Sulfate Attack on Pastes Made with Different C3A and C4AF Contents and Stored at 5°C

Authors: Konstantinos Sotiriadis, Radosław Mróz

Abstract:

In the present work the internal sulfate attack on pastes made from pure clinker phases was studied. Two binders were produced: (a) a binder with 2% C3A and 18% C4AF content; (b) a binder with 10% C3A and C4AF content each. Gypsum was used as the sulfate bearing compound, while calcium carbonate added to differentiate the binders produced. The phases formed were identified by XRD analysis. The results showed that ettringite was the deterioration phase detected in the case of the low C3A content binder. Carbonation occurred in the specimen without calcium carbonate addition, while portlandite was observed in the one containing calcium carbonate. In the case of the high C3A content binder, traces of thaumasite were detected when calcium carbonate was not incorporated in the binder. A solid solution of thaumasite and ettringite was found when calcium carbonate was added. The amount of C3A had not fully reacted with sulfates, since its corresponding peaks were detected.

Keywords: tricalcium aluminate, calcium aluminate ferrite, sulfate attack, calcium carbonate, low temperature

Procedia PDF Downloads 297