Search results for: mechanical and tribological behaviour

Authors: Shan Faiz, Arfat Anis, Saeed M. Al-Zarani

Abstract:

High density polyethylene (HDPE) and poly benzimidazole fiber (PBI) composites were prepared by melt blending in a twin screw extruder (TSE). The thermo-mechanical properties of PBI fiber reinforced HDPE composite samples (1%, 4% and 8% fiber content) of fiber lengths 3 mm and 6 mm were investigated using differential scanning calorimeter (DSC), universal testing machine (UTM), rheometer and scanning electron microscopy (SEM). The effect of fiber content and fiber lengths on the thermo-mechanical properties of the HDPE-PBI composites was studied. The DSC analysis showed decrease in crystallinity of HDPE-PBI composites with the increase of fiber loading. Maximum decrease observed was 12% at 8% fiber length. The thermal stability was found to increase with the addition of fiber. T50% was notably increased to 40oC for both grades of HDPE using 8% of fiber content. The mechanical properties were not much affected by the increase in fiber content. The optimum value of tensile strength was achieved using 4% fiber content and slight increase of 9% in tensile strength was observed. No noticeable change was observed in flexural strength. In rheology study, the complex viscosities of HDPE-PBI composites were higher than the HDPE matrix and substantially increased with even minimum increase of PBI fiber loading i.e. 1%. We found that the addition of the PBI fiber resulted in a modest improvement in the thermal stability and mechanical properties of the prepared composites.

Keywords: PBI fiber, high density polyethylene, composites, melt blending

Procedia PDF Downloads 345

Authors: Jaroslava Sucha, Martin Dolejs, Helena Pipova, Panajotis Cakirpaloglu

Abstract:

The paper introduces the research project which is focused on evaluating the level of pathological relation towards computer or video games playing (including any games played by using a screen such as a mobile or a tablet). The study involves representative sample of the Czech adolescents between ages 11 and 19. This poster presents the psychometric indicators of the new psychologic assessment method (mean, standard deviation, reliability, validity) which will be able to detect an acceptable level of games’ playing and at the same time will detect and describe the level of gaming which might be potentially risky. The prevalence of risky computer game playing at Czech adolescents in age 11 to 19 will be mentioned. The research study also aims to describe the personality profile of the problematic players with respect to the digital games. The research area will encompass risky behaviour, aggression, the level of self-esteem, impulsivity, anxiety and depression. The contribution will introduce a new test method for the assessment of pathological playing computer games. The research will give the first screening information of playing computer games in the Czech Republic by adolescents between 11-19 years. The results clarify what relationship exists between playing computer games and selected personality characteristics (it will describe personality of the gamer, who is in the category of ‘pathological playing computer games’).

Keywords: adolescence, computer games, personality traits, risk behaviour

Procedia PDF Downloads 217

Authors: Racholsan Raj Nirmal, B. S. V. Patnaik, R. Jayaganthan

Abstract:

The deformation behaviour of additively manufactured AlSi10Mg alloy under low strains, high strain rates and elevated temperature conditions is essential to analyse and predict its response against dynamic loading such as impact and thermomechanical fatigue. The constitutive relation of Johnson-Cook is used to capture the strain rate sensitivity and thermal softening effect in AlSi10Mg alloy. Johnson-Cook failure model is widely used for exploring damage mechanics and predicting the fracture in many materials. In this present work, Johnson-Cook material and damage model parameters for additively manufactured AlSi10Mg alloy have been determined numerically from four types of uniaxial tensile test. Three different uniaxial tensile tests with dynamic strain rates (0.1, 1, 10, 50, and 100 s^-1) and elevated temperature tensile test with three different temperature conditions (450 K, 500 K and 550 K) were performed on 3D printed AlSi10Mg alloy in ABAQUS/Explicit. Hexahedral elements are used to discretize tensile specimens and fracture energy value of 43.6 kN/m was used for damage initiation. Levenberg Marquardt optimization method was used for the evaluation of Johnson-Cook model parameters. It was observed that additively manufactured AlSi10Mg alloy has shown relatively higher strain rate sensitivity and lower thermal stability as compared to the other Al alloys.

Keywords: ABAQUS, additive manufacturing, AlSi10Mg, Johnson-Cook model

Procedia PDF Downloads 143

Authors: Naresh Radaliyagoda, Nigel M. Jennett, Rong Lan, David Parfitt

Abstract:

A series of length scale engineered multilayer material with temperature robust mechanical properties has been suggested. A range of polycrystalline copper sub-layers with the thickness varying from 1 to 25μm and buried in between two nickel layers was produced using electrodeposition dual bath technique. The structure of the multilayers was characterized using Electron Backscatter Diffraction and Scanning Electron Microscope. The interface effect on the hardness and elastic modulus was tested using Nano-indentation. Results of the grain size and layer thickness measurements, and indentation hardness have been compared. It is found that there is a combined length scale effect that improves mechanical properties in Ni/Cu multilayer structures.

