Search results for: whey powder

Authors: Behnam Mahdiyan Nasl

Abstract:

In a lab-scale research, the effects of feeding whey into the biogas system and how to solve the probable problems arising were analysed. In the study a semi-continuous glass reactor, having a total capacity of 13 liters and having a working capacity of 10 liters, was placed in an incubator, and the temperature was tried to be held at 38 °C. At first, the reactor was operated by adding 5 liters of animal manure and water with a ratio of 1/1. By passing time, the production rate of the gas reduced intensively that on the fourth day there was no production of gas and the system stopped working. In this condition, the pH was adjusted and by adding NaOH, it was increased from 5.4 to 7. On 48th day, the first gas measurement was done and an amount of 12.07 % of CH₄ was detected. After making buffer in the ambient, the number of bacteria existing in the cattle’s manure and contributing to the gas production was thought to be not adequate, and up to 20 % of its volume 2 liters of mud was added to the reactor. 7 days after adding the anaerobic mud, second gas measurement was carried out, and biogas including 43 % CH₄ was obtained. From the 61st day of the study, the cheese whey with the animal manure was started to be added with an amount of 40 mL per day. However, by passing time, the raising of the microorganisms existed in the whey (especially Ni and Co), the percent of methane in the biogas decreased. In fact, 2 weeks after adding PAS, the gas measurement was done and 36,97 % CH₄ was detected. 0,06 mL Ni-Co (to gain a concentration of 0.05 mg/L in the reactor’s mixture) solution was added to the system for 15 days. To find out the effect of the solution on archaea, 7 days after stopping addition of the solution, methane gas was found to have a 9,03 % increase and reach 46 %. Lastly, the effects of adding molasses to the reactor were investigated. The effects of its activity on the bacteria was analysed by adding 4 grams of it to the system. After adding molasses in 10 days, according to the last measurement, the amount of methane gas reached up to 49%.

Keywords: biogas, cheese whey, cattle manure, energy

Procedia PDF Downloads 305

Authors: Todor N. Penchev, Dimitar N. Karastoianov, Stanislav D. Gyoshev

Abstract:

For compacting of iron powder are used hydraulic presses and high velocity hammers. In this paper are presented initial research on application of an innovative powder compacting method, which uses a hammer working with controlled impact. The results show that by this method achieves the reduction of rebounds and improve efficiency of impact, compared with a high-speed compacting. Depending on the power of the engine (industrial rocket engine), this effect may be amplified to such an extent as to obtain a impact without rebound (sticking impact) and in long-time action of the impact force.

Keywords: powder metallurgy, impact, iron powder compacting, rocket engine

Procedia PDF Downloads 497

Authors: Muhammad Arif Mahmood, Andrei C. Popescu, Mihai Oane, Diana Chioibascu, Carmen Ristoscu, Ion N. Mihailescu

Abstract:

Powder flow and temperature distributions are recognized as influencing factors during laser melting deposition (LMD) process, that not only affect the consolidation rate but also characteristics of the deposited layers. Herewith, two simplified analytical models will be presented to simulate the powder flow with the inclusion of powder particles size distribution in Gaussian form, under three powder jet nozzles, and temperature analyses during LMD process. The output of the 1st model will serve as the input in the 2nd model. The models will be validated with experimental data, i.e., weight measurement method for powder particles distribution and infrared imaging for temperature analyses. This study will increase the cost-efficiency of the LMD process by adjustment of the operating parameters for reaching optimal powder debit and energy. This research has received funds under the Marie Sklodowska-Curie grant agreement No. 764935, from the European Union’s Horizon 2020 research and innovation program.

Keywords: laser additive manufacturing, powder particles size distribution in Gaussian form, powder stream distribution, temperature analyses

Procedia PDF Downloads 113

Authors: Hyeonuk Shin, Hun Song, Yongsik Chu, Jongkyu Lee, Dongcheon Park

Abstract:

Although much current research has been devoted to reusing concrete in the form of recycled aggregate, insufficient attention has been given to researching the utilization of waste concrete powder, which constitutes 20 % or more of waste concrete and therefore the majority of waste cementitious powder is currently being discarded or buried in landfills. This study consists of foundational research for the purpose of reusing waste cementitious powder in the form of recycled cement that can answer the need for low carbon green growth. Progressing beyond the conventional practice of using the waste cementitious powder as inert filler material, this study contributes to the aim of manufacturing high value added materials that exploits the chemical properties of the waste cementitious powder, by presenting a pre-treatment method for the material and an optimal method of proportioning the mix of materials to develop a low carbon type of recycled cement.

Keywords: Low carbon type cement, Waste cementitious powder, Waste recycling

Procedia PDF Downloads 431

Authors: I. Graur, V. Bria, C. Muntenita

Abstract:

Recent ecological interests have resulted in scientific concerns regarding natural-organic powder composites. Because natural-organic powders are cheap and biodegradable, green composites represent a substantial contribution in polymer science area. The aim of this study is to point out the effect of natural-organic powder resulting from the grinding of pine needles used as a modifying agent for Epiphen epoxy resin and is focused on friction coefficient behavior. A pin-on-disc setup is used for friction coefficient experiments. Epiphen epoxy resin was used with the different ratio of organic powder from the grinding of pine needles. Because of the challenges of natural organic powder, more and more companies are looking at organic composite materials.

