The Mechanical and Electrochemical Properties of DC-Electrodeposited Ni-Mn Alloy Coating with Low Internal Stress

Authors: Chun-Ying Lee, Kuan-Hui Cheng, Mei-Wen Wu

Abstract:

The nickel-manganese (Ni-Mn) alloy coating prepared from DC electrodeposition process in sulphamate bath was studied. The effects of process parameters, such as current density and electrolyte composition, on the cathodic current efficiency, microstructure, internal stress and mechanical properties were investigated. Because of its crucial effect on the application to the electroforming of microelectronic components, the development of low internal stress coating with high leveling power was emphasized. It was found that both the coating’s manganese content and the cathodic current efficiency increased with the raise in current density. In addition, the internal stress of the deposited coating showed compressive nature at low current densities while changed to tensile one at higher current densities. Moreover, the metallographic observation, X-ray diffraction measurement, and polarization curve measurement were conducted. It was found that the Ni-Mn coating consisted of nano-sized columnar grains and the maximum hardness of the coating was associated with (111) preferred orientation in the microstructure. The grain size was refined along with the increase in the manganese content of the coating, which accordingly, raised its hardness and resistance to annealing softening. In summary, the Ni-Mn coating prepared at lower current density of 1-2 A/dm2 had low internal stress, high leveling power, and better corrosion resistance.

Keywords: DC plating, internal stress, leveling power, Ni-Mn coating.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1108472

References:

[1] L. T. Romankiw, “A Path: From Electroplating Through Lithographic Masks in Electronics to LIGA in MENS,” Electrochimica Acta, vol. 41, no. 20-22, 1997, pp. 2985-3005.
[2] K. H. Cheng, F. J. Chen, C. Y. Lee, C. S. Lin, J. T. Huang, C. C. Lan, P. H. Tsou, T. I. Ho, ”Fabrication of Ni-Mn Microprobe Structure with Low Internal Stress and High Hardness by Employing DC Electrodeposition,” Advances in Materials Science and Engineering, vol. 2014, 2014, Article ID 890814, 6 pages.
[3] G. A. Malone, “New Developments in Electroformed Nickel-Based Structural Alloys,” Plating and Surface Finishing, 1987, vol. 74, pp. 50-56.
[4] R. J. Tzou, H. S. Chou, “The Electroforming of Nickel-Based Alloys,” Journal of Chinese Corrosion Engineering, vol.6, no.3,1992, pp.32 -38
[5] N. Y. C. Yang, T. J. Headley, “Metallurgy of High Strength Ni-Mn Microsystems Fabricated by Electrodeposition,” Scripta Materialia, vol.51, 2004, pp.761 -766.
[6] A. V. Ryazhkin, Yu. A. Babanov, T. Miyanaga, T. Ogasawara, K. Nitta, S. Ohwada, V. P. Pilyugin, A. M. Patchelov, E. G. Chernyishov, ”Lattice Parameters for Ni-Mn Disordered Alloys by EXAFS,” Materials Science, vol.12C, vol.22, 2005, pp.131.
[7] S. H. Goods, J. J. Kelly, N. Y. C. Yang, “Electrodeposited Nickel- Manganese: An Alloy for Microsystem Applications,” Microsystem Technologies, vol.10, 2004, pp. 498-505.
[8] E. A. Marquis, A. A. Talin, “Effect of Current Density on the Structure of Ni and Ni-Mn Electrodeposits,” Journal of Materials Engineering, vol.36, 2006, pp.669-676.
[9] N. Atanassov, V. Mitreva, “Electrodeposition and Properties of Nickel-Manganese Layers,” Surface & Coating Technology, vol.78, 1996, pp. 144-149.
[10] W. B. Stephenson, Fermer Jr., “Development and Utilization of a High Strength Alloy for Electroform,” Plating, vol. 52, no. 2, 1966, pp.183- 192.
[11] W. B. Stephenson, Cincinnati, Jr., R. F. Edward, “Electrodepostion of a Nickel-Manganese Alloy,” US Patent No. 3244603, 1968.
[12] A. Stephen, “Corrosion Behaviour of Electrodeposited Ni-Mn Alloys- Electrochemical Impedance Measurements,” Anti-Corrosion Methods and Materials, Vol.46, no.2, 1999, pp.117 – 121.
[13] W. R. Wearmouth, K. C. Belt, “Electroforming with Heat-resistant, Sulfur-hardened Nickel,” Plating, vol. 66, no. 10, 1979, pp.53-57.
[14] W. R. Wearmouth, “Hard, Heat-resistant Nickel Electrodeposits,” US Patent No. 4108740, 1977.
[15] G. A. Malone, “Study of High Performance Alloy Electroforming,” NASA-CR- 173828, US NTIS, 1984.
[16] G. A. Malone, “Study of High Performance Alloy Electroforming,” NASA-CR- 175494, US NTIS, 1985.
[17] J. W. Dini, H. R. Johnson, “High-Temperature Ductility of Electrodeposited Nickel,” SAND77-8020, US Sandia Laboratories.
[18] J. W. Dini, H. R. Johnson, L. A. West, “On the High-Temperature Ductility Properties of Electrodeposited Sulfamate Nickel,” Plating, vol. 65, no. 2, 1978, pp.36-40.
[19] J. J. Kelly, S. H. Goods, “High Performance Nanostructured Ni-Mn Alloy for Microsystem Applications,” Electrochemical and Solid – State Letters, vol.6, no.6, 2003, pp.C81 – C91.
[20] G. Lucadamo, D. L. Medlin, “Characterization of Twinning in Electrodeposited Ni-Mn Alloys,” Philosophical Magazine, vol.85, vol.22, 2005, pp.2549 – 2560.
[21] F. J. Chen, “Study on Hexavalent Chromium Process Alternatives”, Ph.D. Dissertation, Department of Mechanical Engineering, National Taiwan University, Taipei, Taiwan, Nov. 2009.
[22] Y. Tsuru, M. Nomura, “Effects of Chloride, Bromide and Iodide Ions on Internal Stress in Films Deposited during High Speed Nickel Electroplating from a Nickel Sulfamate Bath,” Journal of Applied Electrochemistry, vol.30, 2000, pp.231 – 238.
[23] A. Stephen, “Magnetic Properties of Electrodeposited Nickel-Manganese Alloys: Effect of Ni/Mn Bath Ratio,” Journal of Applied Electrochemistry, vol. 30, 2000, pp.1313 – 1316.
[24] M. Pushpavanam, V. Raman, “Leveling in Bright Nickel-Iron,” Metal Finishing, vol. 84, no. 5, 1986, pp.51-55.
[25] S. J. Hearne, J. A. Floro, M. A. Rodriguez, R. T. Tissot, C. S. Frazer, L. Brewer, P. Hlava, and S. Foiles, “Stress Creation during Ni-Mn Alloy Electrodeposition,” Journal of Applied Physics, vol.99, 2006, pp.053517_1 – 053517_4.
[26] M. A. Meyers and K. K. Chawla, Mechanical Behavior of Materials, Prentice Hall, New Jersey, US, 1999.
[27] C. W. Chu, “Effects of Manganese Doped Ba1.002(Ti0.82Zr0.18)O3+δ on Insulation Resistance and Dielectric Properties,” Master Thesis, Department of Materials Science and Engineering, National Cheng-Kung University, Tainan, Taiwan, June 2005.