Keywords: nano-indentation, size effect, multilayers, electrodeposition

Procedia PDF Downloads 137

Authors: A. Siva, K. Bala Subramanian, Kinson Prabu

Abstract:

Concrete is widely used construction materials all over the world. Now a day’s fibers are used in this construction due to its advantages like increase in stiffness, energy absorption, ductility and load carrying capacity. The fiber used in the concrete to increases the structural integrity of the member. It is one of the emerging techniques used in the construction industry. In this paper, the effective utilization of high-performance fiber reinforced concrete (HPFRC) beams has been experimental investigated. The experimental investigation has been conducted on different steel fibers (Hooked, Crimpled, and Hybrid) under cyclic loading. The behaviour of HPFRC beams is compared with the conventional beams. Totally four numbers of specimens were cast with different content of fiber concrete and compared conventional concrete. The fibers are added to the concrete by base volume replacement of concrete. The silica fume and superplasticizers were used to modify the properties of concrete. Single point loading was carried out for all the specimens, and the beam specimens were subjected to cyclic loading. The load-deflection behaviour of fibers is compared with the conventional concrete. The ultimate load carrying capacity, energy absorption and ductility of hybrid fiber reinforced concrete is higher than the conventional concrete by 5% to 10%.

Keywords: cyclic loading, ductility, high performance fiber reinforced concrete, structural integrity

Procedia PDF Downloads 251

Authors: D. C. Soares, J. T. S. Santos, D. G. Costa, A. K. S. Abud, T. P. Nunes, A. V. D. Figueiredo, A. M. de Oliveira Junior

Abstract:

Mangabeira (Hancornia speciosa Gomes), a native plant in Brazil, is found growing spontaneously in various regions of the country. The high perishability of tropical fruits such as mangaba, causes it to be necessary to use technologies that promote conservation, aiming to increase the shelf life of this fruit and add value. The objective of this study was to compare the mangabas lyophilisation curves behaviours with different sizes and maturation stages. The fruits were freeze-dried for a period of approximately 45 hours at lyophilizer Liotop brand, model L -108. It has been considered large the fruits between 38 and 58 mm diameter and small, between 23 and 28 mm diameter and the two states of maturation, intermediate and mature. Large size mangabas drying curves in both states of maturation were linear behaviour at all process, while the kinetic drying curves related to small fruits, independent of maturation state, had a typical behaviour of drying, with all the well-defined steps. With these results it was noted that the time of lyophilisation was suitable for small mangabas, a fact that did not happen with the larger one. This may indicate that the large mangabas require a longer time to freeze until reaches the equilibrium level, as it happens with the small fruits, going to have constant moisture at the end of the process. For both types of fruit were analysed water activity, acidity, protein, lipid, and vitamin C before and after the process.

Keywords: freeze dryer, mangaba, conservation, chemical characteristics

Procedia PDF Downloads 281

Authors: Mandira Mishra, Mark Allen

Abstract:

This meta-analysis explored whether rejection sensitivity relates to facets of romantic relationships. A comprehensive literature search identified 60 studies (147 effect sizes; 16,955 participants) that met inclusion criteria. Data were analysed using inverse-variance weighted random effects meta-analysis. Mean effect sizes from 21 meta-analyses provided evidence that more rejection sensitive individuals report lower levels of relationship satisfaction and relationship closeness, lower levels of perceived partner satisfaction, a greater likelihood of intimate partner violence (perpetration and victimization), higher levels of relationship concerns and relationship conflict, and higher levels of jealousy and self-silencing behaviours. There was also some evidence that rejection sensitive individuals are more likely to engage in risky sexual behaviour and are more prone to sexual compulsivity. There was no evidence of publication bias and various levels of heterogeneity in computed averages. Random effects meta-regression identified participant age and sex as important moderators of pooled mean effects. These findings provide a foundation for the theoretical development of rejection sensitivity in romantic relationships and should be of interest to relationship and marriage counsellors and other relationship professionals.

Keywords: intimate partner violence, relationship satisfaction, commitment, sexual orientation, risky sexual behaviour

Procedia PDF Downloads 68

Authors: S. P. Raut, S. K. Soni, A. W. Kolhatkar

Abstract:

Denim is widely used by every age of people all over the world. As the use of denim is increasing progressively, till now the handle properties of denim fabric not reported at significant level. In the present study, five commercial denim fabric samples were used. Denim samples, weighing from 8.5oz/sq yds to 14.5 oz/sq yds, were processed as per standard commercial procedure for denim finishing. These finished denim samples were tested on Kawabata Evaluation System(KES) for low stress mechanical properties. The results of KES values are used for calculation of Total Hand value(THV) using equation for summer suit. The obtained result for THV using equation for summer suit for denim samples is in the range from 1.62 to 3.30. These values of low stress mechanical properties values given by KES, can be used to engineer the denim fabric for bottom wear.

