It possesses diverse anti-inflammatory and anti-cancer properties following oral or topical administration. The buccal delivery of curcumin can be useful for both systemic and local disease treatments such as gingivitis, periodontal diseases, oral carcinomas, and precancerous oral lesions. Despite of its high activity, it suffers a limited application due to its low oral bioavailability, poor aqueous solubility, and instability. Aim: Preparation and characterization of curcumin solid lipid nanoparticles with a high loading capacity into a mucoadhesive gel for buccal application. Methodology: Curcumin was formulated as nanoparticles using different lipids, namely Gelucire 39/01, Gelucire 50/13, Precirol, Compritol, and Polaxomer 407 as a surfactant. The SLN were dispersed in a mucoadhesive gel matrix to be applied to the buccal mucosa. All formulations were evaluated for their content, entrapment efficiency, particle size, in vitro drug dialysis, ex vivo mucoadhesion test, and ex vivo permeation study using chicken buccal mucosa. Clinical evaluation was conducted on 15 cases suffering oral erythroplakia and erosive lichen planus. Results: The results showed high entrapment efficiency reaching almost 90 % using Gelucire 50, the loaded gel with Cur-SLN showed good adhesion property and 25 minutes in vivo residence time. In addition to stability enhancement for the Cur powder. All formulae did not show any drug permeated however, a significant amount of Cur was retained within the mucosal tissue. Pain and lesion sizes were significantly reduced upon topical treatment. Complete healing was observed after 6 weeks of treatment. Conclusion: These results open a room for the pharmaceutical technology to optimize the use of this golden magical powder to get the best out of it. In addition, the lack of local anti-inflammatory compounds with reduced side effects intensifies the importance of studying natural products for this purpose.

Keywords: curcumin, erythroplakia, mucoadhesive, pain, solid lipid nanoparticles

Procedia PDF Downloads 429

Authors: Shashikant R. Kuchekar, Haribhau R. Aher, Priti M. Dhage

Abstract:

The removal vanadium from aqueous solution using natural exchanger was investigated. The effects of pH, contact time and exchanger dose were studied at ambient temperature (25 ⁰C ± 2 ⁰C). The equilibrium process was described by the Langmuir isotherm model with adsorption capacity for vanadium. The natural exchanger i.e. tamarindus seeds powder was treated with formaldehyde and sulpuric acid to increase the adsorptivity of metals. The maximum exchange level was attained as 80.1% at pH 3 with exchanger dose 5 g and contact time 60 min. Method is applied for removal of vanadium from industrial effluents.

Keywords: industrial effluent, natural ion exchange, Tamarindous indica, vanadium

Procedia PDF Downloads 218

Authors: Vasant Reddy, Shivani A. Singh, Pravin S. More

Abstract:

In the present investigation, we demonstrated the fabrication of few-layers of graphene sheets with alkali metal i.e. Rb-G using chemical route method. The obtained materials were characterized by means of chemical, structural and electrical techniques, using the ultraviolet-visible spectroscopy (UV-Vis), Fourier transform infrared spectroscopy (FTIR), X-ray powder diffraction (XRD), scanning electron microscopy (SEM) and 4 points probe, respectively. The XRD studies were carried out to understand the phase of the samples where we found a sharp peak of Rb-G at 26.470. UV-Spectroscopy of Graphene and Rb-modified graphene samples shows the absorption peaks at ~248 nm and ~318 nm respectively. These analyses show that this modified material can be useful for gas sensing applications and to be used in diverse areas.

