Search results for: sulfur doping

Authors: Abdel Khalek Selim, Safaa Mahmoud

Abstract:

Experiments were designed to study nitrogen loss through leaching in soil columns treated with different nitrogen sources and elemental sulfur. The soil material (3 kg alluvial or calcareous soil) were packed in Plexiglas columns (10 cm diameter). The soil columns were treated with 2 g N in the form of Ca(NO3)2, urea, urea + inhibitor (Nitrapyrin), another set of these treatments was prepared to add elemental sulfur. During incubation period, leaching was performed by applying a volume of water that allows the percolation of 250-ml water throughout the soil column. The leachates were analyzed for NH4-N and N03-N. After 10 weeks, soil columns were cut into four equal segments and analyzed for ammonium, nitrate, and total nitrogen. Results indicated the following: Ca(NO3)2 treatment showed a rapid NO3 leaching, especially in the first 3 weeks, in both clay and calcareous soils. This means that soil texture did not play any role in this respect. Sulfur addition also did not affect the rate of NO3 leaching. In urea treatment, there was a steady increase of NH4- and NO3–N from one leachate to another. Addition of sulfur with urea slowed down the nitrification process and decreased N losses. Clay soil contained residual N much more than calcareous soil. Almost one-third of added nitrogen might have been immobilized by soil microorganisms or lost through other loss paths. Nitrification inhibitor can play a role in preserving added nitrogen from being lost through leaching. Combining the inhibitor with elemental sulfur may help to stabilize certain preferred ratio of NH4 to NO3 in the soil for the benefit of the growing plants.

Keywords: alluvial soil, calcareous soil, elemental sulfur, nitrate leaching

Procedia PDF Downloads 289

Authors: E. Y. Jo, S. M. Park, I. S. Yeo, K. K. Kim, S. J. Park, Y. K. Kim, Y. D. Kim, C. G. Park

Abstract:

SO3 is created in small quantities during the combustion of fuel that contains sulfur, with the quantity produced a function of the boiler design, fuel sulfur content, excess air level, and the presence of oxidizing agents. Typically, about 1% of the fuel sulfur will be oxidized to SO3, but it can range from 0.5% to 1.5% depending on various factors. Combustion of fuels that contain oxidizing agents, such as certain types of fuel oil or petroleum coke, can result in even higher levels of oxidation. SO3 levels in the flue gas emitted by combustion are very high, which becomes a cause of machinery corrosion or a visible blue plume. Because of that, power plants firing petroleum residues need to installation of SO3 removal system. In this study, SO3 removal system using salt solution was developed and several salts solutions were tested for obtain optimal solution for SO3 removal system. Response surface methodology was used to optimize the operation parameters such as gas-liquid ratio, concentration of salts.

Keywords: flue gas desulfurization, petroleum cokes, Sulfur trioxide, SO3 removal

Procedia PDF Downloads 486

Authors: Prakash Chand, Anurag Gaur, Ashavani Kumar

Abstract:

In the present study, we have synthesized Cr and Fe doped zinc oxide (ZnO) nano-structures (Zn1-δCraFebO; where δ= a + b=20%, a = 5, 6, 8 & 10% and b=15, 14, 12 & 10%) via sol-gel method at different doping concentrations. The synthesized samples were characterized for structural properties by X-ray diffractometer and field emission scanning electron microscope and the optical properties were carried out through photoluminescence and UV-visible spectroscopy. The particle size calculated through field emission scanning electron microscope varies from 41 to 96 nm for the samples synthesized at different doping concentrations. The optical band gaps calculated through UV-visible spectroscopy are found to be decreasing from 3.27 to 3.02 eV as the doping concentration of Cr increases and Fe decreases.

Keywords: nano-structures, optical properties, sol-gel method, zinc oxide

Procedia PDF Downloads 288

Authors: Abid Boudiar

Abstract:

We propose a simple model to obtain an exact expression of Tc/(Tc,max) for the temperature-doping phase diagram of superconducting cuprates. We showed that our model predicted most phase diagram scenario. We found the exact special doping points p(opt), p(qcp) and an accurate E(g,max). Some other properties such as the stripes length 100.1°A and the energy gap in cuprates chain
6meV can also be calculated exactly. Another interesting consequence of this simple picture is the new magic numbers and the ability to express everything using a (Tc,p) diagram via the golden ratio.

