Authors: Surjit Angra, Gajanan Rane, Vinod Kumar, Sushma Rani

Abstract:

This paper presents metallurgical investigation of failed helical gear of diesel engine gear box used in a car. The failure had occurred near the bottomland of the tooth spacing. The failed surface was studied under Scanning Electron Microscope (SEM) and also visually investigated. The images produced through SEM at various magnifications were studied. Detailed metallurgical study indicates that failure was due to foreign material inclusion which is a casting defect. Further study also revealed pitting, spalling and inter-granular fracture as the causes of gear failure.

Keywords: helical gear, scanning electron microscope, casting defect, pitting

Procedia PDF Downloads 436

Authors: Parisa Hasanpour, Bahram Borooghani, Vahid Asadi

Abstract:

In the current research, a catastrophic failure of a 304 stainless steel flange at pipeline transportation of ethylene in a petrochemical refinery was studied. Cracking was found in the flange after about 78840h service. Through the chemical analysis, tensile tests in addition to microstructural analysis such as optical microscopy and Scanning Electron Microscopy (SEM) on the failed part, it found that the fatigue was responsible for the fracture of the flange, which originated from bumps and depressions on the outer surface and propagated by vibration caused by the working condition.

Keywords: failure analysis, 304 stainless steel, fatigue, flange, petrochemical refinery

Procedia PDF Downloads 53

Authors: Arjun G. Koppad

Abstract:

The study was conducted in Joida taluk of Uttara Kannada district, Karnataka, India, to assess the land use land cover (LULC) and forest aboveground biomass using L band SAR data. The study area covered has dense, moderately dense, and sparse forests. The sampled area was 0.01 percent of the forest area with 30 sampling plots which were selected randomly. The point center quadrate (PCQ) method was used to select the tree and collected the tree growth parameters viz., tree height, diameter at breast height (DBH), and diameter at the tree base. The tree crown density was measured with a densitometer. Each sample plot biomass was estimated using the standard formula. In this study, the LULC classification was done using Freeman-Durden, Yamaghuchi and Pauli polarimetric decompositions. It was observed that the Freeman-Durden decomposition showed better LULC classification with an accuracy of 88 percent. An attempt was made to estimate the aboveground biomass using SAR backscatter. The ALOS-2 PALSAR-2 L-band data (HH, HV, VV &VH) fully polarimetric quad-pol SAR data was used. SAR backscatter-based regression model was implemented to retrieve forest aboveground biomass of the study area. Cross-polarization (HV) has shown a good correlation with forest above-ground biomass. The Multi Linear Regression analysis was done to estimate aboveground biomass of the natural forest areas of the Joida taluk. The different polarizations (HH &HV, VV &HH, HV & VH, VV&VH) combination of HH and HV polarization shows a good correlation with field and predicted biomass. The RMSE and value for HH & HV and HH & VV were 78 t/ha and 0.861, 81 t/ha and 0.853, respectively. Hence the model can be recommended for estimating AGB for the dense, moderately dense, and sparse forest.

Keywords: forest, biomass, LULC, back scatter, SAR, regression

Procedia PDF Downloads 10

Authors: Lennart Dimberg, Lala Joulha Ian

Abstract:

Introduction: Overweight (BMI 25-30) and obesity (BMI 30+) have consistently been associated with cardiovascular (CV) risk and death since the Framingham heart study in 1948, and BMI was included in the original Framingham risk score (FRS). Background: Myocardial infarction (MI) poses a serious threat to the patient's life. In addition to BMI, several other indices of overweight have been presented and argued to replace FRS as more relevant measures of CV risk. These indices include waist circumference (WC), waist/hip ratio (WHR), sagittal abdominal diameter (SAD), and sagittal abdominal diameter to height (SADHtR). Specific research question: The research question of this study is to evaluate the interrelationship between the various body measurements, BMI, WC, WHR, SAD, and SADHtR, and which measurement is strongly associated with MI and death. Methods: In 1993, 1,000 middle-aged Caucasian, randomly selected working men of the Swedish Volvo-Renault cohort were surveyed at a nurse-led health examination with a questionnaire, EKG, laboratory tests, blood pressure, height, weight, waist, and sagittal abdominal diameter measurements. Outcome data of myocardial infarction over 28 years come from Swedeheart (the Swedish national myocardial infarction registry) and the Swedish death registry. The Aalen-Johansen and Kaplan–Meier methods were used to estimate the cumulative incidences of MI and death. Multiple logistic regression analyses were conducted to compare BMI with the other four body measurements. The risk for the various measures of obesity was calculated with outcomes of accumulated first-time myocardial infarction and death as odds ratios (OR) in quartiles. The ORs between the 4th and the 1st quartile of each measure were calculated to estimate the association between the body measurement variables and the probability of cumulative incidences of myocardial infarction (MI) over time. Double-sided P values below 0.05 will be considered statistically significant. Unadjusted odds ratios were calculated for obesity indicators, MI, and death. Adjustments for age, diabetes, SBP, and the ratio of total cholesterol/HDL-C and blue/white collar status were performed. Results: Out of 1000 people, 959 subjects had full information about the five different body measurements. Of those, 90 participants had a first MI, and 194 persons died. The study showed that there was a high and significant correlation between the five different body measurements, and they were all associated with CVD risk factors. All body measurements were significantly associated with MI, with the highest (OR=3.6) seen for SADHtR and WC. After adjustment, all but SADHtR remained significant with weaker ORs. As for all-cause mortality, WHR (OR=1.7), SAD (OR=1.9), and SADHtR (OR=1.6) were significantly associated, but not WC and BMI. However, after adjustment, only WHR and SAD were significantly associated with death, but with attenuated ORs.

Keywords: BMI, death, epidemiology, myocardial infarction, risk factor, sagittal abdominal diameter, sagittal abdominal diameter to height, waist circumference, waist-hip ratio

Procedia PDF Downloads 74

Authors: Hee Yong Kang, Hyeon Ho Shin, Jung Cheol Yoo, Il Taek Lee, Sung Mo Yang

Abstract:

Lightweight technology using composites is being developed for vehicle seat structures, and its design must meet the safety requirements. According to the Federal Motor Vehicle Safety Standard (FMVSS) 207 seating systems test procedure, the back moment load is applied to the seat back frame structure for the safety evaluation of the vehicle seat. The seat back frame using the composites is divided into three parts: upper part frame, and left- and right-side frame parts following the manufacturing process. When a rear moment load is applied to the seat back frame, the side frame receives the bending load and the torsional load at the same time. This results in the largest loaded strength. Therefore, strength test of the component unit is required. In this study, a component test method based on the FMVSS 207 seating systems test procedure was proposed for the strength analysis of bending load and torsional load of the automotive Bulk Molding Compound (BMC) Seat Back Side Frame. Moreover, strength evaluation according to the carbon band reinforcement was performed. The back-side frame parts of the seat that are applied to the test were manufactured through BMC that is composed of vinyl ester Matrix and short carbon fiber. Then, two kinds of reinforced and non-reinforced parts of carbon band were formed through a high-temperature compression molding process. In addition, the structure that is applied to the component test was constructed by referring to the FMVSS 207. Then, the bending load and the torsional load were applied through the displacement control to perform the strength test for four load conditions. The results of each test are shown through the load-displacement curves of the specimen. The failure strength of the parts caused by the reinforcement of the carbon band was analyzed. Additionally, the fracture characteristics of the parts for four strength tests were evaluated, and the weakness structure of the back-side frame of the seat structure was confirmed according to the test conditions. Through the bending and torsional strength test methods, we confirmed the strength and fracture characteristics of BMC Seat Back Side Frame according to the carbon band reinforcement. And we proposed a method of testing the part strength of a seat back frame for vehicles that can meet the FMVSS 207.

Keywords: seat back frame, bending and torsional strength, BMC (Bulk Molding Compound), FMVSS 207 seating systems

Procedia PDF Downloads 194

Authors: Farhad Abbas Gandomkar, Mona Danesh

Abstract:

This paper aims to determine Fundamental Natural Frequency (FNF) of a structural composite floor system known as Chromite. To achieve this purpose, FNFs of studied panels are determined by development of Finite Element Models (FEMs) in ABAQUS program. American Institute of Steel Construction (AISC) code in Steel Design Guide Series 11, presents a fundamental formula to calculate FNF of a steel framed floor system. This formula has been used to verify results of the FEMs. The variability in the FNF of the studied system under various parameters such as dimensions of floor, boundary conditions, rigidity of main and secondary beams around the floor, thickness of concrete slab, height of composite joists, distance between composite joists, thickness of top and bottom flanges of the open web steel joists, and adding tie beam perpendicular on the composite joists, is determined. The results show that changing in dimensions of the system, its boundary conditions, rigidity of main beam, and also adding tie beam, significant changes the FNF of the system up to 452.9%, 50.8%, -52.2%, %52.6%, respectively. In addition, increasing thickness of concrete slab increases the FNF of the system up to 10.8%. Furthermore, the results demonstrate that variation in rigidity of secondary beam, height of composite joist, and distance between composite joists, and thickness of top and bottom flanges of open web steel joists insignificant changes the FNF of the studied system up to -0.02%, -3%, -6.1%, and 0.96%, respectively. Finally, the results of this study help designer predict occurrence of resonance, comfortableness, and design criteria of the studied system.

Keywords: Fundamental Natural Frequency, Chromite Composite Floor System, Finite Element Method, low and high frequency floors, Comfortableness, resonance.

Procedia PDF Downloads 441

Authors: Shima Soleimani, Steven Eckels

Abstract:

One area of special importance for surface-level study of heat exchangers is tubes with internal micro-fins (< 0.5 mm tall). Micro-finned surfaces are a kind of extended solid surface in which energy is exchanged with water that acts as the source or sink of energy. Significant performance gains are possible for either shell, tube, or double pipe heat exchangers if the best surfaces are identified. The parametric studies of micro-finned tubes that have appeared in the literature left some key parameters unexplored. Specifically, they ignored three-dimensional (3D) micro-fin configurations, conduction heat transfer in the fins, and conduction in the solid surface below the micro-fins. Thus, this study aimed at implementing a parametric study of 3D micro-finned tubes that considered micro-fin height and discontinuity features. A 3D conductive and convective heat-transfer simulation through coupled solid and periodic fluid domains is applied in a commercial package, ANSYS Fluent 19.1. The simulation is steady-state with turbulent water flow cooling inner wall of a tube with micro-fins. The simulation utilizes a constant and uniform temperature on the tube outer wall. Performance is mapped for 18 different simulation cases, including a smooth tube using a realizable k-ε turbulence model at a Reynolds number of 48,928. Results compared the performance of 3D tubes with results for the similar two-dimensional (2D) one. Results showed that the micro-fin height has greater impact on performance factor than discontinuity features in 3D micro-fin tubes. A transformed 3D micro-fin tube can enhance heat transfer and pressure drop up to 21% and 56% compared to a 2D one, respectfully.

Keywords: three-dimensional micro-finned tube, heat transfer, friction factor, heat exchanger

Procedia PDF Downloads 102

Authors: Gopika Rajagopal, Sudheesh Thiyyakkandi

Abstract:

Back-to-back reinforced earth (RE) walls are extensively used in these days as bridge abutments and highway ramps, owing to their cost efficiency and ease of construction. High quality select fill is the most suitable backfill material due to its excellent engineering properties and constructability. However, industries are compelled to use low quality, locally available soil because of its ample availability on site. However, several failure cases of such walls are reported, especially subsequent to rainfall events. The stiffness of reinforcement is one of the major factors affecting the performance of RE walls. The present study focused on analyzing the effect of reinforcement stiffness on the performance of complete select fill, complete marginal fill, and hybrid-fill (i.e., combination of select and marginal fills) back-to-back RE walls, immediately after construction and upon rainwater infiltration through finite element modelling. A constant width to height (W/H) ratio of 3 and height (H) of 6 m was considered for the numerical analysis and the stiffness of reinforcement layers was varied from 500 kN/m to 10000 kN/m. Results showed that reinforcement stiffness had a noticeable influence on the response of RE wall, subsequent to construction as well as rainwater infiltration. Facing displacement was found to decrease and maximum reinforcement tension and factor of safety were observed to increase with increasing the stiffness of reinforcement. However, beyond a stiffness of 5000 kN/m, no significant reduction in facing displacement was observed. The behavior of fully marginal fill wall considered in this study was found to be reasonable even after rainwater infiltration when the high stiffness reinforcement layers are used.

Keywords: back-to-back reinforced earth wall, finite element modelling, rainwater infiltration, reinforcement stiffness

Procedia PDF Downloads 138

Authors: Emad Rashwan, M. Mousa, Ayman EL Sabagh, Celaleddin Barutcular

Abstract:

Flax is a potential winter crop for Egypt that can be grown for both seed and fiber. The study was conducted during two successive winter seasons of 2013/2014, and 2014/2015 in the experimental farm of El-Gemmeiza Agricultural Research Station, Agriculture research Centre, Egypt. The objective of this work was to evaluate the effect of irrigation intervals (25, 35 and 45) on the seed yield and quality of flax cultivars (Sakha1, Giza9 and Giza10). Obtained results indicate that highly significant for all studied traits among irrigation intervals except oil percentage that was not significant in both seasons. Irrigated flax plants every 35 days gave the maximum values for all characters. In contrast, irrigation every 45 days gave the minimum values for all studied characters under this study. In respect to cultivars, significant differences in most yield and quality characters were found. Furthermore, the performance of Sakha1 cultivar was superior in total plant height, main stem diameter, seed index, seed, oil, biological and straw yield /ha as well as fiber length and fiber fineness. Meanwhile, Giza9 and Giza10 cultivars were surpassed in fiber yield/hand fiber percentage, respectively. The interactions between irrigation intervals and flax cultivars were highly significant for total plant height, main stem diameter, seed, oil, biological and straw yields /ha. Based on the results, all flax cultivars recorded the maximum values for major traits were measured under irrigation of flax plants every 35 days.