Keywords: denim, handle value, Kawabata evaluation system, objective evaluation

Procedia PDF Downloads 265

Authors: Ji Chan Kim, Seok Hong Min, Tae Kwon Ha

Abstract:

Effect of boron addition on the microstructure and mechanical properties of AZ91D Mg alloy was investigated in this study. Through calculation of phase equilibria, carried out by using FactSage® and FTLite database, solution treatment temperature was decided as 420 °C where supersaturated solid solution can be obtained. Solid solution treatment was conducted at 420 °C for 24 hrs followed by hot rolling at 420 °C and the total reduction was about 60%. Recrystallization heat treatment was followed at 420 °C for 6 hrs to obtain equiaxed microstructure. After recrystallization treatment, aging heat treatment was conducted at temperature of 200 °C for time intervals from 1 min to 200 hrs and hardness of each condition was measured by micro-Vickers method. Peak hardness was observed after 20 hrs. Tensile tests were also conducted on the specimens aged for various time intervals and the results were compared with hardness.

Keywords: AZ91D Mg alloy, boron, heat treatment, microstructure, mechanical properties, hardness

Procedia PDF Downloads 294

Authors: Nakarin Prempri

Abstract:

Single-phase induction motors are widely used in industry. Most manufacturing processes use capacitor-run single-phase induction motors to drive mechanical loads. The selection of a suitable motor for driving is important. The optimum operating range of the motor can help the motor operate efficiently. Thus, this paper presents an operating range analysis of capacitor-run single-phase induction motors and a determination of suitability between motor and mechanical loads. an observational study found that the optimum operating range of the motor can be used to determine the suitability between the motor and the mechanical load. Such considerations ensure that the motor uses no more current than necessary and operates efficiently.

Keywords: single phase induction motor, operating range, torque curve, efficiency curve

Procedia PDF Downloads 88

Authors: P. Vosynek, T. Návrat, M. Peč, J. Pořízka, P. Diviš

Abstract:

Changes of mechanical properties and response behavior of bones is an important external sign of medical problems like osteoporosis, bone remodeling after fracture or surgery, osteointegration, or bone tissue loss of astronauts in space. Measuring of mechanical behavior of bones in physiological and osteoporotic states, quantified by different degrees of protein (collagen) and mineral loss, is thus an important topic in biomechanical research. This contribution deals with the relation between mechanical properties of the turkey long bone–tibia in physiological, demineralized, and deproteinized state. Three methods for comparison were used: densitometry, three point bending and harmonic response analysis. The results help to find correlations between the methods and estimate their possible application in medical practice.

Keywords: bone properties, long bone, osteoporosis, response behavior

Procedia PDF Downloads 467

Authors: Lingaraju Dumpala, Laxmi Mohan Kumar Chintada, Devadas Deepu, Pravin Kumar Yadav

Abstract:

Friction stir welding is the new-fangled and cutting-edge technique in welding applications; it is widely used in the fields of transportation, aerospace, defense, etc. For thriving significant welding joints and properties of friction stir welded components, it is essential to carry out this advanced process in a prescribed systematic procedure. At this moment, Underwater Friction Stir Welding (UFSW) Process is the field of interest to do research work. In the continuous assessment, the study of UFSW process is to comprehend problems occurred in the past and the structure through which the mechanical properties of the welded joints can be value-added and contributes to conclude results an acceptable and resourceful joint. A meticulous criticism is given on how to modify the experimental setup from NFSW to UFSW. It can discern the influence of tool materials, feeds, spindle angle, load, rotational speeds and mechanical properties. By expending the DEFORM-3D simulation software, the achieved outcomes are validated.

Keywords: Underwater Friction Stir Welding(UFSW), Al alloys, mechanical properties, Normal Friction Stir Welding(NFSW)

Procedia PDF Downloads 267

Authors: Shital Jhunjhunwala, Shweta Saraf

Abstract:

Research Question: The study, based on a survey, empirically tests the impact of the board’s engagement in the decision-making process on firm outcomes. It also examines the moderating effect of board leadership and board independence on the relationship. Research Findings: Boards’ engagement in the decision-making process is found to be vital for firm performance, wherein effective monitoring by the board outperforms their strategic guidance role in achieving desired outcomes. The separation of CEO and Chairman positively moderates the board’s engagement in protecting stakeholders’ interests, but lack of independence and passive behaviour of independent directors raises concern on the efficacy of independent directors. Theoretical Implications: The study provides the framework for process-oriented corporate governance research, where investigation of boards’ behaviour inside the boardroom develops a deeper understanding of board processes. Practitioner Implications: The study highlights the necessity of developing boards’ focus in a company on monitoring managerial actions. It suggests the need to separate the position of CEO and Chairman for addressing the interest of all stakeholders. It recommends policymakers review the existing mandate on board independence and create alternate monitoring mechanisms for addressing agency conflict.

