Development of Mechanical Properties of Self Compacting Concrete Contain Rice Husk Ash

Authors: M. A. Ahmadi, O. Alidoust, I. Sadrinejad, M. Nayeri

Abstract:

Self-compacting concrete (SCC), a new kind of high performance concrete (HPC) have been first developed in Japan in 1986. The development of SCC has made casting of dense reinforcement and mass concrete convenient, has minimized noise. Fresh self-compacting concrete (SCC) flows into formwork and around obstructions under its own weight to fill it completely and self-compact (without any need for vibration), without any segregation and blocking. The elimination of the need for compaction leads to better quality concrete and substantial improvement of working conditions. SCC mixes generally have a much higher content of fine fillers, including cement, and produce excessively high compressive strength concrete, which restricts its field of application to special concrete only. To use SCC mixes in general concrete construction practice, requires low cost materials to make inexpensive concrete. Rice husk ash (RHA) has been used as a highly reactive pozzolanic material to improve the microstructure of the interfacial transition zone (ITZ) between the cement paste and the aggregate in self compacting concrete. Mechanical experiments of RHA blended Portland cement concretes revealed that in addition to the pozzolanic reactivity of RHA (chemical aspect), the particle grading (physical aspect) of cement and RHA mixtures also exerted significant influences on the blending efficiency. The scope of this research was to determine the usefulness of Rice husk ash (RHA) in the development of economical self compacting concrete (SCC). The cost of materials will be decreased by reducing the cement content by using waste material like rice husk ash instead of. This paper presents a study on the development of Mechanical properties up to 180 days of self compacting and ordinary concretes with rice-husk ash (RHA), from a rice paddy milling industry in Rasht (Iran). Two different replacement percentages of cement by RHA, 10%, and 20%, and two different water/cementicious material ratios (0.40 and 0.35), were used for both of self compacting and normal concrete specimens. The results are compared with those of the self compacting concrete without RHA, with compressive, flexural strength and modulus of elasticity. It is concluded that RHA provides a positive effect on the Mechanical properties at age after 60 days. Base of the result self compacting concrete specimens have higher value than normal concrete specimens in all test except modulus of elasticity. Also specimens with 20% replacement of cement by RHA have the best performance.

Keywords: Self compacting concrete (SCC), Rice husk ash(RHA), Mechanical properties.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1334602

References:

[1] Ozawa, K., Maekawa, K., and Okamura, H., (1992) "Development of High Performance Concrete" Journal of the Faculty of Engineering, The University of Tokyo (B) Vol. XLI, No.3, pp. 381-439.
[2] Okamura,Hajime,Self-compacting high-performance concrete, (1997) Concrete International, 19 (7), pp. 50-54.
[3] Ozawa, K, "Development of high performance concrete based on the durability design of concrete structures", EASEC-2, Vol. 1, pp.445-450 (1989).
[4] Peter Billberg, Form Pressure Generated by Self-Compacting Concrete ÔÇö Influence of Thixotropy and Structural Behaviour at Rest Doctoral Thesis, School of Architecture and the Built Environment Division of Concrete Structures Royal Institute of Technology SE-100 44 Stockholm, Sweden.
[5] A. A. Maghsoudi, Dahooei, Engineering properties of performance self compacting concrete, conference of Tarbiyat Moddaress.2006.
[6] Specifications and Guidelines for Self Compacting Concrete. (2002)European Federation of Products and Contractors of Specialist Products for Structures (EFNARC).
[7] Hayakawa M, et. al. Development & application of super workable concrete, RILEM International Workshop on Special Concretes: Workability and Mixing, Paisley, 1993.