Keywords: flax, fiber, irrigation intervals, oil, seed yield

Procedia PDF Downloads 237

Authors: Somnath Bhattacharya, Kamal Sharma, Vaibhav Sonkar

Abstract:

Composite materials emerged in the middle of the 20th century as a promising class of engineering materials providing new prospects for modern technology. Recently, a new class of composite materials known as functionally graded materials (FGMs) has drawn considerable attention of the scientific community. In general, FGMs are defined as composite materials in which the composition or microstructure or both are locally varied so that a certain variation of the local material properties is achieved. This gradual change in composition and microstructure of material is suitable to get gradient of properties and performances. FGMs are synthesized in such a way that they possess continuous spatial variations in volume fractions of their constituents to yield a predetermined composition. These variations lead to the formation of a non-homogeneous macrostructure with continuously varying mechanical and / or thermal properties in one or more than one direction. Lightweight functionally graded composites with high strength to weight and stiffness to weight ratios have been used successfully in aircraft industry and other engineering applications like in electronics industry and in thermal barrier coatings. In the present work, elastic-plastic crack growth problems (using Ramberg-Osgood Model) in an FGM plate under cyclic load has been explored by extended finite element method. Both edge and centre crack problems have been solved by taking additionally holes, inclusions and minor cracks under plane stress conditions. Both soft and hard inclusions have been implemented in the problems. The validity of linear elastic fracture mechanics theory is limited to the brittle materials. A rectangular plate of functionally graded material of length 100 mm and height 200 mm with 100% copper-nickel alloy on left side and 100% ceramic (alumina) on right side is considered in the problem. Exponential gradation in property is imparted in x-direction. A uniform traction of 100 MPa is applied to the top edge of the rectangular domain along y direction. In some problems, domain contains major crack along with minor cracks or / and holes or / and inclusions. Major crack is located the centre of the left edge or the centre of the domain. The discontinuities, such as minor cracks, holes, and inclusions are added either singly or in combination with each other. On the basis of this study, it is found that effect of minor crack in the domain’s failure crack length is minimum whereas soft inclusions have moderate effect and the effect of holes have maximum effect. It is observed that the crack growth is more before the failure in each case when hard inclusions are present in place of soft inclusions.

Keywords: elastic-plastic, fatigue crack, functionally graded materials, extended finite element method (XFEM)

Procedia PDF Downloads 372

Authors: L. Abubakar, B. M. Sokoto, I. U. Mohammed, M. S. Na’allah, A. Mohammad, A. N. Garba, T. S. Bubuche

Abstract:

Onion (Allium cepa var. cepa L.) is the most important species of the Allium group belonging to family Alliaceae and genus Allium. It can be regarded as the single important vegetable species in the world after tomatoes. Despite the similarities, which bring the species together, the genus is a strikingly diverse one, with more than five hundred species, which are perennial and mostly bulbous plants. Out of these, only seven species are in cultivation, and five are the most important species of the cultivated Allium. However, Allium cepa (onion) and Allium sativum (Garlic) are the two major cultivated species grown all over the world of which the onion crop is the most important. North Western Nigeria (Sokoto, Kebbi and Zamfara States) constitute the major onion producing zone in Nigeria, which is primarily during the dry season. However, onion production in the zone is seriously affected by two main factors i.e. diseases and storage losses, in addition to other constraints that limits the cultivation of the crop during the rainy season which include lack of prolonged rainy season to allow for proper maturation of the crop. The major onion disease in this zone is purple blotch caused by a fungus Alternaria porri and currently efforts are on to develop onion hybrids resistant to the disease. Genetic diversity plays an important role in plant breeding either to exploit heterosis or to generate productive recombinants. Assessment of a large number of genotypes for a genetic diversity is the first step in this direction. The objective of this research therefore is to evaluate the genetic potentials of the onion cultivars of North Western Nigeria, with a view of developing new cultivars that address the major production challenges to onion cultivation in North Western, Nigeria. Thirteen onion cultivars were collected during an expedition covering North western Nigeria and Southern part of Niger Republic during 2013, which are areas noted for onion production. The cultivars were evaluated at two locations; Sokoto, in Sokoto State and Jega in Kebbi State all in Nigeria during the 2013/14 onion season (dry season) under irrigation. The objective of the research was to determine the genetic potentials of onion cultivars of north western Nigeria as a basis for breeding purposes. Combined analysis of the results revealed highly significant variation between the cultivars across the locations with respect to plant height, number of leaves/plant, bolting %, bulb height, bulb weight, mean bulb yield and cured bulb weight, with significant variation in terms of bulb diameter. Tasa from Warra Local Government Area of Kebbi State (V4) recorded the greatest mean fresh bulb yield with Jar Albasa (V8) from Illela Local Government Area of Sokoto State recording the least. Similarly Marsa (V5) from Silame Local Government Area recorded the greatest mean cured bulb yield (marketable bulb)with Kiba (V11) from Goronyo Local Government of Sokoto State recording the least. Significant variation was recorded between the locations with respect to all characters, with Sokoto being better in terms of plant height, number of leaves/plant, bolting % and bulb diameter. Jega was better in terms of bulb height, bulb yield and cured bulb weight. Significant variation was therefore observed between the cultivars.