Keywords: board, decision-making process, engagement, independence, leadership, innovation, stakeholders, firm performance, qualitative, India

Procedia PDF Downloads 89

Authors: L. Vivet, L. Benabou, O. Simon

Abstract:

With highly demanding applications in the field of power electronics, there is an increasing need to have interconnection materials with properties that can ensure both good mechanical assembly and high thermal/electrical conductivities. So far, lead-free solders have been considered an attractive solution, but recently, sintered joints based on nano-silver paste have been used for die attach and have proved to be a promising solution offering increased performances in high-temperature applications. In this work, the main parameters of the bonding process using silver oxalates are studied, i.e., the heating rate and the bonding pressure mainly. Their effects on both the mechanical and thermal properties of the sintered layer are evaluated following an experimental design. Pairs of copper substrates with gold metallization are assembled through the sintering process to realize the samples that are tested using a micro-traction machine. In addition, the obtained joints are examined through microscopy to identify the important microstructural features in relation to the measured properties. The formation of an intermetallic compound at the junction between the sintered silver layer and the gold metallization deposited on copper is also analyzed. Microscopy analysis exhibits a nanoporous structure of the sintered material. It is found that higher temperature and bonding pressure result in higher densification of the sintered material, with higher thermal conductivity of the joint but less mechanical flexibility to accommodate the thermo-mechanical stresses arising during service. The experimental design allows hence the determination of the optimal process parameters to reach sufficient thermal/mechanical properties for a given application. It is also found that the interphase formed between silver and gold metallization is the location where the fracture occurred after the mechanical testing, suggesting that the inter-diffusion mechanism between the different elements of the assembly leads to the formation of a relatively brittle compound.

Keywords: nanoporous structure, silver oxalate, sintering, mechanical strength, thermal conductivity, microelectronic packaging

Procedia PDF Downloads 82

Authors: Valeria Abreu Minero, Edward Barker, Hannah Dickson, Francois Husson, Sandra Flynn, Jennifer Shaw

Abstract:

Purpose – The purpose of this paper is to identify offender typologies based on aspects of the offenders’ psychopathology and their associations with crime scene behaviours using data derived from the National Confidential Enquiry into Suicide and Safety in Mental Health concerning homicides in England and Wales committed by offenders in contact with mental health services in the year preceding the offence (n=759). Design/methodology/approach – The authors used multiple correspondence analysis to investigate the interrelationships between the variables and hierarchical agglomerative clustering to identify offender typologies. Variables describing: the offender’s mental health history; the offenders’ mental state at the time of offence; characteristics useful for police investigations; and patterns of crime scene behaviours were included. Findings – Results showed differences in the offender’s histories in relation to their crime scene behaviours. Further, analyses revealed three homicide typologies: externalising, psychosis and depression. Analyses revealed three homicide typologies: externalising, psychotic and depressive. Practical implications – These typologies may assist the police during homicide investigations by: furthering their understanding of the crime or likely suspect; offering insights into crime patterns; provide advice as to what an offender’s offence behaviour might signify about his/her mental health background; findings suggest information concerning offender psychopathology may be useful for offender profiling purposes in cases of homicide offenders with schizophrenia, depression and comorbid diagnosis of personality disorder and alcohol/drug dependence. Originality/value – Empirical studies with an emphasis on offender profiling have almost exclusively focussed on the inference of offender demographic characteristics. This study provides a first step in the exploration of offender psychopathology and its integration to the multivariate analysis of offence information for the purposes of investigative profiling of homicide by identifying the dominant patterns of mental illness within homicidal behaviour.

Keywords: offender profiling, mental illness, psychopathology, multivariate analysis, homicide, crime scene analysis, crime scene behviours, investigative advice

Procedia PDF Downloads 115

Authors: B. Tiseo, V. Quaranta, G. Bruno, R. Gardi, T. Watts, S. Dussy

Abstract:

This paper describes the qualification test campaign performed on the Demise Observation Capsule DOC-EQM as part of the Future Launch Preparatory Program FLPP3. The mechanical environment experienced during launch ascent and separation phase was first identified and then replicated in terms of sine, random and shock vibration. The loads identification is derived by selecting the worst possible case. Vibration and shock qualification test performed at CIRA Space Qualification laboratory is herein described. Mechanical fixtures’ design and validation, carried out by means of FEM, is also addressed due to its fundamental role in the vibrational test campaign. The Demise Observation Capsule (DOC) successfully passed the qualification test campaign. Functional test and resonance search have not been point any fault and damages of the capsule.

