Utilization of Nanoclay to Reinforce Flax Fabric-Geopolymer Composites

Authors: H. Assaedi, F. U. A. Shaikh, I. M. Low

Abstract:

Geopolymer composites reinforced with flax fabrics and nanoclay are fabricated and studied for physical and mechanical properties using X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), and Scanning Electron Microscope (SEM). Nanoclay platelets at a weight of 1.0%, 2.0%, and 3.0% were added to geopolymer pastes. Nanoclay at 2.0 wt.% was found to improve density and decrease porosity while improving flexural strength and post-peak toughness. A microstructural analysis indicated that nanoclay behaves as filler and as an activator supporting geopolymeric reaction while producing a higher content geopolymer gel improving the microstructure of binders. The process enhances adhesion between the geopolymer matrix and flax fibres.

Keywords: Flax fibres, geopolymer, mechanical properties, nanoclay.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1110473

References:

[1] V. F. Barbosa, K. J. D. MacKenzie, C. Thaumaturgo, "Synthesis and characterisation of materials based on inorganic polymers of alumina and silica: sodium polysialate polymers," Int. J. Inorg. Mater., vol. 2, pp. 309-17, 2000.
[2] F. J. Silva, C. Thaumaturgo, "Fibre reinforcement and fracture response in geopolymeric mortars," Fatigue. Fract. Eng. Mater. Struct., vol. 26, no. 2 SPEC., pp. 167-72, 2003.
[3] Q. Zhao, B. Nair, T. Rahimian, P. Balaguru, "Novel geopolymer based composites with enhanced ductility," J. Mater. Sci., vol. 42, pp. 3131-7, 2007.
[4] A. Hakamy, F. U. A. Shaikh, I.M. Low, "Thermal and mechanical properties of hemp fabric-reinforced nanoclay–cement nanocomposites" J. Mater. Sci., vol. 49, pp. 1684-94, 2013.
[5] C. A. U. Shanshan, H. Wang, X. Wang, "Chemical and Mechanical Properties Studies of Chinese Linen Flax and its Composites," Poly. Poly. Compos. vol. 21, pp. 275-85, 2013.
[6] H. Assaedi, F. U. A, Shaikh, I. M. Low, "Characterisation of mechanical and thermal properties in flax fabric reinforced geopolymer composites," J. Adv. Cer., submitted for publication.
[7] T. Phoo-ngernkham, P. Chindaprasirt, V. Sata, S. Hanjitsuwan, S. Hatanaka, "The effect of adding nano-SiO2 and nano-Al2O3 on properties of HVFA geopolymer cured at ambient temperature," Mater. Des., vol. 55, pp. 58-65, 2014.
[8] A. Nazari, J. G. Sanjayan, "Hybrid effects of alumina and silica nanoparticles on water absorption of geopolymers: Application of Taguchi approach," Measurement, vol. 60, pp. 240-6, 2015.
[9] M. Saafi, Andrew K., Tang P. L., McGhon D., Taylor S., Rahman M., et al., "Multifunctional properties of carbon nanotube/fly ash geopolymeric nanocomposites, "Constr. Build. Mater., vol. 49, pp. 46-55, 2013.
[10] F. U. A. Shaikh, S. W. M. Supit, "Mechanical and durability properties of high volume fly ash (HVFA) concrete containing calcium carbonate (CaCO3) nanoparticles," Constr. Build. Mater., vol. 70, pp. 309-21, 2014.
[11] ASTM C20, "Standard test methods for apparent porosity, water absorption, apparent specific gravity, and bulk density of burned refractory brick and shapes by boiling water", 2010.
[12] ASTM D790, “Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials," 2010.
[13] A. Fernandez-Jimenez, Palomo A., "Composition and microstructure of alkali activated fly ash binder: Effect of the activator," Cem Concr Res, vol. 35, no. 10, pp. 1984-92, 2005.
[14] T. Alomayri, I.M. Low, "Synthesis and characterization of mechanical properties in cotton fiber-reinforced geopolymer composites," J. Asian Ceram. Soc., vol. 1, no. 1, pp. 30-4, 2013.
[15] N.C. Tanw, A.v. Riessen, "Determining the Reactivity of a Fly Ash for Production of Geopolymer," J. Amer. Ceram. Soc., vol. 92, pp. 881-7, 2009.
[16] T. Bakharev, "Thermal behaviour of geopolymers prepared using class F fly ash and elevated temperature curing," Cem Concr Res, vol. 36, no. 6, pp. 1134-47, 2006.
[17] W. D. A. Rickard, R. Williams, J. Temuujin, A.v. Riessen, "Assessing the suitability of three Australian fly ashes as an aluminosilicate source for geopolymers in high temperature applications," Mater Sci Eng., vol. 528, no. 9, pp. 3390-7, 2011.
[18] J. W. Phair, J.S.J. Deventer, "Effect of the silicate activator pH on the microstructural characteristics of waste-based geopolymers," Int. J Miner. Process., vol. 66, no. 1-4, pp. 121-43, 2002.
[19] E. ul-Haq, S. K. Padmanabhan, A. Licciulli, "Synthesis and characteristics of fly ash and bottom ash based geopolymers–A comparative study," Ceram. Int., vol. 40, no. 2, pp. 2965-71, 2014.
[20] T. Alomayri, H. Assaedi, F. U. A. Shaikh, I. M. Low, "Effect of water absorption on the mechanical properties of cotton fabric-reinforced geopolymer composites," J Asian Ceram. Soc., vol. 2, pp. 223-30, 2014.
[21] F. Shaikh, S. Supit, P. Sarker, "A study on the effect of nano silica on compressive strength of HVFA mortars and concretes," Mater. Des., vol. 60, pp. 433-42, 2014.
[22] M. Alzeer, K. MacKenzie, "Synthesis and mechanical properties of novel composites of inorganic polymers (geopolymers) with unidirectional natural flax fibres," App. Clay Sci., vol. 76, pp. 148-52, 2013.
[23] J. Sim, C. Park, D.Y. Moon, "Characteristics of basalt fiber as a strengthening material for concrete structures," Compos. B, vol. 36, no. 6-7, pp. 504-12, 2005.