Keywords: superconducting cuprates, phase, pseudogap, hole doping, strips, golden ratio, soliton

Procedia PDF Downloads 446

Authors: Yuban Sebastian Cuartas-Agudelo, Sandra Marcela López-Hincapié, Vivianna Alexandra Garrido-Altamar, María de los Ángeles Rodríguez-Gázquez, Camilo Ruiz-Mejía, Lina María Martínez-Sánchez, Gloria Inés Martínez-Domínguez, Luis Eduardo Contreras, Felipe Eduardo Marino-Isaza

Abstract:

Introduction: Doping is a prohibited practice in competitive sports with potential adverse effects; therefore, it is crucial to describe the attitudes of athletes towards this behavior and to determine which o these increase the susceptibility to carry out this practice. Objective: To determine the attitude of high-performance athletes towards doping in a sports institute in the city of Medellin, Colombia. Methods: We performed a cross-sectional study during 2016, with a sample taken to convenience consisting of athletes over 18 years old enrolled in a sports institute of the city of Medellin (Colombia). The athletes filled by themselves the Petroczi and Aidman questionnaire: Performance Enhancement Attitude Scale (PEAS) adapted to the Spanish language by Morente-Sánchez et al. This scale has 17 items with likert answer options, with a score ranging from 1 to 6, with a higher score indicating a stronger tendency towards doping practices. Results: 112 athletes were included with an average age of 21.6 years old, a 60% of them were male and the most frequent sports were karate 17%, judo 12.5% and athletics 9.8%. The average score of the questionnaire was 35.5 points of a 102 possible points. The lowest score was obtained in the following items: Is Doping necessary 1,4 and Doping isn’t cheating, everyone does it 1,5. Conclusion: In our population, there is a low tendency towards doping practices.

Keywords: sports, doping in sports, athletic performance, attitude

Procedia PDF Downloads 190

Authors: Pallavi Marathe

Abstract:

Voice is considered to be a unique biometric property of human beings. Unlike other biometric evidence, for example, fingerprints and retina scans, etc., voice can be easily changed or mimicked. The present paper talks about how the inhalation of helium and sulfur hexafluoride (SF6) gas affects the voice formant frequencies that are the resonant frequencies of the vocal tract. Helium gas is low-density gas; hence, the voice travels with a higher speed than that of air. On the other side in SF6 gas voice travels with lower speed than that of air due to its higher density. These results in decreasing the resonant frequencies of voice in helium and increasing in SF6. Results are presented with the help of Praat software, which is used for voice analysis.

Keywords: voice formants, helium, sulfur hexafluoride, gas inhalation

Procedia PDF Downloads 90

Authors: Dawit Burusie Abdi, Mamidala Jagadesh Kumar

Abstract:

In this paper, using 2D TCAD simulations, the application of a dual material gate (DMG) for suppressing ambipolar conduction in a tunnel field effect transistor (TFET) is demonstrated. Using the proposed DMG concept, the ambipolar conduction can be effectively suppressed even if the drain doping is as high as that of the source doping. Achieving this symmetrical doping, without the ambipolar conduction in TFETs, gives the advantage of realizing both n-type and p-type devices with the same doping sequences. Furthermore, the output characteristics of the DMG TFET exhibit a good saturation when compared to that of the gate-drain underlap approach. This improved behavior of the DMG TFET makes it a good candidate for inverter based logic circuits.

Keywords: dual material gate, suppressing ambipolar current, symmetrically doped TFET, tunnel FETs, PNPN TFET

Procedia PDF Downloads 342

Authors: Melissa Chavez Portillo, Hector Juarez Santiesteban, Mauricio Pacio Castillo, Oscar Portillo Moreno

Abstract:

Nanocrystalline Li-doped PbS thin films have been deposited by chemical bath deposition technique. The goal of this work is to study the modification of the optoelectronic and structural properties of Lithium incorporation. The increase of Li doping in PbS thin films leads to an increase of band gap in the range of 1.4-2.3, consequently, quantum size effect becomes pronounced in the Li-doped PbS films, which lead to a significant enhancement in the optical band gap. Doping shows influence in the film growth and results in a reduction of crystallite size from 30 to 14 nm. The refractive index was calculated and a relationship with dielectric constant was investigated. The dc conductivities of Li-doped and undoped samples were measured in the temperature range 290-340K, the conductivity increase with increase of Lithium content in the PbS films.

