Authors: Chaojie Song, Lianhui Ding, Craig Fairbridge, Hansan Liu, Rob Hui, Jiujun Zhang

Abstract:

Two novel hydrodesulfurization (HDS) catalysts: FeN4/C and FeN2/C, were prepared using an impregnation-pyrolysis method. The two materials were investigated as catalysts for hydrodesulfurization (HDS) and hydrodearomitization (HDA) of model compounds. The turnover frequency of the two FeN catalysts is comparable to (FeN4/C) or even higher (FeN2/C) than that of MoNi/Al2O3. The FeN4/C catalyst also exhibited catalytic activity toward HDA.

Keywords: catalyst, FeN2/C, FeN4/C, HDS, HDA

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2646

Authors: Aptullah Karakaş, Murat Baydoğan

Abstract:

In the HDA process, Al or Al-Si molten baths are mostly used. However, in this study, three different Al alloys such as Al4043 (Al-Mg), Al5356 (Al-Si) and Al7020 (Al-Zn) were used as the molten bath in order to see their effects on morphological and mechanical properties of the resulting aluminide layers. AISI 4140 low alloyed steel was used as the substrate. Parameters of the HDA process were bath composition, bath temperature, and dipping time. These parameters were considered within a Taguchi L9 orthogonal array. After the HDA process and subsequent diffusion annealing, coating thickness measurement, microstructural analysis and hardness measurement of the aluminide layers were conducted. The optimum process parameters were evaluated according to coating morphology such as cracks, Kirkendall porosity and hardness of the coatings. According to the results, smooth and clean aluminide layer with less Kirkendall porosity and cracks were observed on the sample, which was aluminized in the molten Al7020 bath at 700 C for 10 minutes, and subsequently diffusion annealed at 750 C. Hardness of the aluminide layer was in between 1100-1300 hardness of Vickers (HV) and the coating thickness was approximately 400 µm. The results were promising such that a hard and thick aluminide layer with less Kirkendall porosity and cracks could be formed. It is therefore, concluded that Al7020 bath may be used in the HDA process of AISI 4140 steel substrate.

Keywords: Aluminum alloys, coating, hot-dip aluminizing, microstructure.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 175