Keywords: capsule, demise, demise observation capsule, DOC, launch environment, re-ntry, qualification

Procedia PDF Downloads 128

Authors: Hasan Şahan Arel

Abstract:

In this study, literature related to the replacement of cement with waste marble and the use of waste marble as an aggregate in concrete production was examined. Workability of the concrete decreased when marble powder was used as a substitute for fine aggregate. Marble powder contributed to the compressive strength of concrete because of the CaCO₃ and SiO₂ present in the chemical structure of the marble. Additionally, the use of marble pieces in place of coarse aggregate revealed that this contributed to the workability and mechanical properties of the concrete. When natural standard sand was replaced with marble dust at a ratio of 15% and 75%, the compressive strength and splitting tensile strength of the concrete increased by 20%-26% and 10%-15%, respectively. However, coarse marble aggregates exhibited the best performance at a 100% replacement ratio. Additionally, there was a greater improvement in the mechanical properties of concrete when waste marble was used in a coarse aggregate form when compared to that of when marble was used in a dust form. If the cement was replaced with marble powder in proportions of 20% or more, then adverse effects were observed on the compressive strength and workability of the concrete. This study indicated that marble dust at a cement-replacement ratio of 5%-10% affected the mechanical properties of concrete by decreasing the global annual CO₂ emissions by 12% and also lowering the costs from US$40/m³ to US$33/m³.

Keywords: cement production, concrete, CO2 emission, marble, mechanical properties

Procedia PDF Downloads 302

Authors: Javad Karimi

Abstract:

The grain morphology and size of the additively manufactured (AM) aluminium alloys play a vital role in the performance and mechanical properties. AM-fabricated aluminium parts exhibit a relatively coarse microstructure with a columnar morphology. Ceramic nanoparticles, such as Titanium carbide (TiC), have shown great potential to reduce grain size and consequently influence the mechanical properties. In this study, the microstructural and mechanical properties of aluminium parts with TiC nanoparticles will be investigated. AM aluminium components will be fabricated using wire arc additive manufacturing (WAAM). The effect of the addition of TiC nanoparticles with different wt% on the melt pool geometry will be examined, and the obtained results will be compared to those obtained from pure ER5183. The impact of TiC nanoparticles addition in the AM parts will be analyzed comprehensively, and the results will be discussed in detail.

Keywords: additive manufacturing, wire arc additive manufacturing, nanoparticles, grain refinement

Procedia PDF Downloads 63

Authors: El Miloudi Djelloul

Abstract:

Teaching program of `A plan for educating and training outstanding engineers' is divided into intramural teaching program and enterprise practice teaching program. Based on analyzing the basic principles of teaching plans which teaching plan follows for undergraduate mechanical and electrical engineering, major contents of specialty teaching project are studied amply. The study contents include the system optimization and reform of common curriculum, specialty curriculum and practice curriculum. The practice indicated that under outstanding engineers training mode, the optimized curriculum system have practicability, and achieve the training objectives.

Keywords: curriculum system, mechanical and electronic engineering, outstanding engineers, teaching program

Procedia PDF Downloads 501

Authors: Natalie M. Wride, Xueyu Geng

Abstract:

Subgrade soils of railway infrastructure are subjected to a significant number of load applications over their design life. The use of slab track on existing and future proposed rail links requires a reduced maintenance and repair regime for the embankment subgrade, due to restricted access to the subgrade soils for remediation caused by cyclic deformation. It is, therefore, important to study the deformation behaviour of soft cohesive subsoils induced as a result of long term cyclic loading. In this study, a series of oedometer tests and cyclic triaxial tests (10,000 cycles) have been undertaken to investigate the undrained deformation behaviour of soft kaolin. X-ray Computer Tomography (CT) scanning of the samples has been performed to determine the change in porosity and soil structure density from the sample microstructure as a result of the laboratory testing regime undertaken. Combined with the examination of excess pore pressures and strains obtained from the cyclic triaxial tests, the results are compared with an existing analytical solution for long term settlement considering repeated low amplitude loading. Modifications to the analytical solution are presented based on the laboratory analysis that shows good agreement with further test data.