Keywords: evaluation, genetic, onions, North Western Nigeria

Procedia PDF Downloads 384

Authors: Maretha Le Roux, Corinna Walsh, Mariette M. Nel

Abstract:

Introduction: The first 1000 days from conception to 24 months, is a critical period for healthy growth and development. In South Africa, stunting is a major public health issue with significant health consequences. We determined associations between demographic, health and anthropometric indicators of mothers and their infants. Methods: A cross-sectional study was conducted in all districts in the Northern Cape. All mothers with 5-7 week old babies visiting PHC facilities could participate. A questionnaire was completed in a structured interview with each mother. Weight and length of the baby at birth and at 6 weeks were used to determine stunting, while weight and height of the mother were measured for body mass index (BMI). Results: Eight hundred questionnaires were completed in 92 facilities. The median age of mothers was 26 years (range 10-46 years), and 44,9% were married. Almost 40% relied on a government grant as main source of income. Two-thirds (64,9%) had not planned the pregnancy, and 19.4% had a Caesarian section. Although 79% breastfed exclusively, more than a quarter (26,1%) smoked cigarettes or used snuff during pregnancy, while 9,4% drank alcohol. At birth, 17.7% of boys and 13.0% of girls were stunted (height-for-age below -2SD from the WHO reference values), while at 6 weeks this had increased to 30.8% of boys and 14.1% of girls. In terms of mothers, 25,4% were classified as obese and 24,6% as overweight at 6 weeks. Compared to babies that were not stunted, significantly more babies of mothers that were older, overweight, used ART, relied on a grant and smoked/snuffed during pregnancy were stunted. Conclusion: To address stunting, interventions aimed at encouraging healthy lifestyles with the emphasis on maintaining a healthy weight, healthy eating and smoking cessation before pregnancy are urgently required.

Keywords: growth, health, South Africa, stunting

Procedia PDF Downloads 110

Authors: Razali Bin Abidin

Abstract:

This paper presents the development of a portable water jet cutter for soft materials such as meat. Twelve geometries of nozzles were simulated using finite element method. Water pressure was set to 1500 lb/in². Through the simulation, highest average water output speed was 133.04 m/s. The nozzle was fabricated from Al - alloy 5052 with the Factor of Safety~ 3. This indicates that the nozzle made of Al-alloy 5052 is capable of performing the cutting process without any fracture. Preliminary design of mobile water jet hand tool is presented at the end of this paper.

Keywords: water jet, finite element, Al-alloy 5052, nozzle geometry

Procedia PDF Downloads 357

Authors: Armand Okende, Joëlle De Weerdt, Esther Fichtler, Maaike De Ridder, Hans Beeckman

Abstract:

The rainforest plays a crucial role in regulating the climate balance. The biodiversity of tropical rainforests is undeniable, but many aspects remain poorly known, which directly influences its management. Despite the efforts of sustainable forest management, human pressure in terms of exploitation and smuggling of timber forms a problem compared to exploited species whose status is considered "vulnerable" on the IUCN red list compiled by. Commercial species in Class III of the Democratic Republic of Congo are the least known in the market operating, and their biology is unknown or non-existent. Identification of wood in terms of descriptions and anatomical measurements of the wood is in great demand for various stakeholders such as scientists, customs, IUCN, etc. The objective of this study is the qualitative and quantitative description of the anatomical characteristics of commercial species in Class III of DR Congo. The site of the Luki Biosphere Reserve was chosen because of its high tree species richness. This study focuses on the wood anatomy of 14 commercial species of Class III of DR Congo. Thirty-four wooden discs were collected for these species. The following parameters were measured in the field: Diameter at breast height (DBH), total height and geographic coordinates. Microtomy, identification of vessel parameters (diameter, density and grouping) and photograph of the microscopic sections and determining age were performed in this study. The results obtained are detailed anatomical descriptions of species in Class III of the Democratic Republic of Congo.

Keywords: sustainable management of forest, rainforest, commercial species of class iii, vessel diameter, vessel density, grouping vessel

Procedia PDF Downloads 193

Authors: Tigist Girma Kedane

Abstract:

The purpose of the current research work is to measure the physical properties of bamboo species in Ethiopia on the impact of age, harvesting seasons and culm height. Three representatives of bamboo plants are harvested in three groups of ages, 2 harvesting months, and 3 regions of Ethiopia. Research has not been done on the physical properties of bamboo species in Ethiopia so far. Moisture content and shrinkage of bamboo culm increase when the culm ages younger and moves from top to bottom position. The harvesting month of November has a higher moisture content and shrinkage compared to February. One year old of Injibara, Kombolcha, and Mekaneselam bamboo culm has 40%, 30%, and 33% higher moisture content, 29%, 24%, and 28% higher radial shrinkage, 32%, 37%, and 32% higher tangential shrinkage compared to 3 years old respectively. The bottom position of Injibara, Kombolcha, and Mekaneselam in November have 45%, 28%, and 25% higher moisture content, 41%, 29%, and 34% radial shrinkage, 29%, 28%, and 42% tangential shrinkage than the top position, respectively. The basic density increases as the age of the bamboo becomes older and moves from the bottom to the top position. November has the lowest basic density compared to February. 3 years old of Injibara, Kombolcha, and Mekaneselam at the age of 3 years have 32%, 50%, and 24% higher basic density compared to 1 year, whereas the top position has 35%, 26%, and 22% higher than the bottom position in February, respectively. The current research proposed that 3 years and February are suited for structural purposes and furniture making, but 1 year and November are suited for fiber extraction in the composite industry. The existence of water in the culm improves an easy extraction of the fibers without damage from the culm.

Keywords: bamboo age, bamboo height, harvesting seasons, physical properties

Procedia PDF Downloads 39

Authors: Hong Je Kang, Young Chae Choi, Jin Sung Park, Isac Kim

Abstract:

Purpose: Osteoporotic fractures are an important among postmenopausal women. When osteoporotic distal radial fractures occur, osteoporosis must be treated to prevent the hip and spine fractures. Intravenous injection of Zoledronic acid is expected to improve preventing osteoporotic fractures. Many articles reported the effect of intravenous Zoledronic acid to BMD of the hip and spine fracture or non-fracture patients with low BMD. However, that with distal radial fractures has rarely been reported. Therefore, the authors decided to study the effect of Zoledronic acid in BMD score, bone union, and bone turnover markers in the patients who underwent volar plating due to osteoporotic distal radial fractures. Materials: From April 2018 to May 2022, postmenopausal women aged 55 years or older who had osteoporotic distal radial fractures and who underwent surgical treatment using volar plate fixation were included. Zoledronic acid (5mg) was injected intravenously between 3 and 5 days after surgery. BMD scores after 1 year of operation were compared with the initial scores. Bone turnover markers were measured before surgery, after 3 months, and after 1 year. Radiological follow-up was performed every 2 weeks until the bone union and at 1 year postoperatively. Clinical outcome indicators were measured one year after surgery, and the occurrence of side effects was observed. Result: Total of 23 patients were included, with a lumbar BMD T score of -2.89±0.2 before surgery to -2.27±0.3 one year after surgery (p=0.012) and a femoral neck BMD T score of -2.45±0.3 before surgery to -2.36±0.3 (p=0.041) after one year, and all were statistically significant. Measured as bone resorption markers, serum CTX-1 was 337.43±10.4 pg/mL before surgery, 160.86±8.7 pg/mL (p=0.022) after three months, and 250.12±12.7 pg/mL (p=0.031) after one year. Urinary NTX-1 was 39.24±2.2 ng/mL before surgery, 24.46±1.2 ng/mL (p=0.014) after three months and 30.35±1.6 ng/mL (p=0.042) after one year. Measured as bone formation markers, serum osteocalcin was 13.04±1.1 ng/mL before surgery, 8.84±0.7 ng/mL (p=0.037) after 3 months and 11.1±0.4 ng/mL (p=0.026) after one year. Serum bone-specific ALP was 11.24±0.9 IU/L before surgery, 8.25±0.9 IU/L (p=0.036) after three months, and 10.2±0.9 IU/L (p=0.027) after one year. All were statistically significant. All cases showed bone union within an average of 6.91±0.3 weeks without any signs of failure. Complications were found in 5 out of 23 cases (21.7%), such as headache, nausea, muscle pain, and fever. Conclusion: When Zoledronic acid was used, BMD was improved in both the spine and femoral neck. This may reduce the likelihood and subsequent morbidity of additional osteoporotic fractures. This study is meaningful in that there was no difference in the duration of bone union and radiological characteristics in patients with distal radial fractures administrated with intravenous BP early after the fractures, and improvement in BMD and bone turnover indicators was measured.

