Search results for: physicochemical properties of amino acid

Authors: Omid Gholipoor Bashiri, Ghafur Mosavi, Aliasghar Behnamghader, Seyed Mahmood Rabiee

Abstract:

Objective: To determine the effect of selected bone graft on the compression properties of radial bone in rabbit. Design-Experimental in vivo study. Animals: A total of 45 adult male New Zealand white rabbits. Procedures: The rabbits were anesthetized and a one-cm-full thickness piece of radial bone was removed using oscillating saw in the all rabbit. The rabbits were divided into 5 groups on the basis of the material used to fill the bone defect: group 1: the paste of bone cement calcium phosphate; group II: the paste of calcium phosphate mixture with type I collagen; group III: tricalcium phosphate mixed with hydroxyapatite (TCP & HP) with 5% porosity; group IV: the same scaffold as group III with 10% porosity; and group V: the same scaffold as group III and IV with 20% porosity, with 9 rabbits in each group. Subsequently subdivided into 3 subgroups of 3 rabbits each. Results: There was a significant increase in compression properties of radial bone in the group II and V in 2nd and 3rd months as compared with groups I, III and IV. The mean endurable crack-strength in group II and V were slightly higher than that of normal radius (P<0.05). Conclusion and clinical relevance: Application of calcium phosphate paste with type I collagen and scaffold of tricalcium phosphate with hydroxyapatite having 20% porosity indicated to have positive effect in integral formation of qualitative callus at the site of fracture and early re-organization of callus to regain mechanical strength too.

Keywords: calcium phosphate, tricalcium phosphate, hydroxyapatite, radial bone, compressive properties, porosity, type i collagen, rabbit

Procedia PDF Downloads 439

Authors: Mohamed M. Ali, Adel Nofal, Amr Kandil, Mahmoud Agour

Abstract:

High phosphorus gray iron (HPGI) is used to connect the steel stub of an anode rod to a prebaked anode carbon block in the aluminium reduction cells. In this paper, a complete characterization for HPGI was done, includes studying the chemical composition of the HPGI collar, anodic voltage drop, collar temperature over 30 days anode life cycle, microstructure and mechanical properties. During anode life cycle, the carbon content in HPGI was lowed from 3.73 to 3.38%, and different changes in the anodic voltage drop at the stub- collar-anode connection were recorded. The collar temperature increases over the anode life cycle and reaches to 850°C in four weeks after anode changing. Significant changes in the HPGI microstructure were observed after 3 and 30 days from the anode changing. To simulate the actual operating conditions in the steel stub/collar/carbon anode connection, a bench-scale experimental set-up was designed and used for electrical resistance and resistivity respectively. The results showed the current HPGI properties needed to modify or producing new alloys with excellent electrical and mechanical properties. The steel stub and HPGI thermal expansion were measured and studied. Considerable permanent expansion was observed for the HPGI collar after the completion of the heating-cooling cycle.

Keywords: high phosphorus gray iron (HPGI), aluminium reduction cells, anodic voltage drop, microstructure, mechanical and electrical properties

Procedia PDF Downloads 440

Authors: A. Attaf, I. Bouhaf Kharkhachi

Abstract:

Hexagonal tin disulfide (SnS2) films were deposited by spray ultrasonic technique on glass substrates at different experimental conditions. The effect of deposition time (2, 4, 6, and 7 min) on different properties of SnS2 thin films was investigated by XRD and UV spectroscopy visible spectrum. X-ray diffraction study detected the preferential orientation growth of SnS2 compound having structure along (001) plane increased with the deposition time. The results of UV spectroscopy visible spectrum showed that films deposited at 4 min have high transmittance, up to 60%, in the visible region.

Keywords: structural and optical properties, tin sulfide, thin films, ultrasonic spray

Procedia PDF Downloads 457

Authors: Ravi Prasher

Abstract:

In nanostructured material thermal transport is dominated by contact resistance. Theoretical models describing thermal transport at interfaces assume perfectly flat surface whereas in reality surfaces can be rough with roughness ranging from sub-nanoscale dimension to micron scale. Here we introduce a model which includes both nanoscale contact mechanics and nanoscale heat transfer for rough nanoscale surfaces. This comprehensive model accounts for the effect of phonon acoustic mismatch, mechanical properties, chemical properties and randomness of the rough surface.

Keywords: adhesion and contact resistance, Kaptiza resistance of rough surfaces, nanoscale thermal transport

Procedia PDF Downloads 355

Authors: Ahmed El-Banbi

Abstract:

Several PVT models exist to represent how PVT properties are handled in sub-surface and surface engineering calculations for oil and gas production. The most commonly used models include black oil, modified black oil (MBO), and compositional models. These models are used in calculations that allow engineers to optimize and forecast well and reservoir performance (e.g., reservoir simulation calculations, material balance, nodal analysis, surface facilities, etc.). The choice of which model is dependent on fluid type and the production process (e.g., depletion, water injection, gas injection, etc.). Based on close to 2,000 reservoir fluid samples collected from different basins and locations, this paper presents some conclusions on the occurrence of reservoir fluids. It also reviews the common methods used to classify reservoir fluid types. Based on new criteria related to the production behavior of different fluids and economic considerations, an updated classification of reservoir fluid types is presented in the paper. Recommendations on the use of different PVT models to simulate the behavior of different reservoir fluid types are discussed. Each PVT model requirement is highlighted. Available methods for the calculation of PVT properties from each model are also discussed. Practical recommendations and tips on how to control the calculations to achieve the most accurate results are given.

