Abstract:

The pH of the body plays a great role in the degradation kinetics of biodegradable Mg-Ca orthopedic implants. At the location of fracture, the pH of the body becomes no longer neutral which draws the attention towards studying a range of different pH values of the body fluid. In this study, the pH of Hank’s balanced salt solution (HBSS) was modified by phosphate buffers into an aggressive acidic pH 1.8, a slightly acidic pH 5.3 and an alkaline pH 8.1. The biodegradation of Mg-0.8Ca implant was tested in those three different media using immersion test and electrochemical polarization means. It was proposed that the degradation rate has increased with decreasing the pH of HBSS. The immersion test revealed weight gain for all the samples followed by weight loss as the immersion time increased. The highest weight gain was pronounced for the acidic pH 1.8 and the least weight gain was observed for the alkaline pH 8.1. This was in agreement with the electrochemical polarization test results where the degradation rate was found to be high (7.29 ± 2.2 mm/year) in the aggressive acidic solution of pH 1.8 and relatively minimum (0.31 ± 0.06 mm/year) in the alkaline medium of pH 8.1. Furthermore, it was confirmed that the pH of HBSS has reached a steady state of an alkaline pH (~pH 11) at the end of the two-month immersion period regardless of the initial pH of the solution. Finally, the corrosion products formed on the samples’ surface were investigated by SEM, EDX and XRD analyses that revealed the formation of magnesium and calcium phosphates with different morphologies according to the pH.

Keywords: biodegradable, electrochemical polarization means, orthopedics, immersion test, simulated body fluid

Procedia PDF Downloads 123

Authors: Musa D. Aliyu, Ouahid Harireche, Colin D. Hills

Abstract:

The incapability of supercritical C02 to transport and dissolve mineral species from the geothermal reservoir to the fracture apertures and other important parameters in heat mining makes it an attractive substance for Heat extraction from hot dry rock. In other words, the thermodynamic efficiency of hot dry rock (HDR) reservoirs also increases if supercritical C02 is circulated at excess temperatures of 3740C without the drawbacks connected with silica dissolution. Studies have shown that circulation of supercritical C02 in homogenous geothermal reservoirs is quite encouraging; in comparison to that of the water. This paper aims at investigating the aforementioned processes in the case of the heterogeneous geothermal reservoir located at the Soultz site (France). The MultiPhysics finite element package COMSOL with an interface of coupling different processes encountered in the geothermal reservoir stimulation is used. A fully coupled numerical model is developed to study the thermal and hydraulic processes in order to predict the long-term operation of the basic reservoir parameters that give optimum energy production. The results reveal that the temperature of the SCC02 at the production outlet is higher than that of water in long-term stimulation; as the temperature is an essential ingredient in rating the energy production. It is also observed that the mass flow rate of the SCC02 is far more favourable compared to that of water.

Keywords: FEM, HDR, heterogeneous reservoir, stimulation, supercritical C02

Procedia PDF Downloads 385

Authors: D. W. Mohammed, J. Bowen, S. N. Kukureka

Abstract:

Successful design and fabrication of flexible devices for electrode components requires a low sheet resistance, high optical transmittance, high mechanical reliability. Indium tin oxide (ITO) film is currently the predominant transparent conductive oxide (TCO) film in potential applications such as flexible organic light- emitting diodes, flat-panel displays, solar cells, and thin film transistors (TFTs). However ITO films are too brittle and their resistivity is rather high in some cases compared with ITO/Ag/ ITO, and they cannot completely meet flexible optoelectronic device requirements. Therefore, in this work the mechanical properties of ITO /Ag/ITO multilayer film that deposited on Polyethylene terephthalate (PET) compared with the single layered ITO sample were investigated using bending fatigue, twisting fatigue and thermal cycling experiments. The electrical resistance was monitored during the application of mechanical and thermal loads to see the pattern of relationship between the load and the electrical continuity as a consequent of failure. Scanning electron microscopy and atomic force microscopy were used to provide surface characterization of the mechanically-tested samples. The effective embedment of the Ag layer between upper and lower ITO films led to metallic conductivity and superior flexibility to the single ITO electrode, due to the high failure strain of the ductile Ag layer. These results indicate that flexible ITO/Ag/ITO multilayer electrodes are a promising candidate for use as transparent conductor in flexible displays. They provided significantly reduced sheet resistance compared to ITO, and improved bending and twisting properties both as a function of radius, angle and thermal cycling.

Keywords: ITO/Ag/ITO multilayer, failure strain, mechanical properties, PET

Procedia PDF Downloads 296

Authors: Joshua Russell, Omar Zubair, Reuben Ndegwa

Abstract:

Introduction: Mesenteric ischemia is an uncommon condition that can be challenging to diagnose in the acute setting, with the potential for significant morbidity and mortality. Very rarely has acute acalculous cholecystitis been described in the setting of mesenteric ischemia. Case: This was the case in a 78-year-old male, who initially presented with clinical and radiological evidence of small bowel obstruction, thought likely secondary to malignancy. The patient had a 6-week history of anorexia, worsening lower abdominal pain, and ~30kg of unintentional weight loss over a 12-month period and a CT- scan demonstrated a transition point in the distal ileum. The patient became increasingly hemodynamically unstable and peritonitic, and an emergency laparotomy was performed. Intra-operatively, however, no obvious transition point was identified, and instead, the gallbladder was markedly gangrenous and oedematous, consistent with acalculous cholecystitis. An open total cholecystectomy was subsequently performed. The patient was admitted to the Intensive Care Unit post-operatively and continued to deteriorate over the proceeding 48 hours, with two re-look laparotomies demonstrating progressively worsening bowel ischemia, initially in the distribution of the superior mesenteric artery and then the coeliac trunk. On review, the patient was found to have an aberrant right hepatic artery arising from the superior mesenteric artery. The extent of ischemia was considered non-survivable, and the patient was palliated. Discussion: Multiple theories currently exist for the underlying pathophysiology of acalculous cholecystitis, including biliary stasis, sepsis, and ischemia. This case lends further support to ischemia as the underlying etiology of acalculous cholecystitis. This is particularly the case when considered in the context of the patient’s aberrant right hepatic artery arising from the superior mesenteric artery, which occurs in 11-14% of patients. Conclusion: This case report adds further insight to the debate surrounding the pathophysiology of acalculous cholecystitis. It also presents acalculous cholecystitis as a complication of mesenteric ischemia that should always be considered, especially in the elderly patient and in the context of relatively common anatomical variations. Furthermore, the case brings to attention the importance of maintaining dynamic working diagnoses in the setting of evolving pathophysiology and clinical presentations.

