The Effect of SIO2 Addition on the Formation and Superconducting Properties of BI2SR2CACU2O8+D System

Authors: N. Boussouf, M. F. Mosbah, M.Hamel, S. Menassel

Abstract:

SiO2 particles were inserted (added) into Bi2Sr2CaCu2O8+d precursor powders in various weight fractions. The influence of Si addition to the Bi2212 system on its phase formation, microstructure and transport properties is investigated. Samples are characterized by means of X ray diffraction analysis (XRD), scanning electron microscopy (SEM/EDX), magnetic AC susceptibility and resistivity measurements. For 1% of added Si, the results showed an increase of the apparent superconducting volume fraction. All the samples doped with Si contained a majority fraction of the high TC superconducting Bi2212 phase. SEM observation showed that the average grain size of the Si added samples increased more than that of the sample without Si. From resistivity measurement the Tconset was found to be increased by 7 K for 1% and 5% of added Si compared to the pure sample.

Keywords: superconductors, Bi2212, doping, SiO2 particles