Keywords: epoxy, friction coefficient, organic powder, pine needles

Procedia PDF Downloads 145

Authors: Nassier A. Nassir, Robert Birch, Zhongwei Guan

Abstract:

The aim of this study is to investigate the fundamental science/technology related to novel S-glass fiber reinforced polyether- ketone-ketone (GF/PEKK) composites and to gain insight into bonding strength and failure mechanisms. Different manufacturing techniques to make this high-temperature pre-impregnated composite (prepreg) were conducted i.e. mechanical deposition, electrostatic powder deposition, and dry powder prepregging techniques. Generally, the results of this investigation showed that it was difficult to control the distribution of the resin powder evenly on the both sides of the fibers within a specific percentage. Most successful approach was by using a dry powder prepregging where the fibers were coated evenly with an adhesive that served as a temporary binder to hold the resin powder in place onto the glass fiber fabric.

Keywords: sry powder technique, PEKK, S-glass, thermoplastic prepreg

Procedia PDF Downloads 186

Authors: Sergejs Kolesovs, Pavels Semjonovs

Abstract:

Whey and dairy wastewaters if disposed in the environment without proper treatment, cause serious environmental risks contributing to overall and particular environmental pollution and climate change. Biological treatment of wastewater is considered to be most eco-friendly approach, as compared to the chemical treatment methods. Research shows, that dairy wastewater can potentially be remediated by use of microalgae thussignificantly reducing the content of carbohydrates, P, N, K and other pollutants. Moreover, it has been shown, that use of dairy wastewaters results in higher microalgae biomass production. In recent decades microalgal biomass has entailed a big interest for its potential applications in pharmaceuticals, biomedicine, health supplementation, cosmetics, animal feed, plant protection, bioremediation and biofuels. It was shown, that lipids productivity on whey and dairy wastewater is higher as compared with standard cultivation media and occurred without the necessity of inducing specific stress conditions such as N starvation. Moreover, microalgae biomass production as usually associated with high production costs may benefit from perspective of both reasons – enhanced microalgae biomass or target substances productivity on cheap growth substrate and effective management of whey and dairy wastewaters, which issignificant for decrease of total production costs in both processes. Obviously, it became especially important when large volume and low cost industrial microalgal biomass production is anticipated for further use in agriculture of crops as plant growth stimulants, biopesticides soil fertilisers or remediating solutions. Environmental load of dairy wastewaters can be significantly decreased when microalgae are grown in coculture with other microorganisms. This enhances the utilisation of lactose, which is main C source in whey and dairy wastewaters when it is not metabolised easily by most microalgal species chosen. Our study showsthat certain microalgae strains can be used in treatment of residual sugars containing industrial wastewaters and decrease of their concentration thus approving that further extensive research on dairy wastewaters pre-treatment optionsfor effective cultivation of microalgae, carbon uptake and metabolism, strain selection and choice of coculture candidates is needed for further optimisation of the process.

Keywords: microalgae, whey, dairy wastewaters, sustainability, plant biostimulants

Procedia PDF Downloads 70

Authors: Siti Noor Suzila Maqsood-Ul-Haque, Ummi Kalthum Ibrahim, Norekanadirah Abdul Rahman

Abstract:

Banana are rich in vitamins, potassium and carbohydrate.The objective for this research work is to produce banana milk powder that can help children that suffers from constipation. Two types of the most common dryers used for this purpose are the spray and freeze dryer. The effects of the type of dryers, pump feed speed in the spray dryer and the ratio proportion of the banana milk powder were investigated in the study. The result indicate that increasing proportion ratio of the banana milk powder produce lower yield of the powder.From the result it is also concluded that speed 2 is more suitable in the production of the banana milk powder since the value of the moisture content is lower.

Keywords: freeze dryer, spray dryer, moisture content, dissolution, banana, milk

Procedia PDF Downloads 467

Authors: Talah Aissa

Abstract:

This paper reports an experimental study of the influence of marble powder used as a partial substitute for Portland cement (PC) on the mechanical properties and durability of high-performance concretes. The analysis of the experimental results on concrete at 15% content of marble powder with a fineness modulus of 11500 cm2/g, in a chloride environment, showed that it contributes positively to the perfection of its mechanical characteristics, its durability with respect to migration of chloride ions and oxygen permeability. On the basis of the experiments performed, it can be concluded that the marble powder is suitable for formulation of high performance concretes (HPC) and their properties are significantly better compared to the reference concrete (RC).

