Influence of Initial Surface Roughness on Severe Wear Volume for SUS304 Austenitic Stainless Steels

Authors: A. Kawamura, K. Ishida, K. Okada, T. Sato

Abstract:

Simultaneous measurements of the curves for wear versus distance, wear rate versus distance, and coefficient of friction versus distance were performed in situ to distinguish the transition from severe running-in wear to mild wear. The effects of the initial surface roughness on the severe running-in wear volume were investigated. Disk-on-plate friction and wear tests were carried out with SUS304 austenitic stainless steel in contact with itself under repeated dry sliding conditions at room temperature. The wear volume was dependent on the initial surface roughness. The wear volume when the initial surfaces on the plate and disk had dissimilar roughness was lower than that when these surfaces had similar roughness. For the dissimilar roughness, the wear volume decreased with decreasing initial surface roughness and reached a minimum; it stayed nearly constant as the roughness was less than the mean size of the oxide particles.

Keywords: Austenitic stainless steel, initial surface roughness, running-in, severe wear.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1088800

References:

[1] Luis. C. Sreabra, A. M. Bapista, “Tribological behavior of food grade polymers against stainless steel in dry sliding and with sugar,” Wear, vol.253, 2002, pp. 394-402.
[2] J. R. Laguna-Camacho, A. Marquina-Chavez, J. V. Mendez-Mendez, M. Vite-Torres, E. A. Gallardo-hemandez, “Solid particle erosion of AISI304, 316 and 420 stainless steels,” Wear, Available online 16 January, 2013.
[3] Y. Sun, T. Bell, “Dry sliding wear resistance of low temperature plasma carburized austenitic stainless steel,” Wear, vol.253, 2002, pp. 689-693.
[4] Zhao Cheng, C. X. Li, H. Dong, T. Bell, “Low temperature plasma nitrocarburising of AISI 316 austenitic stainless steel, ” Surface and Coating Technology, vol.191, 2005, pp. 195-200.
[5] M. O. Speeidel, “Nitrogen containing austenitic stainless steels,” Mat-wissa. a. Werkstoiftech, vol.37, no.10, 2006, pp. 875-880.
[6] W. Hirst, J. K. Lancaster, “Surface film formation and metallic wear,” Journal of Applied Physics, vol.27, 1956, pp. 1057-1065.
[7] N. C. Welsh, “The dry wear of steels Ⅰ. The general pattern of behavior,” Philosophical Transactions of the Royal Society of London. Series A, vol.257, no.1077, 1965, pp. 31-50.
[8] F. P. Bowden, D. Tabor, The friction and lubrication of solids, Clarendon press, Oxford, London, 1954, pp. 306-314.
[9] S. M. Mahdavian, Y. W, Mai, B. Conttrell, “Friction metallic transfer and debris analysis of sliding surfaces,” Wear, vol.82, 1982, pp. 221-232.
[10] M. Braunovic, N. K. Myshkin, V. Konchits, Electrical contacts: fundamentals, applications and technology, CRC Press, Danvers, MA, 2007, pp. 166-180.
[11] H. Kato, “Severe-mild wear transition by supply of particles on sliding surface,” Wear, vol.255, 2003, pp. 426-429.
[12] I. M. Feng, B. G. Rightmire, “An experimental study of fretting,” Proceedings of the Institution of Mechanical Engineers, vol.70, 1956, pp. 1055-1064.
[13] E. Rabinowicz, Friction and wear, Jhon Willy and son, Inc, New York, 1965, pp. 125-166.
[14] K. Hokkirigawa, K. Kato, “An experimental and theoretical investigation of ploughing, cutting and wedge formation during abrasive wear,” Tribology International, vol.21, no.1, 1988, pp.51-57.