Keywords: PVT models, fluid types, PVT properties, fluids classification

Procedia PDF Downloads 57

Authors: H. S. Assaedi, F. U. A. Shaikh, I. M. Low

Abstract:

Geopolymer composites reinforced with flax fabrics and nano-clay are fabricated and studied for physical and mechanical properties using X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR) and Scanning Electron Microscope (SEM). Nanoclay platelets at a weight of 1.0%, 2.0%, and 3.0% were added to geopolymer pastes. Nanoclay at 2.0 wt.% was found to improve density and decrease porosity while improving flexural strength and post-peak toughness. A microstructural analysis indicated that nanoclay behaves as filler and as an activator supporting geopolymeric reaction while producing a higher content geopolymer gel improving the microstructure of binders. The process enhances adhesion between the geopolymer matrix and flax fibres.

Keywords: flax fibres, geopolymer, mechanical properties, nanoclay

Procedia PDF Downloads 227

Authors: Abdul Basit, Gildas Lhostis, Bernard Durand

Abstract:

Shape memory polymers (SMPs) are replacing shape memory alloys (SMAs) in many applications as SMPs have certain superior properties than SMAs. However, SMAs possess some properties like recovery under stress that SMPs lack. SMPs cannot give complete recovery even under a small load. SMPs are initially heated close to their transition temperature (glass transition temperature or the melting temperature). Then force is applied to deform the heated SMP to a specific position. Subsequently, SMP is allowed to cool keeping it deformed. After cooling, SMP gets the temporary shape. This temporary shape can be recovered by heating it again at the same temperature that was given it while heating it initially. As a result, it will recover its original position. SMP can perform unconstrained recovery and constrained recovery, however; under the load, it only recovers partially. In this work, the recovery under the load of an asymmetrical shape memory composite called as CBCM-SMPC has been investigated. It is found that it has the ability to recover under different loads. Under different loads, it shows powerful complete recovery in reference to initial position. This property can be utilized in many applications.

Keywords: shape memory, polymer composite, thermo-mechanical testing, recovery under load

Procedia PDF Downloads 416

Authors: Sima Shakoorjavan, Dawid Stawski, Somaye Akbari

Abstract:

In this study, the adsorption-desorption behavior of poly(amidoamine) (PAMAM) as a polycation and poly (acrylic acid) (PAA) as a polyanion deposited on aminolyzed-PLA nonwoven through layer-by-layer technique (lbl) was studied. The adsorption-desorption behavior was monitored by UV adsorbance spectroscopy and turbidity tests of the waste polyelectrolytes after each deposition. Also, the drying between each deposition step was performed to study the effect of drying on adsorption-desorption behavior. According to UV adsorbance spectroscopy of the waste polyelectrolyte after each deposition, it was revealed that drying has a great effect on the deposition behavior of the next layer. Regarding the deposition of the second layer, drying caused more desorption and removal of the previously deposited layer since the turbidity and the absorbance of the waste increased in comparison to pure polyelectrolyte. To deposit the third layer, the same scenario occurred and drying caused more removal of the previously deposited layer. However, the deposition of the fourth layer drying after the deposition of the third layer did not affect the adsorption-desorption behavior. Since the adsorbance and turbidity of the samples that were dried and those that were not dried were the same. As a result, it seemed that deposition of the fourth layer could be the starting point where lbl reached its constant state. The decrease in adsorbance and remaining turbidity of the waste same as a pure polyelectrolyte can indicate that most portion of the polyelectrolyte was adsorbed onto the substrate rather than complex formation in the bath as the subsequence of the previous layer removal.

Keywords: Adsorption-desorption behavior, lbl technique, poly(amidoamine), poly (acrylic acid), weak polyelectrolytes

Procedia PDF Downloads 39

Authors: Sharmili Routray, Kishor Chandra Biswal

Abstract:

The use of corrosion resistant fiber reinforced polymer (FRP) reinforcement is beneficial in structures particularly those exposed to deicing salts, and/or located in highly corrosive environment. Generally Glass, Carbon and Aramid fibers are used for the strengthening purpose of the structures. Due to the necessities of low weight and high strength materials, it is required to find out the suitable substitute with low cost. Recent developments in fiber production technology allow the strengthening of structures using Basalt fiber which is made from basalt rock. Basalt fiber has good range of thermal performance, high tensile strength, resistance to acids, good electro‐magnetic properties, inert nature, resistance to corrosion, radiation and UV light, vibration and impact loading. This investigation focuses on the effect of fibre content and fiber orientation of basalt fibre on mechanical properties of the fabricated composites. Specimen prepared with unidirectional Basalt fabric as reinforcing materials and epoxy resin as a matrix in polymer composite. In this investigation different fiber orientation are taken and the fabrication is done by hand lay-up process. The variation of the properties with the increasing number of plies of fiber in the composites is also studied. Specimens are subjected to tensile strength test and the failure of the composite is examined with the help of INSTRON universal testing Machine (SATEC) of 600 kN capacities. The average tensile strength and modulus of elasticity of BFRP plates are determined from the test Program.

