Post Elevated Temperature Effect on the Strength and Microstructure of Thin High Performance Cementitious Composites (THPCC)

Authors: A. Q. Sobia, A. Shyzleen, M. S. Hamidah, I. Azmi, S. F. A. Rafeeqi, S. Ahmad

Abstract:

Reinforced Concrete (RC) structures strengthened with fiber reinforced polymer (FRP) lack in thermal resistance under elevated temperatures in the event of fire. This phenomenon led to the lining of strengthened concrete with thin high performance cementitious composites (THPCC) to protect the substrate against elevated temperature. Elevated temperature effects on THPCC, based on different cementitious materials have been studied in the past but high-alumina cement (HAC)-based THPCC have not been well characterized. This research study will focus on the THPCC based on HAC replaced by 60%, 70%, 80% and 85% of ground granulated blast furnace slag (GGBS). Samples were evaluated by the measurement of their mechanical strength (28 & 56 days of curing) after exposed to 400°C, 600°C and 28°C of room temperature for comparison and corroborated by their microstructure study. Results showed that among all mixtures, the mix containing only HAC showed the highest compressive strength after exposed to 600°C as compared to other mixtures. However, the tensile strength of THPCC made of HAC and 60% GGBS content was comparable to the THPCC with HAC only after exposed to 600°C. Field emission scanning electron microscopy (FESEM) images of THPCC accompanying Energy Dispersive X-ray (EDX) microanalysis revealed that the microstructure deteriorated considerably after exposure to elevated temperatures which led to the decrease in mechanical strength.

Keywords: Ground granulated blast furnace slag, high aluminacement, microstructure at elevated temperature and residual strength.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1074563

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2295

References:


[1] V. Kodur, F. Cheng, and T. Wang, "Effect of strength and fiber reinforcement on fire resistance of high-strength concrete columns," Journal of Structural Engineering, vol. 129, no. 2, pp. 253-259, 2003.
[2] S. Qazi, M. S. Hamidah, A. Ibrahim, S.F.A. Rafeeqi and S. Ahmad, "State-of-the-art review- behaviour of thin high performance cementitious composites (THPCC) at elevated temperatures," in 11th International Conference on Concrete Engineering and Technology 2012 (CONCET-2012), 2012, pp. 83-89.
[3] L. Sarvaranta and E. Mikkola, "Fibre mortar composites under fire conditions: effects of ageing and moisture content of specimens," Materials and Structures, pp. 532-538, 1994.
[4] M. M. Shoaib, S. A. Ahmed, and M. M. Balaha, "Effect of fire and cooling mode on the properties of slag mortars," vol. 31, pp. 1533-1538, 2001.
[5] M. S. Cülfik and T. Özturan, "Effect of elevated temperatures on the residual mechanical properties of high-performance mortar," Cement and Concrete Research, vol. 32, no. 5, pp. 809-816, 2002.
[6] C. Leiva, L. Vilches, J. Vale, and C. Fernandezpereira, "Influence of the type of ash on the fire resistance characteristics of ash-enriched mortars," Fuel, vol. 84, no. 11, pp. 1433-1439, 2005.
[7] S. Aydin and B. Baradan, "Effect of pumice and fly ash incorporation on high temperature resistance of cement based mortars," Cement and Concrete Research, vol. 37, no. 6, pp. 988-995, 2007.
[8] S. Aydin, "Development of a high-temperature-resistant mortar by using slag and pumice," Fire Safety Journal, vol. 43, no. 8, pp. 610-617, 2008.
[9] H. Wang, "The effects of elevated temperature on cement paste containing GGBFS," Cement and Concrete Composites, vol. 30, no. 10, pp. 992-999, 2008.
[10] D. Bentz, M. Peltz, A. Duran-Herrera, P. Valdez, and C. Juarez, "Thermal properties of high-volume fly ash mortars and concretes," Journal of Building Physics, vol. 34, no. 3, pp. 263-275, 2010.
[11] J. Formosa, J. M. Chimenos, A. M. Lacasta, L. Haurie, and J. R. Rosell, "Novel fire-protecting mortars formulated with magnesium byproducts," Cement and Concrete Research, vol. 41, no. 2, pp. 191-196, 2011.
[12] J. P. Won, H.-B. Kang, S.-J. Lee, and J.-W. Kang, "Eco-friendly fireproof high-strength polymer cementitious composites," Construction and Building Materials, vol. 30, pp. 406-412, May 2012.
[13] S. Djaknoun, E. Ouedraogo, and A. Ahmed Benyahia, "Characterisation of the behaviour of high performance mortar subjected to high a b c temperatures," Construction and Building Materials, vol. 28, no. 1, pp. 176-186, 2012.
[14] R. K. Ibrahim, R. Hamid, and M. R. Taha, "Fire resistance of highvolume fly ash mortars with nanosilica addition," Construction and Building Materials, vol. 36, pp. 779-786, Nov. 2012.
[15] ASTM. Standard practice for mechanical mixing of hydraulic cement pastes and mortars of plastic consistency ASTM C305-11. West Conshocken (PA): ASTM International; 2011
[16] A. Ahmed, "Behavior of FRP-strengthened reinforced concrete beams under fire conditions," Michigan State University, Michigan, USA, 2010.
[17] ASTM. Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens ASTM C39/C39M-10. West Conshocken (PA): ASTM International; 2010
[18] ASTM. Standard Test Method for splitting tensile strength of cylindrical concrete specimens ASTM C496/C496M-11. West Conshocken (PA): ASTM International; 2011
[19] Y. Fu, F. Ding, and J. Beaudoin, "Temperature dependence of compressive strength of conversion-inhibited high alumina cement concrete," ACI materials journal, vol. 94, no. 6, pp. 540-544, 1997.
[20] S. Diamond, "Reply to the discussion by S. Chatterji of the paper "Hydration of C12A7 and Granulated Blast furnace Slag," Cement and Concrete Research, vol. 31, no. 11, p. 1655, Nov. 2001.
[21] A. Majumdar, B. Singh, and R. Edmonds, "Hydration of mixtures of C12A7 and granulated blastfurnace slag," Cement and Concrete Research, vol. 19, pp. 848-856, 1989.
[22] S. Martinović, M. Vlahović, J. Majstorović, and B. Matović, "Thermal and mechanical properties of high alumina low cement castable," Metall. Mater. Eng., vol. 18, no. 1, pp. 53-65, 2011.
[23] H. G. Midgley and A. Midgley, "Conversion of high alumina cement," Magazine of Concrete Research, vol. 27, no. 91, pp. 59-77, 1975.
[24] N. Ukrainczyk, J. ┼áipu┼íić, P. Dabić, T. Matusinović, , "Microcalorimetric study on calcium aluminate cement hydration," in International conference on Materials, processes, friction and wear- MATRIB-08, 2008, pp. 382-388.
[25] D. Madej, J. Szczerba, W. Nocuń-Wczelik, and R. Gajerski, "Hydration of Ca7ZrAl6O18 phase," Ceramics International, vol. 38, no. 5, pp. 3821-3827, Jul. 2012.
[26] P. Myers, "Calcium Aluminate Hydrates - Phases and Structure of Calcium Aluminate Hydrates," 2002.
[27] A. J. Majumdar, B. Singh, and R. N. Edmonds, "Hydration of mixtures of ÔÇÿciment fondu- aluminous cement and granulated blast furnace slag," Cement and Concrete Research, vol. 20, no. 2, pp. 197-208, 1990.