Search results for: niobium

Authors: Htet Htike Htwe, Kay Thi Lwin

Abstract:

The principal objective of this study is to be able to extract niobium oxide from columbite-tantalite concentrate of Thayet Kon Area in Nay Phi Taw. It is recovered from columbite-tantalite concentrate which contains 19.29 % Nb2O5.The recovery of niobium oxide from columbite-tantalite concentrate can be divided into three main sections, namely, digestion of the concentrate, recovery from the leached solution and precipitation and calcinations. The concentrate was digested with hydrofluoric acid and sulfuric acid. Of the various parameters that effect acidity and time were studied. In the recovery section solvent extraction process using methyl isobutyl ketone was investigated. Ammonium hydroxide was used as a precipitating agent and the precipitate was later calcined. The percentage of niobium oxide is 74%.

Keywords: Calcination, Digestion, Precipitation, SolventExtraction.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 3462

Authors: S. Zhuiykov, E. Kats

Abstract:

In recent times there has been a growing interest in the development of quasi-two-dimensional niobium pentoxide (Nb2O5) as a semiconductor for the potential electronic applications such as capacitors, filtration, dye-sensitised solar cells and gas sensing platforms. Therefore once the purpose is established, Nb2O5 can be prepared in a number of nano- and sub-micron-structural morphologies that include rods, wires, belts and tubes. In this study films of Nb2O5 were prepared on gold plated silicon substrate using spin-coating technique and subsequently by mechanical exfoliation. The reason this method was employed was to achieve layers of less than 15nm in thickness. The sintering temperature of the specimen was 800oC. The morphology and structural characteristics of the films were analyzed by Atomic Force Microscopy (AFM), Raman Spectroscopy, X-ray Photoelectron Spectroscopy (XPS).

Keywords: Mechanical exfoliation, niobium pentoxide, quazitwo- dimensional, semiconductor, sol-gel, spin-coating, two dimensional semiconductors.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2348

Authors: Ming-Hsun Tsai, Ming-Chyuan Lin, Fu-Tsai Chung, Ling-Jhen Chen, Yu-Hang Lin, Meng-Shu Yeh, Lee-Long Han

Abstract:

Since 2005, an SRF module of CESR type serves as the accelerating cavity at the Taiwan Light Source in the National Synchrotron Radiation Research Center. A 500-MHz niobium cavity is immersed in liquid helium inside this SRF module. To reduce heat load, the liquid helium vessel is thermally shielded by liquid-nitrogen-cooled copper layer, and the beam chambers are also anchored with pipes of the liquid nitrogen flow in middle of the liquid helium vessel and the vacuum vessel. A strong correlation of the movement of the cavity-s frequency tuner with the temperature variation of parts cooled with liquid nitrogen was observed. A previous study on a spare SRF module with the niobium cavity cooled by liquid nitrogen instead of liquid helium, satisfactory suppression of the thermal oscillation was achieved by attaching a temporary buffer tank for the vented shielding nitrogen flow from the SRF module. In this study, a home-made buffer tank is designed and integrated to the spare SRF module with cavity cooled by liquid helium. Design, construction, integration, and preliminary test results of this buffer tank are presented.

Keywords: Cryogenics, flow control, oscillation.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1890

Authors: Maria V. Morozova, Yulia V. Emelyanova, Anastasia A. Levina, Elena S. Buyanova, Zoya A. Mikhaylovskaya, Sofia A. Petrova

Abstract:

The solid solutions of lanthanum niobates substituted by yttrium, bismuth and tungsten were synthesized. The structure of the solid solutions is either LaNbO₄-based monoclinic or BiNbO₄-based triclinic. The series where niobium is substituted by tungsten on B site reveals phase-modulated structure. The values of cell parameters decrease with increasing the dopant concentration for all samples except the tungsten series although the latter show higher total conductivity.

Keywords: Impedance spectroscopy, LaNbO4, lanthanum ortho-niobates.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1515

Authors: Jung-Ho Moon, Tae Kwon Ha

Abstract:

In the present study, the effect of Si, Al, Ti, Zr, and Nb addition on the microstructure and hot workability of cast M42 tool steels, basically consisting of 1.0C, 0.2Mn, 3.8Cr, 1.5W, 8.5Co, 9.2Mo, and 1.0V in weight percent has been investigated. Tool steels containing Si of 0.25 and 0.5wt.%, Al of 0.06 and 0.12wt.%, Ti of 0.3wt.%, Zr of 0.3wt.%, and Nb of 0.3wt.% were cast into ingots of 140mm ´ 140mm ´ 330mm by vacuum induction melting. After solution treatment at 1150^oC for 1.5hr followed by furnace cooling, hot rolling at 1180^oC was conducted on the ingots. Addition of titanium, zirconium and niobium was found to retard the decomposition of the eutectic carbides and result in the deterioration of hot workability of the tool steels, while addition of aluminum and silicon showed relatively well decomposed carbide structure and resulted in sound hot rolled plates.

Keywords: High speed steels, alloying elements, eutectic carbides, microstructure, hot workability.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2581

Authors: G. Rosaz, V. Semblanet, S. Calatroni, A. Sublet, M. Taborelli

Abstract:

We report in this paper the design and qualification of a cylindrical unbalanced magnetron source. The dedicated magnetic assemblies were simulated using a finite element model. A hall-effect magnetic probe was then used to characterize those assemblies and compared to the theoretical magnetic profiles. These show a good agreement between the expected and actual values. The qualification of the different magnetic assemblies was then performed by measuring the ion flux density reaching the surface of the sample to be coated using a commercial retarding field energy analyzer. The strongest unbalanced configuration shows an increase from 0.016 A.cm^-2 to 0.074 A.cm^-2 of the ion flux density reaching the sample surface compared to the standard balanced configuration for a pressure 5.10^-3 mbar and a plasma source power of 300 W.

Keywords: Ion energy distribution, niobium, retarding field energy analyzer, sputtering, SRF cavity, unbalanced magnetron.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1153

Authors: M. I. Equbal, R.K. Ohdar, B. Singh, P. Talukdar

Abstract:

Micro-alloyed steel components are used in automotive industry for the necessity to make the manufacturing process cycles shorter when compared to conventional steel by eliminating heat treatment cycles, so an important saving of costs and energy can be reached by reducing the number of operations. Microalloying elements like vanadium, niobium or titanium have been added to medium carbon steels to achieve grain refinement with or without precipitation strengthening along with uniform microstructure throughout the matrix. Present study reports the applicability of medium carbon vanadium micro-alloyed steel in hot forging. Forgeability has been determined with respect to different cooling rates, after forging in a hydraulic press at 50% diameter reduction in temperature range of 900-11000C. Final microstructures, hardness, tensile strength, and impact strength have been evaluated. The friction coefficients of different lubricating conditions, viz., graphite in hydraulic oil, graphite in furnace oil, DF 150 (Graphite, Water-Based) die lubricant and dry or without any lubrication were obtained from the ring compression test for the above micro-alloyed steel. Results of ring compression tests indicate that graphite in hydraulic oil lubricant is preferred for free forging and dry lubricant is preferred for die forging operation. Exceptionally good forgeability and high resistance to fracture, especially for faster cooling rate has been observed for fine equiaxed ferrite-pearlite grains, some amount of bainite and fine precipitates of vanadium carbides and carbonitrides. The results indicated that the cooling rate has a remarkable effect on the microstructure and mechanical properties at room temperature.

Keywords: Cooling rate, Hot forging, Micro-alloyed, Ring compression.

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 3617