Wear Behavior of Commercial Aluminium Engine Block and Piston under Dry Sliding Condition

Authors: M. S. Kaiser, Swagata Dutta

Abstract:

In the present work, the effect of load and sliding distance on the performance tribology of commercially used aluminium-silicon engine block and piston was evaluated at ambient conditions with humidity of 80% under dry sliding conditions using a pin-on-disc with two different loads of 5N and 20N yielding applied pressure of 0.30MPa and 1.4MPa, respectively, at sliding velocity of 0.29ms-1 and with varying sliding distance ranging from 260m- 4200m. Factors and conditions that had significant effect were identified. The results showed that the load and the sliding distance affect the wear rate of the alloys and the wear rate increased with increasing load for both the alloys. Wear rate also increases almost linearly at low loads and increase to a maximum then attain a plateau with increasing sliding distance. For both applied loads the piston alloy showed the better performance due to higher Ni and Mg content. The worn surface and wear debris was characterized by optical microscope, SEM and EDX analyzer. The worn surface was characterized by surface with shallow grooves at loads while the groove width and depth increased as the loads increases. Oxidative wear was found to be the predominant mechanisms in the dry sliding of Al-Si alloys at low loads.

Keywords: Wear, friction, gravimetric analysis, aluminiumsilicon alloys, SEM, EDX.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1096765

References:

[1] A. Mazahery and M. O. Shabanih, “Microstructural and abrasive wear properties of SiC reinforced aluminum-based composite produced by compocasting”, Trans. Nonferrous Met. Soc. China, 2013, 23, 1905- 1914.
[2] M.M. Haque and A. Sharif, “Study on wear properties of aluminium– silicon piston alloy”, Journal of Materials Processing Technology, 2001, 118, 69-73.
[3] A. D. Sarkar and J. Clarke, “Friction and wear of aluminium-silicon alloys”, Journal of Wear, 1980, 61(1-2), 157-167.
[4] M. M. Maru and D. K. Tanaka, “Influence of loading, contamination and additive on the wear of a metallic pair under rotating and reciprocating lubricated sliding”, J. Braz. Soc. Mech. Sci. & Eng., 2006, 28(3), 278- 285.
[5] H. Liao, Y. Sun and G. Sun, “Correlation between mechanical properties and amount of dendritic α-Al phase in as-cast near-eutecticAl-11.6%Si alloys modified with strontium”, Materials Scienceand Engineering A, 2002, 335(1-2): 62-66.
[6] R. Kilaas, V. Radmil, “Structure determination and structurerefinement of Al2CuMg precipitates by quantitative high-resolutionelectron microscopy”, Journal of Ultramicroscopy, 2001, 88(1), 63−72.
[7] L. Lasa, J. M. Rodrigues-Ibade, “Wear behaviour of eutectic andhypereutectic Al-Si-Cu-Mg casting alloys tested against a composite brake pad”, Materials Science and Engineering A, 2003, 363(1-2),193-202
[8] Z. Muzaffer, K. Erdem and G. Serap, “Influence of Cu addition on microstructure and hardness of near-eutectic Al-Si- xCu-alloys”, Trans. Nonferrous Met. Soc. China, 2011, 21, 1698-1702.
[9] J. Clarke and A. D. Sarkar, “Wear characteristics of as-cast binary aluminium-silicon alloys”, Journal of Wear, 1979, 54(1), 7-16.
[10] R. L. Deuis, C. Subramonian and J. M. Yellup, “Dry sliding wear of aluminium composites- a review”, Journal of composites science and technology, 1996, 57, 415-435.
[11] R. L. Deuis, C. Subramonian and J. M. Yellup, “Reviews on the Influences of Alloying elements on the Microstructure and Mechanical Properties of Aluminum Alloys and Aluminum Alloy Composites”, International Journal of Scientific and Research Publications, 2012, 2(6), 1-7.