Separation of Manganese and Cadmium from Cobalt Electrolyte Solution by Solvent Extraction

Authors: Shafiq Alam, Mirza Hossain, Hesam Hassan Nejad

Abstract:

Impurity metals such as manganese and cadmium from high-tenor cobalt electrolyte solution were selectively removed by solvent extraction method using Co-D2EHPA after converting the functional group of D2EHPA with Co2+ ions. The process parameters such as pH, organic concentration, O/A ratio, kinetics etc. were investigated and the experiments were conducted by batch tests in the laboratory bench scale. Results showed that a significant amount of manganese and cadmium can be extracted using Co-D2EHPA for the optimum processing of cobalt electrolyte solution at equilibrium pH about 3.5. The McCabe-Thiele diagram, constructed from the extraction studies showed that 100% impurities can be extracted through four stages for manganese and three stages for cadmium using O/A ratio of 0.65 and 1.0, respectively. From the stripping study, it was found that 100% manganese and cadmium can be stripped from the loaded organic using 0.4 M H2SO4 in a single contact. The loading capacity of Co-D2EHPA by manganese and cadmium were also investigated with different O/A ratio as well as with number of stages of contact of aqueous and organic phases. Valuable information was obtained for the designing of an impurities removal process for the production of pure cobalt with less trouble in the electrowinning circuit.

Keywords: Manganese, Cadmium, Cobalt, D2EHPA, Solvent extraction.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1083883

References:

[1] C. Y. Cheng, C. A. Hughes, K. R. Barnard, and K. Larcombe, "Manganese in Copper Solvent Extraction and Electrowinning," Hydrometallurgy, vol. 58, pp. 135-150, 2000.
[2] W. Zhang, and C. Y. Cheng, "Manganese Metallurgy Review. Part II: Manganese Separation and Recovery from Solution," Hydrometallurgy, vol. 89(3-4), pp. 160-177, 2007.
[3] K. G. Mishra, P. Singh, and D. M. Muir, "Electrowinning of Cobalt from Sulphate Solutions Contaminated with Organic Impurities, "Hydrometallurgy, vol. 65(2-3), pp. 97-102, 2002.
[4] N. B. Devi, K. C. Nathsarma, and V. Chakravortty, "Separation of Divalent Manganese and Cobalt Ions from Sulfate Solutions using Sodium Salts of D2EHPA, PC 88A and Cyanex 272," Hydrometallurgy, vol. 54, pp. 117-131, 2000.
[5] L. F. Cook and W. W. Szmokaluk. "Refinery of Cobalt and Nickel Sulphate Solution by Solvent Extraction using D2EHPA," in Proc. Int. Solv. Ext. Conf. ISEC ÔÇÿ71, Soc. Chem. Ind., London, 1971, pp. 451-462.
[6] P. M. Cole, "The Introduction of Solvent Extraction Steps During Upgrading of a Cobalt Refinery," Hydrometallurgy, vol. 64, pp. 69-77, 2002.
[7] D. Senapati, G. R. Chaudhury, and P. V. R. B. Sarma, "Purification of Nickel Sulphate Solutions Containing Iron, Copper, Cobalt, Zinc and Manganese," Journal of Chemical Technology and Biotechnology, vol. 59(4), pp. 335-339, 1994.
[8] I. Ortiz, and M. F. San Román, "Analysis of the Back-extraction of Cadmium-nickel-D2EHPA Organic Phases," Separation Science and Technology, vol. 37(3), pp. 607-625, 2002.
[9] B. R. Reddy, D. N. Priya, and J. R. Kumar, "Solvent Extraction of Cadmium (II) from Sulphate Solution using TOPS 99, PC 88A, Cyanex 272 and their Mixtures," Hydrometallurgy, vol. 74(3-4), pp. 277-283,2004.
[10] V. Kumar, M. Kumar, M. K. Jha, J. Jeong, and J.-C Lee, "Solvent Extraction of Cadmium from Sulfate Solution with Di-(2-ethylhexyl) Phosphoric Acid Diluted in Kerosene," Hydrometallurgy, vol. 96(3), pp. 230-234, 2009.
[11] A. M. Sastre, and M. Muhammed, "The Extraction of Zinc (II) from Sulphate and Perchlorate Solutions by Di(2-ethylhexyl)phosphoric Acid Dissolved in Isopar-H," Hydrometallurgy, vol. 12, pp. 177-193, 1984.