Keywords: BFRP, fabrication, Fiber Reinforced Polymer (FRP), strengthening

Procedia PDF Downloads 275

Authors: John O. Efosa, S. Egielewa, M. A. Azeke

Abstract:

Hibiscus sabdariffa (Hs) is known for its delicacy and also for medicinal properties. The flower calyces are usually sun- or oven-dried after harvesting. There are unverified claims that calyces dried at lower temperatures have better medicinal potentials than those dried at higher temperatures. The present work, therefore, aimed to study the effects of drying temperatures on the photochemical composition and antioxidant potential of aqueous extracts of the calyces of Hs. The calyces were dried at different temperatures (freeze-drying at -580C, drying at 300C, 400C, and 500 C.) respectively to constant weight. Samples (25 g) of dried calyces from each drying temperatures were weighed and placed in clean conical flasks and extracted; each was used for the analysis. Validated analytical assays were used for the determination of the different Phytochemicals. From the results obtained, it was observed that drying at 30°C resulted in the highest retention of total phenols, total flavonoids, tannins, alkaloids and saponins. Using the Inhibition Concentration values (IC50), some antioxidant parameters were found to follow the same trend as the earlier mentioned phytochemicals. Drying at 30°C resulted in the highest retention of DPPH Radical Scavenging Activity, Ferric Reducing Antioxidant Potential (FRAP), Nitrite radical scavenging Activity, 2, 2-azinobis-3-ethylbenzotiazoline-6-sulfonic acid (ABTS) radical scavenging activity There were, however, significant reductions in vitamin C and oxalate contents as the drying temperature increased (P < 0.05). From the results, it recommended that the calyces of Hibiscus sabdariffa be dried at 30°C in order to optimally elicit its medicinal potentials.

Keywords: antioxidant, drying temperature, hibiscus sabdariffa, phytochemicals, quantitative

Procedia PDF Downloads 152

Authors: Ruby Priya, O. P. Pandey

Abstract:

Herein, we report the structural and luminescent properties of undoped and Eu doped SrY₂O₄ phosphors. The phosphors are synthesized via the combustion synthesis route using glycine as a fuel. The structural, morphological, and optical characterizations are done via X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescent (PL) techniques. The pure phase SrY₂O₄ is obtained at 1100℃, below which impure phases such as Y₂O₃ and SrO were dominant. All the phosphors are excited under UV excitation and exhibited intense emission around 611 nm, which is the typical transition of Eu ions. The phase formation of the synthesized phosphors is studied via analyzing XRD patterns. The as-synthesized phosphors find tremendous applications in optoelectronic devices, light-emitting diodes, and sensors.

Keywords: combustion, europium, glycine, luminescence

Procedia PDF Downloads 143

Authors: L. Bouqbis, H.W. Koyro, M. C. Harrouni, S. Daoud, L. F. Z. Ainlhout, C. I. Kammann

Abstract:

The application of biochar to soils is becoming more and more common. Its application which is generally reported to improve the physical, chemical, and biological properties of soils, has an indirect effect on soil health and increased crop yields. However, many of the previous results are highly variable and dependent mainly on the initial soil properties, biochar characteristics, and production conditions. In this study, two biochars which are biochar II (BC II) derived from a blend of paper sludge and wheat husks and biochar 005 (BC 005) derived from sewage sludge with a KCl additive, are used, and the physical and chemical properties of BC II are characterized. To determine the potential impact of salt stress and toxic and volatile substances, the second part of this study focused on the effect biochars have on germination of salad (Lactuca sativa L.), barley (Hordeum vulgare), and cress (Lepidium sativum) respectively. Our results indicate that Biochar II showed some unique properties compared to the soil, such as high EC, high content of K, Na, Mg, and low content of heavy metals. Concerning salad and barley germination test, no negative effect of BC II and BC 005 was observed. However, a negative effect of BC 005 at 8% level was revealed. The test of the effect of volatile substances on germination of cress revealed a positive effect of BC II, while a negative effect was observed for BC 005. Moreover, the water holding capacities of biochar-sand mixtures increased with increasing biochar application. Collectively, BC II could be safely used for agriculture and could provide the potential for a better plant growth.

