Search results for: Yoshikazu Todaka

Authors: Frank Jaksoni Mweta, Nozomu Adachi, Yoshikazu Todaka, Hirokazu Sato, Yuta Sato, Hiromi Miura, Masakazu Kobayashi, Chihiro Watanabe, Yoshiteru Aoyagi

Abstract:

Advances in the consumption of hydrogen fuel increase demands of high strength steel pipes and storage tanks. However, high strength steels are highly sensitive to hydrogen embrittlement. Because the introduction of hydrogen into steel during the fabrication process or from the environment is unavoidable, it is essential to improve hydrogen embrittlement resistance of high strength steels through microstructural control. In the present study, the heterogeneous nanostructure with a tensile strength of about 1.8 GPa and the homogeneous nanostructure with a tensile strength of about 2.0 GPa of 316LN steels were generated after 92% heavy cold rolling and high-pressure torsion straining, respectively. The heterogeneous nanostructure is composed of twin domains, shear bands, and lamellar grains. The homogeneous nanostructure is composed of uniformly distributed ultrafine nanograins. The influence of heterogeneous and homogenous nanostructures on the hydrogen embrittlement resistance was investigated. The specimen for each nanostructure was electrochemically charged with hydrogen for 3, 6, 12, and 24 hours, respectively. Under the same hydrogen charging time, both nanostructures show almost the same concentration of the diffusible hydrogen based on the thermal desorption analysis. The tensile properties of the homogenous nanostructure were severely affected by the diffusible hydrogen. However, the diffusible hydrogen shows less impact on the tensile properties of the heterogeneous nanostructure. The difference in embrittlement behavior between the heterogeneous and homogeneous nanostructures was elucidated based on the mechanism of the cracks' growth observed in the tensile fractography. The hydrogen embrittlement was suppressed in the heterogeneous nanostructure because the twin domain became an obstacle for crack growth. The homogeneous nanostructure was not consisting an obstacle such as a twin domain; thus, the crack growth resistance was low in this nanostructure.

Keywords: diffusible hydrogen, heterogeneous nanostructure, homogeneous nanostructure, hydrogen embrittlement

Procedia PDF Downloads 122

Authors: Santhita Tungkajiwangkoon, Yoshikazu Hoshi

Abstract:

Three Japaneses Drosera species are the good model to study genome organization with highly specialized morphological group for insect trapping, and has revealed anti-inflammatory, and antibacterial effects, so there must be a reason for botanists are so appealing in these plants. Cytology and Flow cytometry were used to investigate the genetic stability and ploidy estimation in three related species. The cytological and Flow cytometry analysis were done in Drosera rotundifolia L., Drosera spatulata Labill and Drosera tokaiensis. The cytological studies by fluorescence staining (DAPI) showed that D. tokaiensis was an alloploid (2n=6x=60, hexaploid) which is a natural hybrid polyploids of D. rotundifolia and D. spatulata. D. rotundifolia was a diploid with the middle size of metaphase chromosomes (2n=2x=20) as a paternal origin and D. spatulata was a tetraploid with small size of metaphase chromosome (2n=4x=40) as a maternal origin. We confirmed by Flow cytometry analysis to determine the ploidy level and DNA content of the plants. The 2C-DNA values of D. rotundiflolia were 2.8 pg, D. spatulata was 1.6 pg and D. tokaiensis was 3.9 pg. However, 2C- DNA values of D. tokaiensis should be related from their parents but in the present study the 2C-DNA values of D. tokaiensis was no relation from the theoretical of hybrids representing additive parental. Possibility of D. tokaiensis is a natural hybrid, which is also hybridization in natural evolution can cause the genome reduction in plant.

Keywords: drosera, hybrid, cytology, flow cytometry

Procedia PDF Downloads 382