Effects of Aggressive Ammonium Nitrate on Durability Properties of Concrete Using Sandstone and Granite Aggregates

Authors: L. Wong, H. Asrah, M.E. Rahman, M.A. Mannan

Abstract:

The storage of chemical fertilizers in concrete building often leads to durability problems due to chemical attack. The damage of concrete is mostly caused by certain ammonium salts. The main purpose of the research is to investigate the durability properties of concrete being exposed to ammonium nitrate solution. In this investigation, experiments are conducted on concrete type G50 and G60. The leaching process is achieved by the use of 20% concentration solution of ammonium nitrate. The durability properties investigated are water absorption, volume of permeable voids, and sorptivity. Compressive strength, pH value, and degradation depth are measured after a certain period of leaching. A decrease in compressive strength and an increase in porosity are found through the conducted experiments. Apart from that, the experimental data shows that pH value decreases with increased leaching time while the degradation depth of concrete increases with leaching time. By comparing concrete type G50 and G60, concrete type G60 is more resistant to ammonium nitrate attack.

Keywords: Normal weight concrete durability, Aggressive Ammonium Nitrate Solution, G50 & G60 concretes, Chemical attack.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1063130

References:

[1] British Standards Institution. 1997. Structural Use of Concrete, Code of Practice for Design and Construction. BS8110. BSI, London. Pp. 122.
[2] Schneider, U. & Chen, S.-W. 1999. Behavior of high-performance concrete (HPC) under ammonium nitrate solution and sustained load. America Concrete Institute, ACI Materials Journal 96(1): 47-51.
[3] Ukraincik, V., Bjegovic, D. & Djurekovic, A. 1978. Concrete corrosion in a nitrogen fertilizer plant. In Peter J. Sereda & G. G. Litvan. Durability of Building Materials and Components: Proceedings of the First International Conference. Ottawa, Canada. Pp. 397-409.
[4] Lea, F.M. 1965. The action of ammonium salts on concrete. Magazine of Concrete Research 17(52): 115-116.
[5] Maltais, Y., Samson, E. & Marchand, J. 2004. Predicting the durability of Portland Cement systems in aggressive environments: laboratory validation. Cement and Concrete Research 34(9): 1579-1589.
[6] Barr, B.I.G. 2003. Failure of concrete structures. Cardiff, UK: University of Wales.
[7] ASTM C150/C150M - 11 "Standard Specification for Portland Cement."
[8] Shan Somayaji. 2001. Civil Engineering Materials-Second Edition. New Jersey: Prentice Hall.
[9] BS 1881: Part 116•1983. 1983. Method for Determination of Compressive Strength of Concrete Cubes. London: British Standards Institution.
[10] Carde, C. & Francois, R. 1997 (a). Aging damage model of concrete behavior during the leaching process. Materials and structures constructions 30: 465-472.
[11] ASTM C642. 2002. Standard Test Method for Density, Absorption, and Voids in Hardened Concrete. Annual Book of ASTM Standards 2002, 04.02. Philadelphia: American Society for Testing and Materials.
[12] Agostini, F., Lafhaj, Z., Skoczylas, F. & Loodsveldt, H. 2007. Experimental study of accelerated leaching on hollow cylinders of mortar. Cement and Concrete Research 37: 71-78.
[13] Yang, H., Jiang L., Zhang Y., Pu, Q., Xu, Y. 2012. Predicting the calcium leaching behavior of cement pastes in aggressive environments. Construction and Building Materials 29: 88-96.
[14] Jain, J., & Neithalath, N. 2009. Analysis of calcium leaching behavior of plain and modified cement pastes in pure water. Cement & Concrete Composites 31: 176-185.
[15] Dias, W.P.S. 1995. Sorptivity Testing for Assessing Concrete Quality. Proc. Int. Conf on Concrete under Severe Exposure Conditions (CONSEC '95). Spon, London. Pp. 433-442.
[16] Chan, SYN. and Ji X. 1998. Water sorptivity and chloride diffusivity of oil shale ash concrete. Construct Build Mater 12(4): 177-183.
[17] Haga, K., Sutou, S., Hironaga, M., Tanaka, S. & Nagasaki, S. 2005. Effect of porosity on leaching of Ca from hardened ordinary portland cement paste. Cement and Concrete Research 35: 1764-1775.
[18] Geotechnical Engineering Bureau. 2007. Test Method for the determination of pH value of water or soil by pH meter. New York State Department of Transportation.
[19] Kamali, S., Gerard, B. & Moranville, M. 2003. Modelling the leaching kinetics of cement-based materials: Influence of materials and environment. Cement and Concrete Composites 25: 451-458.
[20] Nguyen, V. H., Colina, H., Torrenti, J.M., Boulay, C. & Nedjar, B. 2007. Chemo mechanical coupling behavior of leached concrete part I: Experimental results. Nuclear Engineering and Design 237: 2083-2089.