Keywords: doping, quantum confinement, optical band gap, PbS

Procedia PDF Downloads 352

Authors: Kriti Tyagi, Bhasker Gahtori

Abstract:

Various groups have attempted on enhancing the thermoelectric figure-of-merit (ZT) of the Cu₃SbSe₄ compound by employing doping process. Efforts are made to study the thermoelectric performance of Cu₃SbSe₄ material doped with Te in different compositions (i. e. Cu₃Sb₁₋ₓTeₓSe₄, x = 0.005, 0.01, 0.015, 0.02). The different doping concentration has been selected to identify the suitable doping to increase the thermoelectric performance. Compared to pristine Cu₃SbSe₄, an enhancement of thermoelectric figure-of-merit was achieved for 0.005 Te doped Cu₃SbSe₄. This improvement can be attributed to the reduction of thermal conductivity for 0.005 Te doped Cu₃SbSe₄.

Keywords: figure-of-merit, polycrystalline, thermal conductivity, thermoelectric

Procedia PDF Downloads 211

Authors: Osama Madkhali

Abstract:

GdAl₃(BO₃)₄ phosphors, incorporating Dy³+ and Dy³+/Eu³+ activators, were successfully synthesized via the gel combustion method. Powder X-ray diffraction (XRD) was utilized to ascertain phase purity and assess the impact of dopant concentration on the crystallographic structure. Photoluminescence (PL) measurements revealed that luminescence properties' intensity and lifetime varied with Dy³+ and Eu³+ ion concentrations. The relationship between luminescence intensity and doping concentration was explored in the context of the energy transfer process between Eu³+ and Dy³+ ions. An increase in Eu³+ co-doping concentrations resulted in a decrease in luminescence lifetime. Energy transfer efficiency was significantly enhanced from 26% to 84% with Eu³+ co-doping, as evidenced by decay curve analysis. These findings position GdAl₃(BO₃)4: Dy³+, Eu³+ phosphors as promising candidates for LED applications in solid-state lighting and displays.

Keywords: GdAl₃(BO₃)₄ phosphors, Dy³+/Eu³+ co-doping, photoluminescence (PL) measurements, luminescence properties, LED applications, solid-state lighting

Procedia PDF Downloads 23

Authors: P. Jost, L. Muckova, M. Matula, J. Pejchal, D. Jun, R. Stetina

Abstract:

Sulfur mustard (bis(2-chlorethyl) sulfide) is highly toxic, chemical warfare agent that has been used in the past in several armed conflicts. Except for the skin, respiratory tract is one of the important routes of exposure. The elucidation and understanding of the mechanism of toxicity of SM have been effort intensive research. The multiple targets character of SM caused cellular damage resulted in activation of many different mechanisms which contribute to cellular response and participate in the final cytopathology effect. In our present work, we compared time-dependent changes in sulfur mustard exposed adult human lung fibroblasts NHLF and lung epithelial alveolar cell line A-549. Cell viability (MTT assay, Calcein-AM assay, and xCELLigence - real-time cell analysis), apoptosis (flow cytometry), mitochondrial membrane potential (Δψm, flow cytometry), reactive oxygen species induction (DC and cell cycle distribution (flow cytometry) were studied. We observed significantly decreased mitochondrial membrane potential and subsequent induction of apoptosis correlating with decreased cellular viability in the sulfur mustard exposed cells. In low concentrations, sulfur mustard-induced S-phase cell cycle arrest, on the other hand, high concentrations, cell cycle phase distribution of sulfur mustard exposed cells resembled cell cycle phase distribution of control group, which implies nonspecific cell cycle inhibition. Epithelial cells A-549 was found as more sensible to sulfur mustard toxicity. Acknowledgements: This work was supported by a long-term organization development plan Medical Aspects of Weapons of Mass Destruction of the Faculty of Military Health Sciences, University of Defence.