Keywords: marble powder, durability, concrete, cement

Procedia PDF Downloads 264

Authors: Eitedal Daoud, Reda M.Daoud, Khaled Abdel-Wahhab, Maha M.Saber, Lobna Saber

Abstract:

Background: Cis-platin is a widely used chemotherapeutic drug to treat many malignant disorders including head and neck malignancies. Oto-nephrotxicity is an important and dose - limiting side effect of cis - platin therapy. Nowadays, more attention had been paid to oto-toxicity caused with cis-platin. Aim of the Work: This study was designed to investigate the potential protective effect of Whey protein (WP) against cis-platin induced ototoxicity compared to the effect of N-acetylcysteine (NAC) in rats. Methodology: Male albino rats were randomly divided into 6 groups: untreated rats (control), rats orally treated with whey protein (1g/kg b.w/day) for seven executive days, rats treated orally with N-acetylcysteine (500 mg/kgb.w /day) for seven executive days, rates intoxicated intraperitoneal (ip) with cis- platin (10 mg/kgb.w. once), rats treated with whey protein (1g/kgb.w./day) for seven executive days) followed by one injection (ip) of cis-platin(10 mg/kg b.w.) one hour after the last oral administration of whey protein, rats treated with N- acetylcysteine (for seven executive days followed by one injection (ip) of cis-platin (10 mg/kgb.w) one hour after the last oral administration of N-acetylcysteine. The organ of Corti, the stria vascularis and spiral ganglia were visualized by light microscopy at different magnifications. Results: Cis-platin intoxicated animals showed a significant decrease in serum level of total antioxidant capacity (TAC),with inhibition in the activity of serum glutathione-s transferase(GST) and paraoxonnase-1 (PON-1) in comparison with control. Group treated with either NAC or WP with cis-platin showed significant elevation in the activity of both GST & PON-1 with increased serum level of TAC when compared with cis-platin intoxicated rats. Animals treated with NAC or WP with cis-platin compared to those treated with cis-platin alone showed marked degree of improvement towards control rats as there was significant drop in the serum level of cortecosterone, nitric oxide (NO), and melandialdehyde (MDA).Histopathologic, in NAC pretreated group there was no changes in stria vascularis or spiral ganglia. In group pretreated with WP, there was no histopathologic alteration detected in the organ of Corti and Reissers membrane but oedema and haemorrhage were founded in the stria vascularis in small focal manner. Conclusion: Our finding showed that Whey protein is a natural dietary supplement product proved its ability of protection of anti-oxidant system and the cochlea against cis-platin induced ototoxicity.

Keywords: anti-oxidant, cis-platin, N-acetylcysteine, ototoxicity, whey protein

Procedia PDF Downloads 499

Authors: Chanunya Fahwan, Supat Chaiyakul

Abstract:

A lactose-free diet is imperative for those with lactose intolerance and experiencing milk intolerance. This entails eliminating milk-based products, which may result in dietary and nutritional challenges and the main problems of Lactose hydrolyzed milk powder during production were the adhesion in the drying chamber and low-yield and low-quality powder. The use of lactose-free milk to produce lactose-free milk powder was studied here. Development of two milk powder formulas from cow's milk and lactose-free cow's milk by using a substitute for maltodextrin, Polydextrose (PDX), Resistant Starch (RS), Cellobiose (CB), and Resistant Maltodextrin (RMD) to improve quality and reduce the glycemic index from maltodextrin, which are carriers that were used in industry at three experimental levels 10%, 15% and 20% the properties of milk powder were studied such as color, moisture content, percentage yield (%yield) and solubility index. The experiment revealed that prebiotic carriers could replace maltodextrin and improve quality, such as solubility and percentage yield, and enriched nutrients, such as dietary fiber. CB, RMD, and PDX are three possible carriers, which are applied to both regular cow's milk formula and lactose-free cow milk.

Keywords: lactose-free milk powder, prebiotic carrier, co-particle, glycemic index

Procedia PDF Downloads 36

Authors: Xia Chen, Hua-Quan Yang, Shi-Hua Zhou

Abstract:

Alkali-active sandstone aggregate was ground by vertical and ball mill into particles with residue over 45 μm less than 12%, and investigations have been launched on particles distribution and characterization of ground sandstone powder, fluidity, heat of hydration, strength as well as hydration products morphology of pastes with incorporation of ground sandstone powder. Results indicated that ground alkali-active sandstone powder with residue over 45 μm less than 8% was easily obtainable, and specific surface area was more sensitive to characterize its fineness with extension of grinding length. Incorporation of sandstone powder resulted in higher water demand and lower strength, advanced hydration of C₃A and C₂S within 3days and refined pore structure. Based on its manufacturing, characteristics and influence on properties of pastes, it was concluded that sandstone powder was a good selection for use in concrete as mineral admixture.