Keywords: creep, cyclic loading, deformation, long term settlement, train loading

Procedia PDF Downloads 279

Authors: Mahmoud Mohamed Emam, Yasser Fathy Hendawy Al-Mahdy

Abstract:

Higher education institutions (HEIs) in Arab countries have witnessed large scope transformations as a result of embracing globalised practices. The introduction of program academic accreditation in HEIs in the Arab context has been regarded as a change enterprise that has proponents and opponents. In essence, introducing new systems or practices trigger changes that may shatter employees at a given organization. Therefore, it is argued that the interaction between organizational, contextual, and individual-related variables are likely to determine how the organization succeeds in facing resistance to change. This study investigated a mediated-effects model of organizational support and citizenship behavior. The model proposes organizational support as an antecedent of citizenship behavior and commitment to change as a mediator in the organizational support–citizenship behavior relationship. Survey data were collected and analyzed from university faculty (n=221) using structural equation modeling. Findings showed that organizational support significantly contributes to increasedcitizenshipbehaviour and the commitment of university faculty to program accreditation as a change enterprise, which has a significant and direct impact on their citizenship behaviour. We conclude that university-level organizational support shapes faculty’s commitment to change both directly and indirectly. The findings have significant practical implications for HEIs in Arab countries when they introduce new practices that aim at improving institutional effectiveness.

Keywords: organizational support, accreditation, commitment, citizenship behaviour

Procedia PDF Downloads 76

Authors: Karla Hrbackova, Irena Balaban Cakirpaloglu

Abstract:

This paper is a report on self-regulation in socially rejected pupils. A certain form of social rejection can be found in almost every class within the school environment. Research shows that due to social rejection mechanisms supporting the individual´s effort of reintegration into the group are not triggered. Paradoxically the opposite tendency arises, i.e., an increase in selfish and defeating behaviour. The link between peer exposure and self-regulation is likely to vary as a function of a type and quality of peer interaction (e.g., rejection or acceptance). The paper aims to clarify the level of self-regulation related to interpersonal cognitive problem-solving within the process of social rejection in a school class. The research was done on a sample of 1,133 upper-primary school pupils using the Means-Ends Problem Solving technique (MEPS) and peer sociometric nomination. The results showed that the level of self-regulated skills is related to the status of social rejection. Socially rejected pupils achieve lower levels of self-regulation than other classmates. We found deficiency in the regulation of behaviour, emotions and the regulation of will in the peer rejected pupils with the exception of cognitive regulation in which no differences were detected between socially rejected pupils and other classmates. The results have implications for early prevention and intervention efforts to foster adaptive self-regulation and reduce the risk of later social rejection.

Keywords: interpersonal cognitive problem-solving, self-regulation, socially rejected pupils, upper-primary school pupils

Procedia PDF Downloads 155

Authors: Atena Naeimi, Mehri-Sadat Ekrami-Kakhki

Abstract:

Fe3O4 is one of the important magnetic oxides with spinel structure; it has exhibited unique electric and magnetic properties based on the electron transfer between Fe2+ and Fe3+ in the octahedral sites. Fe3O4 have received considerable attention in various areas such as cancer therapy, drug targeting, enzyme immobilization catalysis, magnetic cell separation, magnetic refrigeration systems and super-paramagnetic materials. Fe3O4–ZnO nanostructures were synthesized via a surfactant-free ultrasonic reaction at room temperatures. The effect of various parameters such as temperature, time, and power on the size and morphology of the product was investigated. Alternating gradient force magnetometer shows that Fe3O4 nanoparticles exhibit super-paramagnetic behaviour at room temperature. For preparation of nanocomposite 1 g of Fe3O4 nanostructures were dispersed in 100 mL of distilled water. 0.25 g of Zn (NO3)2 and 20 mL of NH3 solution 1 M were then slowly added to the solution under ultrasonic irradiation. The product was centrifuged, washed with distilled water and dried in the air. The photocatalytic behaviour of Fe3O4–ZnO nanoparticles was evaluated using the degradation of a methyl orange aqueous solution under ultraviolet light irradiation. As time increased, more and more methyl orange was adsorbed on the nanoparticles catalyst, until the absorption peak vanish. The methyl orange concentration decreased rapidly with increasing UV-irradiation time.