Keywords: apoptosis, cell cycle, cytotoxicity, sulfur mustard

Procedia PDF Downloads 160

Authors: Nayeon, Lee, Won-Young, Cho, Hyun Joo, Jang, Chi-Ho, Lee

Abstract:

This study investigated the effects of the dietary supplementation of the Allium hookeri root, and processed sulfur, on the growth performance of guinea pigs. The guinea pigs were fed a control diet (CON), as well as the control diet including 1% freeze-dried Allium hookeri root (AH), or 0.1% processed sulfur (S), or including both the freeze-dried Allium hookeri root and the processed sulfur (AHS). The weight of perirenal adipose tissue (PAT) and the epididymal adipose tissue (EAT) in the AH were significantly lower than CON (p < 0.05). The serum cholesterols levels of the AH and the AHS were significantly lower than the S (p < 0.05). While the total saturated fatty acid content in the serum of the AH and AHS groups showed a tendency to decrease, the total monounsaturated fatty acid increased. The results of this study suggested that dietary consumption of Allium hookeri root may help to decrease fat accumulation, lower serum cholesterol levels, and control serum free fatty acid contents in the guinea pigs.

Keywords: Allium hookeri, dietary supplementation, growth performance, processed sulfur, Guinea pig

Procedia PDF Downloads 237

Authors: Liyew Yizengaw Yitayih

Abstract:

This nanotechnology study focuses on how potassium ions (K+) affect lithium-ion (Li-ion) battery performance. By adding potassium ions (K+) to the lithium tin oxide (LiSnO) anode and employing styrene-butadiene rubber (SBR) as a binder, the doping of K+ was specifically studied. The methods employed in this study include computer modeling and simulation, material fabrication, and electrochemical characterization. The potassium ions (Li+) were successfully doped into the LiSnO lattice during charge/discharge cycles, which increased the lithium-ion diffusivity and electrical conductivity within the anode. However, it was found that internal doping of potassium ions (K+) into the LiSnO lattice occurred at high potassium ion concentrations (>16.6%), which hampered lithium ion transfer because of repulsion and physical blockage. The electrochemical efficiency of lithium-ion batteries was improved by this comprehensive study's presentation of potassium ions' (K+) potential advantages when present in the appropriate concentrations in electrode materials.

Keywords: lithium-ion battery, LiSnO anode, potassium doping, lithium-ion diffusivity, electronic conductivity

Procedia PDF Downloads 36

Authors: Yasaman Tabari-Saadi, Kaiwen Sun, Jialiang Huang, Martin Green, Xiaojing Hao

Abstract:

Optical and electrical properties of p-type AgBiS₂ absorber material have been improved by copper doping on silver sites. X-Ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) analysis suggest that complete solid solutions of Ag₁₋ₓCuₓBiS₂ thin film have been formed. The carrier concentration of pure AgBiS₂ thin film deposited by the chemical process is 4.5*E+14 cm⁻³, and copper doping leads to the improved carrier concentration despite the semiconductor AgBiS₂ remains p-type semiconductor. Copper doping directly changed the absorption coefficient and increased the optical band gap (~1.5eV), which makes it a promising absorber for thin-film solar cell applications.

Keywords: copper doped, AgBiS₂, thin-film solar cell, carrier concentration, p-type semiconductor

Procedia PDF Downloads 89

Authors: Avinashkumar Karre

Abstract:

Sulfur recovery unit, most commonly called as Claus process, is very significant gas desulfurization process unit in refinery and gas industries. Explorations of new natural gas fields, refining of high-sulfur crude oils, and recent crude expansion projects are needing capacity expansion of Claus unit for many companies around the world. In refineries, the sulphur recovery units take acid gas from amine regeneration units and sour water strippers, converting hydrogen sulfide to elemental sulfur using the Claus process. The Claus process is hydraulically limited by mass flow rate. Reducing the pressure drop across control valves, flow meters, lines, knock-out drums, and packing improves the capacity. Oxygen enrichment helps improve the capacity by removing nitrogen, this is more commonly done on all capacity expansion projects. Typical upgrades required due to oxygen enrichment are new burners, new refractory in thermal reactor, resizing of 1st condenser, instrumentation changes, and steam/condensate heat integration. Some other capacity expansion options typically considered are tail gas compressor, replacing air blower with higher head, hydrocarbon minimization in the feed, water removal, and ammonia removal. Increased capacity related upgrades in sulfur recovery unit also need changes in the tail gas treatment unit, typical changes include improvement to quench tower duty, packing area upgrades in quench and absorber towers and increased amine circulation flow rates.

