Search results for: Yassir M. Abbas

Authors: Ibtisam A. Abbas Al-Darkazly

Abstract:

In this study, the mechanical properties of alginate hydrogel material for self-standing 3D scaffold architecture with proper shape fidelity are investigated. In-lab built 3D bio-printer extrusion-based technology is utilized to fabricate 3D alginate scaffold constructs. The pressure, needle speed and stage speed are varied using a computer-controlled system. The experimental result indicates that the concentration of alginate solution, calcium chloride (CaCl₂) cross-linking concentration and cross-linking ratios lead to the formation of alginate hydrogel with various gelation states. Besides, the gelling conditions, such as cross-linking reaction time and temperature also have a significant effect on the mechanical properties of alginate hydrogel. Various experimental tests such as the material gelation, the material spreading and the printability test for filament collapse as well as the swelling test were conducted to evaluate the fabricated 3D scaffold constructs. The result indicates that the fabricated 3D scaffold from composition of 3.5% wt alginate solution, that is prepared in DI water and 1% wt CaCl₂ solution with cross-linking ratios of 7:3 show good printability and sustain good shape fidelity for more than 20 days, compared to alginate hydrogel that is prepared in a phosphate buffered saline (PBS). The fabricated self-standing 3D scaffold constructs measured 30 mm × 30 mm and consisted of 4 layers (n = 4) show good pore geometry and clear grid structure after printing. In addition, the percentage change of swelling degree exhibits high swelling capability with respect to time. The swelling test shows that the geometry of 3D alginate-scaffold construct and of the macro-pore are rarely changed, which indicates the capability of holding the shape fidelity during the incubation period. This study demonstrated that the mechanical and physical properties of alginate hydrogel could be tuned for a 3D bio-printing extrusion-based system to fabricate self-standing 3D scaffold soft structures. This 3D bioengineered scaffold provides a natural microenvironment present in the extracellular matrix of the tissue, which could be seeded with the biological cells to generate the desired 3D live tissue model for in vitro and in vivo tissue engineering applications.

Keywords: Biomaterial, calcium chloride, 3D bio-printing, extrusion, scaffold, sodium alginate, tissue engineering.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 774

Authors: Muhammad Fiaz, Baseerat Rizwan, Naqvi Najam Abbas, Yang Naiding

Abstract:

The aspiration of this research article is to target and focus the gains of university-Industry (U-I) collaborations and exploring those hurdles which are the obstacles for attaining these gains. University-Industry collaborations have attained great importance since 1980 in USA due to its application in all fields of life. U-I collaboration is a bilateral process where academia is a proactive member to make such alliances. Universities want to ameliorate their academic-base with the technicalities of technobabbles. U-I collaboration is becoming an essential lane for achieving innovative goals in this century. Many developed nations have set successful examples to prove this phenomenon as a catalyst to reduce costs, efforts and personnel for R&D projects. This study is exploits amplitudes of UI collaboration incentives in the light of success stories of developed countries. Many universities in USA, UK, Canada and various European Countries have been engaged with enterprises for numerous collaborative agreements. A long list of strategic and short term R&D projects has been executed in developed countries to accomplish their intended purposes. Due to the lack of intentions, genuine research and research-oriented environment, the mentioned field could not grow very well in developing countries. During last decade, a new wave of research has induced the institutes of developing countries to promote R&D culture especially in Pakistan. Higher Education Commission (HEC) has initiated many projects and funding supports for universities which have collaborative intentions with industry. Findings show that rapid innovation, overwhelm the technological complexities and articulated intellectual-base are major incentives which steer both partners to establish faculty-industry alliances. Everchanging technologies, concerned about intellectual property, different research environment and culture, research relevancy (Basic or applied), exposure differences and diversity of knowledge (bookish or practical) are main barriers to establish and retain joint ventures. Findings also concluded that, it is dire need to support and enhance cooperation among academia and industry to promote highly coordinated research behaviors. Author has proposed a roadmap for developing countries to promote R&D clusters among faculty and industry to deal the technological challenges and innovation complexities. Based on our research findings, Model for R&D Collaboration for developing countries also have been proposed to promote articulated R&D environment. If developing countries follow this phenomenon, rapid innovations can be achieved with limited R&D budget heads.

Keywords: University-Industry Collaboration, Academia, Innovation, R&D Barriers

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1872