Keywords: chemical route, graphene, gas sensing, UV-spectroscopy

Procedia PDF Downloads 233

Authors: Shian Guan, Marie Bourdin, Isabelle Trenque, Younes Messaddeq, Thierry Cardinal, Nicolas Penin, Issam Mjejri, Aline Rougier, Etienne Duguet, Stephane Mornet, Manuel Gaudon

Abstract:

At the interface of the studies performed by 3 Ph.D. students: Shian Guan (2017-2020), Marie Bourdin (2016-2019) and Isabelle Trenque (2012-2015), a single synthesis route: polyol-mediated process, was used with success for the preparation of different inorganic oxides. Both of these inorganic oxides were elaborated for their potential application as smart optical compounds. This synthesis route has allowed us to develop nanoparticles of zinc oxide, vanadium oxide or tungsten oxide. This route is with easy implementation, inexpensive and with large-scale production potentialities and leads to materials of high purity. The obtaining by this route of nanometric particles, however perfectly crystalline, has notably led to the possibility of doping these matrix materials with high doping ion concentrations (high solubility limits). Thus, Al3+ or Ga3+ doped-ZnO powder, with high doping rate in comparison with the literature, exhibits remarkable infrared absorption properties thanks to their high free carrier density. Note also that due to the narrow particle size distribution of the as-prepared nanometric doped-ZnO powder, the original correlation between crystallite size and unit-cell parameters have been established. Also, depending on the annealing atmosphere use to treat vanadium precursors, VO2, V2O3 or V2O5 oxides with thermochromic or electrochromic properties can be obtained without any impurity, despite the versatility of the oxidation state of vanadium. This is of more particular interest on vanadium dioxide, a relatively difficult-to-prepare oxide, whose first-order metal-insulator phase transition is widely explored in the literature for its thermochromic behavior (in smart windows with optimal thermal insulation). Finally, the reducing nature of the polyol solvents ensures the production of oxygen-deficient tungsten oxide, thus conferring to the nano-powders exotic colorimetric properties, as well as optimized photochromic and electrochromic behaviors.

Keywords: inorganic oxides, electrochromic, photochromic, thermochromic

Procedia PDF Downloads 197

Authors: Ahmed. Abdel Bary, Omneya. Khowessah, Mojahed. al-jamrah

Abstract:

Introduction: The major challenge with the design of oral dosage forms lies with their poor bioavailability. The most frequent causes of low oral bioavailability are attributed to poor solubility and low permeability. The aim of this study was to develop solid nanodispersed tablet formulation of Glimepiride for the enhancement of the solubility and bioavailability. Methodology: Solid nanodispersions of Glimepiride (GMP) were prepared using two different ratios of 2 different carriers, namely; PEG6000, pluronic F127, and by adopting two different techniques, namely; solvent evaporation technique and fusion technique. A full factorial design of 2 3 was adopted to investigate the influence of formulation variables on the prepared nanodispersion properties. The best chosen formula of nanodispersed powder was formulated into tablets by direct compression. The Differential Scanning Calorimetry (DSC) analysis and Fourier Transform Infra-Red (FTIR) analysis were conducted for the thermal behavior and surface structure characterization, respectively. The zeta potential and particle size analysis of the prepared glimepiride nanodispersions was determined. The prepared solid nanodispersions and solid nanodispersed tablets of GMP were evaluated in terms of pre-compression and post-compression parameters, respectively. Results: The DSC and FTIR studies revealed that there was no interaction between GMP and all the excipients used. Based on the resulted values of different pre-compression parameters, the prepared solid nanodispersions powder blends showed poor to excellent flow properties. The resulted values of the other evaluated pre-compression parameters of the prepared solid nanodispersion were within the limits of pharmacopoeia. The drug content of the prepared nanodispersions ranged from 89.6 ± 0.3 % to 99.9± 0.5% with particle size ranged from 111.5 nm to 492.3 nm and the resulted zeta potential (ζ ) values of the prepared GMP-solid nanodispersion formulae (F1-F8) ranged from -8.28±3.62 mV to -78±11.4 mV. The in-vitro dissolution studies of the prepared solid nanodispersed tablets of GMP concluded that GMP- pluronic F127 combinations (F8), exhibited the best extent of drug release, compared to other formulations, and to the marketed product. One way ANOVA for the percent of drug released from the prepared GMP-nanodispersion formulae (F1- F8) after 20 and 60 minutes showed significant differences between the percent of drug released from different GMP-nanodispersed tablet formulae (F1- F8), (P<0.05). Conclusion: Preparation of glimepiride as nanodispersed particles proven to be a promising tool for enhancing the poor solubility of glimepiride.