Keywords: zeoldreonic acid, BMD, osteoporosis, distal radius

Procedia PDF Downloads 103

Authors: Shima Soleimani, Steven Eckels

Abstract:

One area of special importance for the surface-level study of heat exchangers is tubes with internal micro-fins (< 0.5 mm tall). Micro-finned surfaces are a kind of extended solid surface in which energy is exchanged with water that acts as the source or sink of energy. Significant performance gains are possible for either shell, tube, or double pipe heat exchangers if the best surfaces are identified. The parametric studies of micro-finned tubes that have appeared in the literature left some key parameters unexplored. Specifically, they ignored three-dimensional (3D) micro-fin configurations, conduction heat transfer in the fins, and conduction in the solid surface below the micro-fins. Thus, this study aimed at implementing a parametric study of 3D micro-finned tubes that considered micro-fine height and discontinuity features. A 3D conductive and convective heat-transfer simulation through coupled solid and periodic fluid domains is applied in a commercial package, ANSYS Fluent 19.1. The simulation is steady-state with turbulent water flow cooling the inner wall of a tube with micro-fins. The simulation utilizes a constant and uniform temperature on the tube outer wall. Performance is mapped for 18 different simulation cases, including a smooth tube using a realizable k-ε turbulence model at a Reynolds number of 48,928. Results compared the performance of 3D tubes with results for the similar two-dimensional (2D) one. Results showed that the micro-fine height has a greater impact on performance factors than discontinuity features in 3D micro-fin tubes. A transformed 3D micro-fin tube can enhance heat transfer, and pressure drops up to 21% and 56% compared to a 2D one, respectfully.

Keywords: three-dimensional micro-fin tube, heat transfer, friction factor, heat exchanger

Procedia PDF Downloads 98

Authors: Shaher A. I. Shalfawi, Fredrik Hviding, Bjornar Kjellstadli

Abstract:

The main purpose of this study was to measure the effect of two different strength training methods on muscle strength, muscle mass, fat mass and endurance factors. Fourteen physical education students accepted to participate in this study. The participants were then randomly divided into three groups, traditional training group (TTG), cluster training group (CTG) and control group (CG). TTG consisted of 4 participants aged ( ± SD) (22.3 ± 1.5 years), body mass (79.2 ± 15.4 kg) and height (178.3 ± 11.9 cm). CTG consisted of 5 participants aged (22.2 ± 3.5 years), body mass (81.0 ± 24.0 kg) and height (180.2 ± 12.3 cm). CG consisted of 5 participants aged (22 ± 2.8 years), body mass (77 ± 19 kg) and height (174 ± 6.7 cm). The participants underwent a hypertrophy strength training program twice a week consisting of 4 sets of 10 reps at 70% of one-repetition maximum (1RM), using barbell squat and barbell bench press for 8 weeks. The CTG performed 2 x 5 reps using 10 s recovery in between repetitions and 50 s recovery between sets, while TTG performed 4 sets of 10 reps with 90 s recovery in between sets. Pre- and post-tests were administrated to assess body composition (weight, muscle mass, and fat mass), 1RM (bench press and barbell squat) and a laboratory endurance test (Bruce Protocol). Instruments used to collect the data were Tanita BC-601 scale (Tanita, Illinois, USA), Woodway treadmill (Woodway, Wisconsin, USA) and Vyntus CPX breath-to-breath system (Jaeger, Hoechberg, Germany). Analysis was conducted at all measured variables including time to peak VO2, peak VO2, heart rate (HR) at peak VO2, respiratory exchange ratio (RER) at peak VO2, and number of breaths per minute. The results indicate an increase in 1RM performance after 8 weeks of training. The change in 1RM squat was for the TTG = 30 ± 3.8 kg, CTG = 28.6 ± 8.3 kg and CG = 10.3 ± 13.8 kg. Similarly, the change in 1RM bench press was for the TTG = 9.8 ± 2.8 kg, CTG = 7.4 ± 3.4 kg and CG = 4.4 ± 3.4 kg. The within-group analysis from the oxygen consumption measured during the incremental exercise indicated that the TTG had only a statistical significant increase in their RER from 1.16 ± 0.04 to 1.23 ± 0.05 (P < 0.05). The CTG had a statistical significant improvement in their HR at peak VO2 from 186 ± 24 to 191 ± 12 Beats Per Minute (P < 0.05) and their RER at peak VO2 from 1.11 ± 0.06 to 1.18 ±0.05 (P < 0.05). Finally, the CG had only a statistical significant increase in their RER at peak VO2 from 1.11 ± 0.07 to 1.21 ± 0.05 (P < 0.05). The between-group analysis showed no statistical differences between all groups in all the measured variables from the oxygen consumption test during the incremental exercise including changes in muscle mass, fat mass, and weight (kg). The results indicate a similar effect of hypertrophy strength training irrespective of the methods of the training used on untrained subjects. Because there were no notable changes in body-composition measures, the results suggest that the improvements in performance observed in all groups is most probably due to neuro-muscular adaptation to training.