Keywords: biochar, phytotoxic tests, seedlings growth, water holding capacity

Procedia PDF Downloads 232

Authors: Yezli-Touiker Samira, Amrani-Kirane Leila, Soltani Mazouni Nadia

Abstract:

Due to secondary effects of conventional insecticides on the environment, the agrochemical research has resulted in the discovery of novel molecules. That research work will help in the development of a new group of pesticides that may be cheaper and less hazardous to the environment and non-target organisms which is the main desired outcome of the present work. Angiotensin-converting enzyme as a target for the development of novel insect growth regulators. Captopril is an inhibitor of angiotensin converting enzyme (ACE) it was tested in vivo by topical application on reproduction of Ephestia kuehniella Zeller (Lepidoptera: Pyralidae). The compound is diluted in acetone and applied topically to newly emerged pupae (10µg/ 2µl). The effects of this molecule was studied,on the biochemistry of ovary (on amounts nucleic acid, proteins, the qualitative analysis of the ovarian proteins and the reproductive potential (duration of the pre-oviposition, duration of the oviposition, number of eggs laid and hatching percentage). Captopril reduces significantly quantity of ovarian proteins and nucleic acid. The electrophoresis profile reveals the absence of tree bands at the treated series. This molecule reduced the duration of the oviposition period, the fecundity and the eggviability.

Keywords: environment, ephestia kuehniella, captopril, reproduction, the agrochemical research

Procedia PDF Downloads 270

Authors: S. A. Nirmal, J. M. Ingale, G. S. Asane, S. C. Pal, Subhash C. Mandal

Abstract:

The present work was undertaken to determine the effects of Amaranthus roxburghianus Nevski. (Amaranthaceae) root alone and in combination with piperine in treating ulcerative colitis (UC) in mice. Swiss albino mice were divided into seven groups (n = 6). Standard group received prednisolone (5 mg/kg, i.p.). Treatment groups received hydroalcoholic extract of roots of A. roxburghianus (50 and 100 mg/kg, p.o.) and a combination of hydroalcoholic extract of roots of A. roxburghianus (50 and 100 mg/kg, p.o.) and piperine (5 mg/kg, p.o.). Ulcer index, colitis severity, myeloperoxidase (MPO), malondialdehyde and glutathione were estimated from blood and tissue. Column chromatography of the extract was done and purified fractions were analyzed by gas chromatography-mass spectroscopy (GC-MS). Treatment with the combination of hydroalcoholic extract of A. roxburghianus and piperine showed minimal ulceration, hemorrhage, necrosis and leucocyte infiltration by histopathological observation. Acetic acid increased MPO levels in blood and colon tissue to 355 U/mL and 385 U/mg, respectively. The combination of hydroalcoholic extract (100 mg/kg) and piperine (5 mg/kg) significantly decreased MPO in blood and tissue to 182 U/mL and 193 U/mg, respectively. Similarly, this combination significantly reduced MPO and increased glutathione levels in blood and tissue. Various phytoconstituents were detected by GC-MS. The combination of hydroalcoholic extract and piperine is effective in the treatment of UC and the effects are comparable with the standard drug prednisolone. 4H-pyran-4-one, 2,3-dihydro-3,5-dihydroxy-6-methyl, eugenol and benzene, and 1-(1,5-dimethyl-4-hexenyl)-4-methyl are reported having analgesic, anti-inflammatory, and antioxidant properties; they may play a role in the biological activity of A. roxburghianus root.

Keywords: Amaranthus roxburghianus, ulcerative colitis, anti-inflammatory, ulcerative colitis

Procedia PDF Downloads 511

Authors: Ertuğ Yıldırım, Dile Kara, Salih Zeki Yıldız

Abstract:

Metal containing polymers (MCPs) are macro molecules usually containing metal-ligand coordination units and are a multidisciplinary research field mainly based at the interface between coordination chemistry and polymer science. The progress of this area has also been reinforced by the growth of several other closely related disciplines including macro molecular engineering, crystal engineering, organic synthesis, supra molecular chemistry and colloidal and material science. Schiff base ligands are very effective in constructing supra molecular architectures such as coordination polymers, double helical and triple helical complexes. In addition, Schiff base derivatives incorporating a fluorescent moiety are appealing tools for optical sensing of metal ions. MCPs are well-known systems in which the combinations of local parameters are possible by means of fluoro metric techniques. Generally, without incorporation of the fluorescent groups with polymers is unspecific, and it is not useful to analyze their fluorescent properties. Therefore, it is necessary to prepare a new type epoxy polymers with fluorescent groups in terms of metal sensing prop and the other photo chemical applications. In the present study metal containing polymers were prepared via poly functional monomeric Schiff base metal chelate complexes in the presence of dis functional monomers such as diglycidyl ether Bisphenol A (DGEBA). The synthesized complexes and polymers were characterized by FTIR, UV-VIS and mass spectroscopies. The preparations of epoxy polymers have been carried out at 185 °C. The prepared composites having sharp and narrow excitation/emission properties are expected to be applicable in various systems such as heat-resistant polymers and photo voltaic devices. The prepared composite is also ideal for various applications, easily prepared, safe, and maintain good fluorescence properties.

