%0 Journal Article
	%A P. Worathanakul and  P. Kongkachuichay
	%D 2008
	%J International Journal of Chemical and Molecular Engineering
	%B World Academy of Science, Engineering and Technology
	%I Open Science Index 23, 2008
	%T New SUZ-4 Zeolite Membrane from Sol-Gel Technique
	%U https://publications.waset.org/pdf/9754
	%V 23
	%X A new SUZ-4 zeolite membrane with
tetraethlyammonium hydroxide as the template was fabricated on
mullite tube via hydrothermal sol-gel synthesis in a rotating
autoclave reactor. The suitable synthesis condition was SiO2:Al2O3
ratio of 21.2 for 4 days at 155 °C crystallization under autogenous
pressure. The obtained SUZ-4 possessed a high BET surface area of
396.4 m2/g, total pore volume at 2.611 cm3/g, and narrow pore size
distribution with 97 nm mean diameter and 760 nm long of needle
crystal shape. The SUZ-4 layer obtained from seeding crystallization
was thicker than that of without seeds or in situ crystallization.
	%P 332 - 336