Marcelo B. Mansur

Publications

1 Selective Solvent Extraction of Calcium and Magnesium from Concentrate Nickel Solutions Using Mixtures of Cyanex 272 and D2EHPA

Authors: Alexandre S. Guimarães, Marcelo B. Mansur

Abstract:

The performance of organophosphorus extractants Cyanex 272 and D2EHPA on the purification of concentrate nickel sulfate solutions was evaluated. Batch scale tests were carried out at pH range of 2 to 7 using a laboratory solution simulating concentrate nickel liquors as those typically obtained when sulfate intermediates from nickel laterite are re-leached and treated for the selective removal of cobalt, zinc, manganese and copper with Cyanex 272 ([Ca] = 0.57 g/L, [Mg] = 3.2 g/L, and [Ni] = 88 g/L). The increase on the concentration of D2EHPA favored the calcium extraction. The extraction of magnesium is dependent on the pH and of ratio of extractants D2EHPA and Cyanex 272 in the organic phase. The composition of the investigated organic phase did not affect nickel extraction. The number of stages is dependent on the magnesium extraction. The most favorable operating condition to selectively remove calcium and magnesium was determined.

Keywords: Nickel, solvent extraction, organophosphorus extractants, alkaline earth metals

Procedia APA BibTeX Chicago EndNote Harvard JSON MLA RIS XML ISO 690 PDF Downloads 1897

Abstracts

2 Magnetic Solvent Extraction Using Nanoparticles Coated by Oleic Acid

Authors: Marcelo B. Mansur, Natália C. C. Lobato, Ângela M. Ferreira

Abstract:

In solvent extraction operations, large sedimentation areas in the mixer-settler are required when the disengagement of the aqueous and the organic phases is slow and/or difficult. The use of a magnetic organic liquid (also known as ferrofluid), consisting of magnetite nanoparticles coated by oleic acid dispersed in the organic diluent, has proven successful to speed up phase disengagement. The method, however, has never been used industrially; therefore, the aim of this study is to raise its main limitations. Tests were carried out using a ferrofluid containing 30 g/l of magnetite dissolved in commercial aliphatic kerosene Exxsol D80. The efficiency of cobalt extraction ([Co] = 1 g/l) with 10% v/v Cyanex 272 (bis-2,4,4-trimethylpentyl phosphinic acid) at changing pH of the aqueous phase (2 to 7) was found unaffected in the conditions studied. However, the chemical resistance of the ferrofluid in contact with deionized water at changing acidity (from 10-7 to 2 mol/l) revealed that the nanoparticles are not resistant when contacted to aqueous solutions with a pH ≤ 2. Such result represents a serious limitation to the applicability of the method mainly to hydrometallurgical systems because solvent extraction operations are normally done in acid conditions, therefore more effective strategies to coat the particles are required.

Keywords: magnetite nanoparticles, oleic acid, magnetic solvent extraction, cyanex 272

Procedia PDF Downloads 249
1 Selective Solvent Extraction of Calcium and Magnesium from Concentrate Nickel Solutions Using Mixtures of Cyanex 272 and D2EHPA

Authors: Alexandre S. Guimarães, Marcelo B. Mansur

Abstract:

The performance of organophosphorus extractants Cyanex 272 and D2EHPA on the purification of concentrate nickel sulfate solutions was evaluated. Batch scale tests were carried out at pH range of 2 to 7 using a laboratory solution simulating concentrate nickel liquors as those typically obtained when sulfate intermediates from nickel laterite are re-leached and treated for the selective removal of cobalt, zinc, manganese and copper with Cyanex 272 ([Ca] = 0.57 g/L, [Mg] = 3.2 g/L, and [Ni] = 88 g/L). The increase on the concentration of D2EHPA favored the calcium extraction. The extraction of magnesium is dependent on the pH and of ratio of extractants D2EHPA and Cyanex 272 in the organic phase. The composition of the investigated organic phase did not affect nickel extraction. The number of stages is dependent on the magnesium extraction. The most favorable operating condition to selectively remove calcium and magnesium was determined.

Keywords: Nickel, solvent extraction, organophosphorus extractants, alkaline earth metals

Procedia PDF Downloads 354