Keywords: concrete, mineral admixture, hydration, structure

Procedia PDF Downloads 308

Authors: Chajira Garrote, Laura Arango, Lourdes Merino

Abstract:

This research explains how to obtain nutritious powder from a variety of ripe mango peels Hilacha (Mangifera indica L.) to use it as a food additive. Also, this study intends to use efficiently the by-products resulting from the operations of mango pulp manufacturing process by processing companies with the aim of giving them an added value. The physical and chemical characteristics of the mango peels and the benefits that may help humans, were studied. Unit operations are explained for the processing of mango peels and the production of nutritive powder as a food additive. Emphasis is placed on the preliminary operations applied to the raw material and on the drying method, which is very important in this project to obtain the suitable characteristics of the nutritive powder. Once the powder was obtained, it was subjected to laboratory tests to determine its functional properties: water retention capacity (WRC) and oil retention capacity (ORC), also a sensory analysis for the powder was performed to determine the product profile. The nutritive powder from the ripe mango peels reported excellent WRC and ORC values: 7.236 g of water / g B.S. and 1.796 g water / g B.S. respectively and the sensory analysis defined a complete profile of color, odor and texture of the nutritive powder, which is suitable to use it in the food industry.

Keywords: mango, peel, powder, nutritive, functional properties, sensory analysis

Procedia PDF Downloads 329

Authors: Sanjaykumar R. Patel, Parth R. Kayastha

Abstract:

α-lactose monohydrate is widely used in the pharmaceutical industries as an inactive substance that acts as a vehicle or a medium for a drug or other active substance. It is a byproduct of dairy industries, and the recovery of lactose from whey not only boosts the improvement of the economics of whey utilization but also causes a reduction in pollution as lactose recovery can reduce the BOD of whey by more than 80%. In the present study, levels of process parameters were kept as initial lactose concentration (30-50% w/w), sonication amplitude (20-40%), sonication time (2-6 hours), and crystallization temperature (10-20 ^oC) for the recovery of lactose in ultrasound assisted cooling crystallization. In comparison with cooling crystallization, the use of ultrasound enhanced the lactose recovery by 39.17% (w/w). The parameters were optimized for the lactose recovery using Taguchi Method. The optimum conditions found were initial lactose concentration at level 3 (50% w/w), amplitude of sonication at level 2 (40%), the sonication time at level 3 (6 hours), and crystallization temperature at level 1 (10 °C). The maximum recovery was found to be 85.85% at the optimum conditions. Sonication time and the initial lactose concentration were found to be significant parameters for the lactose recovery.

Keywords: crystallization, lactose, Taguchi method, ultrasound

Procedia PDF Downloads 182

Authors: Farhat Rashid

Abstract:

A study was conducted at the Institute of Food Science and Nutrition, University of Sargodha, Sargodha, Pakistan, to evaluate the effect of different concentration of Aloe vera (Aloe barbadensis Mill.) powder on physicochemical and sensory properties of orange marmalade. All treatments (0, 2, 4 6, 8 and 10% Aloe vera powder) were analyzed for titratable acidity, TSS, pH, moisture, fat, fiber and protein contents. The data indicated gradual increase in titratable acidity (0.08 to 0.18%), moisture (0.23 to 0.48%), protein (0.09 to 0.40%) and fiber (0.12 to 1.03%) among all treatments with increasing concentration of Aloe vera powder. However, a decreasing trend in pH (3.81 to 2.74), TSS (68 to 56 °Brix) and fat content (1.1 to 0.08%) was noticed with gradual increase in concentration of Aloe vera powder in orange marmalade. Sensory attributes like color, taste, texture, flavor and overall acceptability were found acceptable among all treatments but T1 (2% Aloe vera powder) was liked most and T5 (10% Aloe vera powder) was least appealing to the judges. It is concluded from present study that the addition of different concentrations of Aloe vera powder in orange marmalade significantly affected the physicochemical and sensory properties of marmalade.

Keywords: orange marmalade, Aloe vera, Aloe barbadensis mill, physicochemical, characteristics, organoleptic properties, Pakistan, treatments, significance

Procedia PDF Downloads 334

Authors: Vatsal Patel, Niraj Shah

Abstract:

This paper presents the results of a laboratory study on the properties of binary blended High Performance cementitious systems containing blends of ordinary Portland cement (OPC), Porcelain Powder or Marble Powder blend proportions of 100:00, 95:05, 90:10, 85:15, 80:20 for OPC: Porcelain Powder/Marble Powder. Studies on the Engineering Properties of the cementitious concrete, namely compressive strength, flexural strength, sorptivity, rapid chloride penetration test and accelerated corrosion test have been performed and those of OPC concrete. The results show that the inclusion of Porcelain powder or Marble Powder as binary blended cement alters to a great degree the properties of the binder as well as the resulting concrete. In addition, the results show that the Porcelain powder with 85:15 proportions and Marble powder with 90:10 proportions as binary systems to produce high-performance concrete could potentially be used in the concrete construction industry particular in lowering down the volume of OPC used and lowering emission of CO2 produces during manufacturing of cement.