Keywords: hypertrophy strength training, cluster set, Bruce protocol, peak VO2

Procedia PDF Downloads 237

Authors: Nayera E. Hassan, Salah Mostafa, Hamed Elkhayat, Kalled Hassan Sewidan, Sahar A. El-Masry, Manal Mouhamed Ali, Mones M. Abu Shady

Abstract:

Pubertal growth is influenced by many factors including environmental and nutritional factors. Objective: To assess impact of nutritional status on pubertal staging, ovarian and uterine volumes among school girls. Method: Study was cross sectional and carried out on 1000 healthy school girls, aged 8-18 years selected randomly. They were categorized according to their ages into three groups: 8-12 years, 13-15 years and 16-18 years ±6 months, then according to their body mass index percentile to normal weight: (≥15-<85.), overweight (≥85-<95) and obese (≥95). All girls were subjected for physical, anthropometric (weight, height, body mass index), nutritional markers WAZ (weight/age Z score), HAZ (height/age Z score) and BMI-Z (body mass index Z score), pubertal assessment (Tanner stage) and pelvic transabdominal sonography (uterine and ovarian volumes). Results: Highly significant differences in ovarian and uterine volumes and nutritional markers (WAZ, HAZ and BMI-Z score) were detected among different grades of puberty in the two age groups (8-12 years, 13-15 years) coming in advance of obese girls (with increase of BMI); except HAZ in the second age group. Girls aged 16-18 years reached to final volume for the uterus and ovary with insignificant differences. Pubertal stage, ovarian and uterine sizes were highly significantly correlated with nutritional markers. Mean ages of onset: of puberty, menarche and complete puberty were, 11.65 + 1.84, 14.79 + 1.75 and 15.02 + 1.68 years respectively. Conclusion: Nutritional status has a crucial role in determining pubertal stage, ovarian and uterine volumes among Egyptian girls during the pubertal process.

Keywords: pubertal stage, nutritional markers, girls, ovarian and uterine volumes

Procedia PDF Downloads 445

Authors: Shahram Nowrouzieh, Abbas Rezaei Asl, Mohamad Ali Jafari

Abstract:

Cotton, as a strategic crop, plays an important role in providing human food and clothing need, because of its oil, protein, and fiber. Iran has been one of the largest cotton producers in the world in the past, but unfortunately, for economic reasons, its production is reduced now. One of the ways to reduce the cost of cotton production is to expand the mechanization of cotton harvesting. Iranian farmers do not accept the function of cotton harvesters. One reason for this lack of acceptance of cotton harvesting machines is the number of field losses on these machines. So, the majority of cotton fields are harvested by hand. Although the correct setting of the harvesting machine is very important in the cotton losses, the morphological properties of the cotton plant also affect the performance of cotton harvesters. In this study, the effect of some cotton morphological properties such as the height of the cotton plant, number, and length of sympodial and monopodial branches, boll dimensions, boll weight, number of carpels and bracts angle were evaluated on the performance of cotton picker. In this research, the efficiency of John Deere 9920 spindle Cotton picker is investigated on five different Iranian cotton cultivars. The results indicate that there was a significant difference between the five cultivars in terms of machine harvest efficiency. Golestan cultivar showed the best cotton harvester performance with an average of 87.6% of total harvestable seed cotton and Khorshid cultivar had the least cotton harvester performance. The principal component analysis showed that, at 50.76% probability, the cotton picker efficiency is affected by the bracts angle positively and by boll dimensions, the number of carpels and the height of cotton plants negatively. The seed cotton remains (in the plant and on the ground) after harvester in PCA scatter plot were in the same zone with boll dimensions and several carpels.

Keywords: cotton, bract, harvester, carpel

Procedia PDF Downloads 123

Authors: Arunas Emeljanovas, Brigita Mieziene, Vida Cesnaitiene, Ingunn Fjortoft, Lise Kjonniksen

Abstract:

Background: Gender differences in physical fitness were tracked in many studies with lower effect in preschool children and increasing difference among genders across age. In Lithuania, on a population level, secular trends in physical fitness were regularly observed each ten years for the last two decades for 11-18 years old students. However, there is apparently a lack of such epidemiological studies among primary school students. Assessing and monitoring physical fitness from an early age is of particular importance seeking to develop and strengthen physical abilities of youths for future health benefits. The goal of the current study was to indicate age and gender differences in anthropometric measures, musculoskeletal, motor and cardiorespiratory fitness in Lithuanian primary school children. Methods: The study included 3456 1-4th grade students from 6 to 10 years. The data reliably represents the population of primary school children in Lithuania. Among them, 1721 (49.8 percent) were boys. Physical fitness was measured by the 9-item test battery, developed by Fjørtoft and colleagues (2011). Height and weight were measured and body mass index was calculated. Student t test evaluated differences in physical fitness between boys and girls, ANOVA was performed to indicate differences across age. Results: All anthropometric and fitness means that were identified as significantly different were better in boys than in girls and in older than younger students (p < .05). Among anthropometric measures, height was higher in boys aged 7 through 9 years. Weight and BMI differed among boys and girls only at 8 years old. Means of height and weight increased significantly across all ages. Among musculoskeletal fitness tests, means of standing broad jump, throwing a tennis ball and pushing a medicine ball were different between genders within each age group and across all ages. Differences between genders were less likely in motor fitness than in musculoskeletal or cardiorespiratory fitness. Differences in means of shuttle run 10 x 5 test between genders occurred at age 6, 9 and 10 years; running 20 m at age 6 and 9 years, and climbing wall bars at age 9 and 10. Means of Reduced Cooper test representing cardiorespiratory fitness were different between genders within each age group but did not differ among age 6 and 8 as well as 7 and 8 years in boys, and among age 7 and 8 years in girls. Conclusion: In general, the current study confirms gender differences in musculoskeletal, motor and cardiorespiratory fitness found in other studies across the world in primary school and older children. Observed gender differences might be explained by higher physical activity in boys rather than girls. As it is explained by previous literature, older boys and girls had better performances than younger ones, because of the components of fitness change as a function of growth, maturation, development, and interactions among the three processes.

Keywords: primary school children, motor fitness, musculoskeletal fitness, cardiovascular fitness

Procedia PDF Downloads 190

Authors: M. K. Manoj, V. Pancholi, S. K. Nath

Abstract:

Microalloyed dual phase steels have been prepared by intercritical austenitisation (ICA) treatment of normalized steel at different temperature and time. Water quenching wad carried to obtain different martensite volume fraction (MVF) in DP steels. DP steels and normalized steels have been characterized by optical and scanning electron microscopy, Vickers hardness measurements and tensile properties determination. The effect of MVF and martensite morphology on mechanical properties and fracture behavior of microalloyed dual phase steels have been explained in the present work.

Keywords: dual phase steel, martensite morphology, hardness, tensile strength

Procedia PDF Downloads 313

Authors: J. Ismail, F. Zaïri, M. Naït-Abdelaziz, Z. Azari

Abstract:

In this work, a combined approach of continuum damage mechanics (CDM) and fracture mechanics is applied to model a glass plate behavior under static indentation. A spherical indenter is used and a CDM based constitutive model with an anisotropic damage tensor was selected and implemented into a finite element code to study the damage of glass. Various regions with critical damage values were predicted in good agreement with the experimental observations in the literature. In these regions, the directions of crack propagation, including both cracks initiating on the surface as well as in the bulk, were predicted using the strain energy density factor.