Keywords: Claus process, oxygen enrichment, sulfur recovery unit, tail gas treatment unit

Procedia PDF Downloads 94

Authors: P. C. Okafor, A. J. Ekpunobi

Abstract:

Mn doped copper sulphide (CuS:Mn) nano-films were deposited on indiums coated tin oxide (ITO) glass substrates using electrodeposition method. Electrodeposition was carried out using bath of PH = 3 at room temperature. Other depositions parameters such as deposition time (DT) are kept constant while Mn doping was varied from 3% to 23%. Absorption spectra of CuS:Mn films was obtained by using JENWAY 6405 UV-VIS -spectrophotometer. Optical band gap (E_g ), optical conductivity (σo) and electrical conductivity (σe) of CuS:Mn films were determined using absorption spectra and appropriate formula. The effect of Mn doping % on these properties were investigated. Results show that film thickness (t) for the 13.27 nm to 18.49 nm; absorption coefficient (α) from 0.90 x 1011 to 1.50 x 1011 optical band gap from 2.29eV to 2.35 eV; optical conductivity from 1.70 x 1013 and electrical conductivity from 160 millions to 154 millions. Possible applications of such films for solar cells fabrication and optoelectronic devices applications were also discussed.

Keywords: copper sulphide (CuS), Manganese (Mn) doping, electrodeposition, optical band gap, optical conductivity, electrical conductivity

Procedia PDF Downloads 679

Authors: S. M. AL-Shomar, N. B. Ibrahim, Sahrim Hj. Ahmad

Abstract:

ZnO thin films with various Gd doping concentration (0, 0.01, 0.03 and 0.05 mol/L) have been synthesized by sol–gel method on quartz substrates at annealing temperature of 600 ºC. X-ray analysis reveals that ZnO(Gd) films have hexagonal wurtzite structure. No peaks that correspond to Gd metal clusters or gadolinium acetylacetonate are detected in the patterns. The position of the main peak (101) shifts to higher angles after doping. The surface morphologies studied using a field emission scanning electron microscope (FESEM) showed that the grain size and the films thickness reduced gradually with the increment of Gd concentration. The roughness of ZnO film investigated by an atomic force microscopy (AFM) showed that the films are smooth and high dense grain. The roughness of doped films decreased from 6.05 to 4.84 rms with the increment of dopant concentration.The optical measurements using a UV-Vis-NIR spectroscopy showed that the Gd doped ZnO thin films have high transmittance (above 80%) in the visible range and the optical band gap increase with doping concentration from 3.13 to 3.39 eV. The doped films show low electrical resistivity 2.6 × 10-3Ω.cm.at high doping concentration.

Keywords: Gd doped ZnO, electric, optics, microstructure

Procedia PDF Downloads 435

Authors: Mauludi Ariesto Pamungkas, Wafa Maftuhin

Abstract:

Gallium with three outer electrons commonly are used as dopants of silicon to make it P type and N type semiconductor respectively. Silicene, one-atom-thick silicon layer is one of emerging two dimension materials after the success of graphene. The effects of Gallium doping on electronic structure of silicine are investigated by using first principle calculation based on Density Functional Theory (DFT) calculation and norm conserving pseudopotential method implemented in ABINIT code. Bandstructure of Pristine silicene is similar to that of graphene. Effect of Ga doping on bandstructure of silicene depend on the position of Ga adatom on silicene

Keywords: silicene, effects of Gallium doping, Density Functional Theory (DFT), graphene

Procedia PDF Downloads 407

Authors: Mirko Ante, Şeniz Sörgel, Andreas Bund

Abstract:

Li-S- (Lithium-Sulfur-) battery systems provide very high specific gravimetric energy (2600 Wh/kg) and volumetric energy density (2800Wh/l). Hence, Li-S batteries are one of the key technologies for both the upcoming electromobility and stationary applications. Furthermore, the Li-S battery system is potentially cheap and environmentally benign. However, the technical implementation suffers from cycling stability, low charge and discharge rates and incomplete understanding of the complex polysulfide reaction mechanism. The aim of this work is to develop an effective electrocatalyst for the polysulfide reactions so that the electrode kinetics of the sulfur half-cell will be improved. Accordingly, the overvoltage will be decreased, and the efficiency of the cell will be increased. An enhanced electroactive surface additionally improves the charge and discharge rates. To reach this goal, functionalized electrocatalytic coatings are investigated to accelerate the kinetics of the polysulfide reactions. In order to determine a suitable electrocatalyst, apparent exchange current densities of a variety of materials (Ni, Co, Pt, Cr, Al, Cu, ITO, stainless steel) have been evaluated in a polysulfide containing electrolyte by potentiodynamic measurements and a Butler-Volmer fit including diffusion limitation. The samples have been examined by Scanning Electron Microscopy (SEM) after the potentiodynamic measurements. Up to now, our work shows that cobalt is a promising material with good electrocatalytic properties for the polysulfide reactions and good chemical stability in the system. Furthermore, an electrodeposition from a modified Watt’s nickel electrolyte with a sulfur source seems to provide an autocatalytic effect, but the electrocatalytic behavior decreases after several cycles of the current-potential-curve.