Keywords: acalculous cholecystitis, anatomical variation, general surgery, mesenteric ischemia

Procedia PDF Downloads 191

Authors: A. Duncan, A. Blake, A. O'Gara, J. Fitzgerald

Abstract:

Introduction: Acute traumatic rib fractures have significant morbidity and mortality and are a commonly seen injury in trauma patients. Rib fracture pain can often be acute and can prove challenging to manage. We performed an audit on patients with acute traumatic rib fractures with the aim of composing a referral and treatment pathway for such patients. Methods: From January 2021 to January 2022, the pain medicine service encouraged early referral of all traumatic rib fractures to the pain service for a multi-modal management approach. A retrospective audit of analgesic management was performed on a select cohort of 24 patients, with a mean age of 67, of which 19 had unilateral rib fractures. Results: 17 of 24 patients (71%) underwent local, regional block as part of a multi-modal analgesia regime. Only one regional complication was observed, seen with hypotension occurring in one patient with a thoracic epidural. The group who did not undergo regional block had a length of stay (LOS) 17 days longer than those who did (27 vs. 10) and higher rates of pneumonia (29% vs. 18%). Conclusion: Early referral to pain specialists is an important component of the effective management of acute traumatic rib fractures. From our audit, it is evident that regional blocks can be effectively used in these cases as part of a multi-modal analgesia regime and may confer benefits in terms of respiratory complications and length of stay.

Keywords: rib fractures, regional blocks, thoracic epidural, erector spina block

Procedia PDF Downloads 75

Authors: Sadaf Saeed

Abstract:

The consideration of walkability as an urban design parameter in conjunction with transit-oriented development is an established trend in the developed countries but an upcoming trend in developing countries. In Pakistan, the first Bus Rapid Transit (locally called as Metro Bus) has been introduced in the city of Lahore in 2013 where around 40 percent of the riders access to transit stations by walking. To what extent the aspect of walkability has been considered in the local scenario? To address this question, this paper presents an account of urban design parameters regarding pedestrian provisions and quality of walking environment between Metro Bus stations and users’ destination in the transit neighbourhoods (areas up to 500-meter radius). The primary and secondary data for objective and subjective walkability measurements has been used for neighbourhoods of five selected transit stations ranked against the predefined critical assessed factors (CAF). The multi-criteria approach including visual and geospatially-based parameters at street level, along with walkability index score at selected sites linked with CAF evaluation were the selected methods for this study. The acceptability of walkability as an urban design parameter for transit planning in terms of connectivity and social implications of the concept has also been analysed in the local context. The paper highlights that the aspect of walkability in Lahore is being derelict owing to the focus of government on other initiatives such as park and ride and feeder bus services for mobility of passengers. However, the pedestrian-friendly design parameters as a part of future transit planning can enhance social, liveable and interactive walking environment within transit neighbourhoods.

Keywords: walkability, sustainability, transit neighborhoods, social communities

Procedia PDF Downloads 245

Authors: Rachel Luz P. Vivas-rica, Gloria G. Delan, Christine M. Corrales, Alfonso S. Piquero, Irene A. Monte

Abstract:

ABSTRACT -Selected Integrated Coastal Resource Management Program (ICRMP) sites in Southwestern Cebu were studied employing a stratified proportional sampling method using semi-structured questionnaires. Four hundred sixteen (416) respondents from five barangays with Marine Protected Areas (MPAs) and four barangays without marine sanctuaries were considered in the study. Results showed similarity of socio-economic characteristics in terms of average age, majority were middle aged, and married. Households were male dominated, obtained low education for both MPA and Non-MPA areas. In terms of occupation, majority in both areas engaged in fulltime fishing however part time jobs as carpenter, construction worker, driver or farmer as another income source. Most of the households were nuclear families with average family size of five for both MPA and Non-MPA. Fishing experience ranged from less than 1 year to more than 50 years. Fishing grounds were within the 15 kilometer radius of each considered site. Even if the respondents were totally dependent on fishing as a major source of income, still their income is way below the poverty threshold both in the MPA and Non-MPA areas. This is further explained by the marginality of their fishing implements wherein majority uses gill nets, hook & line, spear and paddle boat in fishing. Their volume of catch from an average of 6 hours fishing expedition ranges from half a kilo to a maximum of 4 kilos. Majority are not members of fishing groups or organizations.

Keywords: integrated coastal resource management program, marine protected areas, socio-economic, poverty threshold

Procedia PDF Downloads 518

Authors: Elizabeth Farquhar, Erich Ritter

Abstract:

Studying shark's interaction with humans and their behavioral responses will have enormous implications for other fields of marine biology and oceanography. The health of sharks has direct impacts on the stability of human society with a reported 3.5 billion people depending on the ocean for food and/or livelihood. Discovering how sharks behave and interact with people, will have enormous implications for future studies, along with the development of more effective ways to reduce negative shark/human interactions. This specific study investigates the effects of contrasting ponchos worn by divers on the approach distances of Carcharhinus perezi. Data was collected over a two week period at a test site off the shore of Eleuthera Island in the Bahamas, with a depth of approximately 55 feet during mid-August. Sixty-minute dive trials were conducted and videoed from above with 5-meter radius markers on the ocean floor surrounding the two divers, kneeling back-to-back. Five poncho colors were worn by the two divers (black, navy blue, dark green, yellow and orange), rotating the color permutations randomly to test the distance a shark will approach each color. Results indicate significantly closer approach patterns when divers were wearing orange ponchos, and the combination of orange with black and blue ponchos were found to be statistically significant. These results are relevant to understanding how sharks perceive contrast and dive equipment in the marine environment, which could have the potential to prevent negative shark/human interactions.