Keywords: Schiff base ligands, crystal engineering, fluorescence properties, Metal Containing Polymers (MCPs)

Procedia PDF Downloads 335

Authors: H. B. Mahmud, Syamsul Bahri, Y. W. Yee, Y. T. Yeap

Abstract:

This paper reports the strength and durability properties of high strength high performance concrete incorporating rice husk ash (RHA) having high silica, low carbon content and appropriate fineness. In this study concrete containing 10%, 15% and 20% RHA as cement replacement and water to binder ratio of 0.25 were investigated. The results show that increasing amount of RHA increases the dosage of superplasticizer to maintain similar workability. Partial replacement of cement with RHA did not increase the early age compressive strength of concrete. However, concrete containing RHA showed higher compressive strength at later ages. The results showed that compressive strength of concrete in the 90-115 MPa range can be obtained at 28 curing days and the durability properties of RHA concrete performed better than that of control concrete. The water absorption of concrete incorporating 15% RHA exhibited the lowest value. The porosity of concrete is consistent with water absorption whereby higher replacement of RHA decreased the porosity of concrete. There is a positive correlation between reducing porosity and increasing compressive strength of high strength high performance concrete. The results also indicate that up to 20% of RHA incorporation could be advantageously blended with cement without adversely affecting the strength and durability properties of concrete.

Keywords: compressive strength, durability, high performance concrete, rice husk ash

Procedia PDF Downloads 323

Authors: Yafri Hazbi, Zaenal Bachruddin, Nafiatul Umami, Lies Mira Yusiati

Abstract:

The objective of this study was to identify the benefits of total mixture concentrate based on tofu waste silage (TMC-TWS) as ration containing lactic acid bacteria on performance of lambs. Fifteen weaning lambs (2-3 months old) were randomly divided into two treatment groups, treatment group I (TI) was fed with TMC-TWS as ration and treatment group II (TII) was fed with TMC-TWS fresh (without silage fermentation). The performance of lambs was evaluated on day 0, 15, and 30 to have data of body weight per day. Meanwhile, blood sampling and feces were made on the 30th day to get an analysis on the blood profile (erythrocytes (mill/ml), hemoglobin (g/dL), packed cell volume (%), and leukocytes (mill/ml)) and the number of worm eggs in feces. The results of this study showed no significant difference between the effect of different feed on the blood profile (erythrocytes (mill/ml), hemoglobin (g/dL), packed cell volume (%), as well as the number of worm eggs in the feces. However the results showed significant differences if it is low (P<0.05) due to the treatment group based on sex on body weight gain per day, feed conversion rate and the number of erythrocytes.

Keywords: lambs, total mixture concentrate, silage, acid lactid bacteria, blood profile, eggs worm in feces

Procedia PDF Downloads 163

Authors: Fadwa Alhalaiqa, Othman Alfuqaha, Anas H. Khalifeh, Mahmoud Alsaraireh, Rami Masa’Deh, Natija S Manaa

Abstract:

Background: Post-traumatic stress disorders (PTSD) usually occur after traumatic occurrences that exceed the range of common human experience. This study aimed to test the psychometric properties of PCL-5 checklist for the 20 PTSD symptoms from DSM-5 among Lebanese population and to identify the prevalence of PTSD. Methods: A cross sectional survey of PCL5 among 950 Lebanese using the online survey platform by Google form was conducted. Snowball recruitment was used to identify participants for the survey. STROBE guideline was used in reporting the current study. Results: Face content, construct, discriminant, and convergent validity had been accomplished of PCL-5. The reliability by Cronbach alpha, composite, and average variance extracted were set superior. We found also that more than half of the participants (55.6%) scored 33 or above, which is the cutoff score for a likely diagnosis of PTSD. Conclusion: The current study provides further support for the Arabic version PCL-5 validity and reliability among non-Western populations. This support using this tool in the screening of PTSD.

Keywords: post traumatic stress disorder, psychometric properties, stress, adult population

Procedia PDF Downloads 87

Authors: I. Bouhaf Kharkhachi, A. Attaf

Abstract:

Tin sulfide thin films on glass substrate were prepared by spray ultrasonic technique, at different experimental conditions. The influence of deposition time (2, 4, 6, 8 and 10 min) on different properties of thin films, such us, (XRD) and (UV) spectroscopy visible spectrum was investigated. X-ray diffraction showing that thin films crystallized in SnS, SnS2, and Sn2S3 phases. The results of (UV) spectroscopy visible spectrum show that films deposited at 4 min are large transmittance 60% in the visible region.

Keywords: SnS, thin films, ultrasonic spray, X-ray diffraction, UV spectroscopy visible

Procedia PDF Downloads 507

Authors: Chao Hu, Xinwen Liao, Qing-Hua Qin, Gang Wang

Abstract:

The hierarchical carbon nanotube (CNT)/carbon fiber (CF)/high density polyethylene (HDPE) was fabricated via compound extrusion and injection molding, in which to author’s best knowledge CNT was employed as a nano-coatings on the surface of CF for the first time by spray coating technique. The CNT coatings relative to CF was set at 1 wt% and the CF content relative to the composites varied from 0 to 25 wt% to study the influence of CNT coatings and CF contents on the mechanical, thermal and morphological performance of this hierarchical composites. The results showed that with the rise of CF contents, the mechanical properties, including the tensile properties, flexural properties, and hardness of CNT/CF/HDPE composites, were effectively improved. Furthermore, the CNT-coated composites showed overall higher mechanical performance than the uncoated counterparts. It can be ascribed to the enhancement of interfacial bonding between the CF and HDPE via the incorporation of CNT, which was demonstrated by the scanning electron microscopy observation. Meanwhile, the differential scanning calorimetry data indicated that by the introduction of CNT and CF, the crystallization temperature and crystallinity of HDPE were affected while the melting temperature did not have an obvious alteration.

