Strength and Permeability Characteristics of Steel Fibre Reinforced Concrete

Authors: A. P. Singh

Abstract:

The results reported in this paper are the part of an extensive laboratory investigation undertaken to study the effects of fibre parameters on the permeability and strength characteristics of steel fibre reinforced concrete (SFRC). The effect of varying fibre content and curing age on the water permeability, compressive and split tensile strengths of SFRC was investigated using straight steel fibres having an aspect ratio of 65. Samples containing three different weight fractions of 1.0%, 2.0% and 4.0% were cast and tested for permeability and strength after 7, 14, 28 and 60 days of curing. Plain concrete samples were also cast and tested for reference purposes.

Permeability was observed to decrease significantly with the addition of steel fibres and continued to decrease with increasing fibre content and increasing curing age. An exponential relationship was observed between permeability and compressive and split tensile strengths for SFRC as well as PCC. To evaluate the effect of fibre content on the permeability and strength characteristics, the Analysis of Variance (ANOVA) statistical method was used. An a level (probability of error) of 0.05 was used for ANOVA test. Regression analysis was carried out to develop relationship between permeability, compressive strength and curing age.

Keywords: Permeability, grade of concrete, fibre shape, fibre content, curing age, steady state, Darcy’s law, method of penetration.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1088446

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 3008

References:


[1] Mangat P.S and Gurusamy K. (1987), “Flexural Strength of Steel Fibre Reinforced Cement Composites”, Journal of Material Science, Vol.22, 3103-3110.
[2] Shah Surendra. P. “Do Fibres Increase the Tensile Strength of Cement- Based Matrixes?”, ACI Materials Journal, Vol.88, 595-602.
[3] Agarwal R, Singh A.K and Singhal D. ( 1996), “ Effect of Fibre Reinforcing Index on Compressive and Bond Strength of Steel Fibre reinforced Concrete”, Jl of Institution of Engineers (India), Civil Engineering Division, 77 , 37-40.
[4] Singh A.P. and Singhal D. (1998), “Effect of Fibre Shapes on Compressive and Bond Strengths of SFRC”, Jl of Institution of Engineers (India), Civil Engineering Division, 79, 136-139.
[5] Kumar V and Singhal D. (1996), “Flexural strength of Reinforced Concrete Beams Containing Steel Fibres”, Jl of Structural Engineering, India, V.23, 145-149.
[6] Mangat P.S and Gurusamy K. (1988), “Corrosion Resistance of Steel Fibres in Concrete under Marine Environment”, Cement and Concrete Research, 18, 44-54.
[7] Singhal. D, Agrawal. R. and Nautiyal B.D.( 1999), “ Effect of Chloride Environment on Steel Fibre Reinforced Concrete” , Jl of Institution of Engineers (I), Civil Engineering Division, V.80, 110-116.
[8] Singhal. D, Agrawal. R. and Nautiyal B.D. (2002), “Sulphate Resistance of Steel Fibre Reinforced Concrete”, Jl of Ferro-cement, V.32, No.2, 127-137.
[9] Bamforth P.B (1991), “The Water Permeability of Concrete and its Relationship with Strength”, Magazine of Concrete Research, 43,233- 241.
[10] Min- Hoong Zhang (1991), “Permeability of High Strength Lightweight Concrete”, ACI Materials Journal, 88, 463-469.
[11] Prasit Soongwang et al (1991), “Factors Affecting Strength and Permeability of Concrete with Porous Limestone”, ACI Materials Journal, 88, 400-406.
[12] Lydon I.D. (1994), “Effects of Coarse Aggregate on Relative Permeability of Concrete”, Construction and Building Materials, 18, 165-189.
[13] Khatri R.P, Sirivivantnanon V. (1997), “Methods for the Determination of Water Permeability of Concrete”, ACI Materials Jl., 94, 257-261.
[14] Singh A.P., Agarwal Ramji and Singhal D. (2002), “Permeability and Strength Characteristics of Steel Fibre Reinforced Concrete”, Journal of Ferrocement, Vol. 32, 127-138.
[15] Ozgur E., Khaled M, “ Effects of limestone crusher dust and steel fibres on concrete,” Construction and Building Materials, 2009, 23, 981-987
[16] Banthia N., Bhargava A., “Permeability of stressed concrete and role of fiber reinforcement,” ACI Materials Jl, 2007, 104, 70-76
[17] Gansen N, Sekar R., “Permeability of steel fibre reinforced high performance concrete composites,” Jl of Institution of Engineers (India), Civil Engineering Division, 2005, 83, 145-149.
[18] Sun W. Chen, Luo X, Quin H., “The effect of hybrid fibers and expansive agent on the shrinkage and permeability of high-performance concrete”, Cement and Concrete Research, 2001, 31, 595-601.
[19] IS:8112-1989, “Specifications for High Strength Ordinary Portland Cement” , Bureau of Indian Standards, New – Delhi, 1990, pp. 1-7.
[20] IS: 383-1970, “Specifications for Coarse and Fine Aggregates from Natural Sources for Concrete”, Bureau of Indian Standards, New Delhi, 1971, pp. 5-11.
[21] SP: 23-1982, “Handbook of Concrete Mixes”, Bureau of Indian Standard, New-Delhi, 1983, pp 103-122.
[22] IS: 3065-1965, Method for Determination of Permeability of Concrete. Bureau of Indian Standards, New Delhi, 1966, pp. 4 -10.
[23] ASTM C 642-1990, “Standard Test Method for Specific Gravity, Absorption and Voids in Hardened Concrete”, American Society of Testing of Materials, 315-316.
[24] Kennedy John B., Neville Adam M., “Basic statistical methods for engineers and scientists”, IEP A Dun-Donnelley Publisher, 1976, New York, pp. 147-149.
[25] Mangat P.S. and Azari M.M. 1984, A Theory for the Free Shrinkage of Steel Fibre Reinforced Cement matrices. Jl of Materials Science, 19, pp. 2183-2194.