Keywords: shark behavior, animal behavior, marine biology, conservation

Procedia PDF Downloads 143

Authors: Cláudia Patrocínio, Beatriz Fernandes, Ana Filipa Pires

Abstract:

Background: Mirror therapy (MT) is used to improve motor function after stroke. During MT, a mirror is placed between the two upper limbs (UL), thus reflecting movements of the non- affected side as if it were the affected side. Objectives: The aim of this review is to analyze the evidence on the effec.tiveness of MT in the recovery of UL function in population with post chronic stroke. Methods: The literature search was carried out in PubMed, ISI Web of Science, and PEDro database. Inclusion criteria: a) studies that include individuals diagnosed with stroke for at least 6 months; b) intervention with MT in UL or comparing it with other interventions; c) articles published until 2023; d) articles published in English or Portuguese; e) randomized controlled studies. Exclusion criteria: a) animal studies; b) studies that do not provide a detailed description of the intervention; c) Studies using central electrical stimulation. The methodological quality of the included studies was assessed using the Physiotherapy Evidence Database (PEDro) scale. Studies with < 4 on PEDro scale were excluded. Eighteen studies met all the inclusion criteria. Main results and conclusions: The quality of the studies varies between 5 and 8. One article compared muscular strength training (MST) with MT vs without MT and four articles compared the use of MT vs conventional therapy (CT), one study compared extracorporeal shock therapy (EST) with and without MT and another study compared functional electrical stimulation (FES), MT and biofeedback, three studies compared MT with Mesh Glove (MG) or Sham Therapy, five articles compared performing bimanual exercises with and without MT and three studies compared MT with virtual reality (VR) or robot training (RT). The assessment of changes in function and structure (International Classification of Functioning, Disability and Health parameter) was carried out, in each article, mainly using the Fugl Meyer Assessment-Upper Limb scale, activity and participation (International Classification of Functioning, Disability and Health parameter) were evaluated using different scales, in each study. The positive results were seen in these parameters, globally. Results suggest that MT is more effective than other therapies in motor recovery and function of the affected UL, than these techniques alone, although the results have been modest in most of the included studies. There is also a more significant improvement in the distal movements of the affected hand than in the rest of the UL.

Keywords: physical therapy, mirror therapy, chronic stroke, upper limb, hemiplegia

Procedia PDF Downloads 55

Authors: Muhammad Kamran, Xue Pu, Naveed Ahmed

Abstract:

Sandwich foam structures are efficient in impact energy absorption and making components lightweight; however their efficient use require a detailed understanding of its mechanical response. In this study, the foam core, laminated facings’ sandwich panel with internal triangular rib configuration is impacted by a spherical steel projectile at different angles using ABAQUS finite element package and damage mechanics is studied. Laminated ribs’ structure is sub-divided into three formations; all zeros, all 45 and optimized combination of zeros and 45 degrees. Impact velocity is varied from 250 m/s to 500 m/s with an increment of 50 m/s. The impact damage can significantly demolish the structural integrity and energy absorption due to fiber breakage, matrix cracking, and de-bonding. Macroscopic fracture study of the panel and core along with load-displacement responses and failure modes are the key parameters in the design of smart ballistic resistant structures. Ballistic impact characteristics of panels are studied on different speed, different inclination angles and its dependency on the base, and core materials, ribs formation, and cross-sectional spaces among them are determined. Impact momentum, penetration and kinetic energy absorption data and curves are compiled to predict the first and proximity impact in an effort to enhance the dynamic energy absorption.

Keywords: dynamic energy absorption, proximity impact, sandwich panels, impact momentum

Procedia PDF Downloads 388

Authors: Filimonova Alexanra

Abstract:

Inviscid incompressible fluid flows are considered. The object of the study is a vortex parquet – a structure consisting of distributed vortex spots of different directions, occupying the entire plane. The main attention is paid to the study of advection processes of passive particles in the corresponding velocity field. The dynamics of the vortex structures is considered in a rectangular region under the assumption that periodic boundary conditions are imposed on the stream function. Numerical algorithms are based on the solution of the initial-boundary value problem for nonstationary Euler equations in terms of vorticity and stream function. For this, the spectral-vortex meshless method is used. It is based on the approximation of the stream function by the Fourier series cut and the approximation of the vorticity field by the least-squares method from its values in marker particles. A vortex configuration, consisting of four vortex patches is investigated. Results of a numerical study of the dynamics and interaction of the structure are presented. The influence of the patch radius and the relative position of positively and negatively directed patches on the processes of interaction and mixing is studied. The obtained results correspond to the following possible scenarios: the initial configuration does not change over time; the initial configuration forms a new structure, which is maintained for longer times; the initial configuration returns to its initial state after a certain period of time. The processes of mass transfer of vorticity by liquid particles on a plane were calculated and analyzed. The results of a numerical analysis of the particles dynamics and trajectories on the entire plane and the field of local Lyapunov exponents are presented.

Keywords: ideal fluid, meshless methods, vortex structures in liquids, vortex parquet.

Procedia PDF Downloads 64

Authors: Wenxin Mei, Jinhua Sun, Qingsong Wang

Abstract:

The volume expansion of lithium-ion batteries is mainly induced by intercalation induced stress within the negative electrode, resulting in capacity degradation and even battery failure. Stress generation due to lithium intercalation into graphite particles is investigated based on an electrochemical-mechanical model in this work. The two-dimensional model presented is fully coupled, inclusive of the impacts of intercalation-induced stress, stress-induced intercalation, to evaluate the lithium concentration, stress generation, and displacement intra and inter-particle. The results show that the distribution of lithium concentration and stress exhibits an analogous pattern, which reflects the relation between lithium diffusion and stress. The results of inter-particle stress indicate that larger Von-Mises stress is displayed where the two particles are in contact with each other, and deformation at the edge of particles is also observed, predicting fracture. Additionally, the maximum inter-particle stress at the end of lithium intercalation is nearly ten times the intraparticle stress. And the maximum inter-particle displacement is increased by 24% compared to the single-particle. Finally, the effect of graphite particle arrangement on inter-particle stress is studied. It is found that inter-particle stress with tighter arrangement exhibits lower stress. This work can provide guidance for predicting the intra and inter-particle stress to take measures to avoid cracking of electrode material.