Keywords: carbon fibers, carbon nanotubes, extrusion, high density polyethylene

Procedia PDF Downloads 128

Authors: Artemis Louppis, Michalis Constantinou, Ioanna Kosma, Federica Blando, Michael Kontominas, Anastasia Badeka

Abstract:

The aim of the present study was to differentiate yellow prickly pear according to geographical origin based on the combination of mineral content, physicochemical parameters, vitamins and antioxidants. A total of 240 yellow prickly pear samples from Cyprus, Spain, Italy and Greece were analyzed for pH, titratable acidity, electrical conductivity, protein, moisture, ash, fat, antioxidant activity, individual antioxidants, sugars and vitamins by UPLC-MS/MS as well as minerals by ICP-MS. Statistical treatment of the data included multivariate analysis of variance followed by linear discriminant analysis. Based on results, a correct classification of 66.7% was achieved using the cross validation by mineral content while 86.1% was achieved using the cross validation method by combination of all analytical parameters.

Keywords: geographical differentiation, prickly pear, chemometrics, analytical techniques

Procedia PDF Downloads 129

Authors: Pei-Hsiu Chiang, Ling Hong Huang, Hsin-I Chang

Abstract:

In this research, we used UVA irradiation, which can penetrate into dermis and fibroblasts, the most abundant cells in dermis, to investigate the effect of UV light on dermis, such as inflammation, ECM degradation and elasticity loss. Moreover, this research is focused on the influence of hyaluronic acid (HA) on UVA treated dermal fibroblasts. We aim to establish whether HA can effectively relief ECM degradation, and restore the elasticity of UVA-damaged fibroblasts. Prolonged exposure to UVA radiation can damage fibroblasts and led variation in cell morphology and reduction in cell viability. Besides, UVA radiation can induce IL-1β expression on fibroblasts and then promote MMP-1 and MMP-3 expression, which can accelerate ECM degradation. On the other hand, prolonged exposure to UVA radiation reduced collagen and elastin synthesis on fibroblasts. Due to the acceleration of ECM degradation and the reduction of ECM synthesis, Atomic force microscope (AFM) was used to analyze the elasticity reduction on UVA-damaged fibroblasts. UVA irradiation causes photoaging on fibroblasts. UVA damaged fibroblasts with HA treatment can down-regulate the gene expression of MMP-1, MMP-3, and then slow down ECM degradation. On the other hand, HA may restore elastin and collagen synthesis in UV-damaged fibroblasts. Based on the slowdown of ECM degradation, UVA-damaged fibroblast elasticity can be effectively restored by HA treatment. In summary, HA can relief the photoaging conditions on fibroblasts, but may not be able to return fibroblasts to normal, healthy state. Although HA cannot fully recover UVA-damaged fibroblasts, HA is still potential for repairing photoaging skin.

Keywords: atomic force microscope, hyaluronic acid, UVA radiation, dermal fibroblasts

Procedia PDF Downloads 381

Authors: H. M. Wilhelm, P. O. Fernandes, L. P. Dill, C. Steffens, K. G. Moscon, S. M. Peres, V. Bender, T. Marchesan, J. B. Ferreira Neto

Abstract:

Deterioration of insulating oil is a natural process that occurs during transformers operation. However, this process can be accelerated by some factors, such as oxygen, high temperatures, metals and, moisture, which rapidly reduce oil insulating capacity and favor transformer faults. Parts of building materials of a transformer can be degraded and yield soluble compounds and insoluble particles that shorten the equipment life. Physicochemical tests, dissolved gas analysis (including propane, propylene and, butane), volatile and furanic compounds determination, besides quantitative and morphological analyses of particulate are proposed in this study in order to correlate transformers building materials degradation with insulating oil characteristics. The present investigation involves tests of medium temperature overheating simulation by means of an electric resistance wrapped with the following materials immersed in mineral insulating oil: test I) copper, tin, lead and, paper (heated at 350-400 °C for 8 h); test II) only copper (at 250 °C for 11 h); and test III) only paper (at 250 °C for 8 h and at 350 °C for 8 h). A different experiment is the simulation of electric arc involving copper, using an electric welding machine at two distinct energy sets (low and high). Analysis results showed that dielectric loss was higher in the sample of test I, higher neutralization index and higher values of hydrogen and hydrocarbons, including propane and butane, were also observed. Test III oil presented higher particle count, in addition, ferrographic analysis revealed contamination with fibers and carbonized paper. However, these particles had little influence on the oil physicochemical parameters (dielectric loss and neutralization index) and on the gas production, which was very low. Test II oil showed high levels of methane, ethane, and propylene, indicating the effect of metal on oil degradation. CO₂ and CO gases were formed in the highest concentration in test III, as expected. Regarding volatile compounds, in test I acetone, benzene and toluene were detected, which are oil oxidation products. Regarding test III, methanol was identified due to cellulose degradation, as expected. Electric arc simulation test showed the highest oil oxidation in presence of copper and at high temperature, since these samples had huge concentration of hydrogen, ethylene, and acetylene. Particle count was also very high, showing the highest release of copper in such conditions. When comparing high and low energy, the first presented more hydrogen, ethylene, and acetylene. This sample had more similar results to test I, pointing out that the generation of different particles can be the cause for faults such as electric arc. Ferrography showed more evident copper and exfoliation particles than in other samples. Therefore, in this study, by using different combined analytical techniques, it was possible to correlate insulating oil characteristics with possible contaminants, which can lead to transformers failure.

