Abstract:

A new SUZ-4 zeolite membrane with tetraethlyammonium hydroxide as the template was fabricated on mullite tube via hydrothermal sol-gel synthesis in a rotating autoclave reactor. The suitable synthesis condition was SiO2:Al2O3 ratio of 21.2 for 4 days at 155 °C crystallization under autogenous pressure. The obtained SUZ-4 possessed a high BET surface area of 396.4 m2/g, total pore volume at 2.611 cm3/g, and narrow pore size distribution with 97 nm mean diameter and 760 nm long of needle crystal shape. The SUZ-4 layer obtained from seeding crystallization was thicker than that of without seeds or in situ crystallization.

Keywords: Membrane, seeding, sol-gel, SUZ-4 Zeolite.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1992

Authors: Patcharin Worathanakul, Wisaroot Payubnop, Akhapon Muangpet

Abstract:

Utilization of bagasse ash for silica sources is one of the most common application for agricultural wastes and valuable biomass byproducts in sugar milling. The high percentage silica content from bagasse ash was used as silica source for sodium silicate solution. Different heating temperature, time and acid treatment were studies for silica extraction. The silica was characterized using various techniques including X-ray fluorescence, X-ray diffraction, Scanning electron microscopy, and Fourier Transform Infrared Spectroscopy method,. The synthesis conditions were optimized to obtain the bagasse ash with the maximum silica content. The silica content of 91.57 percent was achieved from heating of bagasse ash at 600°C for 3 hours under oxygen feeding and HCl treatment. The result can be used as value added for bagasse ash utilization and minimize the environmental impact of disposal problems.

Keywords: Bagasse ash, synthesis, silica, extraction, posttreatment