Keywords: electrochemical-mechanical model, graphite particle, lithium concentration, lithium ion battery, stress

Procedia PDF Downloads 198

Authors: Tewodros Abate Alemayehu, Abebe Getahun, Akewake Geremew, Dawit Solomon Demeke, John Recha, Dawit Solomon, Gebremedihin Ambaw, Fasil Dawit Moges

Abstract:

The purpose of this study was to examine the effects of supplementation of zinc oxide (ZnO) nanoparticles and Mannan-oligosaccharide (MOS) on growth performance, feed utilization, fatty acid profiles, hematology, and intestinal morphology of Chamo strain Nile tilapia Oreochromis niloticus (L.) fry reared at optimal temperature (28.62 ± 0.11 ⁰C). Nile tilapia fry (initial weight 1.45 ± 0.01g) were fed basal diet/control diet (Diet-T1), 6 g kg-¹ MOS supplemented diet (Diet-T2), 4 mg ZnO-NPs supplemented diet (Diet-T3), 4 mg ZnO-Bulk supplemented diet (Diet-T4), a combination of 6 g kg-¹ MOS and 4 mg ZnO-Bulk supplemented diet (Diet-T5) and combination of 6 g kg-¹ MOS and 4 mg ZnO-NPs supplemented diet (Diet-T6). Randomly, duplicate aquariums for each diet were assigned and hand-fed to apparent satiation three times daily (08:00, 12:00, and 16:00) for 12 weeks. Fish fed MOS, ZnO-NPs, and a combination of MOS and ZnO-Bulk supplemented diet had higher weight gain, Daily Growth Rate (DGR), and Specific Growth Rate (SGR) than fish fed the basal diet and other feeding groups, although the effect was not significant. According to the GC analysis, Nile tilapia was supplemented with 6 g kg-¹ MOS, 4 mg ZnO-NPs, or a combination of ZnO-NPs, and MOS showed the highest content of EPA, DHA, and higher ratios of PUFA/SFA than other feeding groups. Mean villi length in the proximal and middle portion of the Nile tilapia intestine was affected significantly (p<0.05) by diet. Fish fed Diet-T2 and Diet-T3 had significantly higher villi lengths in the proximal and middle portions of the intestine compared to other feeding groups. The inclusion of additives significantly improved goblet numbers at the proximal, middle, and distal portions of the intestine. Supplementation of additives had also improved some hematological parameters compared with control groups. In conclusion, dietary supplementation of additives MOS and ZnO-NPs could confer benefits on growth performance, fatty acid profiles, hematology, and intestinal morphology of Chamo strain Nile tilapia.

Keywords: chamo strain nile tilapia, fatty acid profile, hematology, intestinal morphology, MOS, ZnO-Bulk, ZnO-NPs

Procedia PDF Downloads 75

Authors: M. M. Hassani, S. Ammann, F. K. Wittel, P. Niemz, H. J. Herrmann

Abstract:

Application of engineered wood, especially in the form of glued-laminated timbers has increased significantly. Recent progress in plywood made of high strength and high stiffness hardwoods, like European beech, gives designers in general more freedom by increased dimensional stability and load-bearing capacity. However, the strong hygric dependence of basically all mechanical properties renders many innovative ideas futile. The tendency of hardwood for higher moisture sorption and swelling coefficients lead to significant residual stresses in glued-laminated configurations, cross-laminated patterns in particular. These stress fields cause initiation and evolution of cracks in the bond-lines resulting in: interfacial de-bonding, loss of structural integrity, and reduction of load-carrying capacity. Subsequently, delamination of glued-laminated timbers made of hardwood elements can be considered as the dominant failure mechanism in such composite elements. In addition, long-term creep and mechano-sorption under changing environmental conditions lead to loss of stiffness and can amplify delamination growth over the lifetime of a structure even after decades. In this study we investigate the delamination process of adhesively bonded hardwood (European beech) elements subjected to changing climatic conditions. To gain further insight into the long-term performance of adhesively bonded elements during the design phase of new products, the development and verification of an authentic moisture-dependent constitutive model for various species is of great significance. Since up to now, a comprehensive moisture-dependent rheological model comprising all possibly emerging deformation mechanisms was missing, a 3D orthotropic elasto-plastic, visco-elastic, mechano-sorptive material model for wood, with all material constants being defined as a function of moisture content, was developed. Apart from the solid wood adherends, adhesive layer also plays a crucial role in the generation and distribution of the interfacial stresses. Adhesive substance can be treated as a continuum layer constructed from finite elements, represented as a homogeneous and isotropic material. To obtain a realistic assessment on the mechanical performance of the adhesive layer and a detailed look at the interfacial stress distributions, a generic constitutive model including all potentially activated deformation modes, namely elastic, plastic, and visco-elastic creep was developed. We focused our studies on the three most common adhesive systems for structural timber engineering: one-component polyurethane adhesive (PUR), melamine-urea-formaldehyde (MUF), and phenol-resorcinol-formaldehyde (PRF). The corresponding numerical integration approaches, with additive decomposition of the total strain are implemented within the ABAQUS FEM environment by means of user subroutine UMAT. To predict the true stress state, we perform a history dependent sequential moisture-stress analysis using the developed material models for both wood substrate and adhesive layer. Prediction of the delamination process is founded on the fracture mechanical properties of the adhesive bond-line, measured under different levels of moisture content and application of the cohesive interface elements. Finally, we compare the numerical predictions with the experimental observations of de-bonding in glued-laminated samples under changing environmental conditions.

