Search results for: Nedjemeddine Bounar

Authors: Bounar Nedjemeddine

Abstract:

Materials with the pyrochlore lattice structure have attracted much recent attention due to their wide applications in ceramic thermal barrier coatings, high-permittivity dielectrics, and potential solid electrolytes in solid-oxide fuel cells. The work described in this paper is devoted to the synthesis and characterization of a pyrochlore structure based on lanthanum (La₂O₃) and tin (SnO₂) oxides of general formula La₂Sn₂O₇, substituted by Sr at the site La. Their structures were determined from X-ray powder diffraction using CELFER analysis. All the compositions present the space group Fd-3m. The substitution of La by Sr in the La₂Sn₂O₇ compound causes a variation of the cell parameters. The difference in charge between La³⁺ and Sr²⁺ and the difference in size cause the cell parameters to decrease from a=10.7165 A° to a=10.6848 A° for the substitution rates (x = 0.05, 0.1, 0.15 ...), which leads to a decrease in the volume of the mesh. For a substitution rate x = 0.25, there is an increase in the cell parameters (a=10.7035A°), which can be explained by a competitiveness of the size effect and the presence of a gap in the structure which go in the opposite direction.

Keywords: solid-oxide fuel cells, structure, pyrochlore, X-ray diffraction

Procedia PDF Downloads 127

Authors: Fatima Melit, Nedjemeddine Bounar

Abstract:

Polycrystalline samples of Ce1-xMxO2-δ (x=0.1, 0.15, 0.2)(M=Gd, Y) were prepared by solid-state chemical reaction from mixtures of pre-dried oxides powders of CeO2, Gd2O3 and Y2O3 in the appropriate stoichiometric ratio to explore their use as solid electrolytes for intermediate temperature solid oxide fuel cells (IT-SOFCs). Their crystal structures and ionic conductivities were characterised by X-ray powder diffraction (XRD) and AC complex impedance spectroscopy (EIS). The XRD analyses confirm that all the resulting synthesised co-doped cerium oxide powders are single-phase and crystallise in the cubic structure system with the space group Fm3m. On the one hand, the lattice parameter (a ) of the phases increases with increasing Gd content; on the other hand, with increasing Y-substitution rate, the latter decreases. The results of complex impedance conductivity measurements have shown that doping has a remarkable effect on conductivity. The co-doped cerium phases showed significant ionic conductivity values, making these materials excellent candidates for solid oxide electrolytes at intermediate temperatures.

Keywords: electrolyte, Ceria, X-ray diffraction, EIS, SEM, SOFC

Procedia PDF Downloads 144