Authors: Abbas Nasir, Xiong Zhang, Sohail Ahmad, Yiping Cui

Abstract:

Non-polar a-plane AlGaN epilayers of high structural quality have been grown on r-sapphire substrate by using metalorganic chemical vapor deposition (MOCVD). A graded non-polar AlGaN buffer layer with variable aluminium concentration was used to improve the structural quality of the non-polar a-plane AlGaN epilayer. The characterisations were carried out by high-resolution X-ray diffraction (HR-XRD), atomic force microscopy (AFM) and Hall effect measurement. The XRD and AFM results demonstrate that the Al-composition-graded non-polar AlGaN buffer layer significantly improved the crystalline quality and the surface morphology of the top layer. A low root mean square roughness 1.52 nm is obtained from AFM, and relatively low background carrier concentration down to 3.9×  cm^-3 is obtained from Hall effect measurement.

Keywords: Non-polar AlGaN epilayer, Al composition-graded AlGaN layer, root mean square, background carrier concentration.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 465

Authors: Li Yuan, Weizhu Wang, Kean Boon Lee, Haifeng Sun, Susai Lawrence Selvaraj, Shane Todd, Guo-Qiang Lo

Abstract:

In this work, the physical based device model of AlGaN/GaN high electron mobility transistors (HEMTs) has been established and the corresponding device operation behavior has been investigated also by using Sentaurus TCAD from Synopsys. Advanced AlGaN/GaN hetero-structures with GaN cap layer and AlN spacer have been considered and the GaN cap layer and AlN spacer are found taking important roles on the gate leakage blocking and off-state breakdown voltage enhancement.

Keywords: AlGaN/GaN, HEMT, Physical mechanism, TCAD simulation

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 3757

Authors: W. Z. Wang, S. Todd, S. B. Dolmanan, K. B. Lee, L. Yuan, H. F. Sun, S. L. Selvaraj, M.Krishnakumar, G. Q. Lo, S. Tripathy

Abstract:

The crystalline quality of the AlGaN/GaN high electron mobility transistor (HEMT) structure grown on a 200 mm silicon substrate has been investigated using UV-visible micro- Raman scattering and photoluminescence (PL). The visible Raman scattering probes the whole nitride stack with the Si substrate and shows the presence of a small component of residual in-plane stress in the thick GaN buffer resulting from a wafer bowing, while the UV micro-Raman indicates a tensile interfacial stress induced at the top GaN/AlGaN/AlN layers. PL shows a good crystal quality GaN channel where the yellow band intensity is very low compared to that of the near-band-edge transition. The uniformity of this sample is shown by measurements from several points across the epiwafer.

Keywords: Raman, photo luminescence, AlGaN/GaN, HEMT.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 3896

Authors: A. Douara, N. Kermas, B. Djellouli

Abstract:

In this study, we report calculations of gate capacitance of AlGaN/GaN HEMTs with nextnano device simulation software. We have used a physical gate capacitance model for III-V FETs that incorporates quantum capacitance and centroid capacitance in the channel. These simulations explore various device structures with different values of barrier thickness and channel thickness. A detailed understanding of the impact of gate capacitance in HEMTs will allow us to determine their role in future 10 nm physical gate length node.

Keywords: AlGaN/GaN, centroid capacitance, gate capacitance, HEMT, quantum capacitance.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1836

Authors: K. Karami, S. Hassan, S. Taking, A. Ofiare, A. Dhongde, A. Al-Khalidi, E. Wasige

Abstract:

We have made a comparative study on the influence of Al2O3 and HfO2 grown using Atomic Layer Deposition (ALD) technique as dielectric in the AlGaN/GaN metal oxide semiconductor high electron mobility transistor (MOS-HEMT) structure. Five samples consisting of 20 nm and 10 nm each of A2lO3 and HfO2 respectively and a Schottky gate HEMT, were fabricated and measured. The threshold voltage shifts towards negative by 0.1 V and 1.8 V for 10 nm thick HfO2 and 10 nm thick Al2O3 gate dielectric layers, respectively. The negative shift for the 20 nm HfO2 and 20 nm Al2O3 were 1.2 V and 4.9 V, respectively. Higher gm/IDS (transconductance to drain current) ratio was also obtained in HfO2 than Al2O3. With both materials as dielectric, a significant reduction in the gate leakage current in the order of 104 was obtained compared to the sample without the dielectric material.