Keywords: engineered wood, adhesive, material model, FEM analysis, fracture mechanics, delamination

Procedia PDF Downloads 436

Authors: Szymon Kowieski, Zygmunt Mikno

Abstract:

The study involved the optimization of process parameters during resistance spot welding of Al-coated martensitic boron steel 22MnB5, applied in hot stamping, performed using a programme with a multiple current impulse mode and a programme with variable pressure force. The aim of this research work was to determine the possibilities of a growth in welded joint strength and to identify the expansion of a welding lobe. The process parameters were adjusted on the basis of welding process simulation and confronted with experimental data. 22MnB5 steel is known for its tendency to obtain high hardness values in weld nuggets, often leading to interfacial failures (observed in the study-related tests). In addition, during resistance spot welding, many production-related factors can affect process stability, e.g. welding lobe narrowing, and lead to the deterioration of quality. Resistance spot welding performed using the above-named welding programme featuring 3 levels of force made it possible to achieve 82% of welding lobe extension. Joints made using the multiple current impulse program, where the total welding time was below 1.4s, revealed a change in a peeling mode (to full plug) and an increase in weld tensile shear strength of 10%.

Keywords: 22MnB5, hot stamping, interfacial fracture, resistance spot welding, simulation, single lap joint, welding lobe

Procedia PDF Downloads 387

Authors: Alparslan A. Balta, Hilmi Yurdakul, Orkun Tunckan, Servet Turan, Arife Yurdakul

Abstract:

A silicon oxynitride (Si2N2O), the mineralogical name is “Sinoite”, reveals the outstanding physical, mechanical and thermal properties, e.g., good oxidation resistance at high temperatures, high fracture toughness with rod shape, high hardness, low theoretical density, good thermal shock resistance by low thermal expansion coefficient and high thermal conductivity. In addition, the orthorhombic crystal structure of Si2N2O allows accommodating the rare earth (RE) element atoms along the “c” axis due to existing large structural interstitial sites. Here, 0.02 to 0.12 wt. % Nd3+ doped Si2N2O samples were successfully synthesized by spark plasma sintering (SPS) method at 30MPa pressure and 1650oC temperature. Li2O was also utilized as a sintering additive to take advantage of low eutectic point during synthesizing. The specimens were characterized in detail by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and cathodoluminescence (CL) in SEM and photoluminescence (PL) spectroscopy. Based on the overall results, the Si2N2O phase was obtained above 90% by the SPS route. Furthermore, Nd3+: Si2N2O samples showed a very broad intense emission peak between 400-700 nm, which corresponds to white color. Therefore, this material can be considered as a promising candidate for white light-emitting diodes (WLEDs) purposes. This study was supported by TUBITAK under project number 217M667.

Keywords: neodymium, oxynitride, Si₂N₂O, WLEDs

Procedia PDF Downloads 138

Authors: Luis Marquez, Ge Zhu, Vikas Srivastava

Abstract:

High-density polyethylene (HDPE) is one of the most commonly used thermoplastic polymer materials for water and gas pipelines. Slow crack growth failure is a well-known phenomenon in high-density polyethylene material and causes brittle failure well below the yield point with no obvious sign. The failure of transportation pipelines can cause catastrophic environmental and economic consequences. Using the non-destructive testing method to predict slow crack growth failure behavior is the primary preventative measurement employed by the pipeline industry but is often costly and time-consuming. Phenomenological slow crack growth models are useful to predict the slow crack growth behavior in the polymer material due to their ability to evaluate slow crack growth under different temperature and loading conditions. We developed a quantitative method to assess the slow crack growth behavior in the high-density polyethylene pipeline material under different thermal conditions based on existing physics-based phenomenological models. We are also working on developing an experimental protocol and quantitative model that can address slow crack growth behavior under different chemical exposure conditions to improve the safety, reliability, and resilience of HDPE-based pipeline infrastructure.

Keywords: mechanics of materials, physics-based modeling, civil engineering, fracture mechanics

Procedia PDF Downloads 205

Authors: Jung-Hwan Oh, Rajesh Kumar, Il-Kwon Oh

Abstract:

Porous graphene has extensive potential applications in variety of fields such as hydrogen storage, CO oxidation, gas separation, supercapacitors, fuel cells, nanoelectronics, oil adsorption, and so on. However, the generation of some carbon atoms vacancies for precise small holes have been not extensively studied to prevent the agglomerates of graphene sheets and to obtain porous graphene with high surface area. Recently, many research efforts have been presented to develop physical and chemical synthetic approaches for porous graphene. But physical method has very high cost of manufacture and chemical method consumes so many hours for porous graphene. Herein, we propose a porous graphene contained holes with atomic scale precision by embedding metal nano-particles through microwave irradiation for hydrogen storage and CO oxidation multi- functionalities. This proposed synthetic method is appropriate for fast and convenient production of three dimensional nanostructures, which have nanoholes on the graphene surface in consequence of microwave irradiation. The metal nanoparticles are dispersed quickly on the graphene surface and generated uniform nanoholes on the graphene nanosheets. The morphological and structural characterization of the porous graphene were examined by scanning electron microscopy (SEM), transmission scanning electron microscopy (TEM) and RAMAN spectroscopy, respectively. The metal nanoparticle-embedded porous graphene exhibits a microporous volume of 2.586cm3g-1 with an average pore radius of 0.75 nm. HR-TEM analysis was carried out to further characterize the microstructures. By investigating the RAMAN spectra, we can understand the structural changes of graphene. The results of this work demonstrate a possibility to produce a new class of porous graphene. Furthermore, the newly acquired knowledge for the diffusion into graphene can provide useful guidance for the development of the growth of nanostructure.

Keywords: CO oxidation, hydrogen storage, nanocomposites, porous graphene

Procedia PDF Downloads 372

Authors: Davoud Jafari, Paolo Di Marco, Alessandro Franco, Sauro Filippeschi

Abstract:

This paper summarizes the results of an investigation into the heat pipe heat transfer for solar collector applications. The study aims to show the feasibility of a concentrating solar collector, which is coupled with a heat pipe. Particular emphasis is placed on the capillary and boiling limits in capillary porous structures, with different mesh numbers and wick thicknesses. A mathematical model of a cylindrical heat pipe is applied to study its behaviour when it is exposed to higher heat input at the evaporator. The steady state analytical model includes two-dimensional heat conduction in the HP’s wall, the liquid flow in the wick and vapor hydrodynamics. A sensitivity analysis was conducted by considering different design criteria and working conditions. Different wicks (mesh 50, 100, 150, 200, 250, and, 300), different porosities (0.5, 0.6, 0.7, 0.8, and 0.9) with different wick thicknesses (0.25, 0.5, 1, 1.5, and 2 mm) are analyzed with water as a working fluid. Results show that it is possible to improve heat transfer capability (HTC) of a HP by selecting the appropriate wick thickness, the effective pore radius, and lengths for a given HP configuration, and there exist optimal design criteria (optimal thick, evaporator adiabatic and condenser sections). It is shown that the boiling and wicking limits are connected and occurs in dependence on each other. As different parts of the HP external surface collect different fractions of the total incoming insolation, the analysis of non-uniform heat flux distribution indicates that peak heat flux is not affecting parameter. The parametric investigations are aimed to determine working limits and thermal performance of HP for medium temperature SC application.