Keywords: accelerated corrosion, binary blended cementitious system, rapid chloride penetration, sorptivity

Procedia PDF Downloads 370

Authors: Monika R. Bhoi, R. F. Sutar, Bhaumik B. Patel

Abstract:

The objective of this research paper is to obtain the premium quality of cinnamon bark powder through cryogenic grinding technology. The effect of grinding temperature (0, -20, -40, -60, -80 and -100˚C), feed rate (8, 9 and 10 kg/h), and sieve size (0.8, 1.0 and 1.5 mm) were evaluated with respect to grinding time, volatile oil content, particle size, energy consumption, and liquid nitrogen consumption. Cryogenic grinding process parameters were optimized to obtain premium quality cinnamon bark powder was carried out using three factorial completely randomized design. The optimization revealed that grinding of cinnamon bark at -80⁰C temperature using 0.8 mm sieve size and 10 kg/h feed rate resulted in premium quality cinnamon bark powder containing volatile oil 3.01%. In addition, volatile oil retention in cryogenically ground powder was 88.23%, whereas control (ambient grinding) had 33.11%. Storage study of premium quality cryogenically ground powder was carried out under accelerated storage conditions (38˚C & 90% R.H). Accelerated storage of cryoground powder was found to be advantageous over the conventional ground for extended storage of the ground cinnamon powder with retention of its nutritional quality. Hence, grinding of spices at optimally low cryogenic temperature is a promising technology for the production of its premium quality powder economically.

Keywords: cinnamon bark, cryogenic grinding, feed rate, volatile oil

Procedia PDF Downloads 139

Authors: Mohammad Goli, Akram Sharifi, Mohammad Yousefi Jozdani, Seyed Ali Mortazavi

Abstract:

An industrial spray dryer was used, and the effects of atomizer speed on the physicochemical properties of milk powder, the textural and sensory characteristics of white cheese made from this milk powder, were evaluated. For this purpose, whole milk was converted into powder by using three different speeds (10,000, 11,000, and 12,000 rpm). Results showed that with increasing atomizer speed in the spray dryer, the average size of casein micelle is significantly decreased (p < 0.05), whereas no significant effect is observed on the chemical properties of milk powder. White cheese characteristics indicated that with increasing atomizer speed, texture parameters, such as hardness, mastication, and gumminess, were significantly reduced (p < 0.05). Sensory evaluation also revealed that cheese samples prepared with dried milk produced at 12,000 rpm were highly accepted by panelists. Overall, the findings suggested that 12,000 rpm is the optimal atomizer speed for milk powder production.

Keywords: spray drying, powder technology, atomizer speed, particle size, white cheese physical properties

Procedia PDF Downloads 444

Authors: Majid Javanmard

Abstract:

In this study, the effects of coating with whey protein concentrate (7.5% w/v) alone and/or in combination with rice bran oil (0.2, 0.4, 0.6 g in 100 ml coating solution) and Zataria multiflora extract (1 and 2 μL in 100 ml coating solution) on the quality attributes and egg shelf life were carefully observed and analyzed. Weight loss, Haugh index, yolk index, pH, air cell depth, shell strength and the impact of this coating on the microbial load of the eggs surface were studied at the end of each week (during the 4 weeks of storage in a room environment temperature and humidity). After 4 weeks of storage, it was observed that the weight loss in all of the treated eggs with whey protein concentrate and 0.2 gr of rice bran oil (experimental group) was significantly lower than that of the control group(P < 0/05). With regard to Haugh index and yolk index, egg shelf life increased about 4 weeks compared with the control samples. Haugh Index changes revealed that the coated samples remained at grade A after 3 weeks of storage, while the control samples were relegated from grade AA to B after one week. Haugh and yolk Indices in all coated eggs were more than those of the control group. In the coated groups, Haugh and yolk indices of the coated samples with whey protein concentrate and 0.2 g rice bran oil and with whey protein concentrate and 0.2g of rice bran oil and 1 micro liter of Zataria multiflora extract were more than those of the other coated eggs and the control group eggs. PH values of the control group were higher than those of the coated groups during the storage of the eggs. The shell strength of the coated group was more than that of the control group (uncoated) and in coated samples, whey protein concentrate and 0.2 gr of rice bran oil coated samples had high shell strength. In the other treatments, no significant differences were observed. The depth of the air cell of the coated groups was determined to be less than that of the control group during the storage period. The minimum inhibitory concentration was 1 μL of Zataria multiflora extract. The results showed that 1 μL concentration of Zataria multiflora extract reduces the microbial load of the egg shell surface to 87% and 2 μL reduced total bacterial load to zero. In sensory evaluation, from evaluator point of view, the coated eggs had more overall acceptance than the uncoated group (control), and in the treatment group coated eggs, those containing a low percentage of rice bran oil had higher overall acceptability. In conclusion, coating as a practical and cost effective method can maintain the quality parameters of eggs and lead to durability of supply conditions in addition to the product marketability.