Keywords: finite element modeling, continuum damage mechanics, indentation, cracks

Procedia PDF Downloads 401

Authors: Adamu Usman, Grace Stanley Balami

Abstract:

Pearl millet (Pennisetum glaucum L. R. Br.) is a cereal cultivated in arid and semi-arid areas of the world. It supports more than 100 million people around the world. Parasitic weed (Striga hermonthica Del. Benth) is a major constraint to its production. Estimated yield losses are put at 10 - 95% depending on variety, ecology and cultural practices. Potentials in selection of traits in pearl millets for grain yield have been reported and it depends on genotypic variability and heritability among landraces. Variability and heritability among cultivars could offer opportunities for improvement. The study was conducted to determine the genetic variability among cultivars and estimate broad sense heritability among grain yield and related traits. F1 breeding populations were generated with 9 parental cultivars, viz; Ex-Gubio, Ex-Monguno, Ex-Baga as males and PEO 5984, Super-SOSAT, SOSAT-C88, Ex-Borno and LCIC9702 as females through Line × Tester mating during 2017 dry season at Lushi Irrigation Station, Bauchi Metropolitan in Bauchi State, Nigeria. The F1 population and the parents were evaluated during cropping season of 2018 at Bauchi and Maiduguri. Data collected were subjected to analysis of variance. Results showed significant difference among cultivars and among traits indicating variability. Number of plants at emergence, days to 50% flowering, days to 100% flowering, plant height, panicle length, number of plants at harvest, Striga count at 90 days after sowing, panicle weight and grain yield were significantly different. Significant variability offer opportunity for improvement as superior individuals can be isolated. Genotypic variance estimates of traits were largely greater than environmental variances except in plant height and 1000 seed weight. Environmental variances were low and in some cases negligible. The phenotypic variances of all traits were higher than genotypic variances. Similarly phenotypic coefficient of variation (PCV) was higher than genotypic coefficient of variation (GCV). High heritability was found in days to 50% flowering (90.27%), Striga count at 90 days after sowing (90.07%), number of plants at harvest (87.97%), days to 100% flowering (83.89%), number of plants at emergence (82.19%) and plant height (73.18%). Greater heritability estimates could be due to presence of additive gene. The result revealed wider variability among genotypes and traits. Traits having high heritability could easily respond to selection. High value of GCV, PCV and heritability estimates indicate that selection for these traits are possible and could be effective.

Keywords: variability, heritability, phenotypic, genotypic, striga

Procedia PDF Downloads 37

Authors: Neda Nabid

Abstract:

Friction-based supplemental devices have been extensively used for seismic protection and strengthening of structures, however, the conventional use of these dampers may not necessarily lead to an efficient structural performance. Conventionally designed friction dampers follow a uniform height-wise distribution pattern of slip load values for more practical simplicity. This can lead to localizing structural damage in certain story levels, while the other stories accommodate a negligible amount of relative displacement demand. A practical performance-based optimization methodology is developed to tackle with structural damage localization of RC frame buildings with friction energy dissipation devices under severe earthquakes. The proposed methodology is based on the concept of uniform damage distribution theory. According to this theory, the slip load values of the friction dampers redistribute and shift from stories with lower relative displacement demand to the stories with higher inter-story drifts to narrow down the discrepancy between the structural damage levels in different stories. In this study, the efficacy of the proposed design methodology is evaluated through the seismic performance of five different low to high-rise RC frames equipped with friction wall dampers under six real spectrum-compatible design earthquakes. The results indicate that compared to the conventional design, using the suggested methodology to design friction wall systems can lead to, by average, up to 40% reduction of maximum inter-story drift; and incredibly more uniform height-wise distribution of relative displacement demands under the design earthquakes.

Keywords: friction damper, nonlinear dynamic analysis, RC structures, seismic performance, structural damage

Procedia PDF Downloads 213

Authors: Scott Draper, Nat Benjanuvatra, Grant Landers, Terry Griffiths, Justin Geldard

Abstract:

Open water swimming has been an Olympic sport since 2008 and is growing in popularity world-wide as a low impact form of exercise. Unlike pool swimming, open water swimmers experience a range of different environmental conditions, including surface waves, variable water temperature, aquatic life, and ocean currents. This presentation will describe experimental research to investigate how freestyle swimming behaviour and performance is influenced by surface waves. A group of 12 swimmers were instructed to swim freestyle in the 54 m long wave flume located at The University of Western Australia’s Coastal and Offshore Engineering Laboratory. A variety of different regular waves were simulated, varying in height (up to 0.3 m), period (1.25 – 4s), and direction (with or against the swimmer). Swimmer’s velocity and acceleration, respectively, were determined from video recording and inertial sensors attached to five different parts of the swimmer’s body. The results illustrate how the swimmers stroke rate and the wave encounter frequency influence their forward speed and how particular wave conditions can benefit or hinder performance. Comparisons to simplified mathematical models provide insight into several aspects of performance, including: (i) how much faster swimmers can travel when swimming with as opposed to against the waves, and (ii) why swimmers of lesser ability are expected to be affected proportionally more by waves than elite swimmers. These findings have implications across the spectrum from elite to ‘weekend’ swimmers, including how they are coached and their ability to win (or just successfully complete) iconic open water events such as the Rottnest Channel Swim held annually in Western Australia.

Keywords: open water, surface waves, wave height/length, wave flume, stroke rate

Procedia PDF Downloads 97

Authors: Choki, Supatchai Boonpratham, Suwannee Luppanapornlarp

Abstract:

The objective of this study was to find a correlation between cephalometric measurements and visual perception of facial profile in skeletal type II patients. In this study, 250 lateral cephalograms of female patients from age, 20 to 22 years were analyzed. The profile outlines of all the samples were hand traced and transformed into silhouettes by the principal investigator. Profile ratings were done by 9 orthodontists on Visual Analogue Scale from score one to ten (increasing level of convexity). 37 hard issue and soft tissue cephalometric measurements were analyzed by the principal investigator. All the measurements were repeated after 2 weeks interval for error assessment. At last, the rankings of visual perceptions were correlated with cephalometric measurements using Spearman correlation coefficient (P < 0.05). The results show that the increase in facial convexity was correlated with higher values of ANB (A point, nasion and B point), AF-BF (distance from A point to B point in mm), L1-NB (distance from lower incisor to NB line in mm), anterior maxillary alveolar height, posterior maxillary alveolar height, overjet, H angle hard tissue, H angle soft tissue and lower lip to E plane (absolute correlation values from 0.277 to 0.711). In contrast, the increase in facial convexity was correlated with lower values of Pg. to N perpendicular and Pg. to NB (mm) (absolute correlation value -0.302 and -0.294 respectively). From the soft tissue measurements, H angles had a higher correlation with visual perception than facial contour angle, nasolabial angle, and lower lip to E plane. In conclusion, the findings of this study indicated that the correlation of cephalometric measurements with visual perception was less than expected. Only 29% of cephalometric measurements had a significant correlation with visual perception. Therefore, diagnosis based solely on cephalometric analysis can result in failure to meet the patient’s esthetic expectation.

