Effect of Miniature Cracks on the Fracture Strength and Strain of Tensile Armour Wires

Authors: Kazeem K. Adewole, Steve J. Bull

Abstract:

Tensile armour wires provide a flexible pipe's resistance to longitudinal stresses. Flexible pipe manufacturers need to know the effect of defects such as scratches and cracks, with dimensions less than 0.2mm which is the limit of the current nondestructive detection technology, on the fracture stress and fracture strain of the wire for quality assurance purposes. Recent research involving the determination of the fracture strength of cracked wires employed laboratory testing and classical fracture mechanics approach using non-standardised fracture mechanics specimens because standard test specimens could not be manufactured from the wires owing to their sizes. In this work, the effect of miniature cracks on the fracture properties of tensile armour wires was investigated using laboratory and finite element tensile testing simulations with the phenomenological shear fracture model. The investigation revealed that the presence of cracks shallower than 0.2mm is worse on the fracture strain of the wire.

Keywords: Cracks, Finite Element Simulations, Fracture Mechanics, Shear Fracture Model, Tensile Armour Wire

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1071035

References:

[1] Mahmoud, k.m. (2007), fracture strength for a high strength steel bridge cable wire with a surface crack, theoretical and applied fracture mechanics, 48 (2), pages 152-160.
[2] Toribio, j., valiente a. (2006), failure analysis of cold drawn eutectoid steel wires for prestressed concrete, engineering failure analysis, 13 (3), pages 301-311.
[3] Toribio, j., valiente a. (2004), approximate evaluation of directional toughness in heavily drawn pearlitic steels. Materials letters, 58 (27-28), pages 3514-3517.
[4] Pardoen, t., scheyvaertsa, f., simara, a., tekoglu, c.,and onck p. (2010), multiscale modeling of ductile failure in metallic alloys. Comptes rendus physique, 11 (3-4), pages 326-345.
[5] Dunand, m., mohr d., (2010), hybrid experimental-numerical analysis of basic ductile fracture experiments for sheet metals. International journal of solids and structures, 47(9), pages 1130-1143.
[6] Simulia, 2007. Abaqus documentation, abaqus incorporation, dassault systemes.
[7] Adewole, k .k., julia m.r., and bull s.j., determination of the appropriate fracture mechanism for flexible pipe tensile armour wires using the micro-mechanism based fracture mechanics. Proceeding of aes- atema'2011 ninth international conference on advances and trends in engineering materials and their applications, montreal, canada, august 01 - 05, 2011, pages 147-154.
[8] Cabezas, e.e., and celentano, d.j., 2004. Experimental and numerical analysis of the tensile test using sheet specimens. Finite elements in analysis and design, vol 40, 2004, pages 555-575.
[9] Dieter, g.e., 1998. Mechanical metallurgy. Mcgraw-hill book company, isbn 0-07-084187-x, page 659.