Keywords: edible coating, chicken egg, whey protein concentrate, rice bran oil, Zataria multiflora extract, shelf life

Procedia PDF Downloads 270

Authors: D. P. Rahardja, M. Rahman Hakim, V. Sri Lestari

Abstract:

An experiment was conducted to elucidate the effects of turmeric powder supplementation on egg production performance of old laying hens (104 weeks of age). There were 40 hens of Hysex Brown strain used in the study. They were caged individually, and randomly divided into 4 treatment groups of diet containing 0 (control), 1, 2 and 4 % oven dried turmeric powder for 3 periods of 4 weeks; Egg production (% hen day) and feed intake of the 4 treatment groups at the commencement of the experiment were not significantly different. In addition to egg production performance (%HD and egg weight), feed and water intakes were measured daily. The results indicated that feed intakes of the hen were significantly lowered when 4% turmeric powder supplemented, while there were no significant changes in water intakes. Egg production (%HD) were significantly increased and maintained at a higher level by turmeric powder supplementation up to 4% compared with the control, while the weight of eggs were not significantly affected. The research markedly demonstrated that supplementation of turmeric powder up to 4% could improve and maintain egg production performance of the old laying hen.

Keywords: curcumin, feed and water intake, old laying hen, egg production

Procedia PDF Downloads 453

Authors: Mostafa Rezaee Saraji, Ali Keshavarz Panahi

Abstract:

In this work, the processing steps for producing alumina parts using powder injection molding (PIM) technique and nano-powder were investigated and the thermal conductivity and flexural strength of samples were determined as a function of sintering temperature and holding time. In the first step, the feedstock with 58 vol. % of alumina nano-powder with average particle size of 100nm was prepared using Extrumixing method to obtain appropriate homogeneity. This feedstock was injection molded into the two cavity mold with rectangular shape. After injection molding step, thermal and solvent debinding methods were used for debinding of molded samples and then these debinded samples were sintered in different sintering temperatures and holding times. From the results, it was found that the flexural strength and thermal conductivity of samples increased by increasing sintering temperature and holding time; in sintering temperature of 1600ºC and holding time of 5h, the flexural strength and thermal conductivity of sintered samples reached to maximum values of 488MPa and 40.8 W/mK, respectively.

Keywords: alumina nano-powder, thermal conductivity, flexural strength, powder injection molding

Procedia PDF Downloads 307

Authors: Munir Tasdemir

Abstract:

Polymer/clay composites have received great attention in the past three decades owing to their light weight coupled with significantly better mechanical and barrier properties than the corresponding neat polymer resins. An investigation was carried out on the effects of red mud powder size and ratio on the mechanical and thermal properties of polypropylene /red mud polymer composites. Red mud, in four different concentrations (0, 10, 20 and 30 wt %) and three different powder size (180, 63 and 38 micron) were added to PP to produce composites. The mechanical properties, including the elasticity modulus, tensile & yield strength, % elongation, hardness, Izod impact strength and the thermal properties including the melt flow index, heat deflection temperature and vicat softening point of the composites were investigated. The structures of the composites were investigated by scanning electron microscopy and compared to mechanical and thermal properties as a function of red mud powder content and size.

Keywords: polypropylene, powder, red mud, mechanical properties

Procedia PDF Downloads 303

Authors: Rim Zgueb, Noureddine Yacoubi

Abstract:

The objective of this study was to investigate the thermal property of magnesium oxychloride cement (MOC) using glass powder as a substitute. Glass powder by proportion 0%, 5%, 10%, 15% and 20% of cement’s weight was added to specimens. At the end of a drying time of 28 days, thermal properties, compressive strength and bulk density of samples were determined. Thermal property is measured by Photothermal Deflection Technique by comparing the experimental of normalized amplitude and the phase curves of the photothermal signal to the corresponding theoretical ones. The findings indicate that incorporation of glass powder decreases the thermal properties of MOC.

Keywords: magnesium oxychloride cement (MOC), phototharmal deflection technique, thermal properties, Ddensity

Procedia PDF Downloads 322

Authors: Kersch-Counet C., Fransen K. H. S., Broyd M., Nyakayiru J. D. O. A., Schoemaker M. H., Mallee L. F., Bovee-Oudenhoven I. M. J.

Abstract:

Background: Around one third of people, including athletes, suffer from feelings of gut discomfort. Fermentation of dairy is a process that has been associated with products that can improve gut health. However, insight in (potential) health benefits of most fermented foods is limited to chemical analyses and in-vitro models. Objective: The aim of this open-label, single-arm explorative trial was to investigate in a real life setting the effect of consumption of a fermented whey product for 3 weeks on self-perceived physical and mental wellbeing and digestive issues in 150 US recreational athletes (20-50 years of age) with self-reported gut complaints at enrolment. Methods: Participants living at the West-Coast of the US received for 3 weeks a daily powder of 15 g of BiotisTM Fermentis to be mixed in water using a supplied shaker. Weekly questionnaires were conducted by MMR research to study the effect on physical/mental health issues and self-perceived gut complaints. Non-parametric tests (e.g., Friedman test) were used to assess statistical differences over time while the Kruskal-Wallis and Wilcoxon signed-rank tests were used for sub-groups analysis. Results: Bloating, stress and anxiety were the top 3 issues of the US recreational athletes. Satisfaction of physical wellbeing increased significantly throughout the 3-weeks of fermented whey product consumption (p<0.0005). Combined digestive issues decreased significantly after 2- and 3-weeks of product consumption, with bloating showing a significant reduction (p<0.05). There was a trend that self-reported stress levels reduced after 3 weeks and participants said to significantly feel more active, energetic, and vital (p<0.05). Subgroup analysis showed that gender and habitual protein supplement consumption were associated with specific health issues and modulated the response to the fermented dairy product. Conclusion: Daily consumption of the fermented BiotisTM Fermentis product is associated with a reduction in self-perceived gastrointestinal symptoms and improved overall wellbeing and mood state in US recreational athletes. This large nutrition and health consumer study brings valuable insights in self-reported gut complaints of recreational athletes in the US and their response to a fermented dairy product. A controlled clinical trial in a targeted population is recommended to scientifically substantiate the product effect as observed in this explorative study.