Keywords: glimepiride, solid Nanodispersion, nanodispersed tablets, poorly water soluble drugs

Procedia PDF Downloads 469

Authors: Uma Shanker, Vidhisha Jassal

Abstract:

A novel green route was used to synthesize few metal hexacyanoferrates (FeHCF, NiHCF, CoHCF and CuHCF) nanoparticles using Sapindus mukorossias a natural surfactant and water as a solvent. The synthesized nanoparticles were characterized by Powder X-ray diffraction (PXRD), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Fourier Transform Infrared Spectroscopy (FTIR) and Thermo gravimetric techniques. Trasmission electron microscopic images showed that synthesized MHCF nanoparticles exhibited cubic and spherical shapes with exceptionally small sizes ranging from 3nm - 186 nm.

Keywords: metal hexacyanoferrates, natural surfactant, Sapindus mukorossias, nanoparticles

Procedia PDF Downloads 498

Authors: Majid Eslami

Abstract:

Functionally graded materials (FGMs) exhibit heterogeneous microstructures in which the composition and properties gently change in specified directions. The common type of FGMs consist of a metal in which ceramic particles are distributed with a graded concentration. There are many processing routes for FGMs. An important group of these methods is casting techniques (gravity or centrifugal). However, the main problem of casting molten metal slurry with dispersed ceramic particles is a destructive chemical reaction between these two phases which deteriorates the properties of the materials. In order to overcome this problem, in the present investigation a suspension of 6061 aluminum and alumina powders in a liquid polymer was used as the starting material and subjected to centrifugal force for making FGMs. The size rang of these powders was 45-63 and 106-125 μm. The volume percent of alumina in the Al/Al2O3 powder mixture was in the range of 5 to 20%. PMMA (Plexiglas) in different concentrations (20-50 g/lit) was dissolved in toluene and used as the suspension liquid. The glass mold contaning the suspension of Al/Al2O3 powders in the mentioned liquid was rotated at 1700 rpm for different times (4-40 min) while the arm length was kept constant (10 cm) for all the experiments. After curing the polymer, burning out the binder, cold pressing and sintering , cylindrical samples (φ=22 mm h=20 mm) were produced. The density of samples before and after sintering was quantified by Archimedes method. The results indicated that by using the same sized alumina and aluminum powders particles, FGM sample can be produced by rotation times exceeding 7 min. However, by using coarse alumina and fine alumina powders the sample exhibits step concentration. On the other hand, using fine alumina and coarse alumina results in a relatively uniform concentration of Al2O3 along the sample height. These results are attributed to the effects of size and density of different powders on the centrifugal force induced on the powders during rotation. The PMMA concentration and the vol.% of alumina in the suspension did not have any considerable effect on the distribution of alumina particles in the samples. The hardness profiles along the height of samples were affected by both the alumina vol.% and porosity content. The presence of alumina particles increased the hardness while increased porosity reduced the hardness. Therefore, the hardness values did not show the expected gradient in same sample. The sintering resulted in decreased porosity for all the samples investigated.

Keywords: FGM, powder metallurgy, centrifugal method, polymeric suspension

Procedia PDF Downloads 190

Authors: S. Besnaci, S. Bensoltane, H. Locif, S. Saadi

Abstract:

To validate an ecotoxicological approach to assessing toxicological effects caused by the oxide powder of nano-iron Fe2O3, we searched in the ecotoxicology laboratory cell bodies bio accumulators and bio-indicators of soil pollution the snail Helix aspersa. In this study, we evaluated the toxicity of nano Fe2O3 during a very sensitive phase of development H.aspersa (embryonic stage). During embryonic development, we observed in treated with various concentrations of nano Fe2O3 (1.25 g/l, 1.5 g/l, and 2 g/l) compared to control, the deformation of the membrane of the egg and accumulation of this molecule at the rear of the egg proven by the photographs, as with the influence on the hatching percentage.

