Influence of Thermal Damage on the Mechanical Strength of Trimmed CFRP

Authors: Guillaume Mullier, Jean François Chatelain

Abstract:

Carbon Fiber Reinforced Plastics (CFRPs) are widely used for advanced applications, in particular in aerospace, automotive and wind energy industries. Once cured to near net shape, CFRP parts need several finishing operations such as trimming, milling or drilling in order to accommodate fastening hardware and meeting the final dimensions. The present research aims to study the effect of the cutting temperature in trimming on the mechanical strength of high performance CFRP laminates used for aeronautics applications. The cutting temperature is of great importance when dealing with trimming of CFRP. Temperatures higher than the glass-transition temperature (Tg) of the resin matrix are highly undesirable: they cause degradation of the matrix in the trimmed edges area, which can severely affect the mechanical performance of the entire component. In this study, a 9.50mm diameter CVD diamond coated carbide tool with six flutes was used to trim 24-plies CFRP laminates. A 300m/min cutting speed and 1140mm/min feed rate were used in the experiments. The tool was heated prior to trimming using a blowtorch, for temperatures ranging from 20°C to 300°C. The temperature at the cutting edge was measured using embedded KType thermocouples. Samples trimmed for different cutting temperatures, below and above Tg, were mechanically tested using three-points bending short-beam loading configurations. New cutting tools as well as worn cutting tools were utilized for the experiments. The experiments with the new tools could not prove any correlation between the length of cut, the cutting temperature and the mechanical performance. Thus mechanical strength was constant, regardless of the cutting temperature. However, for worn tools, producing a cutting temperature rising up to 450°C, thermal damage of the resin was observed. The mechanical tests showed a reduced mean resistance in short beam configuration, while the resistance in three point bending decreases with increase of the cutting temperature.

Keywords: Composites, Trimming, Thermal Damage, Surface Quality.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1109525

References:

[1] Sadat, A. B., "Delamination and other types of damage of graphite/epoxy composite caused by machining." Machining of advanced materials, Vol. 41-52, 1995.
[2] Wang, D. H., Ramulu M., Arola D., "Orthogonal cutting mechanisms of graphite/epoxy composite. Part I: unidirectional laminate." International Journal of Machine Tools and Manufacture, Vol. 35, No. 12, pp. 1623- 1638, 1995.
[3] Ramulu, M., "Preliminary investigation of machining effects on the surface integrity of fiber reinforced plastics." ASME, Petroleum Division, 1994.
[4] Sheikh-Ahmad J., N. U., Hossein Cheraghi, "Machining Damage in Edge Trimming of CFRP." Materials and Manufacturing Processes, Vol. 27, No. 7, pp. 802-808, 2012.
[5] Bhatnagar, N., Nayak D., Singh I., Chouhan H., Mahajan P., "Determination of Machining-Induced Damage Characteristics of Fiber Reinforced Plastic Composite Laminates." Materials and Manufacturing Processes, Vol. 19, No. 6, pp. 1009-1023, 2004.
[6] Ghidossi, P., El Mansori M., Pierron F., "Influence of specimen preparation by machining on the failure of polymer matrix off-axis tensile coupons." Composites Science and Technology, Vol. 66 No. 11– 12, pp. 1857-1872, 2006.
[7] Valavan, U., “Tool life prediction based on cutting forces and surface temperature in edge trimming of multidirectional CFRP composites”, Thesis, Wichita State University, 2007.
[8] Y. Turki, M. H., R. Velasco, P. Vantomme, Z. Aboura, "Étude expérimentale du détourage d’un composite carbone/époxy." 7ème colloque national de la recherche dans les IUT, 2011.
[9] Bérubé, S., "Usinage en détourage de laminés composites carbone/époxy." Master thesis, École de Technologie Supérieure , Québec, Canada, 2012.
[10] Arola, D. and M. Ramulu, "Net shape manufacturing and the performance of polymer composites under dynamic loads." Experimental Mechanics, Vol. 37, No. 4, pp. 379-385, 1997.
[11] Nor Khairusshima, M. K., Che Hassan C.H., Jaharan A.G., Amin A.K.M., Md Idriss A.N., "Effect of chilled air on tool wear and workpiece quality during milling of carbon fibre-reinforced plastic." Wear, Vol. 302, No. 1–2, pp. 1113-1123, 2013.
[12] Shigehiko Sakamoto, H. I., "Effect of Cutting Revolution Speed on Cutting Temperature in Helical Milling of CFRP Composite Laminates." Key Engineering Materials, pp.523-524, 2012.
[13] Madjid Haddad, R. Z., Florent Eyma, Bruno Castanié, "Machinability and surface quality during high speed trimming of multi directional CFRP." Int. J. of Machining and Machinability of Materials, Vol, 13, No.2/3, pp. 289-310, 2013.
[14] Takashi I., M. H., Masao Matsui, Liwei Gu (2009). "Cutting Characteristics of CFRP Materials with End Milling." Key Engineering Materials, Vol. 407-408, pp. 710-713, 2009.
[15] Takashi I., M. H., "Cutting characteristics of CFRP materials with carbon fiber distribution." International Journal of Automation Technology, Vol. 7, No. 3, pp. 285-291, 2013
[16] Han Shengchao, C. Y., Xu Jiuhua, Zhou Jingwen, "Experimental Study of Tool Wear in Milling Multidirectional CFRP Laminates." Materials Science Forum, Vol. 770, pp. 276-280, 2013.
[17] Yashiro, T., Ogawa T., Sasahara H., "Temperature measurement of cutting tool and machined surface layer in milling of CFRP." International Journal of Machine Tools and Manufacture, Vol. 70, No. 0, pp. 63-69, 2013.
[18] Chatterjee, A., "Thermal degradation analysis of thermoset resins." Journal of Applied Polymer Science, Vol. 114, No.3, pp. 1417-1425, 2009.
[19] Frame, B. J. J., Simpson, W. A., Ziegler, R. E., Philpot, H. E., "Composite Heat Damage." Oak Ridge National Laboratory: Oak Ridge Parts 1 and 2, 1990.
[20] Haskins, J. F., "Thermal ageing." SAMPE Journal, Vol. 25, No. 2, pp. 29-33, 1989.
[21] Luoma, G. A. and R. D. Rowland, "Environmental degradation of an epoxy resin matrix." Journal of Applied Polymer Science, Vol. 32, No.7, pp. 5777-5790, 1986.
[22] Herzog, D., Jaeschke P., Meier O., Haferkamp H., "Investigations on the thermal effect caused by laser cutting with respect to static strength of CFRP." International Journal of Machine Tools and Manufacture, Vol. 48, No.12–13, pp.1464-1473, 2008.
[23] Yoshihisa Harada, K. K., Takayuki Suzuki, Tokuo Teramoto, "Evaluation of Cutting Process on the Tensile and Fatigue Strength of CFRP Composites." Materials Science Forum, Vol. 706-709, pp. 649- 654, 2012.
[24] Hamedanianpour H., Chatelain J.-F, “Effect of Tool Wear on Quality of Carbon Fiber Reinforced Polymer Laminate during Edge Trimming”, Applied Mechanics and Materials, Vol. 325-326, pp.34-39, 2013.