Effect of Processing Methods on Texture Evolution in AZ31 Mg Alloy Sheet

Authors: Tae Kwon Ha, Jung-Ho Moon

Abstract:

Textures of AZ31 Mg alloy sheets were evaluated by using neutron diffraction method in this study. The AZ31 sheets were fabricated either by conventional casting and subsequent hot rolling or strip casting. The effect of warm rolling was investigated using the AZ31 Mg alloy sheet produced by conventional casting. Warm rolling of 30% thickness reduction per pass was possible without any side-crack at temperatures as low as 200oC under the roll speed of 30 m/min. The initial microstructure of conventionally cast specimen was found to be partially recrystallized structures. Grain refinement was found to occur actively during the warm rolling. The (0002),(10-10) (10-11),and (10-12) complete pole figures were measured using the HANARO FCD (Neutron Four Circle Diffractometer) and ODF were calculated. The major texture of all specimens can be expressed by ND//(0001) fiber texture. Texture of hot rolled specimen showed the strongest fiber component, while that of strip cast sheet seemed to be similar to random distribution.

Keywords: Texture, Neutron Diffraction, Mg alloy, warm rolling, Pole figure, ODF

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1088346

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1818

References:


[1] R. E. Brown, Proceedings of 59th Annual World Magnesium Conference, Inter. Magnesium Association, VA, USA, p. 25, 2002.
[2] S. S. Park, Y. S. Park, and N. J. Kim,Met. Mater. Int., vol. 8, p. 551, 2002.
[3] L. Chabbi, W. Lehnert, and R. Kawalla,“Magnesium Alloys and Their Applications,” Ed. K. U. Kainer., Wiley-VCH-Verlag, Weinheim, p. 590, 2000.
[4] M. Avedesian and H. Baker, ASM Specialty Handbook, “Magnesium and Magnesium Alloys”, ASM International, 1999.