Authors: Gbenga M. Ayininuola, Olasunkanmi A. Adekitan

Abstract:

Calcined kaolinite clay (CKC) is a pozzolanic material that is current drawing research attention. This work investigates the conditions for the best performance of a CKC from a kaolinite clay source in Ajebo, Abeokuta (southwest Nigeria) known for its commercial availability. Samples from this source were subjected to X-ray diffractometry (XRD) and differential scanning calorimetry (DSC). XRD shows that kaolinite is the main mineral in the clay source. This mineral is responsible for the pozzolanic behavior of CKC. DSC indicates that the transformation from the clay to CKC occurred between 550 and 750 ^oC. Using this temperature range, clay samples were milled and different CKC samples were produced in an electric muffle furnace using temperatures of 550, 600, 650, 700, 750 and 800 ^oC respectively for 1 hour each. This was also repeated for 2 hours. The degree of de-hydroxylation (d_tg) and strength activity index (SAI) were also determined for each of the CKC samples. The d_tg and SAI tests were repeated two more times for each sample and averages were taken. Results showed that peak d_tg occurred at 750 ^oC for 1 hour calcining combination (94.27%) whereas marginal differences were recorded at some lower temperatures (90.97% for 650 ^oC for 2 hours; 91.05% for 700 ^oC for 1 hour and 92.77% for 700 ^oC for 2 hours). Optimum SAI was reported at 700 ^oC for 1 hour (99.05%). Rating SAI as a better parameter than d_tg, 700 ^oC for 1 hour combination was adopted as the best calcining condition. The paper recommends the adoption of this clay source for pozzolan production by adopting the calcining conditions established in this work.

Keywords: Calcined kaolinite clay, calcination, optimum-calcining conditions, pozzolanity.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1316