Effect of Sodium Hydroxide Treatment on the Mechanical Properties of Crushed and Uncrushed Luffa cylindrica Fibre Reinforced rLDPE Composites

Authors: Paschal A. Ubi, Salawu Abdul Rahman Asipita

Abstract:

Sustainability and eco-friendly requirement of engineering materials are sort for in recent times, thus giving rise to the development of bio-composites. However, the natural fibres to matrix interface interactions remain a key issue in getting the desired mechanical properties from such composites. Treatment of natural fibres is essential in improving matrix to filler adhesion, hence improving its mechanical properties. In this study, investigations were carried out to determine the effect of sodium hydroxide treatment on the tensile, flexural, impact and hardness properties of crushed and uncrushed Luffa cylindrica fibre reinforced recycled low density polyethylene composites. The LC (Luffa cylindrica) fibres were treated with 0%, 2%, 4%, 6%, 8% and 10% wt. sodium hydroxide (NaOH) concentrations for a period of 24 hours under room temperature conditions. A formulation ratio of 80/20 g (matrix to reinforcement) was maintained for all developed samples. Analysis of the results showed that the uncrushed luffa fibre samples gave better mechanical properties compared with the crushed luffa fibre samples. The uncrushed luffa fibre composites had a maximum tensile and flexural strength of 7.65 MPa and 17.08 Mpa respectively corresponding to a young modulus and flexural modulus of 21.08 MPa and 232.22 MPa for the 8% and 4% wt. NaOH concentration respectively. Results obtained in the research showed that NaOH treatment with the 8% NaOH concentration improved the mechanical properties of the LC fibre reinforced composites when compared with other NaOH treatment concentration values.

Keywords: Flexural strength, LC fibres, LC/rLDPE composite, Tensile strength.

Digital Object Identifier (DOI): doi.org/10.5281/zenodo.1099686

References:

[1] A.N. Netravali and S. Chabba, “Composites get greener”, Materials Today, vol. 6, Issue 4, April 2003, pp.22-29.
[2] H.D. Rozman, C.Y. Lai, H. Ismail and Z.A. Mohd Ishak, “The effect of coupling agents on the mechanical and physical properties of oil palm empty fruit bunch polypropylene composites”, Polymer International, 49, 2000, pp.1273-1278.
[3] F.P. La Mantia and M. Morreale, “Green Composites: A brief review”, Composites: Part A, 42, 2011, pp.579-588.
[4] M.P.M. Dicker, F.D. Peter, B.B. Anna, F. Guillaume, and K.H. Mark, “Green composites: A review of material attributes and complementary”, Composites: Part A, 56, 2014, pp. 280-289.
[5] Y.H. Mohd, N.R. Mohd, M.A. Azriszul, M.A.Z. Ahmad and A. Saparudin, “Mercerisation treatment parameter effect on natural fibre reinforced polymer matrix composite: A brief review”, World Academy of Science, Engineering and Technology, vol. 6, 2012, pp. 1378-1384.
[6] J. Holbery and D. Houston, “Natural fibre reinforced polymer composites in automotive applications”, Journal of the Minerals, Metals and Materials Society, vol. 58, 2006, pp. 80-86.
[7] M.M. Davoodi, S.M. Sapuan, D. Ahmad, D. Aidy, A. Khalina and J. Mehdi, “Mechanical properties of hybrid kenaf/glass reinforced epoxy composite for passenger car bumper beam” Materials and Design, vol. 31, 2010, pp 4927-4932.
[8] S.N. Chaudhary, S.P. Borkar, S.S. Mantha, “Sunnhemp fibre-reinforced waste polyethylene bag composites”, Journal of reinforced plastics and composites, vol. 29, 2010, pp. 2241-2252.
[9] M.Meheddene, B. Hisham, A.C. Hadi and E. Adel, “Alkali Treatment of fan palm natural fibres for use in fibre reinforced concrete”, European Scientific Journal, vol. 10, No. 12, 2014, pp. 186-194.
[10] A. Elsaid, M. Dawood, R. Seracino and C. Bobko, “Mechanical properties of kenaf fibre reinforced concrete”, Construction and Building Materials, vol. 25, 2011, pp. 1991-2001.
[11] N.J. Rodriguez, M. Yanez-Limon, F.A. Gutierrez-Miceli, O. Gomez- Guzman, T.P. Matadamas-Ortiz, L. Lagunez-Rivera and J.A. Vazquez Feijoo, “Assessment of coconut fibre insulation characteristics and its use to modulate temperatures in concrete slabs with the aid of a finite element methodology”, Energy and Building Materials, vol. 43, 2011, pp. 1264-1272.
[12] X.Y. Zhou, F. Zheng, H.G. Li and C.L. Lu, “An environment friendly thermal insulation material from cotton stalk fibres”, Energy and Buildings, vol. 42, 2010, pp.1070-1074.
[13] C. Girisha, Sanjeevamurthy and R. Gunti, “Tensile properties of natural fibre reinforced epoxy-hybrid composites”, International Journal of Modern Engineering Research, vol. 2, Issue 2, 2012, pp. 471-474.
[14] L. Ghali, M. Slah, Z. Mondher and S. Faouzi, “Effects of fibre weight ratio, structure and fibre modification onto the flexural properties of luffa-polyester composites”, Advances in Materials Physics and Chemistry,1, 2011, pp.78-85.
[15] M. Rokbi, H.Osmani, A. Imad, and N. Benseddiq, “Effect of chemical treatment on flexure properties of natural fibre reinforced polyester composites”, Procedia Engineering, doi:10.1016/j.proeng.2011.04.346.
[16] A. Gomes, M. Takanori, G. Koichi and O. Junji , “Development and effect of alkali treatment on tensile properties of curaua fibre green composites”. Composites: Part A, 38, 2007, pp.1811-1820.
[17] A. Gomes, K. Goda and J. Ohgi, “Effects of alkali treatment to reinforcement on tensile properties of curaua fibre green composites”, JSME Int Journal, 47, 2004, pp.541-546.
[18] D. Ray, B.K. Sarkar, A.K. Rana and N.R. Bose, Bulletin of Material Science, 24, 2001, pp. 129.
[19] A.K. Bledzki and J. Gassan, “Composites reinforced with cellulose based fibres”, Progress in Polymer Science, vol. 63, 1999, pp. 147 – 157.
[20] M.S. Sreekala, M.G. Kumaran, S. Joseph, M. Jacob and S.Thomas, Applied Composite Materials, 7, 2000, pp. 295.
[21] C. Parida, S.K. Dash, and S.C. Das, “Effect of fibre treatment on mechanical and thermal properties of luffa cylindrical-resorcinol composites”, International Journal of Fibre and Textile Research. 3, (1), 2013, pp.13 –17.
[22] L. Xue, G.T. Lope, and P. Satyanarayan, “Chemical treatments of natural fibre for use in natural fibre-reinforced composites: A Review”, Journal of Polymer and Environment, 15, 2007, pp.25-33.
[23] A. Karthikeyan and K. Balamurugan, “The effect of sodium hydroxide treatment and fibre length on the tensile property of coir fibre reinforced epoxy composites”, Journal of Engineering and Applied Sciences, 8(5), 2013, pp. 156-161.
[24] T. Okonu and Y. Nishiyama, “Morphological changes of ramie fibre during mercerization”, Journal of Wood Science. 44: pp. 310–313, 1998.
[25] J. George, J. Ivens, and I. Verpoest, “Surface modification to improve the impact performance of natural fibre composites” In proceedings of ICCM 12, France, 1999.
[26] S. Mishra, A.K. Mohanty, L.T. Drzal, M. Misra, and S. Parija, “Studies on mechanical performance of biofibre/glass reinforced polyester hybrid composites” Composites Science and Technology, 63, 2003, pp. 1377 – 1385.
[27] A.M.M. Edeerozey, H.M. Akil, A.B. Azhar and M.I.Z. Ariffin, “Chemical modification of kenaf fibres", Material Letters. Vol. 61, 2007, pp. 2023 – 2025.
[28] M.A. Paglicawan, M.S. Cabillon, R.P. Cebito and E.O. Santos, “Loofah fibres reinforcement material for composite”, Phillipine Journal of Science, 134(2), 2005, pp. 113 – 120.
[29] S.H. Aziz and M.P. Ansell, “The effect of alkalisation and fibre alignment on the mechanical and thermal properties of kenaf and hemp bast fibre composites: Part 1-Polyester resin matrix”, Composites Science and Technology, 2004, pp. 1219 – 1230.
[30] A.I. Al-Mosawi, “Study of some mechanical properties for polymeric composite material reinforced by fibres”, Al-Qadisiya Journal for Engineering Science, 2(1), 2009, pp. 14 – 24.
[31] A.I. Al-Mosawi, M.H. Al-Maamori and Z.A. Wetwet, “Mechanical properties of composite materials reinforcing by natural-synthetic fibres”, Academic Research International, vol. 3, No.3, 2012, pp.108 – 112.
[32] V. O. A. Tanobe, T.H.S. Flores-Sahagun, S.C. Amico, G..I.B Muniz and K.G. Satyanarayana, “Sponge gourd (luffa cylindrica) reinforced polyester composites: preparation and properties”, Defence Science Journal, vol. 64, No. 3, 2014, pp. 273-280.
[33] R. Wirawan, S.M. Sapuan, R. Yunus and K. Abdan, “Properties of Sugar cane bagasse/poly(vinylchloride) composites after various treatment”, Journal of Composite Materials, vol. 45, 2011, pp. 1667-1674.
[34] S.S. Munawar, K. Umemura, F. Tanaka and S. Kawai, “Effects of Alkali, mild steam and chitosan treatments on the properties of pineapple, ramie and sansevieria fibre bundles”, Journal of Wood Science, vol. 54, 2008, pp. 28-35.