Search results for: M. Stalin

Authors: Zhalmagambetov Yerlanbek, Assymova Dariya, Tashieva Saltanat, and Aliya Bolatkhan

Abstract:

The relevance of the study of everyday life in Almaty and Kyzylorda are associated with the emergence of the modern trends in historiography and socializing areas of government reform. The relevance is due to the fact that in the early twentieth century Kyzylorda and Almaty began to develop as a city and this period has a special place in the life of the state. An interesting aspect of the everyday life of the inhabitants of the new city, which was built in the era of Stalin's Five-Year Plans, can be examined through the eyes of the Soviet people living in a specific environment, reflecting the life of the citizens. The study of industrialization of the Soviet Union and the attention paid to new developments in the first five years of everyday aspects as the impact of the modernization of the 1930s was one of the decisive factors in the lives of residents. Among these factors, we would like to highlight the medical field, which is the basis of all human life, specifically focusing on the state of medicine in Alma-Ata in the first 20-30-years of the twentieth century, and analyze the different aspects of human life, determining the quality of medical care to the population during this period.

Keywords: Alma Ata, capital, epidemic diseases, health care, Kyzylorda, the USSR, Vernyj.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1505

Authors: A. Udayakumar, M. Rizvan Basha, M. Stalin, V.V Bhanu Prasad

Abstract:

Three dimensional non-Interlaced carbon fibre reinforced silicon carbide (3-D-Cf/SiC) composites with pyrocarbon interphase were fabricated using isothermal chemical vapor infiltration (ICVI) combined with polymer impregnation pyrolysis (PIP) process. Polysilazane (PSZ) is used as a preceramic polymer to obtain silicon carbide matrix. Thermo gravimetric analysis (TGA), Infrared spectroscopic analysis (IR) and X-ray diffraction (XRD) analysis were carried out on PSZ pyrolysed at different temperatures to understand the pyrolysis and obtaining the optimum pyrolysing condition to yield β-SiC phase. The density of the composites was 1.94 g cm-3 after the 3-D carbon preform was SiC infiltrated for 280 h with one intermediate polysilazane pre-ceramic PIP process. Mechanical properties of the composite materials were investigated under tensile, flexural, shear and impact loading. The values of tensile strength were 200 MPa at room temperature (RT) and 195 MPa at 500°C in air. The average RT flexural strength was 243 MPa. The lower flexural strength of these composites is because of the porosity. The fracture toughness obtained from single edge notched beam (SENB) technique was 39 MPa.m1/2. The work of fracture obtained from the load-displacement curve of SENB test was 22.8 kJ.m-2. The composites exhibited excellent impact resistance and the dynamic fracture toughness of 44.8 kJ.m-2 is achieved as determined from instrumented Charpy impact test. The shear strength of the composite was 93 MPa, which is significantly higher compared 2-D Cf/SiC composites. Microstructure evaluation of fracture surfaces revealed the signatures of fracture processes and showed good support for the higher toughness obtained.

Keywords: 3-D-Cf/SiC, charpy impact test, composites, dynamic fracture toughness, polysilazane, pyrocarbon, Interphase.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2739