Keywords: real-life study, digestive health, fermented whey, sports

Procedia PDF Downloads 220

Authors: Kar Lin Nyam, Phey Yee Lim

Abstract:

The aim of this study was to determine the antioxidant potential, nutritional composition, and functional properties of kenaf leaves powder. Besides, the effect of kenaf leaves powder in bread qualities, properties, and consumer acceptability were evaluated. Different formulations of bread fortified with 0%, 4% and 8% kenaf leaves powder, respectively were produced. Physical properties of bread, such as loaf volume, dough expansion, crumb colour, and bread texture, were determined. Nine points hedonic scale was utilized in sensory evaluation to determine the best formulation (the highest overall acceptability). Proximate composition, calcium content, and antioxidant properties were also determined for the best formulation. 4% leaves powder bread was the most preferred by the panelists followed by control bread, and the least preferred was being 8% leaves powder bread. 4% leaves powder bread had significantly higher value of DPPH radical scavenging capacity (8.05 mg TE/100g), total phenolic content (12.88 mg GAE/100g) and total flavonoid content (13.26 mg QE/100g) compared to control bread (1.38 mg TE/100g, 8.17 mg GAE/100g, and 8.77 mg QE/100g respectively). Besides, 4% leaves powder bread also showed higher in calcium content and total dietary fiber compared to control bread. Kenaf leaves powder is suitable to be used as a source of natural antioxidant for fortification and nutrient improver in bread.

Keywords: dietary fibre, calcium, total phenolic content, total flavonoid content

Procedia PDF Downloads 99

Authors: Shahram Naghizadeh Raeisi, Ali Alghooneh

Abstract:

The application of whey protein in drink industry to enhance the nutritional value of the products is important. Furthermore, the gelification of protein during thermal treatment and shelf life makes some limitations in its application. So, the main goal of this research is manufacturing of high concentrate whey protein orange drink with appropriate shelf life. In this way, whey protein was 5 to 30% hydrolyzed ( in 5 percent intervals at six stages), then thermal stability of samples with 10% concentration of protein was tested in acidic condition (T= 90 °C, pH=4.2, 5 minutes ) and neutral condition (T=120° C, pH:6.7, 20 minutes.) Furthermore, to study the shelf life of heat treated samples in 4 months at 4 and 24 °C, the time sweep rheological test were done. At neutral conditions, 5 to 20% hydrolyzed sample showed gelling during thermal treatment, whereas at acidic condition, was happened only in 5 to 10 percent hydrolyzed samples. This phenomenon could be related to the difference in hydrodynamic radius and zeta potential of samples with different level of hydrolyzation at acidic and neutral conditions. To study the gelification of heat resistant protein solutions during shelf life, for 4 months with 7 days intervals, the time sweep analysis were performed. Cross over was observed for all heat resistant neutral samples at both storage temperature, while in heat resistant acidic samples with degree of hydrolysis, 25 and 30 percentage at 4 and 20 °C, it was not seen. It could be concluded that the former sample was stable during heat treatment and 4 months storage, which made them a good choice for manufacturing high protein drinks. The Scheffe polynomial model and numerical optimization were employed for modeling and high protein orange drink formula optimization. Scheffe model significantly predicted the overal acceptance index (Pvalue<0.05) of sensorial analysis. The coefficient of determination (R2) of 0.94, the adjusted coefficient of determination (R2Adj) of 0.90, insignificance of the lack-of-fit test and F value of 64.21 showed the accuracy of the model. Moreover, the coefficient of variable (C.V) was 6.8% which suggested the replicability of the experimental data. The desirability function had been achieved to be 0.89, which indicates the high accuracy of optimization. The optimum formulation was found as following: Modified whey protein solution (65.30%), natural orange juice (33.50%), stevia sweetener (0.05%), orange peel oil (0.15%) and citric acid (1 %), respectively. Its worth mentioning that this study made an appropriate model for application of whey protein in drink industry without bitter flavor and gelification during heat treatment and shelf life.

