The Effect of Iron Deficiency on the Magnetic Properties of Ca₀.₅La₀.₅Fe₁₂₋yO₁₉₋δ M-Type Hexaferrites

Authors: Kang-Hyuk Lee, Wei Yan, Sang-Im Yoo

Abstract:

Recently, Ca₁₋ₓLaₓFe₁₂O₁₉ (Ca-La M-type) hexaferrites have been reported to possess higher crystalline anisotropy compared with SrFe₁₂O₁₉ (Sr M-type) hexaferrite without reducing its saturation magnetization (Ms), resulting in higher coercivity (Hc). While iron deficiency is known to be helpful for the growth and the formation of NiZn spinel ferrites, the effect of iron deficiency in Ca-La M-type hexaferrites has never been reported yet. In this study, therefore, we tried to investigate the effect of iron deficiency on the magnetic properties of Ca₀.₅La₀.₅Fe₁₂₋yO₁₉₋δ hexaferrites prepared by solid state reaction. As-calcined powder was pressed into pellets and sintered at 1275~1325℃ for 4 h in air. Samples were characterized by powder X-ray diffraction (XRD), vibrating sample magnetometer (VSM), and scanning electron microscope (SEM). Powder XRD analyses revealed that Ca₀.₅La₀.₅Fe₁₂₋yO₁₉₋δ (0.75 ≦ y ≦ 2.15) ferrites calcined at 1250-1300℃ for 12 h in air were composed of single phase without the second phases. With increasing the iron deficiency, y, the lattice parameters a, c and unite cell volumes were decreased first up to y=10.25 and then increased again. The highest Ms value of 77.5 emu/g was obtainable from the sample of Ca₀.₅La₀.₅Fe₁₂₋yO₁₉₋δ sintered at 1300℃ for 4 h in air. Detailed microstructures and magnetic properties of Ca-La M-type hexagonal ferrites will be presented for a discussion

Keywords: Ca-La M-type hexaferrite, magnetic properties, iron deficiency, hexaferrite