Keywords: electrocatalyst, energy storage, lithium sulfur battery, sulfur electrode materials

Procedia PDF Downloads 340

Authors: Hamidreza Sahaleh

Abstract:

Because of the stringent prerequisite of low sulfur and heavier raw oil feedstock more hydrogen will be devoured in the refineries. Specifically if huge scale limits are the reaction to an expanded hydrogen request, certain configuration and building background are obliged with, which will be depicted in this paper with an illustration. Chosen procedure plan prerequisite will be recorded and portrayed in agreement to the flowsheet. Also, a determination of imaginative outline elements, similar to process condensate reuse, safe reformer start up and prerequisites will be highlighted.

Keywords: low sulfur, raw oil, refineries, flowsheet

Procedia PDF Downloads 264

Authors: Mahadula I. P. Kumari, Kasturiratne A., De Silva AP

Abstract:

Doping refers to an athlete's use of banned substances as a method to improve training and performance in sports. It is known that some young athletes use banned substances in Sri Lanka without knowing their side effects and associated health risks. The main objective of this study was to describe the level of knowledge and attitude among junior athletes and coaches on doping in sports. This is a descriptive cross-sectional study. Four individual sports and six team sports were taken into the study. Schools were selected considering the results of the all-island school sports competitions 2017. Two hundred sixty-two female athletes, 290 male athletes and 30 coaches representing all sports counted into this study. The data collection method was a self-administered questionnaire and SPSS Version 21 was used for the data analysis. According to the result, 79% of athletes have heard of the term "doping," and 21% have never heard of it. This means these children have not been educated on doping. A number of questions were asked to study the level of knowledge of the coaches and players. Those who answered the questions correctly were given a mark. According to the marks, it is evident that the level of knowledge of the players and coaches is very low. All athletes and coaches do not accept the use of banned substances. This shows that athletes and coaches have a good attitude about winning without cheating. It was evident that athletes in athletics, weightlifting, rugby, and badminton had some level of knowledge about banned substances. All coaches stated that school athletes and coaches do not have sufficient knowledge of banned substances. And they should be made aware of it. This study has revealed that school/Junior athletes and coaches have limited knowledge of banned substances. School children and coaches need to be educated about banned substances and their harmful effects.

Keywords: attitude, doping, knowledge, Sri Lanka

Procedia PDF Downloads 220

Authors: A. Kistaubayeva, I. Savitskaya, D. Ibrayeva, M. Abdulzhanova, N. Voronova

Abstract:

36 strains of sulfur-oxidizing bacteria were isolated in Southern Kazakhstan soda-saline soils and identified. Screening of strains according bio-oxidation (destruction thiosulfate to sulfate) and enzymatic (Thiosulfate dehydrogenises and thiosulfate reductase) activity was conducted. There were selected modes of aeration and culture conditions (pH, temperature), which provide optimum harvest cells. These strains can be used in bio-melioration technology.

Keywords: elemental sulfur, oxidation activity, Тhiobacilli, fertilizers, heterotrophic S-oxidizers

Procedia PDF Downloads 361

Authors: Yong-Jie Lin, Yi-Feng Lin

Abstract:

In this study, scandium-doped yttria-stabilized zirconia (ScYSZ) and In2O3 nanoparticles (NPs) with cubic crystalline structures were successfully prepared using a facile hydrothermal process. ScYSZ films were prepared by the pressing of ScYSZ NPs and were further used for the electrolyte of solid oxide fuel cells (SOFCs). To increase the ionic conductivity of the ScYSZ electrolyte, different amounts of In2O3 NPs [0 wt% (X(In2O3)=0), 0.21 wt% (X(In2O3)=0.001) and 1.13 wt% (X(In2O3)=0.005)] were doped in the ScYSZ films to increase their oxygen vacancy. The result shows In2O3 NP/ScYSZ films with 1.13 wt% (X(In2O3 )=0.005) In2O3 NPs doping are with largest ionic conductivity of 0.057Ω-1 cm-1 at 900oC, which is 1.6 and 1.8 times higher than YSZ and In2O3 NP/ScYSZ films with 0.21 wt% (X(In2O3)=0.001) In2O3 NPs doping, respectively.

