Authors: C. H. S. Vidyasagar, D. B. Karunakar

Abstract:

In this present work, five different composite samples with AA2024 as matrix and varying amounts of yttrium (0.1-0.5 wt.%) as reinforcement are developed through cold compaction. The microstructures of the developed composite samples revealed that the yttrium reinforcement caused grain refinement up to 0.3 wt.% and beyond which the refinement is not effective. The microstructure revealed Al2Cu precipitation which strengthened the composite up to 0.3 wt.% yttrium reinforcement. Upon further increase in yttrium reinforcement, the intermetallics and the precipitation coarsen and their corresponding strengthening effect decreases. The mechanical characterization revealed that the composite sample reinforced with 0.3 wt.% yttrium showed highest mechanical properties like 82 HV of hardness, 276 MPa Ultimate Tensile Strength (UTS), 229 MPa Yield Strength (YS) and an elongation (EL) of 18.9% respectively. However, the relative density of the developed composites decreased with the increase in yttrium reinforcement.

Keywords: Mechanical properties, AA 2024 matrix, yttrium reinforcement, cold compaction, precipitation.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 580

Authors: Vidyasagar Shilapuram, Nesrin Ozalp, Anam Waheed

Abstract:

Carboneous catalytical methane decomposition is an attractive process because it produces two valuable products: hydrogen and carbon. Furthermore, this reaction does not emit any green house or hazardous gases. In the present study, experiments were conducted in a thermo gravimetric analyzer using Fluka 05120 as carboneous catalyst to analyze its effectiveness in methane decomposition. Various temperatures and methane partial pressures were chosen and carbon mass gain was observed as a function of time. Results are presented in terms of carbon formation rate, hydrogen production and catalytical activity. It is observed that there is linearity in carbon deposition amount by time at lower reaction temperature (780 °C). On the other hand, it is observed that carbon and hydrogen formation rates are increased with increasing temperature. Finally, we observed that the carbon formation rate is highest at 950 °C within the range of temperatures studied.

Keywords: Catalysis, Fluka 05120, Hydrogen production, Methane decomposition

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1828

Authors: Vidyasagar H. N., S. Gopal Prakash, Shivrudraiah, K. V. Sharma

Abstract:

Thermally insulating ceramic coatings also known as thermal barrier coatings (TBCs) have been essential technologies to improve the performance and efficiency of advanced gas turbines in service at extremely high temperatures. The damage mechanisms of air-plasma sprayed YSZ thermal barrier coatings (TBC) with various microstructures were studied by microscopic techniques after thermal cycling. The typical degradation of plasma TBCs that occurs during cyclic furnace testing of an YSZ and alumina coating on a Titanium alloy are analyzed. During the present investigation the effects of topcoat thickness, bond coat oxidation, thermal cycle lengths and test temperature are investigated using thermal cycling. These results were correlated with stresses measured by a spectroscopic technique in order to understand specific damage mechanism. The failure mechanism of former bond coats was found to involve fracture initiation at the thermally grown oxide (TGO) interface and at the TGO bond coat interface. The failure mechanism of the YZ was found to involve combination of fracture along the interface between TGO and bond coat.

Keywords: Thermal barrier coatings, thermal loading.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1907