Stress versus Strain Behavior of Geopolymer Cement under Triaxial Stress Conditions in Saline and Normal Water

Authors: Haider M. Giasuddin, Jay G. Sanjayan, P. G. Ranjith

Abstract:

Geopolymer cement was evaluated as wellbore sealing material for carbon dioxide geosequestration application. Curing of cement system in saline water and strength testing in triaxial stress state condition under lateral confinement is relevant to primary cementing in CO2 geosequestration wellbore in saline aquifer. Geopolymer cement was cured in saline water (both at ambient conditions for 28 days and heated (60°C) conditions for 12 hours) and tested for triaxial strength at different levels of lateral confinement. Normal water and few other curing techniques were also studied both for geopolymer and API ‘G’ cement. Results reported were compared to evaluate the suitability of saline water for curing of geopolymer cement. Unconfined compression test results showed higher strength for curing in saline water than normal water. Besides, testing strength under lateral confinement demonstrated the material failure behavior from brittle to plastic.

Keywords: Fly ash, Geopolymer, Geosequestration, Saline water, Strength, Traiaxial test.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1086963

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2357

References:


[1] J. W. Carey, M. Wigand, S. J. Chipera, G. W. Gabriel, R. Pawar, P. C. Lichtner, S. C. Wehner, M. A. Raines, and Jr George D. Guthrie, “Analysis and performance of oil well cement with 30 years of CO2 exposure from the Sacroc Unit, West Texas, USA,” International Journal of Greenhouse Gas Control, vol. 1, pp. 75-85, 2007.
[2] V. Barlet-Gouédard, G. Rimmelé, O. Porcherie, N. Quisel, and J. Desroches, “A solution against well cement degradation under CO2 geological storage environment,”International Journal of Greenhouse Gas Control,vol. 3, pp. 206-16,2009.
[3] C. Baumgarte, M. Thiercelin, and D. Klaus, “Case studies of expanding cement to prevent microannular formation,”SPE Annual Technical Conference and Exhibition,pp. 275 -82, Houston, Texas, 1999.
[4] C. Shi, A. Fernández Jiménez, and A. Palomo, “New cements for the 21st century: the pursuit of an alternative to portland cement,” Cement and Concrete Research, vol. 41, pp. 750-763, 2011.
[5] R Thakur and S Ghosh, “Fly Ash Based Geopolymer Composites: Manufacturing and Engineering Properties,” LAMBERT Academic Publishing, 2011.
[6] T. Bakharev, “Resistance of geopolymer materials to acid attack,” Cement and Concrete Research, vol. 35, pp. 658-70, 2005.
[7] D. L. Y. Kong, and J. G. Sanjayan, “Effect of elevated temperatures on geopolymer paste, mortar and concrete,”Cement and Concrete Research, vol. 40, pp. 334-39, 2010.
[8] G. Kovalchuk, A. Fernández-Jiménez, and A. Palomo, “Alkali-activated fly ash: effect of thermal curing conditions on mechanical and microstructural development - part ii,” Fuel, vol. 86, pp.315-22, 2007.
[9] H. Hassanzadeh, M. Pooladi-Darvish, and D.W. Keith, “Accelerating CO2 dissolution in saline aquifers for geological storage - mechanistics and sensitivity studies,” Energy Fuels, pp. 3328 -36, 2009.
[10] K. Michael, A. Golab, V. Shulakova, J. Ennis-King, G. Allinson, S. Sharma, and T. Aiken, “Geological storage of CO2 in saline aquifers - a review of the experience from existing storage operations,” International Journal of Greenhouse Gas Control, vol. 4,pp. 659- 67,2010.
[11] K. Michael, G. Allinson, A. Golab, S. Sharma, and V. Shulakova, “CO2 storage in saline aquifers ii - experience from existing storage operations,” Energy Procedia, vol. 1, pp. 1973-80, 2009.
[12] K. Ravi, “A comparative study of mechanical properties of densityreduced cement compositions,” SPE Drilling & Completion, vol. 22, pp. 119-26, 2007.
[13] X. S. Zhou, X. Lin, M. J. Huo, and Y. Zhang, “The hydration of saline oil-well cement,” Cement and Concrete Research, vol. 26, pp. 1753-59, 1996.
[14] F. Pacheco-Torgal, J. Castro-Gomes, and S. Jalali, “Alkali-activated binders: a review. part 2. about materials and binders manufacture,” Construction and Building Materials, vol. 22, pp. 1315-22, 2008.
[15] J. Temuujin, A. van Riessen, and R. Williams, “Influence of calcium compounds on the mechanical properties of fly ash geopolymer pastes,” Journal of Hazardous Materials, vol. 167, pp. 82-88, 2009.
[16] T.C. Hansen, “Triaxial tests with concrete and cement paste,” Technical University of Denmark, 1995.
[17] J. P. Zhang, “Shear strength of cracked concrete, Part 2,” Technical University of Denmark, 1994.