Keywords: croos over, orange beverage, protein modification, optimization

Procedia PDF Downloads 43

Authors: Maya S. Rathod, Bahadur Singh Hathan

Abstract:

Mustard leaves are rich in folates, vitamin A, K and B-complex. Mustard greens are low in calories and fats and rich in dietary fiber. They are rich in potassium, manganese, iron, copper, calcium, magnesium and low in sodium. It is very rich in antioxidants and Phytonutrients. For the optimization of process variables (moisture content and mustard leave powder), the experiments were conducted according to central composite Face Centered Composite design of RSM. The mustard leaves powder was replaced with composite flour (a combination of rice, chickpea and corn in the ratio of 70:15:15). The extrudate was extruded in a twin screw extruder at a barrel temperature of 120°C. The independent variables were mustard leaves powder (2-10 %) and moisture content (12-20 %). Responses analyzed were bulk density, water solubility index, water absorption index, lateral expansion, hardness, antioxidant activity, total phenolic content and overall acceptability. The optimum conditions obtained were 7.19 g mustard leaves powder in 100 g premix having 16.8 % moisture content (w.b).

Keywords: extrusion, mustard leaves powder, optimization, response surface methodology

Procedia PDF Downloads 507

Authors: Vandana Bali, Manab B. Bera, Parmjit S. Panesar

Abstract:

Microbial production of antimicrobials as biopreservatives is the major area of focus nowadays due to increased interest of consumers towards natural and safe preservation of ready to eat food products. The agro-industrial byproduct based medium and optimized process conditions can contribute in economical production of bacteriocins. Keeping this in view, the present investigation was carried out on agro-industrial byproducts utilization for the production of bacteriocin using Enterococcus faecium BS13 isolated from local fermented food. Different agro-industrial byproduct based carbon sources (whey, potato starch liquor, kinnow peel, deoiledrice bran and molasses), nitrogen sources (soya okra, pea pod and corn steep liquor), metal ions and surfactants were tested for optimal bacteriocin production. The effect of various process parameters such as pH, temperature, inoculum level, agitation and time were also tested on bacteriocin production. The optimized medium containing whey, supplemented with 4%corn steep liquor and polysorbate-80 displayed maximum bacteriocin activity with 2% inoculum, at pH 6.5, temperature 40oC under shaking conditions (100 rpm).

Keywords: Bacteriocin, biopreservation, corn steep liquor, Enterococcus faecium, waste utilization, whey

Procedia PDF Downloads 212

Authors: Eyyüp Murat Karakurt, Yan Huang, Mehmet Kaya, Hüseyin Demirtaş, Alper İncesu

Abstract:

In this study, Ti-(x) Nb (at. %) master alloys (x:10, 20, and 30) were fabricated following a standard powder metallurgy route and were sintered at 1200 ˚C for 6h, under 300 MPa by powder metallurgy method. The effect of the Nb concentration in Ti matrix and porosity level was examined experimentally. For metallographic examination, the alloys were analysed by optical microscopy and energy dispersive spectrometry analysis. In addition, X-ray diffraction was performed on the alloys to determine which compound formed in the microstructure. The compression test was applied to the alloys to understand the mechanical behaviors of the alloys. According to Nb concentration in Ti matrix, the β phase increased. Also, porosity level played a crucial role on the mechanical performance of the alloys.

Keywords: Nb concentration, porosity level, powder metallurgy, The β phase

Procedia PDF Downloads 233

Authors: Amsar Maulana, Rafdea Syafitri, Topanal Gustiranda, Natasya Permatasari, Herviyanti

Abstract:

Coal as an alternative source of humic material that has the potential of 973.92 million tons (sub-bituminous amounted to 673.70 million tons) in West Sumatera. The purpose of this research was to study combination Urea and KCl with powder coal Sub-bituminous to increase nutrient content of Ultisols In Limau Manis Padang West Sumatera. The experiment was designed in Completely Randomized Design with 3 replications, those were T1) 0.5% (50g plot-1) of powder coal Sub-bituminous; T2) T1 and 125% (7.03g plot-1 ) of Urea recommendation; T3) T1 and 125% (5.85g plot-1) of KCl recommendation; T4) 1.0% (100g plot-1) of powder coal Sub-bituminous; T5) T4 and 125% (7.03g plot-1 ) of Urea recommendation; T6) T4 and 125% (5.85g plot-1) of KCl recommendation; T7) 1.5% (150g plot-1) of powder coal Sub-bituminous; T8) T7 and 125% (7.03g plot-1 ) of Urea recommendation; T9) T7 and 125% (5.85g plot-1) of KCl recommendation. The results showed that application 1.5% of powder coal Sub-bituminous and 125% of Urea recommendation could increase nutrient content of Ultisols such as pH by 0.33 unit, Organic – C by 2.03%, total – N by 0.31%, Available P by 14.16 ppm and CEC by 19.38 me 100g-1 after 2 weeks of incubation process.

Keywords: KCl, sub-bituminous, ultisols, urea

Procedia PDF Downloads 242