Keywords: indium oxide/scandium doping Yttria-stabilized zirconia, solid oxide fuel cells, scandium-doped yttria-stabilized zirconia, indium oxide

Procedia PDF Downloads 436

Authors: S. Ivanova, K. Ivanov

Abstract:

Bemitil (2-ethylthiobenzimidazole hydrobromide) is a synthetic adaptogen and actoprotector, with wide-ranging pharmacological activities such as nootropic, antihypoxic, antioxidant, immunostimulant. The intake of Bemitil increases mental and physical performance and could be applied under either normal or extreme conditions. Until 2017 Bemitil was not considered as doping and was used by professional athletes more than 30 years because of its high efficiency and safety. The drug was included in WADA monitoring programme for 2018, and most likely it would be included in WADA Prohibited List for 2019. Usually, a substance/method is included in WADA Prohibited List if it meets any two of the following three criteria: the potential to enhance or enhances sports performance/ potential health risk to the athlete/ violates the spirit of sport. Bemitil has high performance-enhancing potential, but it is also safe- it is controversial whether it should be considered as doping.

Keywords: doping, bemitil, sport, actoprotector

Procedia PDF Downloads 408

Authors: I. Benyamina, B. Benalioua, M. Mansour, A. Bentouami

Abstract:

The aim of this study is to use a synthetic of the layered double hydroxide as a method of doping of zinc by transition metal. The choice of dopant metal being bismuth. The material has been heat treated at different temperatures then tested on the Photo discoloration of indigo carmine under visible irradiation. In contrast, the diffuse reflectance spectroscopic analysis of the UV-visible heat treated material exhibits an absorbance in the visible unlike ZnO and TiO2 P25. This property let the photocatalytic activity of Bi-ZnO under visible irradiation. Indeed, the photocatalytic effectiveness of Bi-ZnO in a visible light was proved by the total discoloration of indigo carmine solution with intial concentration of 16 mg/L after 90 minutes, whereas the TiO2 P25 and ZnO their discolorations are obtained after 120 minutes.

Keywords: photo-catalysis, doping, AOP, ZnO

Procedia PDF Downloads 340

Authors: Ismail Becenen

Abstract:

Air pollution, a consequence of urbanization brought about by modern life, is as global as it is local and regional. Because of the adverse effects of air pollution on human health, air quality is given importance all over the world. According to the decision of the World Health Organization, clean air is the basic necessity for human health and well-being. It poses a very high risk especially for heart diseases and stroke cases. In this study, the positive effects of natural gas usage on air pollution in cities are explained by using literature scans and air pollution measurement values. Natural gas is cleaner than other types of fuel. It contains less sulfur and organic sulfur compounds. When natural gas burns, it does not leave ashes, it does not cause problems in the rubbish mountains. It's a clean fuel, it easily burns and shines. It is a burning gas that is easy and efficient. In addition, there is not a toxic effect for people in case of inhalation. As a result, the use of natural gas needs to be widespread to reduce air pollution around the world in order to provide a healthier life for people and the environment.

Keywords: natural gas, air pollution, sulfur dioxide, particulate matter, energy

Procedia PDF Downloads 164

Authors: Mohamed H. El-Newehy, Badr M. Thamer, Nasser A. M. Barakat, Mohammad A.Abdelkareem, Salem S. Al-Deyab, Hak Y. Kim

Abstract:

In this study, the influence of nitrogen doping on the electrocatalytic activity of carbon nanofibers with nickel nanoparticles toward methanol oxidation is introduced. The modified carbon nanofibers have been synthesized from calcination of electrospun nanofiber mats composed of nickel acetate tetrahydrate, poly(vinyl alcohol) and urea in argon atmosphere at 750oC. The utilized physicochemical characterizations indicated that the proposed strategy leads to form carbon nanofibers having nickel nanoparticles and doped by nitrogen. Moreover, due to the high-applied voltage during the electrospinning process, the utilized urea chemically bonds with the polymer matrix, which leads to form nitrogen-doped CNFs after the calcination process. Investigation of the electrocatalytic activity indicated that nitrogen doping NiCNFs strongly enhances the oxidation process of methanol as the current density increases from 52.5 to 198.5 mA/cm2 when the urea content in the original electrospun solution was 4 wt% urea. Moreover, the nanofibrous morphology exhibits distinct impact on the electrocatalytic activity. Also, nitrogen-doping enhanced the stability of the introduced Ni-based electrocatalyst. Overall, the present study introduces effective and simple strategy to modify the electrocatalytic activity of the nickel-based materials.