Keywords: cephalometric measurements, facial profile, skeletal type II, visual perception

Procedia PDF Downloads 121

Authors: Manjinder Singh, Jasvinder Singh

Abstract:

Existing theories of Titanic/Liberty ship, Sydney bridge accidents and practical experience generated an interest in developing weldments those has high toughness under sub-zero temperature conditions. The purpose was to protect the joint from undergoing DBT (Ductile to brittle transition), when ambient temperature reach sub-zero levels. Metallurgical improvement such as low carbonization or addition of deoxidization elements like Mn and Si was effective to prevent fracture in weldments (crack) at low temperature. In the present research, an attempt has been made to investigate the reason behind ductile to brittle transition of mild steel weldments when subjected to sub-zero temperatures and method of its mitigation. Nickel is added to weldments using manual metal arc welding (MMAW) preventing the DBT, but progressive reduction in charpy impact values as temperature is lowered. The variation in toughness with respect to nickel content being added to the weld pool is analyzed quantitatively to evaluate the rise in toughness value with increasing nickel amount. The impact performance of welded specimens was evaluated by Charpy V-notch impact tests at various temperatures (20 °C, 0 °C, -20 °C, -40 °C, -60 °C). Notch is made in the weldments, as notch sensitive failure is particularly likely to occur at zones of high stress concentration caused by a notch. Then the effect of nickel to weldments is investigated at various temperatures was studied by mechanical and metallurgical tests. It was noted that a large gain in impact toughness could be achieved by adding nickel content. The highest yield strength (462J) in combination with good impact toughness (over 220J at – 60 °C) was achieved with an alloying content of 16 wt. %nickel. Based on metallurgical behavior it was concluded that the weld metals solidify as austenite with increase in nickel. The microstructure was characterized using optical and high resolution SEM (scanning electron microscopy). At inter-dendritic regions mainly martensite was found. In dendrite core regions of the low carbon weld metals a mixture of upper bainite, lower bainite and a novel constituent coalesced bainite formed. Coalesced bainite was characterized by large bainitic ferrite grains with cementite precipitates and is believed to form when the bainite and martensite start temperatures are close to each other. Mechanical properties could be rationalized in terms of micro structural constituents as a function of nickel content.

Keywords: MMAW, Toughness, DBT, Notch, SEM, Coalesced bainite

Procedia PDF Downloads 513

Authors: Narges Razmjoo, Hamid Sefidari, Michael Strand

Abstract:

Biomass combustion is a growing technique for heat and power production due to the increasing stringent regulations with CO2 emissions. Grate-fired systems have been regarded as a common and popular combustion technology for burning woody biomass. However, some grate furnaces are not well optimized and may emit significant amount of unwanted compounds such as dust, NOx, CO, and unburned gaseous components. The combustion characteristics inside the fuel bed are of practical interest, as they are directly related to the release of volatiles and affect the stability and the efficiency of the fuel bed combustion. Although numerous studies have been presented on the grate firing of biomass, to the author’s knowledge, none of them have conducted a detailed experimental study within the fuel bed. It is difficult to conduct measurements of temperature and gas species inside the burning bed of the fuel in full-scale boilers. Results from such inside bed measurements can also be applied by the numerical experts for modeling the fuel bed combustion. The current work presents an experimental investigation into the combustion behavior of wet woody biomass (53 %) in a 4 MW reciprocating grate boiler, by focusing on the gas species distribution along the height of the fuel bed. The local concentrations of gases (CO, CO2, CH4, NO, and O2) inside the fuel bed were measured through a glass port situated on the side wall of the furnace. The measurements were carried out at five different heights of the fuel bed, by means of a bent stainless steel probe containing a type-k thermocouple. The sample gas extracted from the fuel bed, through the probe, was filtered and dried and then was analyzed using two infrared spectrometers. Temperatures of about 200-1100 °C were measured close to the grate, indicating that char combustion is occurring at the bottom of the fuel bed and propagates upward. The CO and CO2 concentration varied in the range of 15-35 vol % and 3-16 vol %, respectively, and NO concentration varied between 10-140 ppm. The profile of the gas concentrations distribution along the bed height provided a good overview of the combustion sub-processes in the fuel bed.

Keywords: experimental, fuel bed, grate firing, wood combustion

Procedia PDF Downloads 314

Authors: Radek Novotny, Michal Novak, Daniela Marusakova, Monika Sipova, Hugo Fuentes, Peter Borst

Abstract:

This research has been conducted within the European HORIZON 2020 project ECC-SMART. The main objective is to assess whether it is feasible to design and develop a small modular reactor (SMR) that would be cooled by supercritical water (SCW). One of the main objectives for material research concerns the corrosion of the candidate cladding materials. The experimental part has been conducted in support of the qualification procedure of the future SCW-SMR constructional materials. The last objective was to identify the gaps in current norms and guidelines. Apart from corrosion, resistance testing of candidate materials stresses corrosion cracking susceptibility tests have been performed in supercritical water. This paper describes part of these tests, in particular, those slow strain rate tensile loading applied for tangential ring shape specimens of two candidate materials, Alloy 800H and 310S stainless steel. These ring tensile tests are one the methods used for tensile testing of nuclear cladding. Here full circular heads with dimensions roughly equal to the inner diameter of the sample and the gage sections are placed in the parallel direction to the applied load. Slow strain rate tensile tests have been conducted in 380 or 500oC supercritical water applying two different elongation rates, 1x10-6 and 1x10-7 s-1. The effect of temperature and dissolved oxygen content on the SCC susceptibility of Alloy 800H and 310S stainless steel was investigated when two different temperatures and concentrations of dissolved oxygen were applied in supercritical water. The post-fracture analysis includes fractographic analysis of the fracture surfaces using SEM as well as cross-sectional analysis on the occurrence of secondary cracks. Assessment of the effect of environment and dissolved oxygen content was by comparing to the results of the reference tests performed in air and N2 gas overpressure. The effect of high temperature on creep and its role in the initiation of SCC was assessed as well. It has been concluded that the applied test method could be very useful for the investigation of stress corrosion cracking susceptibility of candidate cladding materials in supercritical water.

Keywords: stress corrosion cracking, ring tensile tests, super-critical water, alloy 800H, 310S stainless steel

Procedia PDF Downloads 71