2 Effect of Sewing Speed on the Physical Properties of Firefighter Sewing Threads

Authors: Adnan Mazari, Engin Akcagun, Antonin Havelka, Funda Buyuk Mazari, Pavel Kejzlar

Abstract:

This article experimentally investigates various physical properties of special fire retardant sewing threads under different sewing speeds. The aramid threads are common for sewing the fire-fighter clothing due to high strength and high melting temperature. 3 types of aramid threads with different linear densities are used for sewing at different speed of 2000 to 4000 r/min. The needle temperature is measured at different speeds of sewing and tensile properties of threads are measured before and after the sewing process respectively. The results shows that the friction and abrasion during the sewing process causes a significant loss to the tensile properties of the threads and needle temperature rises to nearly 300oC at 4000 r/min of machine speed. The Scanning electron microscope images are taken before and after the sewing process and shows no melting spots but significant damage to the yarn. It is also found that machine speed of 2000r/min is ideal for sewing firefighter clothing for higher tensile properties and production.

Keywords: Kevlar, nomex, sewing, needle temperature

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1024
1 Innovative Techniques for Characterization of Nonwoven Insulation Materials Embedded with Aerogel

Authors: Mohanapriya Venkataraman, Rajesh Mishra, Jakub Weiner, Adnan Mazari, Jiri Militky, Veera Kumar Arumugam

Abstract:

The major objective of this study is to understand the potential of a newly fabricated equipment to study the thermal properties of nonwoven textile fabrics treated with aerogel at subzero temperatures. Thermal conductivity was calculated by using the empirical relation Fourier’s law, The relationship between the thermal conductivity and thermal resistance of the samples were studied at various environmental temperatures (which was set in the clima temperature system between +25oC to -25oC). The newly fabricated equipment was found to be a suitable for measuring at subzero temperatures. This field of measurements is being developed and will be the subject of further research which will be more suitable for measurement of the various thermal characteristics.

Keywords: Nonwoven, Aerogel, Thermal Measurements, Hot plate Heading

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 2893

Abstracts

2 Effect of Superabsorbent for the Improvement of Car Seat's Thermal Comfort

Authors: Adnan Mazari, Jakub Wiener, Antonin Havelka, Funda Buyuk Mazari, Jawad Naeem

Abstract:

The use of super absorbent polymers (SAP) for moisture absorption and comfort is still unexplored. In this research the efficiency of different SAP fibrous webs are determined under different moisture percentage to examine the sorption and desorption efficiency. The SAP fibrous web with low thickness and high moisture absorption are tested with multilayer sandwich structure of car seat cover to determine the moisture absorption through cover material. Sweating guarded hot plate (SGHP) from company Atlas is used to determine the moisture permeability of different car seat cover with superabsorbent layer closed with impermeable polyurethane foam. It is observed that the SAP fibrous layers are very effective in absorbing and desorbing water vapor under extreme high and low moisture percentages respectively. In extreme humid condition (95 %RH) the 20g of SAP layer absorbs nearly 3g of water vapor per hour and reaches the maximum absorption capacity in 6 hours.

Keywords: comfort, superabsorbent, car seat, SAF

Procedia PDF Downloads 288
1 Effect of Sewing Speed on the Physical Properties of Firefighter Sewing Threads

Authors: Adnan Mazari, Engin Akcagun, Antonin Havelka, Funda Buyuk Mazari, Pavel Kejzlar

Abstract:

This article experimentally investigates various physical properties of special fire retardant sewing threads under different sewing speeds. The aramid threads are common for sewing the fire-fighter clothing due to high strength and high melting temperature. 3 types of aramid threads with different linear densities are used for sewing at different speed of 2000 to 4000 r/min. The needle temperature is measured at different speeds of sewing and tensile properties of threads are measured before and after the sewing process respectively. The results shows that the friction and abrasion during the sewing process causes a significant loss to the tensile properties of the threads and needle temperature rises to nearly 300oC at 4000 r/min of machine speed. The Scanning electron microscope images are taken before and after the sewing process and shows no melting spots but significant damage to the yarn. It is also found that machine speed of 2000r/min is ideal for sewing firefighter clothing for higher tensile properties and production.

Keywords: Kevlar, needle temperautre, nomex, sewing

Procedia PDF Downloads 365