Search results for: Mitsunobu%20Iwasaki

Authors: Brigitta Bodnár, Lajos Kovács, Zoltán Kupihár

Abstract:

The cancer cells require higher amount of nucleoside building blocks for their proliferation, therefore they have significantly higher uptake of nucleosides by the different nucleoside transporters. Therefore, the conjugation with nucleosides may significantly increase the efficiency and selectivity of potential active pharmaceutical ingredients. On the other hand, the advantage of using a nucleoside could be either the higher activity on targeted enzymes overrepresented in cancer cells or an enhanced cellular uptake of the bioconjugates in these cells compared to the healthy ones. This fact can be used to make the nucleosides, as targeting moieties covalently bound to anti-cancer drug molecules which can selectively accumulate in cancer cells. However, in order to form the nucleoside-drug conjugates, such nucleoside building blocks are needed, which can selectively be coupled to the drug molecules containing even a high number of diverse functional groups. One of the most selective conjugation techniques is the copper-catalyzed azide-alkyne click reaction that requires the presence of an alkyl group on one of the conjugated molecules and an azide group on the other. In case of nucleosides, the development of azide group is simpler for which the replacement of the 5'-hydroxy group is the most suitable. This transformation generally involves many side reactions and result in very low yields. In addition, during our experiments, the transformation of the 2'-deoxyguanosine to the corresponding 5'-deoxy-5’-azido-2’-deoxyguanosine could not be performed with any of the methods described in the literature. Therefore, we have tried to overcome these difficulties with not only using the traditional process based on the 2 step exchange of tosyl to azide, but also using the Mitsunobu reaction which requires only one step. However, this path proved to be unsuccessful in spite of the optimizing the reaction conditions. Finally, a method has been developed whereby the azide groups were incorporated into the 5’-position resulting in significantly better yields compared to all other previous methods, and we were able to produce all the four nucleoside derivatives.

Keywords: 5'-azidonucleosides, bioconjugate, click reaction, proliferation

Procedia PDF Downloads 214

Authors: Mitsunobu Iwasaki, Akifumi Iseda

Abstract:

Yttrium aluminum garnet doped with cerium (Ⅲ) ions (Y3Al5O12:Ce3+, YAG:Ce3+) has attracted a great attention because it can efficiently convert the blue light into a very broad yellow emission band, which produces white light emitting diodes and is applied for panel displays. To improve the brightness and resolution of the display, a considerable attention has been directed to develop fine phosphor particles. We have prepared YAG:Ce3+ nanophosphors by environmental-friendly wet process. The peak maximum of absorption spectra of surface plasmon of Ag nanopaticles are close to that of the excitation spectra (460 nm) of YAG:Ce3+. It can be expected that Ag nanoparticles supported onto the surface of YAG:Ce3+ (Ag-YAG:Ce3+) enhance the absorption of Ce3+ ions. In this study, we have prepared Ag-YAG:Ce3+ nanophosphors and investigated their photoluminescent properties. YCl3･6H2O and AlCl3･6H2O with a molar ratio of Y:Al=3:5 were dissolved in ethanol (100 ml), and CeCl3•7H2O (0.3 mol%) was further added to the above solution. Then, NaOH (4.6×10-2 mol) dissolved in ethanol (50 ml) was added dropwise to the mixture under reflux over 2 hours, and the solution was further refluxed for 1 hour. After cooling to room temperature, precipitates in the reaction mixture were heated at 673 K for 1 hour. After the calcination, the particles were immersed in AgNO3 solution for 1 hour, followed by sintering at 1123 K for 1 hour. YAG:Ce3+ were confirmed to be nanocrystals with a crystallite size of 50-80 nm in diameter. Ag nanoparticles supported onto YAG:Ce3+ were single nanometers in diameter. The excitation and emission spectra were 454 nm and 539 nm at a maximum wavelength, respectively. The emission intensity was maximum for Ag-YAG:Ce3+ immersed into 0.5 mM AgCl (Ag-YAG:Ce (0.5 mM)). The absorption maximum (461 nm) was increased for Ag-YAG:Ce3+ in comparison with that for YAG:Ce3+, indicating that the absorption was enhanced by the addition of Ag. The external and internal quantum efficiencies became 11.2 % and 36.9 % for Ag-YAG:Ce (0.5 mM), respectively. The emission intensity and absorption maximum of Ag-YAG:Ce (0.5 mM)×n (n=1, 2, 3) were increased with an increase of the number of supporting times (n), respectively. The external and internal quantum efficiencies were increased for the increase of n, respectively. The external quantum efficiency of Ag-YAG:Ce (0.5 mM) (n=3) became twice as large as that of YAG:Ce. In conclusion, Ag nanoparticles supported onto YAG:Ce3+ increased absorption and quantum efficiency. Therefore, the support of Ag nanoparticles enhanced the photoluminescent properties of YAG:Ce3+.

Keywords: plasmon, quantum efficiency, silver nanoparticles, yttrium aluminum garnet

Procedia PDF Downloads 242