Keywords: Ferrography, gas analysis, insulating mineral oil, particle contamination, transformer failures

Procedia PDF Downloads 207

Authors: Fang Bo Yu, Li Bo Guan

Abstract:

Biogas slurry is a low-cost source of crop nutrients and can offer extra benefits to soil fertility and fruit quality. However, its current utilization mode and low content of active ingredients limit its application scale. In this report, one growing season field research was conducted to assess the effects of concentrated biogas slurry on soil property, tomato fruit quality, and composition of the microflora in both non-rhizosphere and rhizosphere soils. The results showed that application of concentrated slurry could cause significant changes to tomato cultivation, including increases in organic matter, available N, P, and K, total N, and P, electrical conductivity, and fruit contents of amino acids, protein, soluble sugar, β-carotene, tannins, and vitamin C, together with the R/S ratios and the culturable counts of bacteria, actinomycetes, and fungi in soils. It could be concluded as the application is a practicable means in tomato production and might better service the sustainable agriculture in the near future.

Keywords: concentrated slurry, fruit quality, soil fertility, sustainable agriculture

Procedia PDF Downloads 444

Authors: N. N. Orlova, A. S. Aronin, Yu. P. Kabanov, S. I. Bozhko, V. S. Gornakov

Abstract:

We have investigated the change of the magnetic structure and the hysteresis properties of iron-based microwires after decreasing levels of internal mechanical stresses. The magnetic structure was investigated by the method of magneto-optical indicator film and the method of magnetic force microscopy. The hysteresis properties were studied by the vibrating sample magnetometer. The stresses were decreased by removing the glass coat and/or by low-temperature isothermal annealing. Previously, the authors carried out experimentally investigation of the magnetic structure of Fe-based microwire using these methods. According to the obtained results the domain structure of a microwire with a positive magnetostriction is composed of the inner cylindrical domains with the magnetization along the wire axis and the surface layer of the ring shape domains with the radial direction of magnetization. Surface ring domains with opposite magnetization direction (i.e., to the axis or from the axis) alternate with each other. For the first time the size of magnetic domains was determined experimentally. In this study it was found that in the iron-based microwires the value of the coercive force can be reduce more than twice by decreasing levels of internal mechanical stresses. Decrease of the internal stress value by the relaxation annealing influence on the magnetic structure. So in the as-prepared microwires observed local deviations of the magnetization of the magnetic core domains from the axis of the wire. After low-temperature annealing the local deviations of magnetization is not observed.

Keywords: amorphous microwire, magnetic structure, internal stress, hysteresis properties, ferromagnetic

Procedia PDF Downloads 558

Authors: Taliman Nisar Ahmad, Hirofume Saneoka

Abstract:

A pot experiment was conducted to investigate the effect of phosphorus (P) and potassium (K) nutrition on grain yield, phytic acid and grain quality of high-phytate (Akimaro) and low-phytate line. Phosphorus and potassium were applied as; P₁ (20 kg ha⁻¹) and P₂ (100 kg ha⁻¹), same as K₁ (20 kg ha⁻¹) and K₂ (100 kg ha⁻¹), respectively. Low-phytate soybean had the highest grain yield, and 75% increase was observed compared to the high-phytate under same treatments. Highly significant differences of seed phytate P were observed in both cultivars, and the phytate P in high-phytate was found 39% higher than low-phytate, whereas no significant differences observed in response to P and K treatment. Percentage of phytate P from total P in seeds was 28 to 35% in low-phytate and 72 to 81% in high-phytate in different treatments. The lipid content in low-phytate was found lowered compared to that of high-phytate. Crude protein in grains was also found significantly higher in PK combined. No significant difference was observed in seed calcium (Ca), magnesium (Mg), and Zinc (Zn) in different treatments, but high-phytate showed 87% increase in seed Ca and 76% of Mg compared to low-phytate; however, low-phytate showed 82% increase in Zn content over high-phytate. The result illustrates that low-phytate soybean achieved higher grain yield and grain Pi in response to increased P and K nutrition. To achieve higher yield and quality seeds from the low-phytate soybean, it is recommended that proper phosphorus and potassium nutrition to be applied suggested in this study.