Keywords: nanocomposite, ultrasonic, paramagnetic, photocatalytic

Procedia PDF Downloads 289

Authors: M. Saidi, I. Djefour, F. Ait Medjber, A. Melouane, A. Gacem

Abstract:

The objective of this research is to study the physical and mechanical properties and durability of self-compacting mortars prepared by substituting a part of cement up to a percentage of 30% pozzolan according to different Blaine specific surface area (SSB1=7000 cm²/g and SSB=9000 cm²/g)). Order to evaluate durability, mortars were subjected to chemical attacks in various aggressive environments, a solution of a mixture of nitric acid and ammonium nitrate (HNO₃ + NH₄NO₃) and a magnesium sulfate salt solution (MgSO₄)) with a concentration of 10%, for a period of one month. This study is complemented by a comparative study of the durability of mortars elaborated with sulphate resistant cement (SRC). The results show that these mortars develop long-term, mechanical and chemical resistance better than mortars based Portland cement with 5% gypsum (CEM 1) and SRC. We found that the mass losses are lowest in mortars elaborated with pozzolanic cement (30% substitution with SSB₂) in both of chemical attack solutions (3.28% in the solution acid and 1.16% in the salt solution) and the compressive strength gains of 14.68% and 8.5% respectively in the two media. This is due to the action of pozzolan which fixes portlandite to form hydrated calcium silicate (CSH) from the hydration of tricalcic silicate (C₃S).

Keywords: aggressive environments, durability, mechanical strengths, pozzolanic cement, self-compacting mortar

Procedia PDF Downloads 214

Authors: Javaid Butt, Habtom Mebrahtu, Hassan Shirvani

Abstract:

The paper presents a new additive manufacturing process for the production of metal and composite parts. It is termed as composite metal foil manufacturing and is a combination of laminated object manufacturing and brazing techniques. The process has been described in detail and is being used to produce dissimilar aluminum to copper foil single lap joints. A three dimensional finite element model has been developed to study the thermo-mechanical characteristics of the dissimilar Al/Cu single lap joint. The effects of thermal stress and strain have been analyzed by carrying out transient thermal analysis on the heated plates used to join the two 0.1mm thin metal foils. Tensile test has been carried out on the foils before joining and after the single Al/Cu lap joints are made, they are subjected to tensile lap-shear test to analyze the effect of heat on the foils. The analyses are designed to assess the mechanical integrity of the foils after the brazing process and understand whether or not the heat treatment has an effect on the fracture modes of the produced specimens.

Keywords: brazing, laminated object manufacturing, tensile lap-shear test, thermo-mechanical analysis

Procedia PDF Downloads 324

Authors: Amy Whelan

Abstract:

This paper presents the reader with the overarching research topic: Examining the drivers to sustainable consumer behavioural intention in the Irish aviation industry. This research will examine the underlying factors that facilitate or hinder a consumer’s sustainable consumption pertaining to aviation, in order to advance the Sustainable Development Goals (SDG’s). The SDG’s were adopted by all United Nations Member States in 2015 as a call to end poverty, to protect the planet and to ensure that all people enjoy peace and prosperity by the year 2030. Consumers are becoming increasingly concerned about environmental, social and economic issues, and are willing to act on those concerns. More recently, the impact of a consumers environmental footprint has led consumers to re-evaluate their purchase habits and in some cases consumers are more willing to spend more on products and services with environmental characteristics. Accordingly, this has pushed businesses to re-examine their sustainable efforts. However, although consumers may feel a moral responsibility to live sustainably, they cannot do so without effective support from governments, NGOs and the businesses with which they interact. Through the use of Ajzen’s amended TPB model, this research seeks to understand consumers attitudes and behavioural intention towards sustainable aviation and travel and examine the attitude-behaviour gap in sustainable tourism and aviation in Ireland. This research is a mixed methods study and will include an initial elicitation study in the form of focus groups supported by a quantitative survey to inform the initial findings of this research.

Keywords: aviation, consumer behaviour, marketing, sustainability

Procedia PDF Downloads 63

Authors: Dalila Hammiche, Lisa Klaai, Amar Boukerrou

Abstract:

Following this trend, natural fiber reinforcements have been gaining importance in the composites sector. The effectiveness of natural fiber–reinforced PLA composite as an alternative material to substitute the non-renewable petroleum-based materials has been examined by researchers. In this study, we investigated the physicochemical, particle size and distribution, and thermal behavior of prickly pear seed flour (PPSF). Then, composites were manufactured with 20% in PPSF. Thermal, morphological, and mechanical properties have been studied, and water absorption tests as well. The characterization of this fiber has shown that cellulose is the majority constituent (30%), followed by hemicellulose (27%). To improve the fiber-matrix adhesion, the PPS was chemically treated with alkali treatment. The addition of PPSF decreases the thermal properties, and the study of the mechanical properties showed that the increase in the fiber content from 0 to 20% increased Young’s modulus. According to the results, the mechanical and thermal behaviors of composites are improved after fiber treatment. However, there is an increase in water absorption of composites compared to the PLA matrix. The moisture sensitivity of natural fiber composites limits their use in structural applications. Degradation of the fiber-matrix interface is likely to occur when the material is subjected to variable moisture conditions.