Keywords: eggs, embryotoxicity, Fe2O3, Helix aspersa, nanoparticles

Procedia PDF Downloads 352

Authors: Yumeho Obata, Mariko Era, Takayoshi Kawahara, Takahide Kanyama, Hiroshi Morita

Abstract:

Dermatophagoides farinae is major mite allergens in indoors. D. farinae is often swarm over powder products (e.g. wheat flour), because it feeds on starch or protein that are included in them. Eating powder products which are mixed D.farinae causes various allergic symptoms. Therefore, the creation of food additive agents with high safety and control of mite effect is required. Fatty acid salts and spices are known that have pesticidal activities. This study describes the effects of fatty acid salts and spices against Dermatophagoides farinae. Materials and Methods: Potassium salts of 9 fatty acids (C4:0, C6:0, C8:0, C10:0, C12:0, C14:0, C18:1, C18:2, C18:3) were prepared by mixing the fatty acid with the appropriate amount of KOH solution to a concentration of 175 mM and pH 10.5. C12Cu and C12Zn were selected as other fatty acid salts. Cayenne pepper, habanero, Japanese pepper, mustard, jalapeno pepper, curry aroma and cinnamon were selected as spices. D. farina, have been cultured in laboratory. To rear the mites, double-soled dishes containing of sterilized food were put on the big plastic container (30.0 × 20.0 × 20.0cm) which had 100% ammonium nitrate solution in the bottom. Plastic container was placed on incubator at 25 °C and 64 % relative humidity (RH) under dark condition. Sterilized food composed of dried bonito flakes and dried yeast (Ebios), 1:1 by weight. The antiproliferative method, sample and medium culture were mixed in double-soled dish and kept at 25 °C and 64 % RH. Decrease rates were determined 1 week and 4 week after treatment under microscope. D. farina was considered to be dead if appendages did not move when prodded with a pin. Results and Conclusions: The results show that the fatty acids potassium showed no antiproliferative effects against D. farinae. On the other hand, Japanese pepper, mustard, curry aroma and cinnamon were effective to decrease propagative rate (over 80 %) after treatment for 1 week against D. farina. Japanese pepper, curry aroma and cinnamon were effective to decrease propagative rate (approximately 100 %) after treatment for 4 weeks against D. farina. Especially, Japanese pepper and cinnamon showed the fasted and the most consecutive antiproliferative effects. These results indicate that Japanese pepper and cinnamon have high antiproliferative effects against D. farina and suggest spices will be used as a food additive agent.

Keywords: fatty acid salts, spices, antiproliferative effects, dermatophagoides farinae

Procedia PDF Downloads 206

Authors: M. Tabatabaee, N. Binavayan, M. R. Nateghi

Abstract:

In this research nano-size of yttrium aluminum garnet (YAG) containing lanthanide metals was synthesized by the sol-gel method in presente citric acid as a complexing agent. Samarium (III) was used to synthesis of YAG:M3+. The prepared powders were characterized by powder X-ray diffraction (PXRD). The size distribution and morphology of the samples were analyzed by scanning electron microscopy (SEM). XRD results show that Sm, La, and ce doped YAG crystallizes in the cubic system and additional peaks compared to pure YAG can be assigned to the presence of Sm in the synthesize YAG. The SEM images show possess spherical nano-sized particle with average 50 nm in diameter.