Keywords: screened heat pipes, analytical model, boiling and capillary limits, concentrating collector

Procedia PDF Downloads 560

Authors: Mustafa Col, Funda Gul Koc, Merve Yangaz, Eylem Subasi, Can Akbasoglu

Abstract:

G38NiCrMo8-4-4 steel is widely used in mining industries, machine parts, gears due to its high strength and toughness properties. In this study, microstructure, wear and mechanical properties of G38NiCrMo8-4-4 steel modified with boron used in the mining industry were investigated. For this purpose, cast materials were alloyed by melting in an induction furnace to include boron with the rates of 0 ppm, 15 ppm, and 50 ppm (wt.) and were formed in the dimensions of 150x200x150 mm by casting into the sand mould. Homogenization heat treatment was applied to the specimens at 1150˚C for 7 hours. Then all specimens were austenitized at 930˚C for 1 hour, quenched in the polymer solution and tempered at 650˚C for 1 hour. Microstructures of the specimens were investigated by using light microscope and SEM to determine the effect of boron and heat treatment conditions. Changes in microstructure properties and material hardness were obtained due to increasing boron content and heat treatment conditions after microstructure investigations and hardness tests. Wear tests were carried out using a pin-on-disc tribometer under dry sliding conditions. Charpy V notch impact test was performed to determine the toughness properties of the specimens. Fracture and worn surfaces were investigated with scanning electron microscope (SEM). The results show that boron element has a positive effect on the hardness and wear properties of G38NiCrMo8-4-4 steel.

Keywords: G38NiCrMo8-4-4 steel, boron, heat treatment, microstructure, wear, mechanical properties

Procedia PDF Downloads 195

Authors: Daniel Francis, Mo Yassin

Abstract:

Transverse patella fractures are routinely fixed using tension band wiring (TBW) using Kirschner wires and a wire in the shape of a figure of 8. The idea of the study was to compare the outcomes of the traditional technique against the more recently used cannulated screws and fiber tape in the shape of a figure of 8. We performed a retrospective cohort study of all the surgically fixed patella fractures from the year 2019 to 2022. The patients were divided into two groups TBW group and cannulated screws group. The primary outcome measure was the failure of fixation and the need for the removal of metalwork. Twenty-six patellar fractures were studied. TBW was used in 14 (53.8%), and cannulated screws were used for fixation in 12 (46.2%). There was one incident of metalwork failure in the TBW and one incident in the cannulated screws group. Five (35.7%) of patients in the TBW needed symptomatic metal work removed and One (8.3%) in the cannulated screw group. In both groups, the rate of fixation failure was low. Symptomatic implants, the most common complication observed, were higher in the TBW group in our practice. Although the small numbers in both groups, the hope of this study is to shine the light on the use of cannulated screws for patella fractures as it would reduce the need for a second operation and reduce the load on the already stretched services as well as improving the patient experience by not requiring further surgery. Although this is not a brand-new technique, it is not commonly used as there have not yet been any studies that demonstrate the lower rates of second surgery needed.

Keywords: patella, tension band wiring, randomised, new technique

Procedia PDF Downloads 75

Authors: Vladyslav Povoroznyuk, Oksana Ivanyk, Nataliia Dzerovych

Abstract:

In the diagnostics of osteoporosis, the gold standard is considered to be bone mineral density; however, X-ray densitometry is not an accurate indicator of osteoporotic fracture risk under all circumstances. In this regard, the search for new methods that could determine the indicators not only of the mineral density, but of the bone tissue quality, is a logical step for diagnostic optimization. One of these methods is the evaluation of trabecular bone quality. The aim of this study was to examine the quality and mineral density of spine bone tissue, femoral neck, and body composition of women depending on the duration of the postmenopausal period, to determine the correlation of body fat with indicators of bone mineral density and quality. The study examined 179 women in premenopausal and postmenopausal periods. The patients were divided into the following groups: Women in the premenopausal period and women in the postmenopausal period at various stages (early, middle, late postmenopause). A general examination and study of the above parameters were conducted with General Electric X-ray densitometer. The results show that bone quality and mineral density probably deteriorate with advancing of postmenopausal period. Total fat and lean mass ratio is not likely to change with age. In the middle and late postmenopausal periods, the bone tissue mineral density of the spine and femoral neck increases along with total fat mass.

Keywords: osteoporosis, bone tissue mineral density, bone quality, fat mass, lean mass, postmenopausal osteoporosis

Procedia PDF Downloads 343

Authors: Seyed Ali Mahdipour, Maryam Shafeei Sarvestani

Abstract:

Radiation pressure acceleration (RPA) and target normal sheath acceleration (TNSA) are the most important methods of Laser-accelerated proton beams (LAP) planning systems.LAP has inspired novel applications that can benefit from proton bunch properties different from conventionally accelerated proton beams. The secondary neutron and photon produced in the collision of protons with beamline components are of the important concern in proton therapy. Various published Monte Carlo researches evaluated the beamline and shielding considerations for TNSA method, but there is no studies directly address secondary neutron and photon production from RPA method in LAP. The purpose of this study is to calculate the flux distribution of neutron and photon secondary radiations on the first area ofLAP and to determine the optimize thickness and radius of the energyselector in a LAP planning system based on RPA method. Also, we present the Monte Carlo calculations to determine the appropriate beam pipe for shielding a LAP planning system. The GEANT4 Monte Carlo toolkit has been used to simulate a secondary radiation production in LAP. A section of new multifunctional LAP beamlinehas been proposed, based on the pulsed power solenoid scheme as a GEANT4 toolkit. The results show that the energy selector is the most important source of neutron and photon secondary particles in LAP beamline. According to the calculations, the pure Tungsten energy selector not be the proper case, and using of Tungsten+Polyethylene or Tungsten+Graphitecomposite selectors will reduce the production of neutron and photon intensities by approximately ~10% and ~25%, respectively. Also the optimal radiuses of energy selectors were found to be ~4 cm and ~6 cm for a 3 degree and 5 degree proton deviation angles, respectively.

