Effect of Aging Treatment on Mechanical Properties of Non-Flammable AZ91D Mg Alloy
Authors: Ju Hyun Won, Hyun Woo Lee, Seok Hong Min, Tae Kwon Ha
Abstract:
Microstructure and mechanical properties of AZ91D Mg alloys for nonflammable use, containing Ca and Y, were investigated in this study. Solid solution treatment of AZ91D Mg alloy with Ca and Y was successfully conducted at 420oC and supersaturated microstructure with almost all beta phases resolved into matrix was obtained. After solid solution treatment, the alloy was annealed at temperatures of 180 and 200oC for time intervals from 1 min to 48 hrs and hardness of each condition was measured by micro-Vickers method. Peak aging conditions were deduced from the results as at the temperature of 200oC for 10 hrs. Hot rolling was also carried out at 400oC by the reduction ratio of 0.6 through 5 passes followed by recrystallization treatment. Tensile and compressive properties were measured at room temperature on the specimens of each process, i.e. as-cast, solution treatment, hot rolling, and recrystallization.Keywords: Mg alloy, AZ91D, nonflammable alloy, hot rolling, peak aging, tensile test.
Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1338614
Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1563References:
[1] B. L. Mordike and T. Ebert, Mater. Sci. Eng. A, vol. 302, p. 37, 2001.
[2] X. Cui, H. Liu, J. Meng, and D. Zhang, Trans. Nonferr. Met. Soc. Of China, vol. 20, p. 435, 2010.
[3] F. Guo, P, Li, X. Gao, and J. Xu, J. Rare Earth, vol. 28, p. 948, 2010.
[4] M. O. Pekguleryuz, and E. Baril, Mater. Trans., vol. 42, p. 1258, 2001.
[5] B. R. Powell, A. A. Lou, V. Rezhets, J. J. Bommarito, and B. L. Tiwari, SAE Tech. Paper 2001-01-0422, Soc. Automotive Eng., p. 406, 2001.
[6] G. Wu, F. Yu, H. Gao, C. Zhai, and Y. P. Zhu, Mater. Sci. Eng. A, vol. 408, p. 255, 2005.
[7] X. Q. Zheng, Q. D. Wang, Y. Z. Lu, W. J. Ding, C. Lu, Y. P. Zhu, C. Q. Zhai, and X. P. Xu, Scripta Mater., vol. 43, p. 403, 2003.
[8] B. S. You, W. W. Park, and L. S. Chung, Scripta Mater., vol. 42, p. 403, 2002.
[9] T. S. shih, J.-H. Wang, and K.-Z. Chong, Mater. Chem. & Phys., vol. 85, p. 302, 2004.