Search results for: ZK60

Authors: Anna Dziubinska

Abstract:

The article presents the results of numerical simulations of the new forging process of the automotive connector forging from cast preform. The high-strength ZK60 alloy (belonging to the Mg-Zn-Zr group of Mg alloys) was selected for numerical tests. Currently, this part of the industry is produced by multi-stage forging consisting of operations: bending, preforming, and finishing. The use of the cast preform would enable forging this component in one operation. However, obtaining specific mechanical properties requires inducing a certain level of strain within the forged part. Therefore, the design of the preform, its shape, and volume are of paramount importance. In work presented in this article, preforms of different shapes were designed and assessed using Finite Element (FE) analysis. The research was funded by the Polish National Agency for Academic Exchange within the framework of the Bekker programme.

Keywords: automotive connector, forging, magnesium alloy, numerical simulation, preform, ZK60

Procedia PDF Downloads 132

Authors: Sijia Hu

Abstract:

Tensile creep tests were performed along the normal direction on the as-solutioned (AS) and as-aged (AA) samples of a commercial ZK60 alloy in this work. The results showed that the AA sample obtained a stronger 0.2% proof stress but a poorer creep resistance in comparison to the AS sample. It was revealed that the creep deformation in the AS sample was attributed to basal slip and twinning, while the creep behavior of the AA sample was controlled by basal slip, pyramidal slip and twinning. Besides, the reasons for the poorer creep resistance of the AA sample were unveiled. Pyramidal dislocations towards various moving directions were found to accelerate the creep deformation, and basal dislocations kinking at twin boundaries were found to induce heavy stress concentration. Furthermore, massive dynamic precipitates, including beta 1 prime and beta 2 prime types, were formed in the AS sample during the creep exposure, contributing to the superior creep resistance. But in the AA sample, plentiful beta 1 prime and beta 2 prime phases generated during the prior peak-aging treatment dissolved into the matrix fast and only beta 1 prime re-precipitated during the creep process. With the decreased area fractions of precipitates, the age-hardening effect slacked off and failed to enhance the creep resistance.

Keywords: Mg alloy, creep, precipitation, microstructure

Procedia PDF Downloads 40