Keywords: neutron, photon, flux distribution, energy selector, GEANT4 toolkit

Procedia PDF Downloads 103

Authors: Rishabh Hans, Saksham Sharma

Abstract:

Drying of a sessile droplet imbibed with colloidal solution is a complex process in many aspects. Till now, most of the work revolves around; conditions for buckling onset, post-buckling effects, nature of change of droplet shape etc. In this work, we are determining the shape of daughter cavity (DC) formed during post-buckling onset, a less explored stage, and its relationship with experimental parameters. We have introduced solid angle as a special parameter that can quantify the shape of DC at any instant. It facilitates us to compare the shape while experimenting across different substrate types, droplet sizes and particle concentration. Furthermore, the angular location of ‘weak spot’ on the periphery of droplet, which marks the initiation of cavity growth, varies in different conditions. To solve this problem, we have evaluated the deflection angle of weak spots w.r.t. the vertical axis going through the middle of droplet. Subsequently, the solid angle subtended by DC is analyzed about that inclined axis. Finally, results of analysis allude that increasing colloidal concentration has inverse effect on the growth rate of cavity’s shape. Moreover, the cap radius of DC is observed lower for high PLR which makes the capillary pressure higher and thus tougher to expedite cavity formation relatively. This analysis can be helpful in further studies to relate the shape, deflection angle, growth rate of daughter cavity to the type of droplet crust formed in the end. Examining DC stage shall add another layer to nano-colloidal research which aims to influence many industrial applications like patterning, coatings, drug delivery, food processing etc.

Keywords: buckling of sessile droplets, daughter cavity, droplet evaporation, nanoporous shell formation, solid angle

Procedia PDF Downloads 270

Authors: Carolina Pereira Lobato Costa, Cristina Pascual-González, Monica Echeverry, Javier LLorca, Carlos Gonzáléz, Juan Pedro Fernández-Bláquez

Abstract:

Although the potential of PLA self-reinforced composites for bone applications, not much literature addresses optimal manufacturing conditions. In this regard, this paper describes the woven self-reinforced PLA composites manufacturing processes: the commingling of yarns, weaving, and hot pressing and characterizes the manufactured laminates. Different structures and properties can be achieved by varying the hot compaction process parameters (pressure, holding time, and temperature). The specimens manufactured were characterized in terms of thermal properties (DSC), microstructure (C-scan optical microscope and SEM), strength (tensile test), and biocompatibility (MTT assays). Considering the final device, 155 ℃ for 10 min at 2 MPa act as the more appropriate hot pressing parameters. The laminate produced with these conditions has few voids/porosity, a tensile strength of 30.39 ± 1.21 MPa, and a modulus of 4.09 ± 0.24 GPa. Subsequently to the tensile testing was possible to observe fiber pullout from the fracture surfaces, confirming that this material behaves as a composite. From the results, no single laminate can fulfill all the requirements, being necessary to compromise in function of the priority property. Further investigation is required to improve materials' mechanical performance. Subsequently, process parameters and materials configuration can be adjusted depending on the place and type of implant to suit its function.

Keywords: woven fabric, self-reinforced polymer composite, poly(lactic acid), biodegradable

Procedia PDF Downloads 196

Authors: Masahiro Takimoto

Abstract:

The present study explored how the metaphor awareness-raising approach affects the involvement of the right hemisphere in developing EFL learners’ knowledge regarding the different degrees of politeness embedded within different request expressions. The present study was motivated by theoretical considerations regarding the conceptual projection and the metaphorical idea of politeness is distance, as proposed; this study applied these considerations to develop Japanese learners’ knowledge regarding the different politeness degrees and to explore the connection between the metaphorical concept projection and right-hemisphere dominance. Japanese EFL learners do not know certain language strategies (e.g., English requests can be mitigated with biclausal downgraders, including the if-clause with past-tense modal verbs) and have difficulty adjusting the politeness degrees attached to request expressions according to situations. The present study used a pre/post-test design to reaffirm the efficacy of the cognitive technique and its connection to right-hemisphere involvement by mouth asymmetry technique. Mouth asymmetry measurement has been utilized because speech articulation, normally controlled mainly by one side of the brain, causes muscles on the opposite side of the mouth to move more during speech production. The present research did not administer the delayed post-test because it emphasized determining whether metaphor awareness-raising approaches for developing EFL learners’ pragmatic proficiency entailed right-hemisphere activation. Each test contained an acceptability judgment test (AJT) along with a speaking test in the post-test. The study results show that the metaphor awareness-raising group performed significantly better than the control group with regard to acceptability judgment and speaking tests post-test. These data revealed that the metaphor awareness-raising approach could promote L2 learning because it aided input enhancement and concept projection; through these aspects, the participants were able to comprehend an abstract concept: the degree of politeness in terms of the spatial concept of distance. Accordingly, the proximal-distal metaphor enabled the study participants to connect the newly spatio-visualized concept of distance to the different politeness degrees attached to different request expressions; furthermore, they could recall them with the left side of the mouth being wider than the right. This supported certain findings from previous studies that indicated the possible involvement of the brain's right hemisphere in metaphor processing.