Keywords: biopolymer, composites, alcali treatment, mechanical properties

Procedia PDF Downloads 111

Authors: H. Zou, B. Wang

Abstract:

Thermal distortion of the machine tool plays a critical role in its machining accuracy. This study investigates the thermal performance of a high-precision machine frame with future-oriented mineral casting components. A thermo-mechanical finite element model (FEM) was established to evaluate the thermal behavior of the frame under environmental thermal fluctuations. The validity of the presented FEM model was confirmed experimentally by a series of laser interferometer tests. Good agreement between numerical and experimental results demonstrates that the proposed model can accurately predict the thermal deformation of the frame with thermo-mechanical coupling effect. The results also show that keeping the workshop in thermally stable conditions is crucial for improving the machine accuracy of the system with large scale components. The goal of this paper is to investigate the feasibility of innovative mineral casting material applied in high-precision drilling machine and to provide a strategy for machine tool industry seeking a perfect substitute for classic frame materials such as cast iron and granite.

Keywords: thermo-mechanical model, finite element method, laser interferometer, mineral casting frame

Procedia PDF Downloads 288

Authors: M. J. Shivaram, Shashi Bhushan Arya, Jagannath Nayak, Bharat Bhooshan Panigrahi

Abstract:

Titanium and its alloys have become more significant implant materials due to their mechanical properties, excellent biocompatibility and high corrosion resistance. Biomaterials can be produce by using the powder metallurgy (PM) methods and required properties can tailored by varying the processing parameters, such as ball milling time, space holder particles, and sintering temperature. The desired properties such as, structural and mechanical properties can be obtained by powder metallurgy method.  In the present study, deals with fabrication of solid and porous Ti-20Nb-5Ag alloy using high energy ball milling for different times (5 and 20 h). The resultant powder particles were used to fabricate solid and porous Ti-20Nb-5Ag alloy by adding space holder particles (NH₄HCO₃). The resultant powder particles, fabricated solid and porous samples were characterized by scanning electron microscopy (SEM). The compressive strength, elastic modulus and microhardness properties were investigated. Solid and porous Ti-20Nb-5Ag alloy samples showed good mechanical properties for 20 h ball milling time as compare to 5 h ball milling.

Keywords: ball milling, compressive strengths, microstructure, porous titanium alloy

Procedia PDF Downloads 286

Authors: Jifeng Zhang , Yongpeng Lei

Abstract:

Continuous carbon fiber reinforced polyamide 6 (CF/PA6) composites are potential for application in the automotive industry due to their high specific strength and stiffness. However, PA6 resin is sensitive to the moisture in the hydrothermal environment and CF/PA6 composites might undergo several physical and chemical changes, such as plasticization, swelling, and hydrolysis, which induces a reduction of mechanical properties. So far, little research has been reported on the assessment of the effects of hydrothermal aging on the mechanical properties of continuous CF/PA6 composite. This study deals with the effects of hydrothermal aging on moisture absorption and mechanical properties of polyamide 6 (PA6) and polyamide 6 reinforced with continuous carbon fibers composites (CF/PA6) by immersion in distilled water at 30 ℃, 50 ℃, 70 ℃, and 90 ℃. Degradation of mechanical performance has been monitored, depending on the water absorption content and the aging temperature. The experimental results reveal that under the same aging condition, the PA6 resin absorbs more water than the CF/PA6 composite, while the water diffusion coefficient of CF/PA6 composite is higher than that of PA6 resin because of interfacial diffusion channel. In mechanical properties degradation process, an exponential reduction in tensile strength and elastic modulus are observed in PA6 resin as aging temperature and water absorption content increases. The degradation trend of flexural properties of CF/PA6 is the same as that of tensile properties of PA6 resin. Moreover, the water content plays a decisive role in mechanical degradation compared with aging temperature. In contrast, hydrothermal environment has mild effect on the tensile properties of CF/PA6 composites. The elongation at breakage of PA6 resin and CF/PA6 reaches the highest value when their water content reaches 6% and 4%, respectively. Dynamic mechanical analysis (DMA) and scanning electron microscope (SEM) were also used to explain the mechanism of mechanical properties alteration. After exposed to the hydrothermal environment, the Tg (glass transition temperature) of samples decreases dramatically with water content increase. This reduction can be ascribed to the plasticization effect of water. For the unaged specimens, the fibers surface is coated with resin and the main fracture mode is fiber breakage, indicating that a good adhesion between fiber and matrix. However, with absorbed water content increasing, the fracture mode transforms to fiber pullout. Finally, based on Arrhenius methodology, a predictive model with relate to the temperature and water content has been presented to estimate the retention of mechanical properties for PA6 and CF/PA6.

Keywords: continuous carbon fiber reinforced polyamide 6 composite, hydrothermal aging, Arrhenius methodology, interface

Procedia PDF Downloads 111