Experimental Study - Inorganic Membranes for Air Separation

Authors: Adesola O. Orimoloye, Mohammed N. Kajama, Edward Gobina

Abstract:

Gas permeation of Oxygen [O2] and Nitrogen [N2] were investigated at room temperature using 15 and 6000nm pore diameter tubular commercial alumina ceramic membranes with pressure values ranging 1.00 to 2.50 bar. The flow rates of up to 2.59 and 2.77 l/min were achieved for O2 and N2 respectively. The ratio of O2/N2 flow rates were used to compute the O2/N2 selectivity. The experimental O2/N2 selectivity obtained for 15 nm was 1.05 while the 6000 nm indicated 0.95.

Keywords: gas separation, nitrogen, oxygen, selectivity