Keywords: AlGaN/GaN HEMTs, Al2O3, HfO2, MOSHEMTs.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 313

Authors: Chia-Jui Yu, Chien-Ju Chen, Jyun-Hao Liao, Chia-Ching Wu, Meng-Chyi Wu

Abstract:

In this letter, we demonstrate high-performance AlGaN/GaN planar Schottky barrier diodes (SBDs) on the silicon substrate with field plate structure for increasing breakdown voltage V_B. A low turn-on resistance R_ON (3.55 mΩ-cm²), low reverse leakage current (< 0.1 µA) at -100 V, and high reverse breakdown voltage V_B (> 1.1 kV) SBD has been fabricated. A virgin SBD exhibited a breakdown voltage (measured at 1 mA/mm) of 615 V, and with the field plate technology device exhibited a breakdown voltage (measured at 1 mA/mm) of 1525 V (the anode–cathode distance was L_AC = 40 µm). Devices without the field plate design exhibit a Baliga’s figure of merit of V_B²/ R_ON = 60.2 MW/cm², whereas devices with the field plate design show a Baliga’s figure of merit of V_B²/ R_ON = 340.9 MW/cm² (the anode–cathode distance was L_AC = 20 µm).

Keywords: AlGaN/GaN heterostructure, silicon substrate, Schottky barrier diode, high breakdown voltage, field plate, Baliga’s figure-of-merit.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 984

Authors: A. Hamdoune, M. Abdelmoumene, A. Hamroun

Abstract:

The objective of this paper is to simulate static I-V and dynamic characteristics of an appropriated and recessed n-GaN/AlxGa1-xN/GaN high electron mobility (HEMT). Using SILVACO TCAD device simulation, and optimized technological parameters; we calculate the drain-source current (lDS) as a function of the drain-source voltage (VDS) for different values ​​of the gate-source voltage (VGS), and the drain-source current (lDS) depending on the gate-source voltage (VGS) for a drain-source voltage (VDS) of 20 V, for various temperatures. Then, we calculate the cut-off frequency and the maximum oscillation frequency for different temperatures.

We obtain a high drain-current equal to 60 mA, a low knee voltage (Vknee) of 2 V, a high pinch-off voltage (VGS0) of 53.5 V, a transconductance greater than 600 mS/mm, a cut-off frequency (f_T) of about 330 GHz, and a maximum oscillation frequency (fmax) of about 1 THz.

Keywords: n-GaN/AlGaN/GaN HEMT, drain-source current (IDS), transconductance (gm), cut-off frequency (fT), maximum oscillation frequency (fmax).

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2304

Authors: AlNPhannee Saengkaew, Armin Dadgar, Juergen Blaesing, Thomas Hempel, Sakuntam Sanorpim, Chanchana Thanachayanont, Visittapong Yordsri, Watcharee Rattanasakulthong, Alois Krost

Abstract:

Group-III nitride material as particularly AlxGa1-xN is one of promising optoelectronic materials to require for shortwavelength devices. To achieve the high-quality AlxGa1-xN films for a high performance of such devices, AlN-nucleation layers are the important factor. To improve the AlN-nucleation layers with a variation of Ga-addition, XRD measurements were conducted to analyze the crystalline quality of the subsequent Al0.1Ga0.9N with the minimum ω-FWHMs of (0002) and (10-10) reflections of 425 arcsec and 750 arcsec, respectively. SEM and AFM measurements were performed to observe the surface morphology and TEM measurements to identify the microstructures and orientations. Results showed that the optimized Ga-atoms in the Al(Ga)Nnucleation layers improved the surface diffusion to form moreuniform crystallites in structure and size, better alignment of each crystallite, and better homogeneity of island distribution. This, hence, improves the orientation of epilayers on the Si-surface and finally improves the crystalline quality and reduces the residual strain of subsequent Al0.1Ga0.9N layers.

Keywords: AlGaN, UV-LEDs, seed layers, AFM, TEM

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1531