The Effects of Wood Ash on Ignition Point of Wood

Authors: Kenneth A. Ibe, Justina I. Mbonu, Godgift K. Umukoro

Abstract:

The effects of wood ash from five common tropical woods on the ignition point of four common tropical woods in Nigeria were investigated. The ash and moisture contents of the wood sawdust from Mahogany (Khaya ivorensis), Opepe (Sarcocephalus latifolius), Abura (Mitragyna ciliata), Rubber (Heavea brasilensis) and Poroporo (Sorghum bicolour) used, were determined using a furnace (Vecstar furnaces, model ECF2, serial no. f3077) and oven (Genlab laboratory oven, model MINO/040) respectively. The metal contents of the five wood sawdust ash samples were determined using a Perkin Elmer optima 3000 dv atomic absorption spectrometer while the ignition points were determined using Vecstar furnaces model ECF2. Poroporo had the highest ash content, 2.263g while rubber had the least, 0.710g. The results for the moisture content range from 2.971g to 0.903g. Magnesium metal had the highest concentration of all the metals, in all the wood ash samples; with mahogany ash having the highest concentration, 9.196ppm while rubber ash had the least concentration of magnesium metal, 2.196 ppm. The ignition point results showed that the wood ashes from mahogany and opepe increased the ignition points of the test wood samples, Danta (Nesogordonia papaverifera), Ekpaya, Akomu (Pycnanthus angolensis) and Oleku when coated on them while the ashes from poroporo, rubber and abura decreased the ignition points of the test wood samples when coated on them. However, Opepe saw dust ash decreased the ignition point in one of the test wood samples, suggesting that the metal content of the test wood sample was more than that of the Opepe saw dust ash. Therefore, Mahogany and Opepe saw dust ashes could be used in the surface treatment of wood to enhance their fire resistance or retardancy. However, the caution to be exercised in this application is that the metal content of the test wood samples should be evaluated as well.

Keywords: Ash, fire, ignition point, retardant, wood saw dust.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1109421

References:

[1] K. A. Ibe, E. E Elemike and S. A. Chukwuma, “Fire extinguishing strength of the combustion product of wood saw dust ash.” J. Appli. Sci. Environ. Management, vol.18 no.3, pp. 553- 557, 2014
[2] National fire protection association.” Fire loss in the U.S. during 2005”, abridged report (http://www.usfa.dhs.gov/statistics/national/), pp. 11- 12f, 2008
[3] G. E. Zaikov and S. M. Lomankin.”Ecological issue of polymer flame retardancy”. Journal of Applied Polymer Science, vol. 86, pp. 2249- 2462, 2002
[4] I. Van Der Veen and J. De Boer (2012). “Phosphorus Flame Retardants: Properties, Production, Environmental Occurrence, Toxicity and Analysis”. Chemosphere, vol. 88, no.10, 1119-1153
[5] M. K. Misra, K. W. Ragland and A.J. Baker. “Wood Ash Composition as Function of Furnace Temperature”. Biomass and Bioenergy, vol. 4, no.2, pp.103, 1993
[6] L. Etiegni and A. G. Campbell. “Physical and Chemical Characteristics of Wood Ash”. Bioresource Technology, vol.37, no.2, pp. 173, 1991.
[7] A. G. Campbell. “ Recycling and Disposing Of Wood Ash,” Tappi Journal, Tappi Press, Norcross, GA, vol.73, no.9, pp. 141-143, 1990
[8] National Council for Air and Stream Improvement, Inc. (NCASI), Alternative Management of Pulp and Paper Industry Solid Wastes, Technical Bulletin No. 655, NCASI, New York, NY, pp. 44, 1993.
[9] C. Jean-Pierre-Barrette and J. M. Hazard. “Memotech Bois and Materiaux Associates”, Casteilla Edition, Paris, pp. 11, 1996.
[10] E. Mikkola. “Charring Of Wood”. Espoo Technical research Center of Finland, pp.35, 1990
[11] E. Mikkola and I. S. Wichman. “The Thermal Ignition of Combustible Materials”. Fire and Materials, vol.14, no. 3, pp. 87-96, 1989
[12] E. Hume. “Wood Ashes: How to Use Them in the Garden”. Ed Hume Seeds. ISO 5660-1 (2002). Reaction- To- Fire Tests- Heat Release, Smoke Production and Mass Loss Rate- Part 1: Heat Release Rate (Cone Calorimeter Method). Geneva: Internal Organization for Standardization, 2002, pp.39, 2006.
[13] B. Kristoffersen, A. Steen Hansen, T. Hakkarainen , B. Ostman, P. Johansson, M. Pauner, O. Grexa and P. J. Hovde (2003). “Using the cone calorimeter for screening and control testing of fire retarded wood products”. Reportnord test project 1526-01. Trondheim: Norwegian fire research laboratory, pp.18 & 63, 2003.s