Keywords: citric acid, nano particle, samarium, yttrium aluminum garnet

Procedia PDF Downloads 285

Authors: Gülşah Çelik Gül, Figen Kurtuluş

Abstract:

The first laboratory synthesis of hard materials such as diamond proceeded to attack of developing materials with high hardness to compete diamond. Boron rich solids are good candidates owing to their short interatomic bond lengths and strong covalent character. Boron containing hard material was synthesized by modified-microwave method under nitrogen atmosphere by using a fuel (glycine or urea), amorphous boron and/or boric acid in appropriate molar ratio. Characterizations were done by x-ray diffraction (XRD), fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy/energy dispersive analyze (SEM/EDS), thermo gravimetric/differantial thermal analysis (TG/DTA).

Keywords: boron containing materials, hard materials, microwave synthesis, powder X-ray diffraction

Procedia PDF Downloads 572

Authors: Maria V. Morozova, Zoya A. Mikhaylovskaya, Elena S. Buyanova, Sofia A. Petrova, Ksenia V. Arishina, Robert G. Zaharov

Abstract:

The present work is devoted to the investigation of two series of doped bismuth molybdates: Bi₂₆-₂ₓMn₂ₓMo₁₀O₆₉-d and Bi₂₆Mo₁₀-₂yMn₂yO₆₉-d. Complex oxides were synthesized by conventional solid state technology and by co-precipitation method. The products were identified by powder diffraction. The powders and ceramic samples were examined by means of densitometry, laser diffraction, and electron microscopic methods. Porosity of the ceramic materials was estimated using the hydrostatic method. The electrical conductivity measurements were carried out using impedance spectroscopy method.

Keywords: bismuth molybdate, columnar structures, impedance spectroscopy, oxygen ionic conductors

Procedia PDF Downloads 405

Authors: Sudip Mondal, Biswanath Mondal, Sudit S. Mukhopadhyay, Apurba Dey

Abstract:

Bioactive materials improve devices for a long lifespan but have mechanical limitations. Mechanical characterization is one of the very important characteristics to evaluate the life span and functionality of the scaffold material. After implantation of scaffold material the primary stage rejection of scaffold occurs due to non biocompatible effect of host body system. The second major problems occur due to the effect of mechanical failure. The mechanical and biocompatibility failure of the scaffold materials can be overcome by the prior evaluation of the scaffold materials. In this study chemically treated Labeo rohita scale is used for synthesizing hydroxyapatite (HAp) biomaterial. Thermo-gravimetric and differential thermal analysis (TG-DTA) is carried out to ensure thermal stability. The chemical composition and bond structures of wet ball-milled calcined HAp powder is characterized by Fourier Transform Infrared spectroscopy (FTIR), X-ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FE-SEM), Transmission Electron Microscopy (TEM), Energy Dispersive X-ray (EDX) analysis. Fish scale derived apatite materials consists of nano-sized particles with Ca/P ratio of 1.71. The biocompatibility through cytotoxicity evaluation and MTT assay are carried out in MG63 osteoblast cell lines. In the cell attachment study, the cells are tightly attached with HAp scaffolds developed in the laboratory. The result clearly suggests that HAp material synthesized in this study do not have any cytotoxic effect, as well as it has a natural binding affinity for mammalian cell lines. The synthesized HAp powder further successfully used to develop porous scaffold material with suitable mechanical property of ~0.8GPa compressive stress, ~1.10 GPa a hardness and ~ 30-35% porosity which is acceptable for implantation in trauma region for animal model. The histological analysis also supports the bio-affinity of processed HAp biomaterials in Wistar rat model for investigating the contact reaction and stability at the artificial or natural prosthesis interface for biomedical function. This study suggests the natural sourced fish scale-derived HAp material could be used as a suitable alternative biomaterial for tissue engineering application in near future.

