Authors: Alparslan A. Balta, Hilmi Yurdakul, Orkun Tunckan, Servet Turan, Arife Yurdakul

Abstract:

Si2N2O (Sinoite) is an inorganic-based oxynitride material that reveals promising phosphor candidates for white light-emitting diodes (WLEDs). However, there is now limited knowledge to explain the synthesis of Si2N2O for this purpose. Here, to the best of authors’ knowledge, we report the first time the production of Si2N2O based phosphors by CeO2, SiO2, Si3N4 from main starting powders, and Li2O sintering additive through spark plasma sintering (SPS) route. The processing parameters, e.g., pressure, temperature, and sintering time, were optimized to reach the monophase Si2N2O containing samples. The lattice parameter, crystallite size, and amount of formation phases were characterized in detail by X-ray diffraction (XRD). Grain morphology, particle size, and distribution were analyzed by scanning and transmission electron microscopes (SEM and TEM). Cathodoluminescence (CL) in SEM and photoluminescence (PL) analyses were conducted on the samples to determine the excitation, and emission characteristics of Ce3+ activated Si2N2O. Results showed that the Si2N2O phase in a maximum 90% ratio was obtained by sintering for 15 minutes at 1650oC under 30 MPa pressure. Based on the SEM-CL and PL measurements, Ce3+: Si2N2O phosphor shows a broad emission summit between 400-700 nm that corresponds to white light. The present research was supported by TUBITAK under project number 217M667.

Keywords: cerium, oxynitride, phosphors, sinoite, Si₂N₂O

Procedia PDF Downloads 107

Authors: Alparslan A. Balta, Hilmi Yurdakul, Orkun Tunckan, Servet Turan, Arife Yurdakul

Abstract:

A silicon oxynitride (Si2N2O), the mineralogical name is “Sinoite”, reveals the outstanding physical, mechanical and thermal properties, e.g., good oxidation resistance at high temperatures, high fracture toughness with rod shape, high hardness, low theoretical density, good thermal shock resistance by low thermal expansion coefficient and high thermal conductivity. In addition, the orthorhombic crystal structure of Si2N2O allows accommodating the rare earth (RE) element atoms along the “c” axis due to existing large structural interstitial sites. Here, 0.02 to 0.12 wt. % Nd3+ doped Si2N2O samples were successfully synthesized by spark plasma sintering (SPS) method at 30MPa pressure and 1650oC temperature. Li2O was also utilized as a sintering additive to take advantage of low eutectic point during synthesizing. The specimens were characterized in detail by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and cathodoluminescence (CL) in SEM and photoluminescence (PL) spectroscopy. Based on the overall results, the Si2N2O phase was obtained above 90% by the SPS route. Furthermore, Nd3+: Si2N2O samples showed a very broad intense emission peak between 400-700 nm, which corresponds to white color. Therefore, this material can be considered as a promising candidate for white light-emitting diodes (WLEDs) purposes. This study was supported by TUBITAK under project number 217M667.

Keywords: neodymium, oxynitride, Si₂N₂O, WLEDs

Procedia PDF Downloads 138