Search results for: Jeetendra%20Yadav

Authors: Chander Shekhar, Jeetendra Yadav, Shaziya Allarakha

Abstract:

Hypertension has been described as an 'iceberg disease' as those who suffered are ignored and hence usually seek healthcare services at a very late stage. It is estimated that more than 2 million Indians are suffering from hypertensive heart disease that contributed to above 0.13 million deaths in 2016. The paper study aims to know the prevalence of Hypertension in India and its variation by socioeconomic backgrounds and to find out risk factors discriminating hypertension with special emphasis on consumption of tobacco and alcohol among men aged 15-54 years in India. The paper uses NFHS (2015-16) data. The paper used binary logistic regression and discriminant analysis to find significant predictors and discriminants of interest. The prevalence of hypertension was 16.5% in the study population. The results suggest that consumption of alcohol and tobacco are significant discriminant characteristics in carrying hypertension irrespective of what socioeconomic background characteristic he possesses.

Keywords: hypertention, alcohol, tobacco, discriminant

Procedia PDF Downloads 121

Authors: Jeetendra Yadav, Geetha Menon, Anita Pal, Rajkumar Verma

Abstract:

Even after encouraging maternal and child wellness programs at worldwide level, lower-middle income nations are not reached the goal set by the UN yet. This study quantified the contribution of socioeconomic determinants of inequality to the utilization of Antenatal Care in South Asian Countries. This study used data from Demographic Health Survey (DHS) of the selected countries were used, and Oaxaca decomposing were applied for socioeconomic inequalities in utilization of antenatal care. Finding from the multivariate analysis shows that mother’s age at the time of birth, birth order and interval, mother’s education, mass media exposure and economic status were significant determinants of the utilization of antenatal care services in South Asian countries. Considering, concentration index curve, the line of equity was greatest in Pakistan which followed by India and Nepal.

Keywords: antenatal care, decomposition, inequalities, South Asian countries

Procedia PDF Downloads 154

Authors: Suraj Makkar, Asis Isor, Jeetendra Gupta, Simran Bareja, Maushumi K. Talukdar

Abstract:

During the exploratory testing phase of an offshore oil and gas well, when the tubing string was pulled out after production testing, it was observed that there was visible corrosion/pitting in a few of the 3-1/2” API 5 CT L-80 Grade tubing. The area of corrosion was at the same location in all the tubing, i.e., just above the pin end. Since the corrosion was observed in the tubing within two months of their installation, it was a matter of concern, as it could lead to premature failures resulting in leakages and production loss and thus affecting the integrity of the asset. Therefore, the tubing was analysed to ascertain the mechanism of the corrosion occurring on its surface. During the visual inspection, it was observed that the corrosion was totally external, which was near the pin end, and no significant internal corrosion was observed. The chemical compositional analysis and mechanical properties (tensile and impact) show that the pipeline material was conforming to API 5 CT L-80 specifications. The metallographic analysis of the tubing revealed tempered martensitic microstructure. The grain size was observed to be different at the pin end as compared to the microstructure at base metal. The microstructures of the corroded area near threads reveal an oriented microstructure. The clearly oriented microstructure of the cold-worked zone near threads and the difference in microstructure represents inappropriate heat treatment after cold work. This was substantiated by hardness test results as well, which show higher hardness at the pin end in comparison to hardness at base metal. Scanning Electron Microscope (SEM) analysis revealed the presence of round and deep pits and cracks on the corroded surface of the tubing. The cracks were stress corrosion cracks in a corrosive environment arising out of the residual stress, which was not relieved after cold working, as mentioned above. Energy Dispersive Spectroscopy (EDS) analysis indicates the presence of mainly Fe₂O₃, Chlorides, Sulphides, and Silica in the corroded part indicating the interaction of the tubing with the well completion fluid and well bore environment. Thus it was concluded that residual stress after the cold working of male pins during threading and the corrosive environment acted in synergy to cause this pitting corrosion attack on the highly stressed zone along the circumference of the tubing just below the threaded area. Accordingly, the following suitable recommendations were given to avoid the recurrence of such corrosion problems in the wells. (i) After any kind of hot work/cold work, tubing should be normalized at full length to achieve uniform microstructure throughout its length. (ii) Heat treatment requirements (as per API 5 CT) should be part of technical specifications while at the procurement stage.

Keywords: pin end, microstructure, grain size, stress corrosion cracks

Procedia PDF Downloads 47