Search results for: Vanchai Laemlaksakul

Authors: Vanchai Laemlaksakul, Sompoap Talabgaew

Abstract:

This research studied the appropriate factors and conditions for laminated bamboo bending by Design of Experiments (DOE). The interested factors affecting the spring back in laminates bamboo were (1) time, (2) thickness, and (3) frequency. This experiment tested the specimen by using high frequency machine and measured its spring back immediately and next 24 hours for comparing the spring back ratio. Results from the experiments showed that significant factors having major influence to bending of laminates bamboo were thickness and frequency. The appropriate conditions of thickness and frequency were 4 mm. and 1.5 respectively.

Keywords: Bamboo, bending, spring back, design of experiments.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1788

Authors: Vanchai Laemlaksakul

Abstract:

This research was to evaluate a technical feasibility of making single-layer experimental particleboard panels from bamboo waste (Dendrocalamus asper Backer) by converting bamboo into strips, which are used to make laminated bamboo furniture. Variable factors were density (600, 700 and 800 kg/m3) and temperature of condition (25, 40 and 55 °C). The experimental panels were tested for their physical and mechanical properties including modulus of elasticity (MOE), modulus of rupture (MOR), internal bonding strength (IB), screw holding strength (SH) and thickness swelling values according to the procedures defined by Japanese Industrial Standard (JIS). The test result of mechanical properties showed that the MOR, MOE and IB values were not in the set criteria, except the MOR values at the density of 700 kg/m3 at 25 °C and at the density of 800 kg/m3 at 25 and 40 °C, the IB values at the density of 600 kg/m3, at 40 °C, and at the density of 800 kg/m3 at 55 °C. The SH values had the test result according to the set standard, except with the density of 600 kg/m3, at 40 and 55 °C. Conclusively, a valuable renewable biomass, bamboo waste could be used to manufacture boards.

Keywords: Particleboard, Urea Formaldehyde Resin, BambooWaste

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 5645

Authors: Sittichai Kaewkuekool, Vanchai Laemlaksakul

Abstract:

At the present, auto part industries have become higher challenge in strategy market. As this consequence, manufacturers need to have better response to customers in terms of quality, cost, and delivery time. Moreover, they need to have a good management in factory to comply with international standard maximum capacity and lower cost. This would lead companies to have to order standard part from aboard and become the major cost of inventory. The development of auto part research by recycling materials experiment is to compare the auto parts from recycle materials to international auto parts (CKD). Factors studied in this research were the recycle material ratios of PU-foam, felt, and fabric. Results of recycling materials were considered in terms of qualities and properties on the parameters such as weight, sound absorption, water absorption, tensile strength, elongation, and heat resistance with the CKD. The results were showed that recycling materials would be used to replace for the CKD.

Keywords: International auto parts, recycling materials.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2074

Authors: S. Talabgaew, V. Laemlaksakul

Abstract:

A new generation product made from bamboo strips, known as laminated bamboo, has gained importance. The objective of this research was to experiment the effect of three factors on the mechanical property of laminated bamboo. The interested factors for experimental design were (A) four bamboo species, namely Bambusa blumeana Schultes (Pai See Suk), Dendrocalamus asper Backer (Pai Tong), Dendrocalamus hamiltonii Nees (Pai Hok) and Dendrocalamus sericeus Munro (Pai Sang Mon), (B) two types of glue adhesive, polyvinyl acetate emulsion (PVAC) fortified with urea-formaldehyde (UF) and urea-formaldehyde (UF) to make parallel-oriented bamboo strips laminates and (C) glue weight per strip area, 150 g/m2 and 190 g/m2. Experimental results showed that Dendrocalamus asper Backer (Pai Tong) and Dendrocalamus sericeus Munro (Pai Sang Mon) were best used for manufacturing due to their highest MOR and MOE. The amount of glue weight 150 g/m2 yielded higher MOR and MOE than the amount of glue weight 190 g/m2. At the conclusion, the laminated bamboo manufacturers can benefit from this research in order to select right materials according to strength, cost and accessibility.

Keywords: Laminated Bamboo, Mechanical Property, 3-WayANOVA.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2093