Keywords: electrospinning, methanol electrooxidation, fuel cells, nitrogen-doping, nickel

Procedia PDF Downloads 393

Authors: G. Sivakumar, T. Pratyusha, D. Gupta, W. Shen

Abstract:

To get ohmic contact between the cathode and organic semiconductor, transport layers are introduced between the active layer and the electrodes. Generally zinc oxide or titanium dioxide are used as electron transport layer. When electron transport layer is doped with lithium, the resultant film exhibited superior electronic properties, which enables faster electron transport. Doping is accomplished by heat treatment of films with Lithium salts. Li-doped films. We fabricated organic solar cell using PTB7(poly(3-hexylthiopene-2,5- diyl):PCBM(phenyl-C61-butyric acid methyl ester) and found that the solar cells prepared using Li doped films had better performance in terms of efficiency when compared to the undoped transport layers.

Keywords: electron transport layer, higher efficiency, lithium doping, ohmic contact

Procedia PDF Downloads 476

Authors: Abdenour Achour, Kan Chen, Mike Reece, Zhaorong Huang

Abstract:

Here we report the synthesis of pure and cost effective of BiCuSeO by a flux method in air, and the enhancement of the thermoelectric performance by Cs doping. The comparison between our synthesis and the usual vacuum furnace method has been studied for the pristine oxyselenides BiCuSeO. We report for very high Seebeck coefficients up to 516 μV K⁻¹ at room temperature with the electrical conductivity of 5.20 S cm⁻¹ which lead to a high power factor of 140 µWm⁻¹K⁻². We also report at the high temperatures the lowest thermal conductivity value of 0.42 µWm⁻¹K⁻¹. Upon doping with Cs, enhanced electrical conductivity coupled with a moderate Seebeck coefficient lead to a power factor of 338 µWm⁻¹K⁻² at 682 K. Moreover, it shows a very low thermal conductivity in the temperature range of 300 to 682 K (0.75 to 0.35 Wm⁻¹K⁻¹). By optimizing the power factor and reducing the thermal conductivity, this results in a high ZT of ~ 0.66 at 682 K for Bi0.995Cs0.005CuSeO.

Keywords: BiCuSeO, Cs doping, thermoelectric, oxyselenide

Procedia PDF Downloads 268

Authors: Y. Boudjadja, A. Amira, A. Saoudel, A. Varilci, S. P. Altintas, C. Terzioglu

Abstract:

In this work, we report the effect of Y3+ doping on structural, mechanical and electrical properties of Bi-2202 phase. Samples of Bi2Sr1.9Ca0.1-xYxCu2O7+δ with x = 0, 0.025, 0.05, 0.075 and 0.1 are elaborated in air by conventional solid state reaction and characterized by X-Ray Diffraction (XRD), Scanning Electronic Microscopy (SEM) combined with EDS spectroscopy, density, Vickers micro-hardness and resistivity measurements. A good correlation between the variations of the bulk density and the Vickers micro-hardness with doping is obtained. The SEM photograph shows that the samples are composed of grains with a flat shape that characterizes the Bi-based cuprates. Quantitative EDS analysis confirms the reduction of Ca content and the increase of Y content when x is increased. The variation of resistivity with temperature shows that only samples with x = 0, 0.025 and 0.05 present an onset transition to the superconducting state. The higher onset transition temperature is obtained for x = 0.025 and is about 93.62 K. The transition is wide and is realized in two steps confirming then the presence of the low Tc Bi-2201 phase in the samples. For x = 0.075 and 0.1, a transition to a semiconducting state is seen at low temperatures. Some physical parameters are extracted from these curves and discussed.

Keywords: Bi-2202 phase, doping, structure, mechanical and electrical properties

Procedia PDF Downloads 298