Keywords: biomaterials, hydroxyapatite, scaffold, mechanical property, tissue engineering

Procedia PDF Downloads 433

Authors: Phakamani Xaba, Robert Huberts, Bilainu Oboirien

Abstract:

It has been over 200 years since margarine was discovered and manufactured using liquid oil, liquified hardstock oils and other oil phase & aqueous phase ingredients. Henry W. Bradley first used vegetable oils in liquid state and around 1871, since then; spreads have been traditionally manufactured using liquified oils. The main objective of this study was to develop a process method to produce spreads using spray dried hardstock fat powders as a structing fats in place of current liquid structuring fats. A high shear mixing system was used to condition the fat phase and the aqueous phase was prepared separately. Using a single scraped surface heat exchanger and pin stirrer, margarine was produced. The process method was developed for to produce spreads with 40%, 50% and 60% fat . The developed method was divided into three steps. In the first step, fat powders were conditioned by melting and dissolving them into liquid oils. The liquified portion of the oils were at 65 °C, whilst the spray dried fat powder was at 25 °C. The two were mixed using a mixing vessel at 900 rpm for 4 minutes. The rest of the ingredients i.e., lecithin, colorant, vitamins & flavours were added at ambient conditions to complete the fat/ oil phase. The water phase was prepared separately by mixing salt, water, preservative, acidifier in the mixing tank. Milk was also separately prepared by pasteurizing it at 79°C prior to feeding it into the aqueous phase. All the water phase contents were chilled to 8 °C. The oil phase and water phase were mixed in a tank, then fed into a single scraped surface heat exchanger. After the scraped surface heat exchanger, the emulsion was fed in a pin stirrer to work the formed crystals and produce margarine. The margarine produced using the developed process had fat levels of 40%, 50% and 60%. The margarine passed all the qualitative, stability, and taste assessments. The scores were 6/10, 7/10 & 7.5/10 for the 40%, 50% & 60% fat spreads, respectively. The success of the trials brought about differentiated knowledge on how to manufacture spreads using non micronized spray dried fat powders as hardstock. Manufacturers do not need to store structuring fats at 80-90°C and even high in winter, instead, they can adapt their processes to use fat powders which need to be stored at 25 °C. The developed process method used one scrape surface heat exchanger instead of the four to five currently used in votator based plants. The use of a single scraped surface heat exchanger translated to about 61% energy savings i.e., 23 kW per ton of product. Furthermore, it was found that the energy saved by implementing separate pasteurization was calculated to be 6.5 kW per ton of product produced.

Keywords: margarine emulsion, votator technology, margarine processing, scraped sur, fat powders

Procedia PDF Downloads 68

Authors: Mohammad Ashraf, Kawther Mohamed

Abstract:

This research tackles a new kind of additions (Nano Clay) and its effect on the features of concrete and both fresh and hardened cement mortar, as well as setting an optimal percentage of adding it to achieve the desired results and obtain on a strong concrete and mortar can be used for skyscrapers. The cementations additions are mineral materials in the form of a fine powder, added to concrete or cement mortar as partly cement substitutes, which means to be added instead of an equivalent amount of cement in order to improve and enhance some features of concrete or both the newly made and hardened cementations materials.

Keywords: nano clay in structure engineering, nanotechnology in construction industry, advanced additions in concrete, special concrete for skyscrapers

Procedia PDF Downloads 299

Authors: Hailemeleak Regassa

Abstract:

Traditional medicines use medicinal plants as a source of ingredients, and many modern medications are indirectly derived from plants. Consumers in affluent nations are growing disenchanted with contemporary healthcare and looking for alternatives. Oxidative stress is the primary cause of multiple diseases, and exogenous antioxidant supplementation or strengthening the body's endogenous antioxidant defenses are potential ways to counteract the negative effects of oxidative damage. Plants can biosynthesize non-enzymatic antioxidants that can reduce ROS-induced oxidative damage. Aging often aids the propagation and development of carcinogenesis, and older animals and older people exhibit increased vulnerability to tumor promoters. Cancer is a major public health issue, with several anti-cancer medications in clinical use. Potential drugs such as flavopiridol, roscovitine, combretastatin A-4, betulinic acid, and silvestrol are in the clinical or preclinical stages of research. Methodology: Microbial Growth media, Dimethyl sulfoxide (DMSO), methanol, ethyl acetate, and n-hexane were obtained from Himedia Labs, Mumbai, India. plant were collected from the Herbal Garden of Shoolini University campus, Solan, India (Latitude - 30.8644° N and longitude - 77.1184° E). The identity was confirmed by Dr. Y.S. Parmar University of Horticulture and Forestry, Nauni, Solan (H.P.), India, and documented in Voucher specimens - UHF- Herbarium no. 13784; vide book no. 3818 Receipt No. 086. The plant materials were washed with tap water, and 0.1% mercury chloride for 2 minutes, rinsed with distilled water, air dried, and kept in a hot air oven at 40ºc on blotting paper until all the water evaporated and became well dried for grinding. After drying, the plant materials were grounded using a mixer grinder into fine powder transferred into airtight containers with proper labeling, and stored at 4ºc for future use (Horablaga et al., 2023). The extraction process was done according to Altemimi et al., 2017. The 5g powder was mixed with 15 ml of the respective solvents (n-hexane, ethyl acetate, and methanol), and kept for 4-5 days on the platform shaker. The solvents used are based on their increasing polarity index. Then the extract was centrifuged at 10,000rpm for 5 minutes and filtered using No.1 Whatman filter paper.

Keywords: cancer, phytomedicine, medicinal plants, oncology

Procedia PDF Downloads 34

Authors: Leonardo Parra, Daniel Martínez, Jorge Pizarro, Fernando Ortega, Manuel Chacón-Fuentes, Andrés Quiroz

Abstract:

Control of Dalaca pallens or blackworms, one of the most important hypogeous pest in grassland in southern Chile, is based on the use of broad-spectrum insecticides such as organophosphates and pyrethroids. However, the rapid development of insecticide resistance in field populations of this insect and public concern over the environmental impact of these insecticides has resulted in the search for other control methods. Specifically, the use of endophyte fungi for controlling pest has emerged as an interesting and promising strategy. Endophytes from ryegrass (Lolium perenne), establish a biotrophic relationship with the host, defined as mutualistic symbiosis. The plant-fungi association produces alkaloids where peramine is the main toxic substance against Listronotus bonariensis, the most important epigean pest of ryegrass. Nevertheless, the effect of peramina on others pest insects, such as D. pallens, to our knowledge has not been studied, and also its possible metabolization in the body of the larvae. Therefore, we addressed the following research question: Do larvae of D. pallens store peramine after consumption of ryegrass endophyte infected (E+)? For this, specimens of blackworms were fed with ryegrass plant of seven experimental lines and one commercial cultivar endophyte free (E-) sown at the Instituto de Investigaciones Agropecuarias Carillanca (Vilcún, Chile). Once the feeding period was over, ten larvae of each treatment were examined. Individuals were dissected, and their gut was removed to exclude any influence of remaining material. The rest of the larva's body was dried at 60°C by 24-48 h and ground into a fine powder using a mortar. 25 mg of dry powder was transferred to a microcentrifuge tube and extracted in 1 mL of a mixture of methanol:water:formic acid. Then, the samples were centrifuged at 16,000 rpm for 3 min, and the supernatant was colected and injected in the liquid chromatography of high resolution (HPLC). The results confirmed the presence of peramine in the larva's body of D. pallens. The insects that fed the experimental lines LQE-2 and LQE-6 were those where peramine was present in high proportion (0.205 and 0.199 ppm, respectively); while LQE-7 and LQE-3 obtained the lowest concentrations of the alkaloid (0.047 and 0.053 ppm, respectively). Peramine was not detected in the insects when the control cultivar Jumbo (E-) was tested. These results evidenced the storage and metabolism of peramine during consumption of the larvae. However, the effect of this alkaloid present in 'future ryegrass cultivars' (LQE-2 and LQE-6) on the performance and survival of blackworms must be studied and confirmed experimentally.

Keywords: blackworms, HPLC, alkaloid, pest

Procedia PDF Downloads 278