Keywords: phytic acid, low-phytate soybean, high-phytate soybean, P and K nutrition, protein content, soybean

Procedia PDF Downloads 119

Authors: Shahab Hasani Nasab, Aran Aeini, Navid Kermanshahi

Abstract:

In order to reduce road building costs and reduce environmental damage, recycled materials can be used instead of mineral materials in the production of asphalt mixtures. Today, in most parts of the world, cold recycled asphalt with bitumen emulsion, has acceptable results. However, Cold Recycled Asphalt have some deficiency such as stripping, thermal cracking, and rutting. This requires the addition of additives to reduce this deficiency of recycled pavement with emulsified asphalt. In this research, nano-alumina and emulsified asphalt were used to modify the properties of recycled asphalt mixtures according to the technical specifications and the operation of cold recycling. Marshall test methods, dynamic creep test, and resiliency modulus test has been used to obtain the nano-alumina’s effects on asphalt mixture properties. The results show that the addition of nano-alumina would reduce the Marshall stability in samples but increases the rutting resistance. The resiliency modulus increases significantly with this additive.

Keywords: cold asphalt, cold recycling, nano-alumina, dynamic creep, bitumen emulsion

Procedia PDF Downloads 147

Authors: Zuzana Sedláková, Magda Kárászová, Jiří Vejražka, Lenka Morávková, Pavel Izák

Abstract:

Membrane separations are mentioned frequently as a possibility for CO2 capture. Selectivity of ionic liquid membranes is strongly determined by different solubility of separated gases in ionic liquids. The solubility of separated gases usually varies over an order of magnitude, differently from diffusivity of gases in ionic liquids, which is usually of the same order of magnitude for different gases. The present work evaluates the selection of an appropriate ionic liquid for the selective membrane preparation based on the gas solubility in an ionic liquid. The current state of the art of CO2 capture patents and technologies based on the membrane separations was considered. An overview is given of the discussed transport mechanisms. Ionic liquids seem to be promising candidates thanks to their tunable properties, wide liquid range, reasonable thermal stability, and negligible vapor pressure. However, the uses of supported liquid membranes are limited by their relatively short lifetime from the industrial point of view. On the other hand, ionic liquids could overcome these problems due to their negligible vapor pressure and their tunable properties by adequate selection of the cation and anion.

Keywords: biogas upgrading, carbon dioxide separation, ionic liquid membrane, transport properties

Procedia PDF Downloads 417

Authors: Yuksel Akinay, Fatih Hayat

Abstract:

The influence of Ni elements on mechanical properties and microstructure of twinning induced plasticity (TWIP) steels were investigated in this study. TWIP 1 (0,6C, 24Mn) and TWIP 2 (0,6C, 24Mn, 1Ni) high Mn TWIP (Twinning Induced Plasticity) steels were fabricated, and were annealed at 700°C, 800°C and 900°C for 150 minute and then air-cooled. The microstructures and mechanical properties of specimens were analysed to investigate influence of Ni element on TWIP steel. The carbide precipitations have seen in microstructure of TWIP 1 and TWIP 2 specimen annealed at 700 °C. However, the microstructures of TWIP 1 annealed at 800°C and 900°C are fully austenite and some grains are including annealing twins. However twining did not occur at TWIP 2 specimens annealed at 700 °C, 800 °C and 900 °C. TWIP 2 steel contains also Ni element differently from TWIP 1 steel. It can conclude that, Nickel (Ni) was restrained formation of twinning. The reversion of the tensile strength occurred between 700°C and 800°C because of the carbide precipitation hardening. Beside that, hardness value has decreased between 800 °C and 900 °C, which show a good agreement with the equilibrium dissolution temperature of M3C carbides. However, the results show that, carbide precipitations also are as strong barriers for the formation of twining. For this reason, twinning was not obtained at 700 °C.

Keywords: high manganese, heat treatment, SEM, TWIP steel, cold rolling, nickel

Procedia PDF Downloads 344

Authors: Sudaff Mohammed, Wahda Shuker Al-Hinkawi, Nada Abdulmueen Hasan

Abstract:

The compatibility of the Rhizome and Complex Adaptive system theory as a strategy within the urban context is the essential interest of this paper since there are only a few attempts to establish a hybrid, multi-scalar, and developable strategy based on the concept of the Rhizome and the CAS theory. This paper aims to establish a Rhizomic CAS strategy for different urban contexts by investigating the principles, characteristics, properties, and mechanisms of Rhizome and Complex Adaptive Systems. The research focused mainly on analyzing three properties: aggregation, non-linearity, and flow through the lens of Rhizome, Rhizomatization of CAS properties. The most intriguing result is that the principal and well-investigated characteristics of Complex Adaptive systems can be ‘Rhizomatized’ in two ways; highlighting commonalities between Rhizome and Complex Adaptive systems in addition to using Rhizome-related concepts. This paper attempts to emphasize the potency of the Rhizome as an apparently stochastic and barely anticipatable structure that can be developed to analyze cities of distinctive contexts for formulating better customized urban strategies.

Keywords: rhizome, complex adaptive system (CAS), system Theory, urban system, rhizomatic CAS, assemblage, human occupation impulses (HOI)

Procedia PDF Downloads 21