Ductile Crack Growth in Surface Cracked Pressure Vessels

Authors: Osama A. Terfas, Abdusalam A. Alaktiwi

Abstract:

Pressure vessels are usually operating at temperatures where the conditions of linear elastic fracture mechanics are no longer met because massive plasticity precedes crack propagation. In this work the development of a surface crack in a pressure vessel subject to bending and tension under elastic-plastic fracture mechanics conditions was investigated. Finite element analysis was used to evaluate the hydrostatic stress, the J-integral and crack growth for semi-elliptical surface-breaking cracks. The results showed non-uniform stress triaxiality and crack driving force around the crack front at large deformation levels. Different ductile crack extensions were observed which emphasis the dependent of ductile tearing on crack geometry and type of loading. In bending the crack grew only beneath the surface, and growth was suppressed at the deepest segment. This contrasts to tension where the crack breaks through the thickness with uniform growth along the entire crack front except at the free surface. Current investigations showed that the crack growth developed under linear elastic fracture mechanics conditions will no longer be applicable under ductile tearing scenarios.

Keywords: Bending, ductile tearing, fracture toughness, stress triaxiality, tension.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1075641

References:

[1] W. Brocks, H. Krafka, G. Kunecke, and K. Wobst, "Ductile crack growth of semi-elliptical surface flaws in pressure vessels,". International Journal of Pressure Vessels and Piping, vol. 43, pp. 301- 316, 1990.
[2] B. Bricksatd, and I. Sattari-Far, "Crack shape development for LBB applications,". Engineering Fracture Mechanics, vol. 67, pp. 625-646, 2000.
[3] L. Hodulak, H. Kordisch, S. Kunzelmann, and E. Sommer, "Influence of the load level on the development of part-through cracks,". International Journal of Fracture, vol. 14, 1978.
[4] J. C. JR. Newman, and I. S. Raju, "An empirical stress-intensity factor equation for the surface crack," Engineering fracture mechanics, vol. 15, pp. 185-192, 1981.
[5] A. Carpinteri, "Shape change of surface cracks in round bars under cyclic axial loading,". International Journal of Fatigue, vol. 15, pp. 21- 26, 1993.
[6] X. B. Lin, and R. A. Smith, "Shape evolution of surface cracks in fatigued round bars with a semicircular circumferential notch,". International Journal of Fatigue, vol. 21, pp. 965-973, 1999.
[7] X. B. Lin, and R. A Smith, "Finite element modelling of fatigue crack growth of surface cracked plates, Part II: Crack shape change,". Engineering Fracture Mechanics, vol. 63, pp. 523-540, 1999.
[8] P. M. Scott, and T. W. Thorpe, "A critical review of crack tip stress intensity factors for semi-elliptic cracks,". Fatigue of Engineering Materials and Structures, vol. 4, pp. 291-309, 1981.
[9] Y. Chen, and S. Lambert, "Numerical modelling of ductile tearing for semi-elliptical surface cracks in wide plates,". International Journal of Pressure Vessels and Piping, vol. 82, pp. 417-426, 2005.
[10] O. Terfas, "The effect of stress biaxiality on crack shape development,". Proceedings of WASET 2012 International conference on materials science and engineering, August 22-23, 2012, Paris, France. 68, pp. 1644-1649.
[11] J. W. Hancock, W. G. Reuter, and D. M. Parks, "Constraint and toughness parameterised by T". "Constraint effect in fracture". ASTM STP 1171. Philadelphia, pp. 21-40, 1993.
[12] N. P. O-Dowd, and C. F. Shih, "Family of crack-tip fields characterised by a triaxiality parameter-1". Structure of fields. Journal of Mechanics and Physics of Solids, vol. 39, pp. 989-1015, 1991.
[13] N. P. O-Dowd, and C. F. Shih, "Family of crack-tip fields characterised by a triaxiality parameter-2". Fracture applications. Journal of Mechanics and Physics of Solids, vol. 40, pp. 939-963, 1992.
[14] X. Gao, J. Faleskog, C. F. Shih, and R. H. Dodds, "Ductile tearing in part-through cracks: Experiments and cell-model predictions". Engineering Fracture Mechanics, vol. 59, pp. 761-777, 1998.