Keywords: metaphor awareness-raising, right hemisphere, L2 politeness, mouth asymmetry

Procedia PDF Downloads 155

Authors: Riccardo Houngbegnon, Loic Chrislin Nguedjio, Valery Doko, José Xavier, Miran Merhar, Rostand Moutou Pitti

Abstract:

Against a backdrop of heightened awareness of environmental impact and the reduction of space debris, the use of sustainable materials for mobility applications is emerging as a promising solution to minimize the environmental footprint of our technologies. Among recent innovative developments in the use of wood, the Japanese species Magnolia obovata attracted particular interest when it was used in the design of the first wooden satellite launched in November 2024. The aim of this project is to explore new species that could replace M. obovata in a mobile context. Khaya ivorensis, a tropical African species, was selected and compared to M. obovata in terms of resistance to cracking, a key criterion in the durability of mobility infrastructures. Prior to the cracking tests, K. ivorensis and M. obovata were characterized to determine their basic mechanical properties. The results presented here relate to this characterization phase, in particular the four-point bending, compression and BING tests, which provided us with strengths and moduli. These results were compared with those found in the literature, which allowed us to observe a number of differences. CHARPY resilience tests were also performed and compare to critical energy release rate in order to estimate the ability of the two species to absorb energy, particularly following impacts and various shocks.

Keywords: energy release rate, Khaya ivorensis, magnolia obovata, wood for mobility

Procedia PDF Downloads 7

Authors: Abhishek Kumar Gupta

Abstract:

Atomistic Molecular Dynamics (MD) Simulations have been performed to study the effect of monovalent salt i.e. NaCl concentration (Cs) and chain degree of neutralization (f) on the structure and dynamics of anionic poly(methacrylic acid) (PMA) in dilute aqueous solutions. In the present study, the attention is to unveil the conformational structure, hydrogen-bonding, local polyion-counterion structure, h-bond dynamics, chain dynamics and thermodynamic enthalpy of solvation of a-PMA in dilute aqueous solutions as a function of salt concentration, Cs and f. The results have revealed that at low salt concentration, the conformational radius of gyration (Rg) increases and then decreases reaching a maximum in agreement with the reported light scattering experimental results. The Rg at f = 1 shows a continual decrease and acquire a plateau value at higher salt concentration in agreement with results obtained by light scattering experiments. The radial distribution functions between PMA, salt and water atoms has been computed with respect to atom and centre-of-mass to understand the intermolecular structure in detail. The results pertaining to PMA chain conformations and hydrogen bond autocorrelation function showcasing the h-bond dynamics will be presented. The results pertaining to chain dynamics will be presented. The results pertaining to counterion condensation on the PMA chain shows greater condensation of Na+ ions on to the carboxylate ions with increase in salt concentration. Moreover, the solvation enthalpy of the system as a function of salt concentration will be presented.

Keywords: conformations, molecular dynamics simulations, NaCl concentration, radial distribution functions

Procedia PDF Downloads 115

Authors: Panyawutthi Rimdusit, Krittapas Charoensuk, Sarawut Rimdusit

Abstract:

A biobased toughening filler for polylactic acid (PLA) based on natural rubber is developed in this work. Deproteinized natural rubber (DPNR) was modified by grafting polymerization with methyl methacrylate monomer (MMA) and further crosslinked by e-beam irradiation and spray drying process to achieve ultrafine full vulcanized powdered natural rubber grafted with polymethylmethacrylate (UFPNRg-PMMA) to solves in the challenges of incompatibility between natural rubber and PLA. Intriguingly, UFPNR-g-PMMA revealed outstanding and unique properties with minimal particle aggregation. The average particle size of rubber powder obtained from UFPNR-g-PMMA at PMMA grafting content of 20 phr reduced to 3.3±1.2 µm, compared to that of neat UFPNR of 5.3±2.3 µm which also showed partial particle aggregation. It is also found that the impact strength of the filled PLA was enhanced to 33.4±5.6 kJ/m2 at PLA/UFPNR-gPMMA 20 wt% compared to neat PLA of 9.6±3 kJ/m2. The thermal degradation temperature of the PLA composites was enhanced with increasing UFPNR-g-PMMA content without affecting the glass transition temperature of the composites. The fracture surface of PLA/ UFPNR-g-PMMA suggested internal cavitation and crazes are the main effects of rubber toughening PLA with substantial interfacial interaction between the filler and the matrix.

Keywords: natural rubber, ultrafine fully vulcanized powder rubber, polylactic acid, polymer composites

Procedia PDF Downloads 11

Authors: Xi Quan Cheng, Yan Chao Xu, Xu Jiang, Lu Shao, Cher Hon Lau

Abstract:

A hydrophilic thin-film-composite (TFC) nanofiltration (NF) membrane has been developed through the interfacial polymerization (IP) of amino-functional polyethylene glycol (PEG) and trimesoyl chloride. The selective layer is formed on a polyethersulfone (PES) support that is characterized using FTIR, XPS and SEM, and is dependent on monomer immersion duration, and the concentration of monomers and additives. The higher hydrophilicity alongside the larger pore size of the PEG-based selective layer is the key to a high water flux of 66.0 L m-2 h-1 at 5.0 bar. With mean pore radius of 0.42 nm and narrow pore size distribution, the MgSO4 rejections of the PEG based PA TFC NF membranes can reach up to 80.2 %. The hydrophilic PEG based membranes shows positive charged since the isoelectric points range from pH=8.9 to pH=9.1 and the rejection rates for different salts of the novel membranes are in the order of R(MgCl2)>R(MgSO4)>R(NaCl)>R(Na2SO4). The pore sizes and water permeability of these membranes are tailored by varying the molecular weight and molecular architecture of amino-functional PEG. Due to the unique structure of the selective layer of the PEG based membranes consisting of saturated aliphatic construction unit (CH2-CH2-O), the membranes demonstrate dual resistance to fouling and chlorine. The membranes maintain good salt rejections and high water flux of PEG based membranes after treatment by 2000 ppm NaClO for 24 hours. Interestingly, the PEG based membranes exhibit excellent fouling resistance with a water flux recovery of 90.2 % using BSA as a model molecule. More importantly, the hydrophilic PEG based NF membranes have been exploited to separate several water soluble antibiotics (such as tobramycin, an aminoglycoside antibiotic applied in the treatment of various types of bacterial infections), showing excellent performance in concentration or removal of antibioics.

Keywords: nanofiltration, antibiotic separation, hydrophilic membrane, high flux

Procedia PDF Downloads 317