Tensile Behavior of Spheroidizing Heat Treated High Carbon Steel

Authors: Seok Hong Min, Tae Kwon Ha

Abstract:

Spheroidization heat treatment was conducted on the  SK85 high carbon steel sheets with various initial microstructures  obtained after cold rolling by various reduction ratios at a couple of  annealing temperatures. On the high carbon steel sheet with fine  pearlite microstructure, obtained by soaking at 800oC for 2hr in a box furnace and then annealing at 570oC for 5min in a salt bath furnace followed by water quenching, cold rolling was conducted by reduction ratios of 20, 30, and 40%. Heat treatment for spheroidization was carried out at 600 and 720oC for the various time intervals from 0.1 to 32 hrs. Area fraction of spheroidized cementite was measured with an image analyzer as a function of cold reduction ratios and duration times. Tensile tests were carried out at room temperature on the spheoidized high carbon steel.

 

Keywords: High carbon steel, SK85, pearlite, cementite, shperoidization, tensile behavior.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1090504

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 4062

References:


[1] Y.L. Tian and R.W. Kraft, Met. Trans. A, Vol. 18A, p. 1403, 1978.
[2] E. Werner, Acta Metall., Vol. 37, p. 2047, 1989.
[3] S.A. Hackney, Scripta Metall., Vol. 25, p. 799, 1991.
[4] N. V. Luzginova, L. Zhao, and J. Sietsma, Metall. Mater. Trans. A, Vol. 39A, p. 513,2008.
[5] C. Chou, J. Mat. Sci., Vol. 21, p. 3339, 1989.
[6] K. Aihara and S. Kanbara, The Sumitomo Search, Vol. 42, p. 1, 1990.
[7] S. E. Nam and D. Y. Lee, J. Mat. Sci., Vol. 22, p. 2319, 1987.